CN102061790A - Ultra-large light-transmission-type decorative board - Google Patents

Ultra-large light-transmission-type decorative board Download PDF

Info

Publication number
CN102061790A
CN102061790A CN 201110024014 CN201110024014A CN102061790A CN 102061790 A CN102061790 A CN 102061790A CN 201110024014 CN201110024014 CN 201110024014 CN 201110024014 A CN201110024014 A CN 201110024014A CN 102061790 A CN102061790 A CN 102061790A
Authority
CN
China
Prior art keywords
light
transmission type
wainscot
decorative panel
deck
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 201110024014
Other languages
Chinese (zh)
Other versions
CN102061790B (en
Inventor
付秀君
杜丽云
程涛
黎燕
杨汉学
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Qinhuangdao Yaohua FRP Co Ltd
Original Assignee
Qinhuangdao Yaohua FRP Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Qinhuangdao Yaohua FRP Co Ltd filed Critical Qinhuangdao Yaohua FRP Co Ltd
Priority to CN2011100240143A priority Critical patent/CN102061790B/en
Publication of CN102061790A publication Critical patent/CN102061790A/en
Application granted granted Critical
Publication of CN102061790B publication Critical patent/CN102061790B/en
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention belongs to building enclosure materials, in particular to a light-transmission-type composite sandwich decorative board with an ultra-large face. In the decorative board, a wholly-reinforced composite sandwich structure of a light-transmission-type FRP (Fiber Reinforced Plastic) panel, a honeycomb core material and latticed FRP reinforcing ribs is adopted, mounting holes are arranged on the periphery and in other specified positions, the product is formed by adopting a die, and the surface is coated with a high-weather-resistant facing layer. The decorative board provided by the invention is suitable for the mass production of boards with ultralarge faces. Compared with hollow glass of a curtain wall, the decorative board provided by the invention has equivalent light transmittance as well as the advantages of great veneer area, light weight, high strength, good impact resistance, sound and heat isolation, good decoration effect, capability of night illumination, easiness for maintenance, long service life, and the like and can meet the demands of curtain walls, enclosures and decoration engineering of buildings and large-scale landscape structures for light-transmission-type decorative boards with ultra-large areas.

Description

Super large light-transmission type decorative panel
Technical field
The invention belongs to a kind of building enclosure material, be specifically related to a kind of light-transmission type compound sandwich decorative panel with super large plate face.
Background technology
Many buildings adopt the light-transmission type material to go along with sb. to guard him this going along with sb. to guard him in whole or in part---and be commonly referred to " curtain wall ", curtain wall is present widely used a kind of light-transmission type space enclosing structure.It singly is not to guarantee effectively to go along with sb. to guard him function that building enclosure adopts the main purpose of light-transmission type material, also will satisfy daylighting and decoration demand simultaneously.Therefore, this light-passing board not only will have bigger veneer area, good mechanical performance, relatively low thermel expansion coefficient, higher thermal resistance and sound insulation property and long application life, also will have good light transmittance, more color, favorable surface quality and texture simultaneously.
Can be used as the light transmissive material that decorating building goes along with sb. to guard him mainly contains: inorganic, organic and composite material light-passing board three major types.The basic material of inorganic light-passing board is mainly sheet glass; The kind of organic light-passing board is more, mainly contain PMMA (acrylic, polymethyl methacrylate), PC (Merlon), PS (polystyrene), PP (polypropylene) and transparent PVC thermoplastic plastics such as (polyvinyl chloride) and adopt the sheet material that prolongs pressure or expressing technique manufacturing; The composite material light-passing board comprises: light-transmission type FRP (glass fiber reinforced plastic) plate, printing opacity stone (man-made stone light-passing board) and compound printing opacity sandwiched plate etc.
