CN101941848A - Autoclaved sawn mud concrete building block and processing technique thereof - Google Patents
Autoclaved sawn mud concrete building block and processing technique thereof Download PDFInfo
- Publication number
- CN101941848A CN101941848A CN2010102480787A CN201010248078A CN101941848A CN 101941848 A CN101941848 A CN 101941848A CN 2010102480787 A CN2010102480787 A CN 2010102480787A CN 201010248078 A CN201010248078 A CN 201010248078A CN 101941848 A CN101941848 A CN 101941848A
- Authority
- CN
- China
- Prior art keywords
- building block
- cement
- saw
- slurry
- percent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses an autoclaved sawn mud concrete building block and a processing technique thereof, belongs to a building material and a production and processing process thereof, and particularly relates to an engineering building block taking sawn mud generated in a stone sawing and processing process as a manufacturing raw material and a processing technique thereof. The building block is characterized by comprising the following raw materials in percentage by weight: 70 to 82 percent of sawn mud, 14 to 22 percent of lime, 3 to 14 percent of cement, 0.8 to 1.8 percent of gypsum and 0.06 to 0.12 percent of aluminum powder, wherein the water cement ratio is 0.5 to 0.68/1. The technique manufactures the high-quality material used in the building industry by fully using a large amount of waste, namely the sawn mud generated in the stone processing industry; and the technique has considerable economic benefit, reduces the pollution emission of the stone processing industry to the environment to a great extent, and meanwhile has good social benefit.
Description
Technical field
The invention belongs to a kind of material of construction and production and processing technology thereof, particularly relating to a kind of is the building block and the processing technology thereof of making raw material with the saw mud that is generated in the stone material sawing course of processing.
Background technology
In civil engineering, using more walling unit is powder ash air-entrained concrete building block and quartz sand air-entrained concrete building block at present, and it mainly makes raw material is flyash and quartz sand.Wherein,
The powder ash air-entrained concrete building block raw material ratio:
Flyash 70%~80% lime 15%~22% cement 3%~7%
Gypsum 0.8%~1.8% aluminium powder 0.06%~0.12% water cement ratio 0.5~0.65/1
Quartz sand air-entrained concrete building block raw material ratio:
Quartz sand 68%~76% lime 13%~21% cement 8%~14%
Gypsum 0.8%~1.6% aluminium powder 0.06%~0.12% water cement ratio 0.5~0.68/1
As seen, in above-mentioned existing walling unit, the consumption of flyash and quartz sand is very big.And the price of these two kinds of materials is higher, and along with the continuous increase of consumption and the implementation of resources regulation policy, its price has the trend that continues to climb to a higher point.On the other hand, saw mud is the main waste in the processing of stone industry, and its growing amount is very big, and does not still have the approach that utilizes again at present.General way is to discharge on the spot, and therefore air and the water source environment to the locality causes severe contamination.
Summary of the invention
Purpose of the present invention promptly is to provide a kind of novel steaming to press saw cement concrete building block and processing technology thereof, to reach utilization of waste material, turns waste into wealth, and reduces environmental pollution, saves the purpose of utilizing resource.
The building block of saw cement concrete is pressed in steaming disclosed in this invention, it is characterized in that raw material ratio (by weight) is:
Saw mud 70%~82% lime 14%~22% cement 3%~14%
Gypsum 0.8%~1.8% aluminium powder 0.06%~0.12% water cement ratio 0.5~0.68/1.
The processing technology of saw cement concrete building block is pressed in steaming disclosed in this invention, it is characterized in that may further comprise the steps:
Step 1: collect the saw mud that is generated in the stone material sawing course of processing, take the method for seasoning or oven dry to make it dehydration, carry out fragmentation with ball mill then, grind, cross 400~600 mesh sieves, it is standby to obtain sawing the mud fine powder;
Step 2: by above-mentioned raw material ratio, saw mud fine powder and gypsum that mill is good are knocked down agitated pool, add water to stir, and the form slurry that stirs is standby;
Step 3: slurry is pumped in the pouring can, add lime, cement stirring 3~4 minutes successively, measure the slurry diffusibleness, diffusibleness requires to reach 16~20, and diffusibleness is by adding water adjustment;
Step 4: after diffusibleness meets the requirements, start the heating rod in the pouring can, aluminium powder is added in the aluminium powder stirrer simultaneously, add entry then, make aluminium powder suspension, after slurry temperature reaches 40~45 degree aluminium powder suspension is added in the pouring can, restir was poured into slurry in the mould after 50~60 seconds;
Step 5: place curing room to carry out maintenance just on mould, the curing room room temperature is at 30~40 degrees centigrade, curing time 3~3.5 hours;
Step 6: treat to release after blank strength reaches 0.7~0.9 MPa, after the demoulding in accordance with regulations size cut;
Step 7: hang on the dolly after the base substrate upset with well cutting, then dolly is pushed autoclave;
Step 8: autoclave was vacuumized 20 minutes, treat to advance when the autoclave internal pressure is shown as zero saturation steam, the autoclave internal pressure reached 1.28Mpa in about about 2.5 hours, carry out 6 hours constant voltage maintenance then, maintenance is carried out exhaust after finishing, pressure is opened the still door after reaching standard atmospheric pressure, and building block is released, and piles up to get final product.
