CN102070889A - PET resin composition with laser mark function and preparation method thereof - Google Patents
PET resin composition with laser mark function and preparation method thereof Download PDFInfo
- Publication number
- CN102070889A CN102070889A CN2011100468910A CN201110046891A CN102070889A CN 102070889 A CN102070889 A CN 102070889A CN 2011100468910 A CN2011100468910 A CN 2011100468910A CN 201110046891 A CN201110046891 A CN 201110046891A CN 102070889 A CN102070889 A CN 102070889A
- Authority
- CN
- China
- Prior art keywords
- pet resin
- laser
- resin combination
- district temperature
- laser labelling
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a polyethylene terephthalate (PET) resin composition with a laser mark function and a preparation method thereof. An additive which can enhance the laser mark effect is used for greatly improving the laser mark effect of the PET resin composition. The preparation method of the PET resin composition comprises the following steps of: uniformly mixing components such as PET resin, a toughening agent, a reinforcing material, a laser marking additive and the like; feeding into a double-screw extruder; and after extruding, cooling, drying and dicing to obtain the finished product. By using the PET resin composition, white characters can be formed on the surfaces of black products, or bright laser marks such as black characters and the like are formed on the surfaces of white products, and the PET resin composition has the good laser mark function and keeps the high-performance characteristics of the PET resin composition.
Description
Technical field
The present invention relates to a kind of PET resin combination and preparation method thereof, belong to technical field of polymer processing with laser labelling function.
Background technology
The laser marks mixture begins to use in products such as low-voltage apparatus shell, relay1 case, computer fan blade, electricity-saving lamp plastic casing gradually at present.The mode of laser marks has substituted marking methods such as impression, heat embossing, ink-jet gradually.Several marking methods than the back, laser marks have aspect advantages such as mark density is big, permanent, antifalsification, the feature of environmental protection.But laser marks is a new mark mode after all, its exist the initial stage have high input, aspect problem such as staff training, therefore still be a process more slowly for promoting, and the modified plastics kind that is specifically applied to laser marks now is limited, and mark sharpness and color are rich etc. also has certain gap than ink-jet.
Japan's publication (2001-302922) disclose comprise ABS resin, maleimide base co-polymer, vinyl cyanide base co-polymer, as the ferric oxide of black pigment and the resin combination that is used for laser labelling of other staining agent.Yet when this resin combination was used to laser labelling, the white colour that is labeled product was also unintelligible.
I take charge of and have successfully developed the glass dimension enhancing PBT resin combination with laser printing marking function, and have applied for corresponding patent.PET resin and PBT resin belong to thermoplastic polyester, and both have similarity at structure, but the processing temperature of PET resin is higher, and the many processing aids that are applied among the PET need higher heat resisting temperature, and its processing is more difficult.
Summary of the invention
In order to overcome above-mentioned defective, the invention provides a kind of PET resin combination and preparation method thereof with laser labelling function, this PET resin combination can go out the black marking by laser ablation on white base, and laser ablation goes out the white marking on black matrix.
The present invention for the technical scheme that solves its technical problem and adopt is: a kind of PET resin combination with laser labelling function, and it adopts the laser marking additive as the laser labelling enhancing ingredients, and the weight percentage of each component is respectively:
Polyethylene terephthalate 43~99.6%;
Continuous glass fibre 0~40%;
Toughner 0~15%;
Carbon black 0~0.5%;
Nucleator 0.2~0.5%;
Laser marking additive 0.2~1.0%.
As a further improvement on the present invention, described pet resin intrinsic viscosity is 0.6~0.8ml/g.
As a further improvement on the present invention, described continuous glass fibre is an alkali free glass fibre, and its diameter is 10~25 μ m.
As a further improvement on the present invention, described toughner is ethylene-propylene acid butyl ester-glycidyl methacrylate copolymer.
As a further improvement on the present invention, described carbon black is the powder with strong black opacifying power.
As a further improvement on the present invention, described nucleator is the saturated carboxylic acid sodium salt of linear long-chain.
As a further improvement on the present invention, described laser marking additive is to have the white powder that strengthens resin combination laser labelling function.
The present invention also provides a kind of preparation method with PET resin combination of laser labelling function, and its concrete steps are:
1. example takes by weighing polyethylene terephthalate, toughner, nucleator, laser marking additive and carbon black by weight percentage;
2. with above-mentioned load weighted polyethylene terephthalate, toughner, nucleator, enter twin screw extruder behind laser marking additive and the carbon black uniform mixing, add continuous glass fibre in the 6th district, forcing machine middle part, the content of this continuous glass fibre is controlled by regulating forcing machine rotating speed and feeding rotating speed, control a district temperature 230-250 ℃ simultaneously, two district temperature 230-250 ℃, three district temperature 240-260 ℃, four district temperature 240-260 ℃, five district temperature 240-260 ℃, six district temperature 240-260 ℃, seven district temperature 240-260 ℃, eight district temperature 240-260 ℃, nine district temperature 240-260 ℃, engine speed 300-400 rev/min;
3. extruding cooling, drying, pelletizing gets product.
The invention has the beneficial effects as follows: employing laser marking additive as the performance enhancement component, is prepared a kind of resin combination that has better mechanical property and laser labelling performance simultaneously as laser labelling enhancing ingredients, continuous glass fibre.This PET resin combination can form white text at the black product surface, perhaps forms distinct laser labellings such as black literal at white product surface, has kept the high performance nature of PET resin combination when having laser labelling function preferably.