In above-mentioned three class light transmissive materials,, any bill of materials goes along with sb. to guard him all on performance more or less the some shortcomings that exist no matter being solely used in curtain wall.For example: there are deficiencies such as fragility height, coefficient of heat conduction height and veneer area be less in sheet glass, makes performance obtain some improvement though can lean on PROCESS FOR TREATMENT such as tempering, plated film, interlayer and improve veneer thickness, and performance is still barely satisfactory.Acrylic in organic light-passing board (organic glass) light transmittance height, the light transmittance of Merlon and comprehensive mechanical performance are all fine, but reason has limited in architectural application because of these material price height, veneer area are less etc.Also have at present adding Al honeycomb (or plastic honeycomb) in the middle of two PMMA plates (or transparent PS plate), make the printing opacity sandwich slab that can under light, manifest honeycomb structure, be used for screen, artistic veneer and cabinet door etc. and located decoration function.These printing opacity sandwich slabs are used for outdoor owing to reasons such as mechanical strength and resistance to ag(e)ing are less.Glass fiber reinforced plastic daylighting in the composite material watt (plate) is used as the printing opacity roofing materials widely, but its thinner thickness can't satisfy the requirement of building enclosure to plate face rigidity and thermal transmittance.
Above-mentioned three major types printing opacity sheet material is because the restriction of material property and manufacturing process, when being used for building enclosure, some inadequate natural endowments are all arranged, particularly the problem of organic material on weatherability is more more, this has just limited the use of organic light transmissive material as the building enclosure material, to such an extent as to formed the helpless situation that present curtain wall " is outshined othersOne branch of the tree is particularly thriving ".Simultaneously, no matter be glass or transparent plastic, all can not provide the sheet material of large format because of the restriction of material property, production technology, capacity of equipment and manufacturing cost.Under common processes, the veneer maximum area of cladding glass is: single (folder) layer glass≤4.5m 2/ piece, hollow glass≤3.2m 2/ piece.At present, some significant famous buildings and large-scale landscape structure have proposed very high requirement to the plate face and the performance of curtain wall cladding.For example, the curtain wall in building, Chinese Central Television new address, the hollow glass that has adopted special technique to make, wherein Zui Da veneer area has 7m 2, thickness 70mm, weight reaches 650kg, can be rated as hollow glass.But if the bigger veneer area of demand, prior art just can't satisfy so.
This shows that under present technical condition, any homogenous material all is difficult to satisfy modern architecture and goes along with sb. to guard him the comprehensive technology requirement of printing opacity sheet material at aspects such as veneer area, mechanical performance, heat insulation, sound insulation and incrustations.
Summary of the invention
Technical problem to be solved by this invention is to overcome the deficiencies in the prior art, provide that a kind of performance than existing light transmissive material is more excellent, cost performance rationally and have a super large light-transmission type decorative panel of super large plate face.
The technical solution used in the present invention is:
Super large light-transmission type decorative panel comprises outer panels, wainscot, comb core, reinforcing rib, wherein: outer panels, wainscot and reinforcing rib are the light-transmission type glass-reinforced plastic material, and the three has formed an integral body that is made of jointly inside and outside covering and latticed rib behind curing molding; Outer panels and wainscot also are equipped with comb core in the folded inner space, and described comb core adopts the transition zone sealing; Described decorative panel is provided with a plurality of installing holes, and is equipped with cushion block between outer panels around described installing hole and the wainscot.
Super large light-transmission type decorative panel as mentioned above, wherein: described outer panels is made up of deck and outer gel coating resin; Described wainscot is made up of deck and interior gel coating resin; It between the deck of described outer panels and the deck of wainscot comb core by the transition zone sealing.
Super large light-transmission type decorative panel as mentioned above, wherein: described comb core adopts glass fiber reinforced plastic, aluminium alloys or polypropylene material to make, and cuts into rectangle sheet material and be arranged between the latticed reinforcing rib; The material of described reinforcing rib and deck is the alkali-free glass fibre weak point and cuts felt and light-transmission type unsaturated polyester resin; Described cushion block adopts glass fiber reinforced plastic light-passing board, poly (methyl methacrylate) plate or the polycarbonate plate with the comb core equal thickness.
Super large light-transmission type decorative panel as mentioned above, wherein: the outer gel coating resin surface applied of described outer panels has finish coat in the surface applied of exterior trim surface layer and or wainscot; Described exterior trim surface layer, interior finish coat adopt fluorocarbon coating or acroleic acid polyurethane coating.
Super large light-transmission type decorative panel as mentioned above, wherein: the base material of described transition zone is a hyposmosis type glass surface felt; The one side employing cementing agent and the comb core of transition zone are bonding, the common curing molding of another side and deck.
