CN101947460A - Synthesis method of nano-zinc sulfide/bamboo charcoal photocatalytic material by hydrothermal process - Google Patents
Synthesis method of nano-zinc sulfide/bamboo charcoal photocatalytic material by hydrothermal process Download PDFInfo
- Publication number
- CN101947460A CN101947460A CN 201010276061 CN201010276061A CN101947460A CN 101947460 A CN101947460 A CN 101947460A CN 201010276061 CN201010276061 CN 201010276061 CN 201010276061 A CN201010276061 A CN 201010276061A CN 101947460 A CN101947460 A CN 101947460A
- Authority
- CN
- China
- Prior art keywords
- bamboo charcoal
- nano
- zinc sulfide
- photocatalytic material
- weighing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a synthesis method of a nano-zinc sulfide/bamboo charcoal photocatalytic material by a hydrothermal process. The method comprises the following steps: (1) weighing 0.0028-0.0560g of zinc sulfate heptahydrate and 0.05-0.15g of polyethylene glycol-6000 and dissolving in 30ml of distilled water, and stirring with an electromagnetic stirrer until being dissolved at low speed and room temperature to obtain a uniform mixed liquid; (2) weighing 0.1-2.0g of bamboo charcoal and placing in the mixed liquid, stirring for about 3 hours, adding 0.0015-0.0300g of thiourea2, and continuously stirring for about 3 hours; and (3) leading the solution obtained in step (2) into a 40ml of high-pressure kettle lined with polytetrafluoroethylene, reacting in a digital display blast drying oven at the constant temperature of 150-160 DEG C for 10-12 hours, naturally cooling to room temperature, filtering and drying to obtain the nano-zinc sulfide/bamboo charcoal photocatalytic material, wherein, ZnS nanoparticles in the nano-zinc sulfide/bamboo charcoal photocatalytic material have hexagonal crystal phases and take a spherical shape, and the average particle size thereof is about 100nm. The preparation method of the invention is simple and feasible and has low cost and high yield.
Description
Technical field
The present invention relates to the hydro-thermal method synthetic method of a kind of nano-zinc sulfide/bamboo charcoal catalysis material.
Background technology
Semiconductor as a kind of important broad stopband, zinc sulfide nano-material is because of its unique character, had in fields such as light-guide material, luminescence generated by light, photocatalysis widely and used, particularly in photocatalysis field, advantages such as it has the photocatalytic activity height, chemical property is stable, nontoxic no burn into cost is low, service life is long, but it is not high to exist the difficulty and the efficiency of light energy utilization of separating and reclaiming in the use of powdery nano-zinc sulfide; Limited the practical application of photocatalysis technology, and bamboo charcoal is as a kind of novel environment-friendly materials and function material, because of its flourishing pore structure, specific area is big, and absorption power is strong, has adsorption function, can be used as good carrier, is the carrier of nano-zinc sulfide with the bamboo charcoal, helps the recycling of catalyst, reduce processing cost, synthetic, sign and the photocatalysis performance of therefore studying nano-zinc sulfide/bamboo charcoal compound are significant.
Summary of the invention
The objective of the invention is with the white vitriol is that zinc source, thiocarbamide are that sulphur source, polyethylene glycol are that dispersant, bamboo charcoal are carrier, adopts the synthetic nano-zinc sulfide/bamboo charcoal composite with high efficiency photocatalysis performance of one step hydro thermal method.
Concrete steps are:
(1) takes by weighing the white vitriol of 0.0028-0.0560g and the polyethylene glycol of 0.05-0.15g-6000 is dissolved in the distilled water of 30ml, and place that the dissolving of room temperature stirring at low speed makes even mixed liquor on the magnetic stirrer;
(2) take by weighing the 0.1-2.0g bamboo charcoal and put into above-mentioned mixed liquor, stir about 3h; The thiocarbamide that adds 0.0015-0.0300g again continues to stir about 3h;
(3) be in the autoclave of inner liner polytetrafluoroethylene of 40ml at last with step (2) gained solution importing capacity, and be placed in the digital display air dry oven with constant temperature 150-160 ℃ of reaction 10-12h, naturally cool to room temperature then, filter, drying promptly makes nano-zinc sulfide/bamboo charcoal catalysis material, the ZnS nano particle is the hexagonal crystal phase in nano-zinc sulfide/bamboo charcoal catalysis material, sphere, and average grain diameter is about 100nm.
With methylene blue is organic target degradation product, estimates the photocatalysis performance of ZnS/ bamboo charcoal compound, and under UV-irradiation, compound is to the photocatalytic degradation reaction 1h of methylene blue, and its percent of decolourization can reach more than 95%.
Preparation method of the present invention is simple, with low cost, the productive rate height.
The specific embodiment
Embodiment:
Take by weighing the white vitriol of 0.0028g and the polyethylene glycol of 0.1000g-6000 is dissolved in the distilled water of 30ml, and place that the dissolving of room temperature stirring at low speed makes even mixed liquor on the magnetic stirrer; Take by weighing the 1.0000g bamboo charcoal and put into above-mentioned mixed liquor, stir about 3h; Add the 0.0015g thiocarbamide again, continue to stir about 3h; Be in the autoclave of inner liner polytetrafluoroethylene of 40ml at last with solution importing capacity, and be placed in the digital display air dry oven with 150 ℃ of reactions of constant temperature 12h, naturally cool to room temperature then, filter, product promptly got nano-zinc sulfide/bamboo charcoal catalysis material down in dry 12 hours at 80 ℃.Through test shows such as XRD and SEM: the ZnS nano particle is the hexagonal crystal phase in nano-zinc sulfide/bamboo charcoal catalysis material, sphere, and average grain diameter is about 100nm.
(concentration is 5.68 * 10 containing the 10mL methylene blue solution
-5Mol/L) nano-zinc sulfide/bamboo charcoal compound that adds 0.2g in the beaker carries out the catalytic degradation experiment respectively under ultraviolet light, natural daylight and dark condition, the reaction time is 0-3 hour.The result shows that the catalytic degradation effect of compound under ultraviolet light and natural daylight is all good, and ultraviolet light is the most obvious.Under ultraviolet light, the percent of decolourization of methylene blue is 95% when reacting 1 hour.
Claims (1)
1. the hydro-thermal method synthetic method of a catalysis material is characterized in that concrete steps are:
(1) takes by weighing the white vitriol of 0.0028-0.0560g and the polyethylene glycol of 0.05-0.15g-6000 is dissolved in the distilled water of 30ml, and place room temperature stirring at low speed dissolving on the magnetic stirrer, make even mixed liquor;
(2) take by weighing the 0.1-2.0g bamboo charcoal and put into above-mentioned mixed liquor, stir about 3h; The thiocarbamide that adds 0.0015-0.0300g again continues to stir about 3h;
(3) be in the autoclave of inner liner polytetrafluoroethylene of 40ml at last with step (2) gained solution importing capacity, and be placed in the digital display air dry oven with constant temperature 150-160 ℃ of reaction 10-12h, naturally cool to room temperature then, filter, drying promptly makes catalysis material, the ZnS nano particle is the hexagonal crystal phase in the catalysis material, sphere, and average grain diameter is about 100nm.