Summary of the invention
The object of the present invention is to provide a kind of exterior coating with compound fast light and toner composition, remedy above-mentioned defective to overcome.
Exterior coating of the present invention comprises the component of following weight part with compound fast light and toner composition:
50 parts in water
1~3 part of polyoxyethylene nonylphenol ether
10~15 parts of nanometer titanium dioxides
8~12 parts of polyvinylpyrrolidones
0.1~0.3 part of sodium butylnaphthalenesulfonate
30~50 parts of ethanol
0.3~0.6 part of silane coupling agent
4~8 parts of two triazine amino-stilbenes
4,4 '-1~3 part in two (diphenylamino-trans-styryl) biphenyl
Salicylic acid is to 1~3 part of tertiary butyl phenyl ester
1~3 part in 1-oxygen base-2.2.6.6-tetramethyl piperidine
The particle diameter of nanometer titanium dioxide is 50~80 nanometers, and preferably rutile-type is selected abundant Xinghua, Shandong chemical product for use.
Silane coupling agent preferred vinyl triethoxyl silane;
The polyvinylpyrrolidone weight-average molecular weight is 3000~6000;
Two triazine amino-stilbenes can adopt the product of Kingsoft, Shanghai longitude and latitude chemical industry company limited trade mark for " 31# white dyes ";
4.4-two (diphenylamino-trans styryl) can adopt Jiangxi Province's Xinhua's chemical plant trade mark of recommending properly qualified persons for service to be the product of " XPS2 white dyes ";
It is the product of CAS:768-66-1 that 1-oxygen base-2.2.6.6-tetramethyl piperidine adopts the Quzhou newly to rise chemical industry company limited model.
The preparation method comprises the steps:
(1) under the normal temperature, nanometer titanium dioxide and polyoxyethylene nonylphenol ether are added to the water, dispersed with stirring 20~40 minutes adds polyvinylpyrrolidone, is warming up to 40~50 ℃, adds sodium butylnaphthalenesulfonate again;
(2) with two triazine amino-stilbenes, 4,4 '-two (diphenylamino-trans styryl) biphenyl and silane coupling agent, be dissolved in the ethanol, add salicylic acid again to tertiary butyl phenyl ester and 1-oxygen base-2.2.6.6-tetramethyl piperidine;
(3) (2) are joined in (1), be warming up to 60~70 ℃, be incubated 1~3 hour, can obtain product.
Exterior coating of the present invention can make an addition in the general exterior coating with compound fast light and toner composition, and adding weight is 1~3%.
Exterior coating of the present invention is with compound fast light and toner composition, utilize UV light absorber ultraviolet powerful absorption and hindered amine as light stabilizer to be caught the synergistic effect of free radical and multiple functions such as hydroperoxide decomposition and quencher singlet oxygen, choke suppress the coating surface layer may take place oxidation, chain rupture, degraded, etc. series of chemical, the Degradation of the aging and polymkeric substance of the coatingsurface that slowed down, titanium dioxide has improved the corrosion-resistant and wear resistance of opacifying power, reducing power of filming, strengthen the mechanical strength of filming, prolonged the life-span of coating.Whitening agent can absorb sightless UV-light simultaneously, be converted to long blue light of wavelength or the visible light of purple, thereby can compensate undesired little yellow in the matrix, reflect simultaneously than the more visible light of original incident wavelength scope, thereby make coatingsurface seem whiter, brighter, more bright-coloured.
Embodiment
Embodiment 1
4 parts of 50 parts of deionized waters, 1 part of polyoxyethylene nonylphenol ether, 10 parts of 50 nano rutile-type titanium dioxides, 8 parts of polyvinylpyrrolidones (molecular weight is 3000), 0.1 part of sodium butylnaphthalenesulfonate, 30 parts of dehydrated alcohols, 0.3 part of silane coupling agent, two triazine amino-stilbene, 4,4 '-two (diphenylamino-trans styryl) 3 parts in biphenyl, salicylic acid is to 3 parts of tertiary butyl phenyl esters.1 part in 1-oxygen base-2.2.6.6-tetramethyl piperidine.