Super large light-transmission type decorative panel as mentioned above, wherein: maximum veneer area≤54m2, thickness of slab 10~90mm.
A kind of process of making super large light-transmission type decorative panel comprises the steps:
A) make the outer board mold of rectangle and the interior board mold of same size according to the length of super large light-transmission type decorative panel to be made, release agent application in mould;
B) the board mold bottom sprays the transparent adhesive tape coating resin outside, and the deposited alkali-free glass fibre weak point in shop is cut felt and formed outer gel coating resin when treating initial set;
C) gel coating resin top is alternately applied the alkali-free glass fibre weak point and is cut felt and spray transparent unsaturated polyester resin in the shop outside, rolling calm the anger bubble and compacting shop layer, forms deck;
D) with two surfaces of modified epoxy bonding agent roller coating in comb core, and the bonding base material hyposmosis type glass surface felt of going up transition zone, standby;
E) before the deck gel, lay forms the comb core plate of laminboard layer above deck, and the alkali-free glass fibre weak point that lay forms latticed reinforcing rib in the slit behind lay between each comb core plate is cut the felt band; The glass fiber reinforced plastic light-passing board that is used to form cushion block or poly (methyl methacrylate) plate or polycarbonate plate in installing hole place lay and comb core equal thickness;
F) sprinkling transparent unsaturated polyester resin on the felt band of reinforcing rib after waiting to soak into, with whole plate face spraying last layer transparent unsaturated polyester resin, is prepared with wainscot bonding;
G) wainscot is in the inner panel die for molding, its technology and above-mentioned steps b), c) identical;
H) it is bonding with the outer panels matched moulds wainscot to be put into outer board mold, and integral body is exerted pressure equably, and pressure is 0.04~0.1kg/cm 2
I) after the curing, molding, the finishing outward appearance, and at cushion block position brill installing hole;
J) treatment surface, spraying exterior trim surface layer and/or interior finish coat.
Super large light-transmission type decorative panel as mentioned above, it is characterized by: the weight ratio of the resinous principle of deck and glass fiber component is 70: 30 in described step c).
Know-why of the present invention is: the plate face that exists at the employed printing opacity sheet material of present building curtain wall is little, intensity is low, the deficiency on shock resistance difference and the decoration functions, the compound sandwich structure that the present invention has adopted latticed whole reinforcing rib to strengthen; Select for use light-transmission type FRP as interior outer panels, can make full use of its light transmittance height, characteristics that mechanical strength is big; The comb core in intermediate layer is not only in light weight, compressive strength is high, and FRP (or PP) comb core also has good light transmittance.By material mechanics principle as can be known, the rigidity of fixed head is directly proportional with elastic modulus E and thickness of slab 3 powers all around.Therefore adopt the cellular sandwich layer, not only can increase thickness of slab significantly, thereby improve the rigidity of plate greatly, also reduced the weight with cladding glass same stiffness plate simultaneously effectively, this just lays a good foundation for the veneer of production overlarge area.Because the light transmittance of stacked object is similar to the product of each layer light transmittance, this has just guaranteed that this composite laminboard has higher light transmission.The surface of this composite laminboard can adopt the technology of coating high weatherability coating to carry out incrustation simultaneously, therefore has good decoration functions and long application life.
The invention has the beneficial effects as follows:
Described super large light-transmission type decorative panel adopts light-transmission type FRP panel and adopts the honeycomb sandwich structure of transition zone sealing, prevented the strike-through in the honeycomb cavity, guaranteed the uniformity of whole plate face printing opacity, the special integral grid shape reinforcing rib that is provided with significantly improves the integral rigidity of decorative panel; This structure is in light weight simultaneously, and its apparent density only is 297.1kg/m 3(5+60+5), it only is 1/4.5 of condition of equivalent thickness hollow glass, and impact resilience and hot strength are greatly improved than hollow glass, the coefficient of thermal expansion of the coefficient of thermal expansion of this plate and steel or steel concrete is similar simultaneously, under the temperature acute variation, the thermal stress that produces is little of ignoring, and makes designer and builder that the anxiety of fragmentation no longer be arranged as worrying glass.Owing to adopted the enhancement measures that adds cushion block in the connection hole, to thickness 16mm (3+10+3) veneer area 14m 2The strength check of (4*3.5m, area surpasses 1 times of maximum monolithic hollow glass) shows, only at the periphery erection bolt of plate, can use safely down at typhoon (v=32.7m/s), and as seen its mechanical strength is far above the curtain wall hollow glass.The thickness 120mm (15+90+15) that adopts this structure to produce, veneer area 54m 2Super large light-transmission type decorative panel (9*6m), gross weight only are 2873kg (apparent density: 443.3kg/m 3, average substance: 53.2kg/m 2).
