CN102002549A - Dry deslagging method of soaking pit - Google Patents

Dry deslagging method of soaking pit Download PDF

Info

Publication number
CN102002549A
CN102002549A CN 201010577624 CN201010577624A CN102002549A CN 102002549 A CN102002549 A CN 102002549A CN 201010577624 CN201010577624 CN 201010577624 CN 201010577624 A CN201010577624 A CN 201010577624A CN 102002549 A CN102002549 A CN 102002549A
Authority
CN
China
Prior art keywords
soaking pit
serpentine
content
slag
tapping
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 201010577624
Other languages
Chinese (zh)
Inventor
边仲元
朱玖栓
薛坤
王郁葱
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanxi Taigang Stainless Steel Co Ltd
Original Assignee
Shanxi Taigang Stainless Steel Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanxi Taigang Stainless Steel Co Ltd filed Critical Shanxi Taigang Stainless Steel Co Ltd
Priority to CN 201010577624 priority Critical patent/CN102002549A/en
Publication of CN102002549A publication Critical patent/CN102002549A/en
Pending legal-status Critical Current

Abstract

The invention relates to a dry deslagging method of a soaking pit, belonging to the steelmaking field. The dry deslagging method of the soaking pit is characterized by comprising the steps of: evenly laying a serpentine isolated layer with a thickness of 180-250mm on the bottom of the soaking pit, wherein the content of MgO of the serpentine is 35-50%, the content of SiO2 is 37-42%, the content of Sigma Fe is less than or equal to 10%, the content of CaO is less than 1%, the loss on ignition is 0.5-6%, the refractoriness is 1520 DEG C, the compression strength is 2.0-3.0mpa, the volume density is 2.35-2.42g/cm<3>, and the particle size is 40-70mm; evenly stirring the steel slag and the serpentine for 10 minutes per tapping of 12-15 heat; and deslagging for 30-50 minutes per tapping of 30-35 heat. The dry deslagging method of the soaking pit can shorten the steel-free empty burn heating high-temperature time, enhance the turnover rate of the soaking pit, and lower the consumption of gas.

Description

A kind of soaking pit is done the slag method
Technical field:
The invention belongs to field of steel-making, be specifically related to a kind of soaking pit and do the slag method.
Background technology:
At present, the mode of slagging tap of soaking pit adopts liquid to slag tap, i.e. after soaking pit tapping finished, empty stove temperature raising 1 hour to 1450 ℃ was incubated one and a half hours, scrapes slag half an hour, and always the time of slagging tap is 3 hours.This mode gas consumption of slagging tap is bigger, and energy dissipation is serious, and furnace campaign shortens, the pollution of environment, and staff's labour intensity is big.
Summary of the invention:
The present invention aims to provide save energy, and a kind of soaking pit simple to operate is done the slag method.Go out slag operation by the soaking crab crane instrument of slagging tap of slinging that collapses, finish the whole technology of slagging tap.
A kind of soaking pit is done the slag method, it is characterized in that at the even laying depth of furnace bottom be 180-250mm serpentine sealing coat, and the MgO content of serpentine is 35-50%, SiO 2Content is 37-42%, ∑ Fe≤10%, and CaO content<1%, igloss is 0.5-6%, and refractoriness is 1520 ℃, and compressive strength is 2.0-3.0mpa, and volume density is 2.35-2.42g/cm 3, granularity is 40-70mm; Every tapping 12-15 stove carries out 10 minutes even stirring to slag and serpentine; Slag tap behind every tapping 30-35 stove, the time of slagging tap is 30-50 minute.
The empty stove of the present invention does not need temperature raising, stirs once every 6 days, needs ten minutes at every turn, does slag (because of the working of a furnace is decided) after every soaking pit stirred five times in every month.The present invention can shorten empty burning of no steel and heat high-temperature time, raising stove turnover rate, and reduces gas consumption.Utilize the no steel sky of saving to burn heat-up time, can correspondingly increase soaking pit output, reduce tapping temperature, reduce thermopair damage, improve stove refractory materials behaviour in service, avoid peeling off of furnace wall refractory concrete, furnace campaign is prolonged, and reduced stocking unit operation ton steel energy consumption index, reduced generation and the discharging of carbon monoxide, oxynitride simultaneously, reduced and pollute.
The economical, societal benefits of its creation are at current price calculated:
Every hole is annual saves heat-up time: 144 hours; The annual coal gas of saving in every hole: 10.28 ten thousand yuan; The annual serpentine cost that adopts in every hole: 3.456 ten thousand; Can reduce expenses every year in every hole: 6.824 ten thousand yuan; If all be used for producing in 144 hours of 1 soaking pit saving, every stove burns the steel time and calculated by six hours, and soaking pit can have more steel: 1440 tons in 24 stoves; Can increase production wound imitates: 48.96 ten thousand yuan.
Compare with the liquid technology of slagging tap, do every annual total creation of value of stove behind the slag: 55.784 ten thousand yuan.
Embodiment:
Embodiment: 1, the even laying depth of furnace bottom is a 180-250mm serpentine sealing coat, and attention will prevent that furnace bottom shop sealing coat from leaking the shop phenomenon.
2, every tapping 12-15 stove carries out stirring about 10 minutes to slag and serpentine, need stir loosening furnace bottom slag.
3, slag tap behind every tapping 30-35 stove.When slagging tap, empty stove does not need temperature raising, and the time of slagging tap is 30-50 minute.
The MgO content of described serpentine is 35-50%, SiO 2Content is 37-42%, ∑ Fe≤10%, and CaO content<1%, igloss is 0.5-6%, and refractoriness is 1520 ℃, and compressive strength is 2.0-3.0mpa, and volume density is 2.35-2.42g/cm 3, granularity is 40-70mm.

Claims (1)

1. a soaking pit is done the slag method, it is characterized in that at the even laying depth of furnace bottom be 180-250mm serpentine sealing coat, and the MgO content of serpentine is 35-50%, SiO 2Content is 37-42%, ∑ Fe≤10, and CaO content<1%, igloss is 0.5-6%, and refractoriness is 1520 ℃, and compressive strength is 2.0-3.0mpa, and volume density is 2.35-2.42g/cm 3, granularity is 40-70mm; Every tapping 12-15 stove carries out 10 minutes even stirring to slag and serpentine; Slag tap behind every tapping 30-35 stove, the time of slagging tap is 30-50 minute.
CN 201010577624 2010-12-04 2010-12-04 Dry deslagging method of soaking pit Pending CN102002549A (en)