CN102002183B - Polypropylene-modified sound insulation material and preparation method thereof - Google Patents
Polypropylene-modified sound insulation material and preparation method thereof Download PDFInfo
- Publication number
- CN102002183B CN102002183B CN2010102989481A CN201010298948A CN102002183B CN 102002183 B CN102002183 B CN 102002183B CN 2010102989481 A CN2010102989481 A CN 2010102989481A CN 201010298948 A CN201010298948 A CN 201010298948A CN 102002183 B CN102002183 B CN 102002183B
- Authority
- CN
- China
- Prior art keywords
- screw extruder
- twin screw
- polypropylene
- preparation
- coupling agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention provides a polypropylene-modified sound insulation material, which consists of the following components in percentage by mass: 10 to 85 percent of polypropylene; 10 to 70 percent of barium sulfate; 4 to 20 percent of glass fibres; and 0.1 to 2 percent of coupling agent. By using the barium sulfate and the glass fibres for filling and modification, the good mechanical property is guaranteed and good sound insulation property is achieved.
Description
Technical field
The present invention relates to a kind of polypropylene modified material and preparation method thereof, especially a kind of polypropylene modified material and preparation method thereof with sound-proofing properties.
Background technology
Vestolen PP 7052 (PP) is as a kind of resins for universal use, and it has good mechanical property and processing characteristics, thermotolerance, and is cheap, in plastics, occupies an important position, and is widely used in the daily life.But Vestolen PP 7052 is used on the parts of some household electrical appliance, and its sound insulation property far can not meet the demands.Sound-proof material adopts polyurethane foam plastic more, but because price is higher, and intensity is less, has also limited its use range.Though the PP source is abundant, low price, also there is the product size poor stability in stable performance, is prone to buckling deformation takes place, and for overcoming these shortcomings, generally adopts filler modified Vestolen PP 7052 at present, to satisfy the request for utilization of goods.
In polypropylene blending modified system, add the raw materials cost that filler can reduce goods, improve the intensity and the rigidity of modified polypropene goods.General choice spun glass and lime carbonate is as filler in the prior art, but during with their filling-modified PP, the shrinking percentage of material is bigger, and sound insulation property is poor.
Summary of the invention
The present invention seeks to deficiency, a kind of polypropylene modified material with sound-proofing properties and preparation method thereof is provided to the prior art existence.
For realizing above-mentioned purpose, polypropylene modified material of the present invention can adopt following scheme:
A kind of sound-proof material of polypropylene modification, the sound-proof material of this polypropylene modification is made up of following component by mass percent:
Vestolen PP 7052 10%-85%; Permanent white 10%-70%; Spun glass 4%-20%; Coupling agent 0.1%-2%.
To the problem that exists in the prior art, the present invention is through using permanent white and spun glass filling-modified in material, to guarantee excellent mechanical property and to increase good sound insulation property.
For realizing above-mentioned purpose, the preparation method of polypropylene modified material of the present invention can adopt following scheme:
A kind of preparation method of sound-proof material of polypropylene modification, this preparation method may further comprise the steps:
(1) handle spun glass with silane coupling agent, handle permanent white with aluminate coupling agent, for use;
(2) high-speed mixer is provided, and according to proportioning as claimed in claim 1 each constituent materials is put into high-speed mixer and form mixture;
(3) twin screw extruder is provided, it is mixing that the mixture in the step (2) is put into twin screw extruder;
(4) extrusion moulding tie rod from twin screw extruder, tie rod is crossed the water cooling pelletizing.
To the problem that exists in the prior art, preparation method of the present invention is through using permanent white and spun glass filling-modified in material, to guarantee excellent mechanical property and to increase good sound insulation property.
Embodiment
Below in conjunction with embodiment; Further illustrate the present invention; Should understand following embodiment only be used to the present invention is described and be not used in the restriction scope of the present invention; After having read the present invention, those skilled in the art all fall within the application's accompanying claims institute restricted portion to the modification of the various equivalent form of values of the present invention.
The sound-proof material of polypropylene modification of the present invention is made up of following component by mass percent:
Vestolen PP 7052 10%-85%; Permanent white 10%-70%; Spun glass 4%-20%; Coupling agent 0.1%-2%.
Wherein, described coupling agent is silane coupling agent and aluminate coupling agent.The particle diameter of described permanent white is more than 1250 orders.
It is the calcium stearate of 0.05%-0.3% that this sound-proof material also can further include oxidation inhibitor and the mass percent that mass percent is 0.5%-1%, and the adding of oxidation inhibitor can weaken the oxidation of Vestolen PP 7052 and iron powder, improves the life-span of material; And calcium stearate can be used as lubricant to make things convenient for the following process of material.
