CN102060978A - Pyridine polyether ionic liquid toughened epoxy resin and preparation method thereof - Google Patents
Pyridine polyether ionic liquid toughened epoxy resin and preparation method thereof Download PDFInfo
- Publication number
- CN102060978A CN102060978A CN 201010565666 CN201010565666A CN102060978A CN 102060978 A CN102060978 A CN 102060978A CN 201010565666 CN201010565666 CN 201010565666 CN 201010565666 A CN201010565666 A CN 201010565666A CN 102060978 A CN102060978 A CN 102060978A
- Authority
- CN
- China
- Prior art keywords
- pyridine type
- polyoxyalkylene nonionic
- type polyoxyalkylene
- epoxy
- pyridine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses pyridine polyether ionic liquid toughened epoxy resin and a preparation method thereof. Pyridine polyether ionic liquid serving as a toughening agent is added into epoxy resin prepolymer in a mass ratio of (20-60):(80-40). The preparation method comprises the following steps of: mixing the pyridine polyether ionic liquid and the epoxy resin prepolymer, and reacting at the temperature of 80 DEG C for 2 hours with stirring; and adding a curing agent, uniformly stirring, and curing at the temperature of between 120 and 160 DEG C for 5 hours to obtain a finished product. By controlling a certain ratio of the ionic liquid to the epoxy resin, the toughness of the epoxy resin can be enhanced.
Description
One, technical field
The present invention relates to a kind of method for toughening of Resins, epoxy, Resins, epoxy that specifically a kind of pyridine type polyoxyalkylene nonionic liquid is toughness reinforcing and preparation method thereof.
Two, background technology
Resins, epoxy is used for many industrial circles with forms such as matrix material, tackiness agent, Embedding Materials.Yet its cured article cross-linking density is big, is tridimensional network, and the slip (plastic deformation) of molecular chain is seldom arranged, and the result causes big, the poor toughness of material fragility; And volumetric shrinkage when solidifying, easily produce bigger stress concentration, reduced its over-all properties so to a great extent.
People once adopted a lot of methods to improve its toughness, commonly in epoxy-resin systems, add at present rubber carry out toughness reinforcing, as the acrylonitrile-butadiene copolymer (CTBN) of carboxy blocking, thiorubber etc.
Ionic liquid is the environment-friendly type solvent that a class of rising in recent years has application prospect, it is with non-volatile, stable to water and air, and inorganic, organic compound and macromolecular material are had good solubility and be widely used in fields such as electrochemistry, organic synthesis, chemical separating, material preparation.Come modified polymer material more and more to receive polymer scholar's concern with ionic liquid.Ionic liquid is incorporated in the organic polymer material, prepares ion liquid modified superpolymer, aspect the raising polymer performance good prospects for application is being arranged.
Pyridine type polyoxyalkylene nonionic liquid has terminal hydroxy group and flexible polyethers long-chain, with pyridine type polyoxyalkylene nonionic liquid the curing system of Resins, epoxy is carried out study on the modification, yet there are no report at present at home and abroad.
Three, summary of the invention
The present invention is for fear of above-mentioned the deficiencies in the prior art part, and toughness reinforcing Resins, epoxy of a kind of toughness height, the simple pyridine type polyoxyalkylene nonionic of preparation technology liquid and preparation method thereof is provided.
Technical solution problem of the present invention adopts following technical scheme:
The characteristics of the Resins, epoxy that a kind of pyridine type polyoxyalkylene nonionic of the present invention liquid is toughness reinforcing are, pyridine type polyoxyalkylene nonionic liquid is added in the epoxy prepolymer as toughner, and the mass ratio of described pyridine type polyoxyalkylene nonionic liquid and epoxy prepolymer is 20-60: 80-40;
The general structure of described pyridine type polyoxyalkylene nonionic liquid is:
Negatively charged ion X wherein
-Be Cl
-, Br
-, I
-, Al
2Cl
7 -, BE
4 -, PF
6 -, NO
3 -, NO
2 -, SO
4 2-, CH
3COO
-, SbF
6 -, ZnCl
3 -, SnCl
3 -, N (CF
3SO
2)
-, N (C
2F
5SO
2)
-, N (FSO
2)
2 -, C (CF
3SO
2)
3 -, CF
3CO
2 -, CF
3SO
3 -Or CH
3SO
3 -
The preparation method's of the Resins, epoxy that a kind of pyridine type polyoxyalkylene nonionic of the present invention liquid is toughness reinforcing characteristics are to operate according to the following steps:
Pyridine type polyoxyalkylene nonionic liquid is mixed with epoxy prepolymer, and 80 ℃ of stirring reactions 2 hours add solidifying agent then and stir, 120-160 ℃ solidified 5 hours finished product;
Described solidifying agent is a quadrol, and addition is 10% of a described epoxy prepolymer quality.