Preparation method: under (1) normal temperature nanometer titanium dioxide is joined in the deionized water, add polyoxyethylene nonylphenol ether then, stirred 30 minutes with dispersion machine (2000 rev/mins), add polyvinylpyrrolidone, progressively be warming up to about 45 ℃, after treating that polyvinylpyrrolidone fully dissolves, add sodium butylnaphthalenesulfonate; (2) with two triazine amino-stilbenes and 4,4 '-two (diphenylamino-trans styryl) biphenyl, silane coupling agent successively are dissolved in the dehydrated alcohol, make it abundant dissolving, add salicylic acid again tertiary butyl phenyl ester and 1-oxygen base-2.2.6.6-tetramethyl piperidine.(3) (2) are joined in (1), and be warming up to 60 ℃, be incubated 2 hours.
Embodiment 2
8 parts of 50 parts of deionized waters, 3 parts of polyoxyethylene nonylphenol ethers, 15 parts of 80 nano rutile-type titanium dioxides, 12 parts of polyvinylpyrrolidones (molecular weight is 6000), 0.3 part of sodium butylnaphthalenesulfonate, 50 parts of dehydrated alcohols, 0.6 part of silane coupling agent, two triazine amino-stilbene, 4,4 '-two (diphenylamino-trans styryl) 1 part in biphenyl, salicylic acid is to 1 part of tertiary butyl phenyl ester.3 parts in 1-oxygen base-2.2.6.6-tetramethyl piperidine.
Preparation method: under (1) normal temperature nanometer titanium dioxide is joined in the deionized water, add polyoxyethylene nonylphenol ether then, stirred 30 minutes with dispersion machine (2000 rev/mins), add polyvinylpyrrolidone, progressively be warming up to about 45 ℃, after treating that polyvinylpyrrolidone fully dissolves, add sodium butylnaphthalenesulfonate; (2) with two triazine amino-stilbenes and 4,4 '-two (diphenylamino-trans styryl) biphenyl, silane coupling agent successively are dissolved in the dehydrated alcohol, make it abundant dissolving, add salicylic acid again tertiary butyl phenyl ester and 1-oxygen base-2.2.6.6-tetramethyl piperidine.(3) (2) are joined in (1), and be warming up to 70 ℃, be incubated 2 hours.
Embodiment 3
5 parts of 50 parts of deionized waters, 2 parts of polyoxyethylene nonylphenol ethers, 12 parts of 70 nano rutile-type titanium dioxides, 9 parts of polyvinylpyrrolidones (molecular weight is 4000), 0.15 part of sodium butylnaphthalenesulfonate, 40 parts of dehydrated alcohols, 0.4 part of silane coupling agent, two triazine amino-stilbene, 4,4 '-two (diphenylamino-trans styryl) 2 parts in biphenyl, salicylic acid is to 2 parts of tertiary butyl phenyl esters.2 parts in 1-oxygen base-2.2.6.6-tetramethyl piperidine.
Preparation method: under (1) normal temperature nanometer titanium dioxide is joined deionized water, add polyoxyethylene nonylphenol ether then, stirred 30 minutes with high speed dispersor (2000 rev/mins), add polyvinylpyrrolidone, progressively be warming up to about 45 ℃, after treating that polyvinylpyrrolidone fully dissolves, add sodium butylnaphthalenesulfonate; (2) with two triazine amino-stilbenes and 4,4 '-two (diphenylamino-trans styryl) biphenyl, silane coupling agent successively are dissolved in the dehydrated alcohol, make it abundant dissolving, add salicylic acid again tertiary butyl phenyl ester and 1-oxygen base-2.2.6.6-tetramethyl piperidine.(3) (2) are joined in (1), and be warming up to 65 ℃, be incubated 2 hours.
Embodiment 4
6 parts of 50 parts of deionized waters, 1.5 parts of polyoxyethylene nonylphenol ethers, 13 parts of 60 nano rutile-type titanium dioxides, 11 parts of polyvinylpyrrolidones (molecular weight is 5000), 0.25 part of sodium butylnaphthalenesulfonate, 45 parts of dehydrated alcohols, 0.5 part of silane coupling agent, two triazine amino-stilbene, 4,4 '-two (diphenylamino-trans styryl) 1.5 parts in biphenyl, salicylic acid is to 1.5 parts of tertiary butyl phenyl esters.1.5 parts in 1-oxygen base-2.2.6.6-tetramethyl piperidine.
Preparation method: under (1) normal temperature nanometer titanium dioxide is joined in the deionized water, add polyoxyethylene nonylphenol ether then, stirred 30 minutes with high speed dispersor (2000 rev/mins), add polyvinylpyrrolidone, progressively be warming up to about 45 ℃, after treating that polyvinylpyrrolidone fully dissolves, add sodium butylnaphthalenesulfonate; (2) with two triazine amino-stilbenes and 4,4 '-two (diphenylamino-trans styryl) biphenyl, silane coupling agent successively are dissolved in the dehydrated alcohol, make it abundant dissolving, add salicylic acid again tertiary butyl phenyl ester and 1-oxygen base-2.2.6.6-tetramethyl piperidine.(3) (2) are joined in (1), and be warming up to 67 ℃, be incubated 2 hours.