The preparation method of the sound-proof material of this polypropylene modification may further comprise the steps:
(1) handle spun glass with silane coupling agent, handle permanent white with aluminate coupling agent, for use;
(2) high-speed mixer is provided, and according to proportioning as claimed in claim 1 each constituent materials is put into high-speed mixer and form mixture;
(3) twin screw extruder is provided, it is mixing that the mixture in the step (2) is put into twin screw extruder;
(4) extrusion moulding tie rod from twin screw extruder, tie rod is crossed the water cooling pelletizing.
Wherein said twin screw extruder includes six sections of separate controlled temperature; The mixed melting temperature is in the step (2): first section and second section extrusion temperature are at 170-190 ℃; Other several sections extrusion temperatures are between 190-220 ℃; Head temperature is 190 ℃, and the twin screw extruder rotating speed is at 250rpm-350rpm.
Below through several kinds of concrete embodiment explanations.
Embodiment 1:
Spun glass, 0.9% (weight) oxidation inhibitor that the permanent white, 14% (weight) that 75% (weight) COPP, 10% (weight) are handled well is handled well, 0.1% (weight) calcium stearate add that to make it thorough mixing in the high-speed mixer even, and mixing in twin screw extruder then, the temperature that twin-screw system is every section is respectively: T1=180 ℃; T2=190 ℃, T3=195 ℃, T4=200 ℃; T5=205 ℃; T6=210 ℃, the twin screw extruder rotating speed is r=300rpm, and is last; Extrude tie rod, cooling and dicing promptly obtains modified polypropylene material.
Embodiment 2:
Spun glass, 0.8% (weight) oxidation inhibitor that the permanent white, 14% (weight) that 65% (weight) COPP, 20% (weight) are handled well is handled well, 0.2% (weight) calcium stearate add that to make it thorough mixing in the high-speed mixer even, and mixing in twin screw extruder then, the temperature that twin-screw system is every section is respectively: T1=185 ℃; T2=190 ℃, T3=195 ℃, T4=205 ℃; T5=210 ℃; T6=215 ℃, the twin screw extruder rotating speed is r=300rpm, and is last; Extrude tie rod, cooling and dicing promptly obtains modified polypropylene material.
Embodiment 3:
Spun glass, 0.7% (weight) oxidation inhibitor that the permanent white, 14% (weight) that 55% (weight) COPP, 30% (weight) are handled well is handled well, 0.3% (weight) calcium stearate add that to make it thorough mixing in the high-speed mixer even, and mixing in twin screw extruder then, the temperature that twin-screw system is every section is respectively: T1=185 ℃; T2=190 ℃, T3=200 ℃, T4=205 ℃; T5=210 ℃; T6=220 ℃, the twin screw extruder rotating speed is r=300rpm, and is last; Extrude tie rod, cooling and dicing promptly obtains modified polypropylene material.
Material of the present invention and existing calcium carbonate modified polypropylene material that embodiment 1,2,3 is obtained carry out Experiments of Machanics, thermal analysis experiment, melting experiment, experiment of hardness, noise experiment relatively; Through the performance of above experimental evaluation analysis material of the present invention, experimental result is with reference to shown in the following table:
Annotate: the test result of making oise insulation factor is for being 2.5mm when sample coupon thickness, and frequency of source is that 400Hz records.
Through testing and verification; The present invention is owing to add permanent white in compound system; Improved the mechanical property of matrix material effectively; Improved the intensity and the hardness of traditional lime carbonate modified polypropylene material, increased the surface gloss of matrix material, especially permanent white replaces the sound-proofing properties that lime carbonate can improve matrix material.
Claims (1)
1. the preparation method of the sound-proof material of a polypropylene modification, it is characterized in that: the sound-proof material of this polypropylene modification is made up of following component by mass percent:
Vestolen PP 7052 10%-85%; Permanent white 10%-70%; Spun glass 4%-20%; Coupling agent 0.1%-2%;
This preparation method may further comprise the steps:
(1) handle spun glass with silane coupling agent, handle permanent white with aluminate coupling agent, for use;
(2) high-speed mixer is provided, and puts into high-speed mixer according to the described set of dispense of above-mentioned mass percent than with each constituent materials and form mixture;
(3) twin screw extruder is provided, it is mixing that the mixture in the step (2) is put into twin screw extruder;
(4) extrusion moulding tie rod from twin screw extruder, tie rod is crossed the water cooling pelletizing;
Said twin screw extruder includes six sections of separate controlled temperature; The mixed melting temperature is in the step (3): first section and second section extrusion temperature are at 170-190 ℃; Other several sections extrusion temperatures are between 190-220 ℃; Head temperature is 190 ℃, and the twin screw extruder rotating speed is at 250rpm-350rpm.