CN101928408A - Composite anti-blocking agent for linear low-density polyethylene film and using method thereof - Google Patents
Composite anti-blocking agent for linear low-density polyethylene film and using method thereof Download PDFInfo
- Publication number
- CN101928408A CN101928408A CN2009101486317A CN200910148631A CN101928408A CN 101928408 A CN101928408 A CN 101928408A CN 2009101486317 A CN2009101486317 A CN 2009101486317A CN 200910148631 A CN200910148631 A CN 200910148631A CN 101928408 A CN101928408 A CN 101928408A
- Authority
- CN
- China
- Prior art keywords
- film
- sodium benzoate
- density polyethylene
- silicon
- linear low
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a composite anti-blocking agent for a linear low-density polyethylene film. The composite anti-blocking agent comprises silicon dioxide and sodium benzoate. A method for using the composite anti-blocking agent comprises the following steps of: dissolving the sodium benzoate in deionized water; uniformly stirring silicasol and solution of sodium benzoate; then spray-drying the mixed solution; adding the anti-blocking agent and an antioxidant into linear low-density polyethylene; and performing extrusion and granulation on the mixture and adding into a film blowing machine to blow the film. Due to the adoption of the anti-blocking agent, the anti-blocking performance of a film blowing product is obviously improved, the longitudinal and transverse tensile strength is improved to a certain extent, and the comprehensive performance is high.
Description
[technical field]
The present invention relates to the linear low-density polyethylene film field, particularly a kind of opening agent that is used to solve film blocking.
[background technology]
Linear low density polyethylene (LLDPE) film is aspect such as the packing of applicable industry product and daily necessities and agriculture production widely, but film can be sticked together because of pressurized in production and storage process, promptly produce " adhesion " phenomenon, thereby influence it in people's daily life and the use in the industrialization automatic packaging production line.
It mainly is because smooth surface makes between the film forms due to the vacuum that the LLDPE film sticks together.The method that solves film blocking is to add the opening agent, and the opening agent can form many fine and hard projections on the surface of film, makes extraneous air be easy to enter between the double-layer films, avoids forming vacuum between the two-layer film that fits together.Reduced the contact area between the film, will reduce the film surface frictional coefficient simultaneously, made film be easy to opening, thereby play the effect that prevents film blocking.The opening agent refers generally to silica-based inorganic powder, as synthetic silica, diatomite etc., inorganic powders such as adopting lime carbonate, talcum powder is also arranged as the agent of polyolefin film opening.
United States Patent (USP) 6,066,691 adopt the mixture of silicon-dioxide or silicon-dioxide and silicate as the opening agent, obtain the film of opening excellent property, when silica gel content was 2000ppm, the stiction force of film surface can be reduced to 0.3N from 0.8N, and because the silica nanometer aperture of adopting is littler, absorption to lubricant reduces, thereby reduces the consumption of lubricant.
United States Patent (USP) 6,465 then is the method for selecting multi-layer compound film in 266, introduces one deck ethylene-propylene copolymer at least on the surface, thereby without additive opening agent, just can reach the purpose that film is easy to opening, reduction skin friction coefficient.
In composite assistant, add 0.05~0.2% lightweight synthetic silica in the Chinese patent 200610097861.1 as the opening agent, the end of LLDPE molecular chain is sucked by the space of silica dioxide granule in the course of processing, this particle becomes nucleation centre simultaneously makes its crystallization, so just significantly reduced the molecular chain that exposes, the winding of molecular chain when having reduced the double-layer films contact, thereby the solution adhesion problems, the LLDPE of gained has opening performance preferably.
Gonda van Essche[Gonda van Essche, Thomas Kromminga, AndreasSchmidt.JOURNAL OF PLASTIC FILM﹠amp; SHEETING, VOL.16-APRIL2000,155-168] a kind of silicon-dioxide with large pore volume of synthetic can effectively improve its antiblocking effect in polyolefin film, even under the low like this content of 1000-1500ppm, the stiction force of film can be reduced to 0.4N, can improve the material scratch resistance simultaneously.
[summary of the invention]
The purpose of this invention is to provide a kind of new composite anti-blocking agent that is applied to the LLDPE film and using method thereof.
Objects of the present invention are achieved through the following technical solutions.
Opening agent of the present invention comprises following component: silicon-dioxide, Sodium Benzoate, wherein the mass ratio of silicon-dioxide and Sodium Benzoate was generally 25: 75 to 90: 10, preferred 50: 50 to 80: 20.
The preparation method of opening agent of the present invention is: at first Sodium Benzoate is dissolved in the deionized water, and silicon sol and Sodium Benzoate solution stirring is even, again the solution that mixes is carried out spraying drying, obtain the mixture of silicon-dioxide and Sodium Benzoate.
The present invention also provides a kind of using method of described opening agent, comprise the steps: to add described opening agent and oxidation inhibitor in the linear low density polyethylene together, through adding blown film in the inflation film manufacturing machine behind the extruding pelletization, the consumption 0.1-1phr of its split shed agent (every hectogram umber, it is the linear low density polyethylene matrix of each hundred umber, the consumption of opening agent is 0.1-1 part), preferred 0.2-0.5phr; The present invention does not have particular requirement to oxidation inhibitor and the processing aid that is adopted, and is the general oxidation inhibitor and the processing aid of polyolefin resin processing, and its addition is difference with the difference of end article purposes, generally is 0.01~1phr of polyvinyl resin matrix.For example, oxidation inhibitor can be following one or more mixture: four [β-(3 ', 5 '-di-t-butyl-4 '-hydroxy phenyl) propionic acid] pentaerythritol ester (being antioxidant 1010); (2, the 4-di-tert-butyl-phenyl) tris phosphite (being oxidation inhibitor 168); Processing aid is as Zinic stearas.