Be air chamber independently between two panels of the honeycomb sandwich structure that described super large light-transmission type decorative panel adopts, and outside plate is different with the intrinsic natural frequency of core, so has the lower coefficient of heat conduction and higher thermal insulation.Measured data is much better than the hollow glass of condition of equivalent thickness.
The light-transmission type honeycomb sandwich structure that described super large light-transmission type decorative panel adopts has higher light transmission.Adopt this structure, the not coated plate of thickness 14mm (2+10+2), the theoretical value of its full light transmission rate can reach 60.5%, work as with the glassy phase of condition of equivalent thickness, but this decorative panel is opaque, has the effect of protecting privacy and not manifesting internal construction.
The panel of the honeycomb sandwich structure that described super large light-transmission type decorative panel adopts can carry out external coating easily to be handled, and is convenient to show different design ideas and building theme.Particularly night building interior light see through decorative panel, make building enclosure produce sparkling decorative effect.
Described super large light-transmission type decorative panel adopts mould-forming process, and homogeneity of product is strong, geometric accuracy is high, is suitable for to produce in batches, can satisfy the decoration of building, view preferably and go along with sb. to guard him needs.
The present invention has adopted the compound sandwich structure of light-transmission type glass reinforced plastic panel, comb core and latticed FRP reinforcing rib overall enhanced, periphery and miscellaneous stipulations position have installing hole, product adopts mould molding, the high weather resistant finish coat of surface-coated is suitable for producing in batches the product of super large-scale plate face.This plate is compared with the curtain wall hollow glass, its light transmission is suitable, and have that the veneer area is big, in light weight, intensity is high, good impact resistance, sound insulation, heat insulation, good decorating effect, can noctilucence, advantages such as easy care and long service life, can satisfy building and large-scale landscape structure curtain wall, go along with sb. to guard him and the demand of decorative engineering overlarge area light-transmission type decorative panel.
Description of drawings
Fig. 1 is the structural representation of super large light-transmission type decorative panel;
Fig. 2 is the A-A sectional drawing of Fig. 1;
Fig. 3 is the enlarged drawing of the local I of Fig. 2;
Fig. 4 is the step schematic diagram of matched moulds after the moulding of the inside and outside plate difference of a kind of super large light-transmission type decorative panel provided by the invention;
Fig. 5 is the process chart of a kind of super large light-transmission type decorative panel provided by the invention;
Among the figure, 1. outer panels, 2. wainscot, 3. comb core, 4. reinforcing rib, 5. cushion block, 6. transition zone, 7. deck, 8. outer gel coating resin, 9. exterior trim surface layer, 10. in gel coating resin, finish coats in 11., 12. installing holes, 13. outer board molds, 14. interior board molds.
The specific embodiment
Embodiment one
Below in conjunction with accompanying drawing specific embodiments of the invention one are described further: the super large light-transmission type decorative panel with a kind of welcome's of being used for view is an example, the appearance and size of this view is: 6 * 2.2 * 21m (length * wide * height), totally 6 layers, the cladding mode of encorbelmenting is adopted in the view outside, the light-transmission type decorative panel is gone along with sb. to guard him as the integral body of its main body structure, and the external surface color is a Chinese red.At night, can light inner mounted LEDs electric light source, see through decorative panel and make the view entirely lighting, make all can represent its global feature round the clock, to reach its welcome's effect.
According to designing requirement and actual work usefulness, positive facade is designed by every layer one packaged plaque: veneer area 21m 2(6 * 3.5m), thickness 16mm, shop layer structure is 3+10+3mm (being that inner and outer plates is 3mm, sandwich panel 10mm), and with spacing≤500mm spaced set installing hole, the external surface color is a Chinese red all around, and inner surface is colourless gel coating resin (a no inner surface decorative layer).
