CN102053035B - 混凝土工程实体强度快速推定方法 - Google Patents
混凝土工程实体强度快速推定方法 Download PDFInfo
- Publication number
- CN102053035B CN102053035B CN2010105789839A CN201010578983A CN102053035B CN 102053035 B CN102053035 B CN 102053035B CN 2010105789839 A CN2010105789839 A CN 2010105789839A CN 201010578983 A CN201010578983 A CN 201010578983A CN 102053035 B CN102053035 B CN 102053035B
- Authority
- CN
- China
- Prior art keywords
- temperature
- test block
- strength
- quick
- concrete
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明提出一种混凝土工程实体强度快速推定方法，包括以下步骤：（1）在拟快速推定的工程实体中，预埋测温仪。（2）按用于工程实体的混凝土配合比成型试块。（3）将试块放入养护箱中进行养护，所述养护箱的养护温度按照测温仪的实测值进行调整。（4）根据试块抗压强度的测量值，推定工程实体的抗压强度。通过本发明推定实体构件的抗压强度，可以缩短推定时间，且具有推定数据吻合度高的优点。
Description
技术领域
本发明涉及混凝土结构抗压强度的推定方法，特别涉及一种高准确性的混凝土工程实体强度快速推定方法。
背景技术
在建筑施工中进行混凝土灌注，需要知道所用的混凝土的抗压强度，通常要使用试块对混凝土的抗压强度进行测试，试块是指在混凝土浇注现场取样制作的试件。
目前，用来评价混凝土结构的实际强度主要是通过标准养护试块或者同条件养护试块的试压强度来间接推断。标准养护是指将试块置于20±2℃的环境下，待养护28天后测试试块的抗压强度。同条件养护是指将试块置于靠近实体结构的外部养护，由于同条件养护可以更真实地反映混凝土实体结构的环境温度，因而相对于标准养护，通过同条件养护试块推测的混凝土抗压强度具有更高的准确性。
但是上述这两种推定方法仍然存在一些缺陷：
1、由于试块与混凝土实体的几何尺寸不相同，通常试块要比实体结构的尺寸小很多，因而上述两种养护方法中试块的温升变化，均不能代表混凝土实体中的实际水化温升变化，因此试块与实体的抗压强度增加快慢也不相同，所以在标准养护或者同条件养护条件下测定的混凝土试块强度无法准确地代表混凝土结构的实际强度。
2、当今施工速度加快，若依据现今采用的28天的混凝土标准养护试块强度不足，再来调整混凝土配合比，工程已施工完毕多层，将造成很大损失。或者发现28天的混凝土标准养护试块强度偏高，也将造成较大的浪费。
发明内容
本发明的目的是提供一种混凝土工程实体强度快速推定方法，以解决现有的混凝土抗压强度推定方法测量不准确、时间过长的问题。
本发明提出一种混凝土工程实体强度快速推定方法，包括以下步骤：（1）在拟快速推定的工程实体中，预埋测温仪。（2）按用于工程实体的混凝土配合比成型试块。（3）将试块放入养护箱中进行养护，所述养护箱的养护温度按照测温仪的实测值进行调整。（4）根据试块抗压强度的测量值，推定工程实体的抗压强度。
优选的，所述的混凝土工程实体强度快速推定方法，测量试块的抗压强度具体为：在1天、2天、3天、5天、7天、9天、12天、14天的养护龄期测量试块的抗压强度。
优选的，所述的混凝土工程实体强度快速推定方法，还包括步骤：记录试块达到混凝土设计强度等级标准值时的时间。
优选的，所述的混凝土工程实体强度快速推定方法，所述测温仪测量的是工程实体构件中部的温度，且根据工程实体构件中部的实测温度进行养护的试块抗压强度，用于推定工程实体构件的最大抗压强度。
优选的，所述的混凝土工程实体强度快速推定方法，所述测温仪测量的是工程实体构件内距离构件边缘15cm处的温度，且根据工程实体构件内距离构件边缘15cm处的实测温度进行养护的试块抗压强度，用于推定工程实体构件的钻芯取样的强度。
优选的，所述的混凝土工程实体强度快速推定方法，按照每2小时实体实测的温度调整一次养护箱中的养护温度。
优选的，所述的混凝土工程实体强度快速推定方法，所述测温仪为无线测温仪。
优选的，所述的混凝土工程实体强度快速推定方法，所述养护箱采用《早期推定混凝土强度试验方法标准》JGJ/T15-2008中的规定的养护箱。
相对于现有技术，本发明的有益效果是：
1、本发明利用对工程实体构件内部的实测温度，来调整试块的养护温度，使试块的养护环境可以真实地反映实体构件内部的水化温升，从而更准确地推定出实体构件的抗压强度。
2、本发明采用定期且多次地对试块强度进行测量，不像传统推定方法那样要等到28天之后才进行测量，而通过试块的强度变化可以对混凝土实体构件的抗压强度有预估性，因此可以提早判断出实体强度不足或过大的情况，缩短了抗压强度的推定时间，也就减少了可能需要拆除的其它相关建筑，可以大大降低经济损失。
附图说明
图1为本发明混凝土工程实体强度快速推定方法实施例一的流程图；
图2为本发明混凝土工程实体强度快速推定方法实施例二的流程图。
具体实施方式
本发明的主要思想是根据对工程实体构件内部实际测量到的温度，来调整试块的养护温度，从而使试块的水化温升与实体构件的内部的水化温升一致，并使试块的抗压强度能更准确地反映工程实体构件的抗压强度。
