CN101947825A - Cable vulcanizing method - Google Patents
Cable vulcanizing method Download PDFInfo
- Publication number
- CN101947825A CN101947825A CN2010102878722A CN201010287872A CN101947825A CN 101947825 A CN101947825 A CN 101947825A CN 2010102878722 A CN2010102878722 A CN 2010102878722A CN 201010287872 A CN201010287872 A CN 201010287872A CN 101947825 A CN101947825 A CN 101947825A
- Authority
- CN
- China
- Prior art keywords
- cable
- temperature
- vulcanizing treatment
- vulcanization
- vulcanizing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a cable vulcanizing method which comprises the following steps: (1) providing a vulcanizing plant with gradually changing temperature; and (2) vulcanizing the semi-finished cable by the vulcanizing plant, wherein the temperature for vulcanizing is 180-330 DEG C.
Description
Technical field
The present invention relates to cable and make the field, relate in particular to a kind of cable vulcanization process.
Background technology
The invention of electricity has brought various facilities for people's life, for example, thereby electricity can be used for throwing light on, cook, warm oneself or driving various machinery equipment motions and realize mechanization production etc., therefore in modern life, people have be unable to do without electricity, and wherein cable plays a part indispensable as the transmission carrier of electricity equally.
The production system of conventional wire cable is mainly by paying out machine, push machine, vulcanization plant, inker, dryer, equipment such as spark test machine and admission machine are formed, the concrete production procedure of cable is: metallic conductor is sent to the described machine of pushing from described actinobacillus device, thereby follow the described machine of pushing and extrude rubber insulation formation cable semi-finished product in the outside of described metallic conductor, moreover described cable semi-finished product are passed through described vulcanization plant carry out vulcanizing treatment, the cable semi-finished product that come out from described vulcanization plant pass through described inker lettering again, thereby and then the cable of printed word is sent to described dryer the printing ink on the described cable is dried processing, moreover pass through described spark test machine described cable is carried out spark test, last described admission machine is packed up the cable of test passes.Wherein, the purpose of the vulcanizing treatment of cable is exactly to change into flexible and product dimensionally stable by the rubber that the chemical crosslinking effect between rubber molecule will be plasticity basically, and the rerum natura of the rubber after the sulfuration is stable, the serviceability temperature expanded range.In the prior art, described vulcanization plant generally is composed in series by the more piece vulcanizing oven, and the same temperature of input is carried out vulcanizing treatment to described cable semi-finished product in the described vulcanizing oven of every joint, yet, because the temperature in the described vulcanizing oven immobilizes, so cure efficiency is not ideal enough; In addition, when the temperature in the described vulcanizing oven is provided with lowly, can cause the cable semi-finished product that come out from described vulcanization plant not print word at described inker, and when the temperature in the described vulcanizing oven is provided with higherly, the cable semi-finished product that come out from described vulcanization plant are in half melting state, thereby can cause lettering smudgy during lettering.
Therefore, be necessary to provide a kind of follow-on cable vulcanization process to overcome above-mentioned defective.
Summary of the invention
The purpose of this invention is to provide a kind of cable vulcanization process, described cable vulcanization process makes the half-finished cure efficiency of cable good and effective through the cable semi-finished product lettering after the described cable vulcanization process processing.
To achieve these goals, the invention provides a kind of cable vulcanization process, may further comprise the steps:
(1) vulcanization plant that provides temperature to gradually change;
(2) the cable semi-finished product are carried out vulcanizing treatment by described vulcanization plant, the temperature of described vulcanizing treatment is 180 ℃-330 ℃.
Preferably, the initial temperature of described vulcanizing treatment is 180 ℃-200 ℃, and the maximum temperature of described vulcanizing treatment is 330 ℃, and the final temperature of described vulcanizing treatment is 270 ℃-290 ℃.
Compared with prior art, the advantage of cable vulcanization process of the present invention is, the cable semi-finished product carry out vulcanizing treatment in temperature range is 180 ℃-330 ℃ vulcanization plant, because the temperature in the described vulcanization plant can gradually change, therefore can control described vulcanization plant initial to maximum temperature in the temperature range that is fit to vulcanizing treatment, the final temperature that can control simultaneously described vulcanization plant is in the temperature range that is fit to lettering, therefore, described cable vulcanization process has also guaranteed the lettering effect when guaranteeing cure efficiency.
By following description also in conjunction with the accompanying drawings, it is more clear that the present invention will become, and these accompanying drawings are used to explain embodiments of the invention.
Description of drawings
Fig. 1 is the flow chart of cable vulcanization process of the present invention.
The specific embodiment
With reference now to accompanying drawing, describe embodiments of the invention, the similar elements label is represented similar elements in the accompanying drawing.As mentioned above, the invention provides a kind of cable vulcanization process, described cable vulcanization process makes the half-finished cure efficiency of cable good and effective through the cable semi-finished product lettering after the described cable vulcanization process processing.
To achieve these goals, the invention provides a kind of cable vulcanization process, may further comprise the steps:
S1, the vulcanization plant that provides temperature to gradually change;
S2, the cable semi-finished product are carried out vulcanizing treatment by described vulcanization plant, the temperature of described vulcanizing treatment is 180 ℃-330 ℃.
Particularly, the initial temperature of described vulcanizing treatment is 180 ℃-200 ℃, and the maximum temperature of described vulcanizing treatment is 330 ℃, and the final temperature of described vulcanizing treatment is 270 ℃-290 ℃.In a specific embodiment of the present invention, the initial temperature of described vulcanizing treatment is 180 ℃, and the final temperature of described vulcanizing treatment is 280 ℃.
Particularly, the cable semi-finished product that come out from described vulcanization plant carry out the lettering processing again, and best lettering temperature is 280 ℃.
Compared with prior art, the advantage of cable vulcanization process of the present invention is, the cable semi-finished product carry out vulcanizing treatment in temperature range is 180 ℃-330 ℃ vulcanization plant, because the temperature in the described vulcanization plant can gradually change, therefore can control described vulcanization plant initial to maximum temperature in the temperature range that is fit to vulcanizing treatment, the final temperature that can control simultaneously described vulcanization plant is in the temperature range that is fit to lettering, therefore, described cable vulcanization process has also guaranteed the lettering effect when guaranteeing cure efficiency.
Above invention has been described in conjunction with most preferred embodiment, but the present invention is not limited to the embodiment of above announcement, and should contain various modification, equivalent combinations of carrying out according to essence of the present invention.
Claims (2)
1. a cable vulcanization process is characterized in that, may further comprise the steps:
(1) vulcanization plant that provides temperature to gradually change;
(2) the cable semi-finished product are carried out vulcanizing treatment by described vulcanization plant, the temperature of described vulcanizing treatment is 180 ℃-330 ℃.
2. cable vulcanization process as claimed in claim 1 is characterized in that, the initial temperature of described vulcanizing treatment is 180 ℃-200 ℃, and the maximum temperature of described vulcanizing treatment is 330 ℃, and the final temperature of described vulcanizing treatment is 270 ℃-290 ℃.