Embodiment
Below in conjunction with embodiment, the present invention is described in further detail:
Matrix resin PET resin selects that engineering plastics factory of Yizheng branch office of assets management Management Co., Ltd of SINOPEC produces for use commonly has a light slicing product; Continuous glass fibre adopts the thermoplastics assembled roving of Chinese megalith group preparation, and the trade mark is 988A.Toughner adopts the ethylene-propylene acid butyl ester-glycidyl methacrylate copolymer (PTW) of du pont company; Nucleator employing section is a kind of long-chain linear saturated carboxylic acid sodium salt of benefactor department how, and the trade mark is NAV101; Carbon black is that Shanghai Yanrun Ray Machine Technology Co., Ltd. produces, and the trade mark is C-311; The laser marking additive is that DSM N. V. produces, and the trade mark is Micabs A206.
The present invention is a kind of PET resin combination with laser labelling function, respectively by embodiment in the table 1 1.~10. with table 2 in the comparative example 1.~2. in weight percent take by weighing polyethylene terephthalate, toughner, nucleator, laser marking additive and carbon black, mix then and enter the twin screw extruder (75A that Rhea company produces, length-to-diameter ratio is 1: 40) produce, complete processing is as follows: a district temperature 230-240 ℃, two district temperature 230-240 ℃, three district temperature 240-250 ℃, four district temperature 240-250 ℃, five district temperature 245-255 ℃, six district temperature 245-255 ℃, seven district temperature 245-255 ℃, eight district temperature 245-255 ℃, nine district temperature 240-250 ℃; Engine speed 300-400 rev/min.
Then the foregoing description and comparative example are carried out following performance test, concrete data see Table 3.
Wherein:
Notched Izod impact strength is tested by ASTM D256 standard, and specimen size is 64mm * 12.7mm * 3.2mm, and notch depth is 2.2mm.Testing apparatus is the Tinius Olisen shock-testing machine of U.S. Willow Grove company;
The tensile property test is tested by ASTM D638 standard, and specimen size is 168mm * 13mm * 3.2mm, and test speed is 50mm/min.Testing apparatus is a Germany
Table 1: embodiment is each composition weight percentage composition 1.~10.
Table 2: the comparative example is each composition weight percentage composition 1.~2.
The electronics pulling experiment machine of Zwick company;
The test of bending property is tested by ASTM D790 standard, and specimen size is 64mm * 12.7mm * 3.2mm, and span is 50mm, and test speed is 1.26mm/min.Testing apparatus is the electronics pulling experiment machine of German Zwick company;
Laser marking equipment is selected the DPY-M50 type laser marking equipment of Taide, Shenzhen laser Science and Technology Ltd. for use, and optical maser wavelength is 1061nm, and mean power is 10-50W.
1.~10. 1.~2. performance is relatively with the comparative example for table 3: embodiment
As can be seen from the above table, the influence of the adding PET resin property of laser marking additive is less, but can significantly improve the laser marking effect of PET resin complexes.It is many more to add the laser marking agent, and the laser marking effect is good more.But beat white font on black background, its effect is poor slightly than the look font of cracking down evil force on white background.
Claims (8)
1. PET resin combination with laser labelling function, it is characterized in that: it adopts the laser marking additive as the laser labelling enhancing ingredients, and the weight percentage of each component is respectively:
Polyethylene terephthalate 43~99.6%;
Continuous glass fibre 0~40%;
Toughner 0~15%;
Carbon black 0~0.5%;
Nucleator 0.2~0.5%;
Laser marking additive 0.2~1.0%.
2. the PET resin combination with laser labelling function according to claim 1 is characterized in that: described pet resin intrinsic viscosity is 0.6~0.8ml/g.
3. the PET resin combination with laser labelling function according to claim 1 is characterized in that: described continuous glass fibre is an alkali free glass fibre, and its diameter is 10~25 μ m.
4. the PET resin combination with laser labelling function according to claim 1 is characterized in that: described toughner is ethylene-propylene acid butyl ester-glycidyl methacrylate copolymer.
5. the PET resin combination with laser labelling function according to claim 1 is characterized in that: described carbon black is the powder with strong black opacifying power.
6. the PET resin combination with laser labelling function according to claim 1 is characterized in that: described nucleator is the saturated carboxylic acid sodium salt of linear long-chain.
7. the PET resin combination with laser labelling function according to claim 1 is characterized in that: described laser marking additive is to have the white powder that strengthens resin combination laser labelling function.
8. one kind as each described preparation method with PET resin combination of laser labelling function in the claim 1 to 7, it is characterized in that its concrete steps are:
1. example takes by weighing polyethylene terephthalate, toughner, nucleator, laser marking additive and carbon black by weight percentage;
2. with above-mentioned load weighted polyethylene terephthalate, toughner, nucleator, enter twin screw extruder behind laser marking additive and the carbon black uniform mixing, add continuous glass fibre in the 6th district, forcing machine middle part, the content of this continuous glass fibre is controlled by regulating forcing machine rotating speed and feeding rotating speed, control a district temperature 230-250 ℃ simultaneously, two district temperature 230-250 ℃, three district temperature 240-260 ℃, four district temperature 240-260 ℃, five district temperature 240-260 ℃, six district temperature 240-260 ℃, seven district temperature 240-260 ℃, eight district temperature 240-260 ℃, nine district temperature 240-260 ℃, engine speed 300-400 rev/min;
3. extruding cooling, drying, pelletizing gets product.