以下结合附图，具体说明本发明。
实施例一
请参见图1，其为本发明混凝土工程实体强度快速推定方法实施例一的流程图：
S101，在拟快速推定的工程实体中，预埋测温仪，测量并记录工程实体构件中部的温度。记录温度测量值的频率可以根据实际需要来设定，本实施例优选的是按照2小时的频率记录温度数据。另外，为了便于布线，测温仪可以选用无线测温仪。
S102，按用于工程实体的混凝土配合比成型试块。
S103，将试块放入养护箱中进行养护，所述养护箱的养护温度按照测温仪的实测值进行调整。
其中，养护箱采用《早期推定混凝土强度试验方法标准》JGJ/T15-2008中的规定的养护箱，试块入箱时的温度应与工程实体构件或实体施工时混凝土入模实测温度相符。第一次调整温度的时间与被测试点的温度开始升高时的时间间隔相等。即如果测温仪是按照每2小时记录一次温度数据，则按照每2小时实体实测的温度调整一次养护温度，如果实体温度保持不变，则养护温度也保持不变，实体温度升高则调高养护温度，实体温度下降则调低养护温度。
S104，定期测量试块的抗压强度，并进行记录。
可以在1天、2天、3天、5天、7天、9天、12天、14天的养护龄期测量试块的抗压强度，并记录试块达到混凝土设计强度等级标准值时的时间。
S105，根据试块抗压强度的测量值，推定工程实体的最大抗压强度。
由于试块的养护温度是按照工程实体构件中部的实测温度进行实时调整的，因而试块的温升可以准确反映实体构件中部的水化温升，所以测量到的试块的抗压强度即为混凝土实体构件的最大抗压强度。
由于本发明在推定过程中是定期且多次对试块强度进行测量的，而不像传统推定方法那样要等到28天之后才进行测量，因而通过本发明的推定方法可以实时地观察试块的强度，从而通过试块的强度变化对混凝土实体构件的抗压强度有预估性。例如在5天时测得的试块强度远达不到规定的标准值，则可以考虑重建该实体构件，并调整混凝土的配比，这样就缩短了抗压强度的推定时间，也就减少了可能需要拆除的其它相关建筑，可以大大降低经济损失。
实施例二
请参见图2，其为本发明混凝土工程实体强度快速推定方法实施例二的流程图：
S201，在拟快速推定的工程实体中，预埋测温仪，测量并记录工程实体构件内距离构件边缘15cm处的温度。记录温度测量值的频率可以根据实际需要来设定，本实施例优选的是按照2小时的频率记录温度数据。另外，为了便于布线，测温仪可以选用无线测温仪。
S202，按用于工程实体的混凝土配合比成型试块。
S203，将试块放入养护箱中进行养护，所述养护箱的养护温度按照测温仪的实测值进行调整。
S204，定期测量试块的抗压强度，并进行记录。
S205，根据试块抗压强度的测量值，推定工程实体的钻芯取样的强度。
由于试块的养护温度是按照工程实体构件内距离构件边缘15cm处的实测温度进行实时调整的，因而试块的温升可以准确反映实体构件内距离构件边缘15cm处的水化温升，所以测量到的试块的抗压强度即为混凝土实体构件的钻芯取样的强度。
与实施例一相比，实施例二仅在测温仪对实体构件的测量部位上存在不同，实施例一测量的是实体构件中部的温度，因而通过实施例一的步骤可以推定出实体构件的最大抗压强度。实施例二测量的是实体构件内距离构件边缘15cm处的温度，因而通过实施例二的步骤可以推定出实体构件的钻芯取样强度。由于实体构件的最大强度和钻芯取样强度是两个较为重要的参数，因而单独以两个实施例来说明，但是本发明测温仪的测量位置并不仅限于此，在实际应用中可以根据实际需要来进行调整。
本发明通过对工程实体构件内部的实测温度，来调整试块的养护温度，使试块的养护环境可以更真实地反映出实体构件内部的水化温升，从而可以更准确地推定出实体构件的抗压强度。
以上公开的仅为本发明的几个具体实施例，但本发明并非局限于此，任何本领域的技术人员能思之的变化，都应落在本发明的保护范围内。
Claims (8)
1.一种混凝土工程实体强度快速推定方法，其特征在于，包括以下步骤：
在拟快速推定的工程实体中，预埋测温仪；
按用于工程实体的混凝土配合比成型试块；
将试块放入养护箱中进行养护，所述养护箱的养护温度按照测温仪的实测值进行调整；
根据试块抗压强度的测量值，推定工程实体的抗压强度。
2.如权利要求1所述的混凝土工程实体强度快速推定方法，其特征在于，测量试块的抗压强度具体为：
在1天、2天、3天、5天、7天、9天、12天、14天的养护龄期测量试块的抗压强度。
3.如权利要求1所述的混凝土工程实体强度快速推定方法，其特征在于，还包括步骤：
记录试块达到混凝土设计强度等级标准值时的时间。
4.如权利要求1所述的混凝土工程实体强度快速推定方法，其特征在于，所述测温仪测量的是工程实体构件中部的温度，且根据工程实体构件中部的实测温度进行养护的试块抗压强度，用于推定工程实体构件的最大抗压强度。
5.如权利要求1所述的混凝土工程实体强度快速推定方法，其特征在于，所述测温仪测量的是工程实体构件内距离构件边缘15cm处的温度，且根据工程实体构件内距离构件边缘15cm处的实测温度进行养护的试块抗压强度，用于推定工程实体构件的钻芯取样的强度。
6.如权利要求1所述的混凝土工程实体强度快速推定方法，其特征在于，按照每2小时实体实测的温度调整一次养护箱中的养护温度。
7.如权利要求1所述的混凝土工程实体强度快速推定方法，其特征在于，所述测温仪为无线测温仪。
8.如权利要求1所述的混凝土工程实体强度快速推定方法，其特征在于，所述养护箱采用《早期推定混凝土强度试验方法标准》JGJ/T15-2008中的规定的养护箱。