The preparation method's of the Resins, epoxy that a kind of pyridine type polyoxyalkylene nonionic of the present invention liquid is toughness reinforcing characteristics also are: described curing is to be incubated 1 hour down at 120 ℃, 140 ℃ of insulations 2 hours, is warming up to 160 ℃ of insulations 2 hours then.
The ionic liquid that the present invention uses has flexible chain and polyether group simultaneously.Toughness reinforcing mechanism is to contain a large amount of polyether soft segments in the pyridine type polyoxyalkylene nonionic liquid, when solidifying with Resins, epoxy, can increase the flexibility of curing cross-linked network, alleviate stress concentration to a certain extent, improved the plastic deformation ability of curing system, so the toughness of curing system is significantly improved.
Compared with the prior art, beneficial effect of the present invention is embodied in:
1, the cost of material of the present invention's use is cheap, and reaction is simple, and mild condition is easy to control, is convenient to industrialization.
2, the present invention can obtain the very strong Resins, epoxy of toughening effect by controlling the certain ionic liquid and the ratio of Resins, epoxy.When pyridine type polyoxyalkylene nonionic liquid and Resins, epoxy mass ratio are 20: 80,40: 60,60: 40, the shock strength of curing system has improved 58%, 160%, 340% respectively than pure epoxy resin, wherein ionic liquid and Resins, epoxy mass ratio are 60: 40 o'clock, although batten thickness reaches 6mm, but can be arbitrarily crooked, present tangible caoutchouc elasticity, wherein pyridine type polyoxyalkylene nonionic liquid and Resins, epoxy mass ratio are that the toughness of 20: 80 o'clock curing systems is greatly improved, and Strength Changes is little.
Four, embodiment
Embodiment 1:
Present embodiment is that pyridine type polyoxyalkylene nonionic liquid is mixed with epoxy prepolymer, 80 ℃ of stirring reactions 2 hours, and it is thick that reaction back system becomes black, add quadrol then and stir, be incubated 1h down at 120 ℃,, be warming up to 160 ℃ of insulation 2h then and get finished product at 140 ℃ of insulation 2h;
Wherein the mass ratio of pyridine type polyoxyalkylene nonionic liquid and epoxy prepolymer is 20: 80, and the consumption of quadrol is 10% of an epoxy prepolymer quality.
Pyridine type polyoxyalkylene nonionic liquid prepares with following method in the present embodiment:
The 40g Hydrin is dissolved in the 50mL toluene, stirs the pyridine that adds 68mL down, 50 ℃ of following stirring reactions 10 hours, add the 50mL ether after being cooled to room temperature, solvent and low-boiling-point organic compound are removed in underpressure distillation 3 hours under 90 ℃, 0.1MPa then, negatively charged ion be Cl
-Pyridine type polyoxyalkylene nonionic liquid, structural formula is as follows:
Embodiment 2:
The preparation method of present embodiment is with embodiment 1, and the mass ratio of different is pyridine type polyoxyalkylene nonionic liquid and epoxy prepolymer is 40: 60, and used pyridine type polyoxyalkylene nonionic liquid is that negatively charged ion is PF
6 -Pyridine type polyoxyalkylene nonionic liquid.
Pyridine type polyoxyalkylene nonionic liquid prepares with following method in the present embodiment:
The 40g Hydrin is dissolved in the 50mL toluene, stirs the pyridine that adds 68mL down, 50 ℃ of following stirring reactions 10 hours, add the 50mL ether after being cooled to room temperature, solvent and low-boiling-point organic compound are removed in underpressure distillation 3 hours under 90 ℃, 0.1MPa then, negatively charged ion be Cl
-Pyridine type polyoxyalkylene nonionic liquid.
With the gained negatively charged ion is Cl
-Pyridine type polyoxyalkylene nonionic liquid be dissolved in the methyl-sulphoxide, the back that stirs adds sodium hexafluoro phosphate, in 50 ℃ of reactions 24 hours, carries out anionresin; Leave standstill and remove by filter sodium-chlor after ion exchange reaction finishes, underpressure distillation 3 hours under 90 ℃, 0.1MPa then, negatively charged ion be PF
6 -Pyridine type polyoxyalkylene nonionic liquid, structural formula is as follows:
Embodiment 3:
The preparation method of present embodiment is with embodiment 1, and the mass ratio of different is pyridine type polyoxyalkylene nonionic liquid and epoxy prepolymer is 60: 40, and used pyridine type polyoxyalkylene nonionic liquid is that negatively charged ion is BF
4 -Pyridine type polyoxyalkylene nonionic liquid.
