CN101942570A - Slag returning method for reducing gold content of smelting slag - Google Patents
Slag returning method for reducing gold content of smelting slag Download PDFInfo
- Publication number
- CN101942570A CN101942570A CN2010102648985A CN201010264898A CN101942570A CN 101942570 A CN101942570 A CN 101942570A CN 2010102648985 A CN2010102648985 A CN 2010102648985A CN 201010264898 A CN201010264898 A CN 201010264898A CN 101942570 A CN101942570 A CN 101942570A
- Authority
- CN
- China
- Prior art keywords
- slag
- smelting slag
- smelting
- return
- gold content
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention belongs to the technical field of smelting slag returning in the smelting industry, and particularly discloses a slag returning method for reducing the gold content of smelting slag, which comprises the following steps of: before the smelting slag is returned and discharged out of a furnace, completely clearing kish slag floating above the smelting slag, simultaneously coating acetylene ash onto the inner wall of a heading die, scooping the returned smelting slag into the heading die, vibrating the heading die, cooling the smelting slag, discharging the smelting slag, and knocking returned alloys at the bottom part of the smelting slag off for recovery. The slag returning method of the invention has the advantages of simplicity, effectiveness and capability of reducing the gold content of the smelting slag to be less than or equal to 80g/t only by once returning; and the returned smelting slag has low gold content and stable index.
Description
Technical field
The invention belongs to the smelting slag return slag technical field in the smelting industry, be specifically related to a kind of return slag method that reduces smelting slag Gold Content.
Background technology
At present, domestic refining process through the golden smelting slag that contains that pyrometallurgical smelting produced, contains gold generally at 300～800g/t.In order further to reduce smelting slag Gold Content, improve recovery of gold and silver, all to handle through the smelting slag return slag, further improve recovery of gold and silver.But the smelting slag through returning contains gold still than higher, is not very desirable, and generally all greater than 150g/t, recovery of gold and silver is undesirable.
Summary of the invention
The object of the present invention is to provide a kind of return slag method that reduces smelting slag Gold Content.
For achieving the above object, the technical scheme taked of the present invention is as follows:
A kind of return slag method that reduces smelting slag Gold Content: before the smelting slag return slag takes the dish out of the pot, cast aside the kish slag that floats only above smelting slag, simultaneously coat the acetylene ash at pier mould inwall, then, the smelting slag that will return is scooped in the pier mould again, and rapping pier mould is after the cooling, smelting slag is knocked out, and the alloy that returns that smelting slag slag bottom is divided knocks out recovery.
For ease of the cooling and demolding of smelting slag, the pier mould of the preferred back taper type of pier mould, rapping pier mould after the cooling, knocks out smelting slag, the alloy that returns of slag nose part is knocked out recovery get final product.
When pier mould inwall was coated the acetylene ash, the thickness of control acetylene ash was at 0.1～0.2mm.
The purpose of rapping pier mould is: promote that fine gold and silver is deposited to pier mould bottom in the melting slag, reduce the Gold Content on clinker top, so rapping pier mould to the actual measurement Gold Content of smelting slag top clinker is less than or equal to 80g/t and gets final product.
During rapping pier mould, can adopt the mechanical vibrator mode, the hand hammer of 250g is artificial uniformly to beat pier mould outer wall 10～15 times such as being not less than with tup weight in two minutes.
Preferably, the tup weight of hand hammer is preferably 250～1000g.
Refinery's silver metallurgy powder, the used crucible of return slag are the big crucible of pure graphite, and in melting silver powder, return slag process, the graphite on the crucible can constantly come off and enter in the smelting slag.Kish slag can adsorb a certain amount of gold and silver, and it is high to cause slag to contain gold, reduces recovery of gold and silver.Therefore the present invention casts aside the kish slag that floats only above smelting slag before the smelting slag return slag takes the dish out of the pot, and helps reducing the Gold Content of smelting slag, improves recovery of gold and silver.Simultaneously, acetylene ash on the pier mould increases the rapping of pier mould, helps that fine gold and silver is deposited to pier mould bottom in the melting slag, reduces clinker top Gold Content.
Return slag method of the present invention is simply effective, and the smelting slag Gold Content that is returned is low, and index is stable, only need return smelting slag Gold Content can be reduced to for one time to be less than or equal to 80g/t.
Embodiment
Below in conjunction with specific embodiment technical scheme of the present invention is done into a ground and introduce in detail, but protection scope of the present invention is not limited thereto:
Embodiment 1
A kind of return slag method that reduces smelting slag Gold Content, the smelting slag treatment capacity is 508kg: before the smelting slag return slag takes the dish out of the pot, cast aside the kish slag that floats only above smelting slag with dragging for the slag spoon, simultaneously evenly be coated with the acetylene ash that last layer thickness is 0.18mm at back taper type pier mould inwall, then, the smelting slag that will return is scooped in the back taper type pier mould again, rapping pier mould (beaing pier mould outer wall 13 times with the hand hammer of tup weight 1000g is artificial uniform in two minutes), after the cooling, smelting slag is knocked out, the alloy that returns of smelting slag slag nose part is knocked out recovery.
