A kind of antibacterial and deodouring hand weaving blended knitting wool
Technical field
The present invention relates to a kind of knitting wool, particularly a kind of antibacterial and deodouring hand weaving blended knitting wool.
Background technology
Hand-knitting wool, be commonly called as knitting wool, fluffy, soft, the plentiful chubbiness of its form, high resilience, extensively in order to multiple haberdasheries such as weaving woolen sweater, scarf, gloves, the clothes of being made by hand-knitting wool have good, the comfortable good wearability such as next to the shin of soft front cover, warmth retention property and hygroscopicity.
At present the animal suede that is adopted in the hand-knitting wool has many types, for example cashmere, rabbit suede, camel's hair etc., but the scratchy and felting that the scale on cashmere fiber surface causes is its inherent shortcoming; Rabbit suede and camel's hair are little because of its initial modulus, at the bottom of fibre cohesion and the intensity, when content was big, the brute force of yarn was unfavorable for smooth braiding, and easily pilling, fall hair.Simultaneously because the made clothing of hand-knitting wool mostly is the warming clothing of wearing autumn and winter, so its cleaning frequency also than summer clothing long, therefore, there are hygienic issues such as flora exceeds standard, peculiar smell in the clothing of being made by hand-knitting wool more, simultaneously, owing to air drying autumn and winter, also there is electrostatic problem in the hand-knitting wool fabric, and the problems referred to above have all influenced the level of comfort of dress.
Summary of the invention
The objective of the invention is to overcome above-mentioned defective of the prior art, provide a kind of and have good antibiosis and deodorization effects, and wear warming comfortable antibacterial and deodouring hand weaving blended knitting wool.
To achieve these goals, antibacterial and deodouring hand weaving blended knitting wool of the present invention has following formation:
A kind of antibacterial and deodouring hand weaving blended knitting wool; it is by fox suede; ermine suede; the sex change ramee; the polyacrylonitrile fibre blending forms; the ratio that each constituent mass accounts for the blended knitting wool gross mass is fox suede 20.5-29.7%; ermine suede 26.6-32.6%; sex change ramie 10-14.2%; polyacrylonitrile fibre 2533.7%; wherein be evenly distributed with nano active charcoal particle in this polyacrylonitrile fibre; nano active charcoal granular mass accounts for the 11.2-22.3% of polyacrylonitrile fibre quality; the average grain diameter of above-mentioned nano active carbon granule is the 500-520 nanometer and ratio≤2.9 of particle diameter and the particle diameter of smallest particles of the largest particles wherein; or adopt another nano active carbon granule: its average grain diameter is the 50-80 nanometer and ratio≤3.2 of particle diameter and the particle diameter of smallest particles of the largest particles wherein; in addition; the part of above-mentioned polyacrylonitrile fibre is through silver-plated processing; its silver-plated mode is an ion plating method; wherein account for the 55-75% of polyacrylonitrile fibre total amount through the polyacrylonitrile fibre of silver-plated processing; polyacrylonitrile fibre adopts nitrogen or argon shield in the silver-plated process, and vacuum is 8.5-9.1 * 10
-5Pa.
Hand-knitting wool among the present invention, owing to contain nano active carbon in the polyacrylonitrile fibre that contains in this knitting wool, because active carbon has the good adsorption performance, so this knitting wool has good deodorization functions, simultaneously, because silver ion has good antibacterial bacteriostatic performance, and the polyacrylonitrile that knitting wool contained among the present invention adopts electroplate to handle, making human body obtain the direct of maximum area with silver contacts, thereby not only make knitting wool itself have good antibacterial performance, also can help skin to avoid the invasion and attack of bacterium, suppress growing of bacterium, thereby reach antibacterial bacteriostatic, beautify the effect of skin, silver itself also belongs to metallics, thus also have certain conducting function, on using, also can play certain anti-static electrification, because ramee itself has the antibacterial bacteriostatic feature, therefore, add the antibacterial bacteriostatic effect that ramee has also further promoted knitting wool among the present invention simultaneously.
