CN102020857A - Reusable whiteboard wax easy to erase and preparation method thereof - Google Patents
Reusable whiteboard wax easy to erase and preparation method thereof Download PDFInfo
- Publication number
- CN102020857A CN102020857A CN 201010608345 CN201010608345A CN102020857A CN 102020857 A CN102020857 A CN 102020857A CN 201010608345 CN201010608345 CN 201010608345 CN 201010608345 A CN201010608345 A CN 201010608345A CN 102020857 A CN102020857 A CN 102020857A
- Authority
- CN
- China
- Prior art keywords
- wax
- paraffin
- reusable
- water
- setting adhesive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a reusable whiteboard wax easy to erase and a preparation method thereof. The reusable whiteboard wax comprises the components in percentage by weight: 50-85 percent of paraffin, 7-33 percent of paraffin emulsifier, 5-10 percent of water and 3-8 percent of non-drying glue. The preparation method comprises the steps of: heating to melt the paraffin, then mixing the molten paraffin with the non-drying glue diluted with water, and then adding the paraffin emulsifier for emulsification to obtain the reusable whiteboard wax. The whiteboard wax is reusable and has good effect, and the preparation method has the advantages of simple operation process, wide raw material source range and low cost.
Description
Technical field
The invention belongs to wax and preparation field thereof, particularly a kind of reusable easy erasable letter stencil wax and preparation method thereof.
Background technology
Wax, the crude substance that former finger is obtained from honeycomb, i.e. beeswax.In materials such as plant and mineral, find similar material afterwards, also all be called wax.In a broad sense, wax is normally referring under certain normal temperature that plant, animal or mineral etc. are produced to be liquefaction or the gasification easily of solid, heating back, burning easily, water insoluble, material with certain lubrication.Wax is distributed in occurring in nature widely, can be divided into insect wax, animal wax, vegetable wax, mineral wax, synthetic wax and wax, and the purposes of wax is also quite extensive.
Common wax surface cure, existing Wax special surface toughness can be reused.
Summary of the invention
Technical problem to be solved by this invention provides a kind of reusable easy erasable letter stencil wax and preparation method thereof.Board wax economy and durability of the present invention, reusable, and safety and Health; This preparation method is simple, and raw material sources are extensive, and cost is low, and technological operation is simple.
A kind of reusable easy erasable letter stencil wax of the present invention, its weight percent component comprises: paraffin 50-85%, paraffin emulsifier 7-33%, water 5-10%, non-setting adhesive 3-8%.
The weight percent of above-mentioned board wax consists of paraffin 60-70%, paraffin emulsifier 15-25%, water 6-9%, non-setting adhesive 4-7%.
The weight percent of above-mentioned board wax consists of paraffin 50%, paraffin emulsifier 33%, water 10%, non-setting adhesive 7%.
The weight percent of above-mentioned board wax consists of paraffin 65%, paraffin emulsifier 17%, water 10%, non-setting adhesive 8%.
The weight percent of above-mentioned board wax consists of paraffin 85%, paraffin emulsifier 7%, water 5%, non-setting adhesive 3%.
The weight percent of above-mentioned board wax consists of paraffin 75%, paraffin emulsifier 15%, water 5%, non-setting adhesive 5%.
The preparation method of a kind of reusable easy erasable letter stencil wax of the present invention comprises: with heating paraffin fusing, then it is mixed with non-setting adhesive behind the thin up, add emulsifying agent again and carry out emulsification, promptly get board wax.
Wax after the emulsification is the milk shape, is oyster white, but dry back is transparent.
The using method of a kind of reusable easy erasable letter stencil wax of the present invention is: board wax of the present invention is coated on the printing surface of board, encloses film again, get final product.
Use the board of board wax of the present invention, can scribble arbitrarily at its film surface, reusable after the wiping, and can keep very good effect.
Beneficial effect
1, board wax economy and durability of the present invention is reusable, and safety and Health.
2, preparation method of the present invention is simple, and raw material sources are extensive, and cost is low, and technological operation is simple.