Saw cement concrete building block and processing technology thereof are pressed in steaming provided by the present invention, made full use of a large amount of wastes that the processing of stone industry is generated---saw mud, and then make the used quality matetrial of building trade, not only has considerable economic, and reduced of the disposal of pollutants of processing of stone industry to a great extent to environment, have good social benefit simultaneously.
Embodiment
1. saw mud is put in storage.With the moisture stone flour that is generated in the stone material sawing process---1000 kilograms in mud of saw adds dog-house with shovel loader, delivers to agitated pool with travelling belt behind ball mill grinding, adds 20 kilograms of gypsum, adds 720 kg water and fully stirs, and form slurry is standby.
2. slurry is pumped in the pouring can, add double centner cement and 200 kilograms of lime, stir, adjust diffusibleness, when treating that diffusibleness reaches 18 left and right sides, start the heating rod in the pouring can, reaching 45 degree backs at slurry temperature, to add concentration be 20 kilograms of 5% aluminium powder suspension, is poured in the mould.
3. mould is pushed curing room, maintenance is 3 hours in the room temperature about 40 degree.
4. mould is released curing room, through after the demoulding to cutting bed, be cut into the fritter of requirement after handling to roll-over table, after the upset unacceptable product is dug, hang onto on the steam-cured dolly with grabbing then.
5. steam-cured dolly is pushed to ferry bus, utilizes ferry bus that aerated blocks is advanced in the autoclave.
6. autoclave vacuumizes, and air inlet was carried out 6 hours constant voltage maintenance about 2.5 hours after pressure reaches 1.28Mpa.After finishing, maintenance carries out exhaust, exhaust 1 hour.
7. after exhaust is finished steam-cured dolly is released autoclave, aerated blocks carries out transporting to inventory area behind the code-disc, carries out the room temperature maintenance, detects to dispatch from the factory after qualified.
After testing, the building block of saw cement concrete is pressed in steaming disclosed in this invention, and its technical indicator reaches:
Ultimate compression strength: 3.8Mpa (mean value)
Monolithic minimum value: 2.9Mpa
Dry volume density: 612kg/m
3
Thermal conductivity (dry state): 0.15W/ (m.K)
Radionuclide is limited the quantity of: I
Ra0.08
Ir 0.15?。
Claims (2)
1. one kind is steamed the building block of pressure saw cement concrete, it is characterized in that raw material ratio (by weight) is:
Saw mud 70%~82% lime 14%~22% cement 3%~14%
Gypsum 0.8%~1.8% aluminium powder 0.06%~0.12% water cement ratio 0.5~0.68/1.
2. the processing technology of saw cement concrete building block is pressed in steaming according to claim 1, it is characterized in that may further comprise the steps:
Step 1: collect the saw mud that is generated in the stone material sawing course of processing, take the method for seasoning or oven dry to make it dehydration, carry out fragmentation with ball mill then, grind, cross 400~600 mesh sieves, it is standby to obtain sawing the mud fine powder;
Step 2: by above-mentioned raw material ratio, saw mud fine powder and gypsum that mill is good are knocked down agitated pool, add water to stir, and the form slurry that stirs is standby;
Step 3: slurry is pumped in the pouring can, add lime, cement stirring 3~4 minutes successively, measure the slurry diffusibleness, diffusibleness requires to reach 16~20, and diffusibleness is by adding water adjustment;
Step 4: after diffusibleness meets the requirements, start the heating rod in the pouring can, aluminium powder is added in the aluminium powder stirrer simultaneously, add entry then, make aluminium powder suspension, after slurry temperature reaches 40~45 degree aluminium powder suspension is added in the pouring can, restir was poured into slurry in the mould after 50~60 seconds;
Step 5: place curing room to carry out maintenance just on mould, the curing room room temperature is at 30~40 degrees centigrade, curing time 3~3.5 hours;
Step 6: treat to release after blank strength reaches 0.7~0.9 MPa, after the demoulding in accordance with regulations size cut;
Step 7: hang on the dolly after the base substrate upset with well cutting, then dolly is pushed autoclave;
Step 8: autoclave is vacuumized, treat to advance saturation steam when the autoclave internal pressure is shown as zero, after the autoclave internal pressure reaches 1.28Mpa, carry out 6 hours constant voltage maintenance, carry out exhaust then, pressure is opened the still door after reaching standard atmospheric pressure, building block is released, piled up and get final product.