Shown in Fig. 1~3, super large light-transmission type decorative panel, comprise outer panels 1, wainscot 2, by the comb core 3 of outer panels 1 and wainscot 2 clampings and the reinforcing rib 4 of continuous grids shape, outer panels 1, wainscot 2 and reinforcing rib 3 are high light-transmission type FRP (glass fiber reinforced plastic) material, have formed an integral body that is made of jointly inside and outside covering and latticed rib behind curing molding.Be provided with installing hole 12 around the super large light-transmission type decorative panel and on the assigned position, and between outer panels 1 around the installing hole 12 and wainscot 2, be equipped with cushion block 5.
Described outer panels 1 is made up of deck 7 and outer gel coating resin 8; Described wainscot 2 is made up of deck 7 and interior gel coating resin 10; It between the deck 7 of described outer panels 1 and the deck 7 of wainscot 2 comb core 3 by transition zone 6 sealings.
Outer gel coating resin 8 surface applied of described outer panels 1 have the interior finish coat 11 of the surface applied of exterior trim surface layer 9 He or wainscot 2; Described exterior trim surface layer 9, interior finish coat 11 can adopt fluorocarbon coating, acroleic acid polyurethane coating or other high weather resistant coating.
Comb core 3 can adopt FRP, Al (aluminium alloys) or PP (polypropylene) material to make, and cuts into rectangle sheet material; Cushion block 5 adopts the FRP light-passing board with comb core 3 equal thickness, also can adopt PMMA (organic glass) plate or PC (Merlon) plate.The base material of transition zone 6 is a hyposmosis type glass surface felt, and the one side of transition zone 6 adopts corresponding cementing agent and comb core 3 bonding, another side and deck 7 common curing moldings; For example: the FRP comb core is then bonding to be connect agent and can directly adopt the light-transmission type mylar if comb core 3 is selected for use, also can adopt the modified epoxy bonding agent; If comb core 3 aluminium honeycombs, then bondingly connect agent and can adopt light-transmission type epoxy resin; If comb core 3 is the PP honeycomb, should select the modified polyurethane bonding agent.
The material of reinforcing rib 4 and deck 7 is the alkali-free glass fibre weak point and cuts felt and light-transmission type unsaturated polyester resin; The weight ratio of resin and glass fiber is 70: 30 in the deck 7.
The maximum veneer area≤54m of super large light-transmission type decorative panel 2, thickness of slab 10~90mm.
Outer panels 1 and wainscot 2 adopt the alkali-free glass fibre weak point to cut felt, light-transmission type unsaturated polyester resin and curing system normal temperature cure moulding, its outer panels 1 and wainscot 2 are respectively by outer board mold 13 and the 14 independent moulding of interior board mold, bonding then is whole, its moulding process step shown in Fig. 4,5, for:
A) require to make veneer area 21m in the present embodiment 2(6 * 3.5m), thickness 16mm, a layer structure in shop is the super large light-transmission type decorative panel of 3+10+3mm, therefore outer board mold 13 of corresponding making box type and interior board mold 14, and in mould release agent application; The preparation method of mould is those skilled in the art's a common practise.
Raw material are: 300g/m 2The alkali-free glass fibre weak point is cut felt, 30g/m 2Alkali-free glass fibre surface felt (promptly being the base material hyposmosis type glass surface felt of transition zone), δ 10mm glass fibre reinforced plastic honeycomb plate (specification: 1.2 * 0.875m/ piece), the modified epoxy cementing agent, 80 * 80 * δ 10mm glass fiber reinforced plastic light-passing board, the light-transmission type gel coating resin, the transparent unsaturated polyester resin, curative system and methyl methacrylate, high weather resistant fluorocarbon coating;
B) transparent adhesive tape of board mold 13 bottoms spraying outside coating resin, the deposited alkali-free glass fibre weak point in shop is cut felt and is formed outer gel coating resin 8 when treating initial set;
C) alternately the shop is applied the alkali-free glass fibre weak point and is cut felt (containing glass fiber component) and spray transparent unsaturated polyester resin (resinous composition), rolls calm the anger bubble and compacting shop layer, forms deck 7 until reaching; Should check the ratio of resinous principle and glass fiber in the layer construction of shop at any time, control the scope that its weight ratio remained on 70: 30; If the index of refraction of resinous principle is higher than 1.514, then need add methyl methacrylate adjustment index of refraction and reach 1.514, reach designing requirement with the light transmittance that guarantees deck 7.