3, use the board of board wax of the present invention, can scribble arbitrarily at its film surface, reusable after the wiping, and can keep very good effect, have a extensive future.
Embodiment
Below in conjunction with specific embodiment, further set forth the present invention.Should be understood that these embodiment only to be used to the present invention is described and be not used in and limit the scope of the invention.Should be understood that in addition those skilled in the art can make various changes or modifications the present invention after the content of having read the present invention's instruction, these equivalent form of values fall within the application's appended claims institute restricted portion equally.
Embodiment 1
With 50% weight ratio heating paraffin fusing, the water of 10% weight ratio is joined in the non-setting adhesive of 7% weight ratio, the non-setting adhesive mixing after paraffin after will melt then and the dilution, the paraffin emulsifier that adds 33% weight ratio again carries out emulsification, promptly.Wax after the emulsification is the milk shape, is oyster white, but dry back is transparent.This board wax wax is coated on the printing surface of board, encloses film again, can be reusable after film surface is scribbled wiping arbitrarily.
Embodiment 2
With 65% weight ratio heating paraffin fusing, the water of 10% weight ratio is joined in the non-setting adhesive of 8% weight ratio, the non-setting adhesive mixing after paraffin after will melt then and the dilution, the paraffin emulsifier that adds 17% weight ratio again carries out emulsification, promptly.Wax after the emulsification is the milk shape, is oyster white, but dry back is transparent.This board wax wax is coated on the printing surface of board, encloses film again, can be reusable after film surface is scribbled wiping arbitrarily.
Embodiment 3
With 85% weight ratio heating paraffin fusing, the water of 5% weight ratio is joined in the non-setting adhesive of 3% weight ratio, the non-setting adhesive mixing after paraffin after will melt then and the dilution, the paraffin emulsifier that adds 7% weight ratio again carries out emulsification, promptly.Wax after the emulsification is the milk shape, is oyster white, but dry back is transparent.This board wax wax is coated on the printing surface of board, encloses film again, can be reusable after film surface is scribbled wiping arbitrarily.
Embodiment 4
With 75% weight ratio heating paraffin fusing, the water of 5% weight ratio is joined in the non-setting adhesive of 5% weight ratio, the non-setting adhesive mixing after paraffin after will melt then and the dilution, the paraffin emulsifier that adds 15% weight ratio again carries out emulsification, promptly.Wax after the emulsification is the milk shape, is oyster white, but dry back is transparent.This board wax wax is coated on the printing surface of board, encloses film again, can be reusable after film surface is scribbled wiping arbitrarily.
Claims (7)
1. reusable easy erasable letter stencil wax, its weight percent component comprises: paraffin 50-85%, paraffin emulsifier 7-33%, water 5-10%, non-setting adhesive 3-8%.
2. a kind of reusable easy erasable letter stencil wax according to claim 1, it is characterized in that: the weight percent of described board wax consists of paraffin 60-70%, paraffin emulsifier 15-25%, water 6-9%, non-setting adhesive 4-7%.
3. a kind of reusable easy erasable letter stencil wax according to claim 1, it is characterized in that: the weight percent of described board wax consists of paraffin 50%, paraffin emulsifier 33%, water 10%, non-setting adhesive 7%.
4. a kind of reusable easy erasable letter stencil wax according to claim 1, it is characterized in that: the weight percent of described board wax consists of paraffin 65%, paraffin emulsifier 17%, water 10%, non-setting adhesive 8%.
5. a kind of reusable easy erasable letter stencil wax according to claim 1, it is characterized in that: the weight percent of described board wax consists of paraffin 85%, paraffin emulsifier 7%, water 5%, non-setting adhesive 3%.
6. a kind of reusable easy erasable letter stencil wax according to claim 1, it is characterized in that: the weight percent of described board wax consists of paraffin 75%, paraffin emulsifier 15%, water 5%, non-setting adhesive 5%.
7. the preparation method of a reusable easy erasable letter stencil wax comprises: with the heating paraffin fusing, then it is mixed with non-setting adhesive behind the thin up, add paraffin emulsifier again and carry out emulsification, promptly get board wax.