Pyridine type polyoxyalkylene nonionic liquid prepares with following method in the present embodiment:
The 40g Hydrin is dissolved in the 50mL toluene, stirs the pyridine that adds 68mL down, 50 ℃ of following stirring reactions 10 hours, add the 50mL ether after being cooled to room temperature, solvent and low-boiling-point organic compound are removed in underpressure distillation 3 hours under 90 ℃, 0.1MPa then, negatively charged ion be Cl
-Pyridine type polyoxyalkylene nonionic liquid.
It is Cl that gained is got negatively charged ion
-Pyridine type polyoxyalkylene nonionic liquid be dissolved in the methyl-sulphoxide, the back that stirs adds sodium tetrafluoroborate, in 50-80 ℃ of reaction 5-7 hour, carries out anionresin; Leave standstill and remove by filter sodium-chlor after ion exchange reaction finishes, underpressure distillation 3 hours under 90 ℃, 0.1MPa then, negatively charged ion be BF
4 -Pyridine type polyoxyalkylene nonionic liquid, structural formula is as follows:
The epoxy resin toughened mechanical property of pyridine type polyoxyalkylene nonionic liquid of embodiment 1-3 preparation sees Table 1, as shown in Table 1, when pyridine type polyoxyalkylene nonionic liquid and Resins, epoxy mass ratio were 20: 80, the shock strength of curing system had improved 58% than pure epoxy resin; When pyridine type polyoxyalkylene nonionic liquid and Resins, epoxy mass ratio were 40: 60, the shock strength of curing system had improved 160% than pure epoxy resin; When pyridine type polyoxyalkylene nonionic liquid and Resins, epoxy mass ratio were 60: 40, the shock strength of curing system had improved 340% than pure epoxy resin, although batten thickness reaches 6mm, can be arbitrarily crooked, and present tangible caoutchouc elasticity.
Table 1 is the pyridine type polyoxyalkylene nonionic liquid of different mass ratio and the mechanical property of epoxy resin solidifying system
| Group | 1 | 2 | 3 | 4 |
| PPIL∶EP | 0∶100 | 20∶80 | 40∶60 | 60∶40 |
| Simple beam impact strength/KJm -2 | 2.13 | 3.37 | 5.54 | 9.39 |
| Flexural strength/MPa | 72.34 | 58.25 | 18.38 | 3.58 |
| Tensile strength/MPa | 45.53 | 55.18 | 18.79 | 16.34 |
| Tension fracture elongation rate/% | 12.73 | 19.29 | 23.02 | 25.58 |
Claims (3)
1. toughness reinforcing Resins, epoxy of pyridine type polyoxyalkylene nonionic liquid, it is characterized in that, pyridine type polyoxyalkylene nonionic liquid is added in the epoxy prepolymer as toughner, and the mass ratio of described pyridine type polyoxyalkylene nonionic liquid and epoxy prepolymer is 20-60: 80-40;
The general structure of described pyridine type polyoxyalkylene nonionic liquid is:
Negatively charged ion X wherein
-Be Cl
-, Br
-, I
-, Al
2Cl
7 -, BF
4 -, PF
6 -, NO
3 -, NO
2 -, 8O
4 2-, CH
3COO
-, SbF
6 -, ZnCl
3 -, SnCl
3 -, N (CF
3SO
2)
-, N (C
2F
5SO
2)
-, N (FSO
2)
2 -, C (CF
3SO
2)
3 -, CF
3CO
2 -, CF
3SO
3 -Or CH
3SO
3 -
2. the preparation method of the toughness reinforcing Resins, epoxy of the described pyridine type polyoxyalkylene nonionic of claim 1 liquid is characterized in that operating according to the following steps:
Pyridine type polyoxyalkylene nonionic liquid is mixed with epoxy prepolymer, and 80 ℃ of stirring reactions 2 hours add solidifying agent then and stir, 120-160 ℃ solidified 5 hours finished product;
Described solidifying agent is a quadrol, and addition is 10% of a described epoxy prepolymer quality.
3. method according to claim 2 is characterized in that: described curing is to be incubated 1 hour down at 120 ℃, 140 ℃ of insulations 2 hours, is warming up to 160 ℃ of insulations 2 hours then.