D) with two surfaces of modified epoxy bonding agent roller coating in comb core 3, and the bonding base material hyposmosis type glass surface felt of going up transition zone 6, standby;
E) before deck 7 gels, the lay glass fibre reinforced plastic honeycomb plate forms comb core 3 plates of laminboard layer above deck 7, and the alkali-free glass fibre weak point that lay forms latticed reinforcing rib 4 in the slit behind lay between each comb core 3 plates is cut the felt band; The glass fiber reinforced plastic light-passing board that is used to form cushion block 5 in installing hole 12 place's laies and comb core 3 equal thickness also can use poly (methyl methacrylate) plate or polycarbonate plate;
F) sprinkling transparent unsaturated polyester resin on the felt band of reinforcing rib 4 after waiting to soak into, with whole plate face spraying last layer transparent unsaturated polyester resin, is prepared with wainscot 2 bonding;
G) wainscot 2 moulding in interior board mold 14, its technology and above-mentioned steps b), c) identical.For raising the efficiency, wainscot 2 and outer panels 1 are made simultaneously.At least should notice that wainscot has cured for before guaranteeing matched moulds, should operate in advance, to reserve hardening time.
H) it is bonding with outer panels 1 matched moulds wainscot 2 to be put into outer board mold 13, and the integral body (pressure 0.04~0.1kg/cm that exerts pressure equably 2), exert pressure and adopt sandbag or water pocket;
I) after the curing, molding, the finishing outward appearance, and at cushion block 5 positions brill installing hole 12;
J) treatment surface, spraying exterior trim surface layer 9, the exterior trim surface layer adopts high weather resistant fluorocarbon coating, for example sprays the coating that color is a Chinese red, sprays 2~3 times; Can spray or the interior finish coat of portion's spraying spraying in the present embodiment as required.
According to the different requirements of product, wainscot 13 also can be at above-mentioned steps f) after, direct c set by step) shop applies molding structure layer 7, carries out step h then successively)~i), note: step j) only outer panels 1 is made facing and handle.
Embodiment two
As shown in Figure 5, this is that inner surface does not need the surface-treated decorative panel, adopts the one-shot forming mode.The specification of present embodiment is: 6 * 9m, area 54m 2, thickness of slab 120mm, external surface is shallow fruit green, requires printing opacity (5~10Lux/m at night 2), inner surface does not have specific (special) requirements.According to customer requirements, the shop layer is designed to: 15+90+15, that is: (inside and outside) FRP deck 7 thickness 15mm; Core adopts FRP cellular board, thickness 90mm, single-block area 2.25m 2(1.5 * 1.5m); Reinforcing rib thickness 10mm adopts the wide alkali-free glass fibre weak point of 90mm to cut the felt suture zone; Disposed at equal distance around the installing hole edge, installing hole spacing≤600mm for guaranteeing safety, is provided with a connecting hole at the center of plate (two diagonal intersection points), the cushion block 5 of connecting hole position is of a size of 250 * 250 * δ 90mm, and its material also is printing opacity sandwiched plate (shop layer 15+60+15).All the other materials of present embodiment are identical with embodiment one.
Present embodiment adopts the normal temperature cure of contact mould, and one-shot forming technique that is: adopts outer board mold, begins molding structure layer 7, honeycomb section bar 3 and transition zone 6, cushion block 5, deck 7 successively from outer gel coating resin 8; Its job practices is with embodiment one.After goods fully solidify, molding, refacing, boring; External surface sprays the high weather resistant fluorocarbon coating of shallow fruit green 2~3 times; After fully solidifying, refine, polishing; Through after the assay was approved, submit the user to.Because this embodiment plate face is excessive, adopt field fabrication.

Claims (8)

1. super large light-transmission type decorative panel comprises outer panels (1), wainscot (2), comb core (3), reinforcing rib (4), it is characterized by: outer panels (1), wainscot (2) and reinforcing rib (3) are the light-transmission type glass-reinforced plastic material, and the three has formed an integral body that is made of jointly inside and outside covering and latticed rib behind curing molding; Also be equipped with comb core (3) in outer panels (1) and the folded inner space of wainscot (2), described comb core (3) adopts transition zone (6) sealing; Described decorative panel is provided with a plurality of installing holes (12), and described installing hole (12) on every side outer panels (1) and wainscot (2) between be equipped with cushion block (5).