Embodiment 2
A kind of return slag method that reduces smelting slag Gold Content, the smelting slag treatment capacity is 510kg: before the smelting slag return slag takes the dish out of the pot, cast aside the kish slag that floats only above smelting slag with dragging for the slag spoon, simultaneously evenly be coated with the acetylene ash that last layer thickness is 0.13mm at back taper type pier mould inwall, then, the smelting slag that will return is scooped in the back taper type pier mould again, rapping pier mould (beaing pier mould outer wall 12 times with the hand hammer of tup weight 750g is artificial uniform in two minutes), after the cooling, smelting slag is knocked out, the alloy that returns of smelting slag slag nose part is knocked out recovery.
Embodiment 3
A kind of return slag method that reduces smelting slag Gold Content, the smelting slag treatment capacity is 506kg: before the smelting slag return slag takes the dish out of the pot, cast aside the kish slag that floats only above smelting slag with dragging for the slag spoon, simultaneously evenly be coated with the acetylene ash that last layer thickness is 0.15mm at back taper type pier mould inwall, then, the smelting slag that will return is scooped in the back taper type pier mould again, rapping pier mould (beaing pier mould outer wall 10 times with the hand hammer of tup weight 500g is artificial uniform in two minutes), after the cooling, smelting slag is knocked out, the alloy that returns of smelting slag slag nose part is knocked out recovery.
Embodiment 4
A kind of return slag method that reduces smelting slag Gold Content, the smelting slag treatment capacity is 503kg: before the smelting slag return slag takes the dish out of the pot, cast aside the kish slag that floats only above smelting slag with dragging for the slag spoon, simultaneously evenly be coated with the acetylene ash that last layer thickness is 0.15mm at back taper type pier mould inwall, then, the smelting slag that will return is scooped in the back taper type pier mould again, rapping pier mould (beaing pier mould outer wall 13 times with the hand hammer of tup weight 750g is artificial uniform in two minutes), after the cooling, smelting slag is knocked out, the alloy that returns of smelting slag slag nose part is knocked out recovery.
Embodiment 5
A kind of return slag method that reduces smelting slag Gold Content, the smelting slag treatment capacity is 512kg: before the smelting slag return slag takes the dish out of the pot, cast aside the kish slag that floats only above smelting slag with dragging for the slag spoon, simultaneously evenly be coated with the acetylene ash that last layer thickness is 0.1mm at back taper type pier mould inwall, then, the smelting slag that will return is scooped in the back taper type pier mould again, rapping pier mould (beaing pier mould outer wall 10 times with the hand hammer of tup weight 250g is artificial uniform in two minutes), after the cooling, smelting slag is knocked out, the alloy that returns of smelting slag slag nose part is knocked out recovery.
Embodiment 6
A kind of return slag method that reduces smelting slag Gold Content, the smelting slag treatment capacity is 505kg: before the smelting slag return slag takes the dish out of the pot, cast aside the kish slag that floats only above smelting slag with dragging for the slag spoon, simultaneously evenly be coated with the acetylene ash that last layer thickness is 0.2mm at back taper type pier mould inwall, then, the smelting slag that will return is scooped in the back taper type pier mould again, rapping pier mould (beaing pier mould outer wall 15 times with the hand hammer of tup weight 1000g is artificial uniform in two minutes), after the cooling, smelting slag is knocked out, the alloy that returns of smelting slag slag nose part is knocked out recovery.
Embodiment 7
A kind of return slag method that reduces smelting slag Gold Content, the smelting slag treatment capacity is 504kg: before the smelting slag return slag takes the dish out of the pot, cast aside the kish slag that floats only above smelting slag with dragging for the slag spoon, simultaneously evenly be coated with the acetylene ash that last layer thickness is 0.12mm at back taper type pier mould inwall, then, the smelting slag that will return is scooped in the back taper type pier mould again, rapping pier mould (beaing pier mould outer wall 10 times with the hand hammer of tup weight 750g is artificial uniform in two minutes), after the cooling, smelting slag is knocked out, the alloy that returns of smelting slag slag nose part is knocked out recovery.
The result of laboratory test such as the following table of 1～7 return slag of the foregoing description:
By test, this technological invention, institute's return slag Gold Content is low, and index is stable, only need return one time and slag Gold Content can be reduced to≤80g/t, far below slag Gold Content before the experiment.
Claims (6)
1. return slag method that reduces smelting slag Gold Content, it is characterized in that: before the smelting slag return slag takes the dish out of the pot, cast aside the kish slag that floats only above smelting slag, simultaneously coat the acetylene ash at pier mould inwall, then, the smelting slag that will return is scooped in the pier mould again, rapping pier mould, after the cooling, smelting slag is knocked out, the alloy that returns that smelting slag slag bottom is divided knocks out recovery.
2. the return slag method of reduction smelting slag Gold Content as claimed in claim 1 is characterized in that: the pier mould is the back taper type.
3. the return slag method of reduction smelting slag Gold Content as claimed in claim 1 or 2 is characterized in that: when pier mould inwall was coated the acetylene ash, the thickness of control acetylene ash was at 0.1～0.2mm.
4. the return slag method of reduction smelting slag Gold Content as claimed in claim 3 is characterized in that: rapping pier mould is to the actual measurement Gold Content≤80g/t of smelting slag top clinker.
5. the return slag method of reduction smelting slag Gold Content as claimed in claim 4 is characterized in that: during rapping pier mould, be not less than that the hand hammer of 250g is artificial uniform to beat pier mould outer wall 10～15 times in two minutes with tup weight.
6. the return slag method of reduction smelting slag Gold Content as claimed in claim 5 is characterized in that: the tup weight of hand hammer is 250～1000g.