Embodiment 5
7 parts of 50 parts of deionized waters, 2.5 parts of polyoxyethylene nonylphenol ethers, 11 parts of 80 nano rutile-type titanium dioxides, 7 parts of polyvinylpyrrolidones (molecular weight is 5000), 0.2 part of sodium butylnaphthalenesulfonate, 35 parts of dehydrated alcohols, 0.4 part of silane coupling agent, two triazine amino-stilbene, 4,4 '-two (diphenylamino-trans styryl) 2.5 parts in biphenyl, salicylic acid is to 2.5 parts of 2.5 parts of tertiary butyl phenyl esters, 1-oxygen base-2.2.6.6-tetramethyl piperidine.
Preparation method: under (1) normal temperature nanometer titanium dioxide is joined in the deionized water, add polyoxyethylene nonylphenol ether then, stirred 30 minutes with high speed dispersor (2000 rev/mins), add polyvinylpyrrolidone, progressively be warming up to about 45 ℃, after treating that polyvinylpyrrolidone fully dissolves, add sodium butylnaphthalenesulfonate; (2) with two triazine amino-stilbenes and 4,4 '-two (diphenylamino-trans styryl) biphenyl, silane coupling agent successively are dissolved in the dehydrated alcohol, make it abundant dissolving, add salicylic acid again tertiary butyl phenyl ester and 1-oxygen base-2.2.6.6-tetramethyl piperidine.(3) (2) are joined in (1), and be warming up to 62 ℃, be incubated 2 hours.
Embodiment 6
8 parts of 50 parts of deionized waters, 2 parts of polyoxyethylene nonylphenol ethers, 14 parts of 50 nano rutile-type titanium dioxides, 8 parts of polyvinylpyrrolidones (molecular weight is 3000), 0.2 part in sodium butylnaphthalenesulfonate powder, 40 parts of dehydrated alcohols, 0.4 part of silane coupling agent, V.B.L whitening agent, 4,4 '-two (diphenylamino-trans styryl) 2. parts in biphenyl, salicylic acid is to 2.5 parts of 2. parts of tertiary butyl phenyl esters, 1-oxygen base-2.2.6.6-tetramethyl piperidine.
Preparation method: under (1) normal temperature nanometer titanium dioxide is joined in the deionized water, add polyoxyethylene nonylphenol ether then, stirred 30 minutes with high speed dispersor (2000 rev/mins), add polyvinylpyrrolidone, progressively be warming up to about 45 ℃, after treating that polyvinylpyrrolidone fully dissolves, add sodium butylnaphthalenesulfonate; (2) with two triazine amino-stilbenes and 4,4 '-two (diphenylamino-trans styryl) biphenyl, silane coupling agent successively are dissolved in the dehydrated alcohol, make it abundant dissolving, add salicylic acid again tertiary butyl phenyl ester and 1-oxygen base-2.2.6.6-tetramethyl piperidine.
(3) (2) are joined in (1), and be warming up to 65 ℃, be incubated 2 hours.
Embodiment 7
One, select for use commercially available exterior coating to carry out application test relatively, in coating, add 2% and of the present inventionly compoundly fast lightly compare test, with reference to regulation and the method for standard GB/T14522-2008, GB/T 9755-2001, GB/T 9266-2009 with toner composition and former coating; Determining instrument: XT-48B measuring brightness instrument, the full-automatic density instrument of MDMDY-300 type.
White exterior coating: the Shanghai proud waterproofing and leakage-stopping of perseverance Engineering Co., Ltd product; MDMDY-3
Sky-blue exterior coating: the prosperous sunshine building external paint construction in Shanghai company limited product;
Light green exterior coating: Jiande City beauty's coating factory product;
Light yellow exterior coating: Baiyun District, Guangzhou City Mt Japan ippon coating factory product;
The contrast sample is not for adding the exterior coating of compound fast light and toner composition of the present invention.
Test result:
Show that from test result the present invention compound fast light and toner composition have extraordinary fast light and hyperchromic effect after joining exterior coating, do not add and of the present inventionly compoundly fast lightly the photoaging reaction all occurs with the exterior coating toner composition.