2. according to the described super large light-transmission type of claim 1 decorative panel, it is characterized by: described outer panels (1) is made up of deck (7) and outer gel coating resin (8); Described wainscot (2) is made up of deck (7) and interior gel coating resin (10); It between the deck (7) of described outer panels (1) and the deck (7) of wainscot (2) comb core (3) by transition zone (6) sealing.
3. according to the described super large light-transmission type of claim 2 decorative panel, it is characterized by: described comb core (3) adopts glass fiber reinforced plastic, aluminium alloys or polypropylene material to make, and cuts into rectangle sheet material and be arranged between the latticed reinforcing rib (4); The material of described reinforcing rib (4) and deck (7) is the alkali-free glass fibre weak point and cuts felt and light-transmission type unsaturated polyester resin; Described cushion block (5) adopts glass fiber reinforced plastic light-passing board, poly (methyl methacrylate) plate or the polycarbonate plate with comb core (3) equal thickness.
4. according to the described super large light-transmission type of claim 2 decorative panel, it is characterized by: outer gel coating resin (8) surface applied of described outer panels (1) has the interior finish coat (11) of the surface applied of exterior trim surface layer (9) and or wainscot (2); Described exterior trim surface layer (9), interior finish coat (11) adopt fluorocarbon coating or acroleic acid polyurethane coating.
5. according to the described super large light-transmission type of claim 2 decorative panel, it is characterized by: the base material of described transition zone (6) is a hyposmosis type glass surface felt; The one side employing cementing agent and the comb core (3) of transition zone (6) are bonding, the common curing molding of another side and deck (7).
6. according to the described super large light-transmission type of claim 1 decorative panel, it is characterized by: maximum veneer area≤54m 2, thickness of slab 10~90mm.
7. a process of making super large light-transmission type decorative panel comprises the steps:
A) make the outer board mold (13) of rectangle and the interior board mold (14) of same size according to the length of super large light-transmission type decorative panel to be made, release agent application in mould;
B) board mold (13) bottom sprays the transparent adhesive tape coating resin outside, and the deposited alkali-free glass fibre weak point in shop is cut felt and formed outer gel coating resin (8) when treating initial set;
C) gel coating resin (8) top is alternately applied the alkali-free glass fibre weak point and is cut felt and spray transparent unsaturated polyester resin in the shop outside, rolling calm the anger bubble and compacting shop layer, forms deck (7);
D) with two surfaces of modified epoxy bonding agent roller coating in comb core (3), and the bonding base material hyposmosis type glass surface felt of going up transition zone (6), standby;
E) before deck (7) gel, form comb core (3) plate of laminboard layer at deck (7) top lay, the alkali-free glass fibre weak point that lay forms latticed reinforcing rib (4) in the slit behind lay between each comb core (3) plate is cut the felt band; Locate the glass fiber reinforced plastic light-passing board that is used to form cushion block (5) or the poly (methyl methacrylate) plate or the polycarbonate plate of lay and comb core (3) equal thickness at installing hole (12);
F) sprinkling transparent unsaturated polyester resin on the felt band of reinforcing rib (4) after waiting to soak into, with whole plate face spraying last layer transparent unsaturated polyester resin, is prepared with wainscot (2) bonding;
G) wainscot (2) moulding in interior board mold (14), its technology and above-mentioned steps b), c) identical;
H) it is bonding with outer panels (1) matched moulds wainscot (2) to be put into outer board mold (13), and integral body is exerted pressure equably, and pressure is 0.04~0.1kg/cm 2
I) after the curing, molding, the finishing outward appearance, and at cushion block (5) position brill installing hole (12);
J) treatment surface, spraying exterior trim surface layer (9) and/or interior finish coat (11).
8. according to the described super large light-transmission type of claim 7 decorative panel, it is characterized by: the resinous principle of deck in described step c) (7) and the weight ratio of glass fiber component are 70:30.
CN2011100240143A 2011-01-21 2011-01-21 Ultra-large light-transmission-type decorative board Expired - Fee Related CN102061790B (en)