The specific embodiment
Embodiment 1:
A kind of antibacterial and deodouring hand weaving blended knitting wool; it is by fox suede; ermine suede; the sex change ramee; the polyacrylonitrile fibre blending forms; the ratio that each constituent mass accounts for the blended knitting wool gross mass is a fox suede 20.5%; ermine suede 32.6%; sex change ramie 14.2%; polyacrylonitrile fibre 32.7%; wherein be evenly distributed with nano active charcoal particle in this polyacrylonitrile fibre; nano active charcoal granular mass accounts for 11.2% of polyacrylonitrile fibre quality; the average grain diameter of the nano active carbon that the specification of nano active carbon granule is is the 500-520 nanometer and ratio≤2.9 of particle diameter and the particle diameter of smallest particles of the largest particles wherein; in addition; a part is through silver-plated processing in the above-mentioned polyacrylonitrile fibre that contains nano active carbon; its silver-plated mode is an ion plating method; wherein the polyacrylonitrile fibre through silver-plated processing accounts for 55% of polyacrylonitrile fibre total amount; polyacrylonitrile fibre adopts nitrogen or argon shield in the silver-plated process, and vacuum is 8.5 * 10
-5Pa.
Embodiment 2
A kind of antibacterial and deodouring hand weaving blended knitting wool; it is by fox suede; ermine suede; the sex change ramee; the polyacrylonitrile fibre blending forms; the ratio that each constituent mass accounts for the blended knitting wool gross mass is a fox suede 29.7%; ermine suede 26.6%; sex change ramie 10%; polyacrylonitrile fibre 33.7%; wherein be evenly distributed with nano active charcoal particle in this polyacrylonitrile fibre; nano active charcoal granular mass accounts for 22.3% of polyacrylonitrile fibre quality; the average grain diameter of the nano active carbon that the specification of nano active carbon granule is is the 50-80 nanometer and ratio≤3.2 of particle diameter and the particle diameter of smallest particles of the largest particles wherein; in addition; a part is through silver-plated processing in the above-mentioned polyacrylonitrile fibre that contains nano active carbon; its silver-plated mode is an ion plating method; wherein the polyacrylonitrile fibre through silver-plated processing accounts for 75% of polyacrylonitrile fibre total amount; polyacrylonitrile fibre adopts nitrogen or argon shield in the silver-plated process, and vacuum is 9.1 * 10
-5Pa.
Embodiment 3
A kind of antibacterial and deodouring hand weaving blended knitting wool; it is by fox suede; ermine suede; the sex change ramee; the polyacrylonitrile fibre blending forms; the ratio that each constituent mass accounts for the blended knitting wool gross mass is a fox suede 29.5%; ermine suede 32.5%; sex change ramie 13%; polyacrylonitrile fibre 25%; wherein be evenly distributed with nano active charcoal particle in this polyacrylonitrile fibre; nano active charcoal granular mass accounts for 16.1% of polyacrylonitrile fibre quality; the average grain diameter of the nano active carbon that the specification of nano active carbon granule is is the 50-80 nanometer and ratio≤3.2 of particle diameter and the particle diameter of smallest particles of the largest particles wherein; in addition; a part is through silver-plated processing in the above-mentioned polyacrylonitrile fibre that contains nano active carbon; its silver-plated mode is an ion plating method; wherein the polyacrylonitrile fibre through silver-plated processing accounts for 65% of polyacrylonitrile fibre total amount; polyacrylonitrile fibre adopts nitrogen or argon shield in the silver-plated process, and vacuum is 8.7 * 10
-5Pa.
Protection scope of the present invention is not limited to the above embodiments, and obviously, those skilled in the art can carry out various changes and distortion and do not depart from the scope of the present invention and spirit the present invention.If these changes and distortion belong in the scope of claim of the present invention and equivalent technologies thereof, then the intent of the present invention also comprises these changes and is out of shape interior.