Composite anti-blocking agent of the present invention is applied in the LLDPE blown film goods, and the film opening excellent property, the frictional coefficient that obtain are low, and film stretching intensity obviously improves, and over-all properties is good.
[embodiment]
The raw material that adopts in the embodiment is the linear low density polyethylene powder.
Spraying drying is equipped for spray drying experiment device (QP-3X model, Beijing northization are ground petrochemical industry designing institute and produced), 140~170 ℃ of processing inlet temperature ranges, 40~70 ℃ of temperature outs.
The equipment of extruding pelletization can be twin screw extruder, single screw extrusion machine.
165~220 ℃ of the temperature ranges of blown film equipment processing.
Testing standard
Film blocking test method GB/T 16276-1996
Film friction coefficient is measured GB/T 10006-88
Film resistance to tearing test method Ai Laimenduofufa GB 11999-89
Film stretching test method GB/T 1040.3-2006
The free dart method of film shock resistance test method GB 9639-1988A method
Embodiment 18404
50 gram Sodium Benzoates (Wuhan flourishing age Fine Chemical Works) are dissolved in the 150 gram deionized waters, add 200 gram silicon sol (ZA-25, SiO again
2Concentration 25%, the chemical plant, Qingdao, pH value about 7), with laboratory high-shearing dispersion emulsifying machine (FA25, FLUKO produces) stirred 30 minutes with 10000 rpms, in spray drying experiment device (QP-3X model, Beijing northization are ground petrochemical industry designing institute and produced), spray, obtain the mixture of Sodium Benzoate and silicon-dioxide.With 12.5 gram said mixtures and antioxidant 1010 (0.5 gram), 168 (2 grams), Zinic stearas (2.5 gram) join 2500 gram linear low density polyethylene powder (melting index 1-1.2g/10min, density 0.917-0.919g/cm simultaneously
3) in, height is mixed and is closed even back twin screw (model C TE35, the mechanical company limited of times Long Keya of section (Nanjing)) granulation, temperature 160-195 ℃, add blown film in the inflation film manufacturing machine (Lvshun, Dalian forcing machine factory) again, temperature 165-200 ℃, film thickness 28-32 micron, 27 centimetres of flat widths, 17 centimetres of frost line height.The dependence test of sample the results are shown in Table 1.
Comparative example 1:8400
Except that the mixture that does not use Sodium Benzoate and silicon-dioxide, all the other are identical with embodiment 1.The dependence test that makes sample the results are shown in Table 1.
Embodiment 2:8403
The Sodium Benzoate of use among the embodiment 1 and the mixture of silicon-dioxide are got 5 grams, and all the other are identical with embodiment 1.The dependence test that makes sample the results are shown in Table 1.
Embodiment 3:8402
20 gram Sodium Benzoates (Wuhan flourishing age Fine Chemical Works) are dissolved in the 60 gram deionized waters, add 320 gram silicon sol (ZA-25, SiO again
2Concentration 25%, the chemical plant, Qingdao, pH value about 7), with laboratory high-shearing dispersion emulsifying machine (FA25, FLUKO produces) stirred 30 minutes with 10000 rpms, in spray drying experiment device (QP-3X model, Beijing northization are ground petrochemical industry designing institute and produced), spray, obtain the mixture of Sodium Benzoate and silicon-dioxide.With 12.5 gram said mixtures and antioxidant 1010 (0.5 gram), 168 (2 grams), Zinic stearas (2.5 gram) join 2500 gram linear low density polyethylene powder (melting index 1-1.2g/10min, density 0.917-0.919g/cm simultaneously
3) in, height is mixed and is closed even back twin screw (model C TE35, the mechanical company limited of times Long Keya of section (Nanjing)) granulation, temperature 160-195 ℃, add blown film in the inflation film manufacturing machine (Lvshun, Dalian forcing machine factory) again, temperature 165-200 ℃, film thickness 28-32 micron, 27 centimetres of flat widths, 17 centimetres of frost line height.The dependence test of sample the results are shown in Table 1.
Embodiment 4:8401
The Sodium Benzoate of use among the embodiment 3 and the mixture of silicon-dioxide are got 5 grams, and all the other are identical with embodiment 3.The dependence test that makes sample the results are shown in Table 1.
Comparative example 2:8405
With 100 gram silicon sol (ZA-25, SiO
2Concentration 25%, chemical plant, Qingdao, pH value about 7), spraying in spray drying experiment device (QP-3X model, Beijing northization are ground petrochemical industry designing institute and produced) obtains silicon-dioxide.With 12.5 above-mentioned silicon-dioxide of gram and antioxidant 1010 (0.5 gram), 168 (2 grams), Zinic stearas (2.5 gram) join 2500 gram linear low density polyethylene powder (melting index 1-1.2g/10min, density 0.917-0.919g/cm simultaneously
3) in, height is mixed and is closed even back twin screw (model C TE35, the mechanical company limited of times Long Keya of section (Nanjing)) granulation, temperature 160-195 ℃, add blown film in the inflation film manufacturing machine (Lvshun, Dalian forcing machine factory) again, temperature 165-200 ℃, film thickness 28-32 micron, 27 centimetres of flat widths, 17 centimetres of frost line height.The dependence test of sample the results are shown in Table 1.
Comparative example 3:8406
The silicon-dioxide that uses in the comparative example 2 is got 5 grams, and all the other are identical with comparative example 2.The dependence test that makes sample the results are shown in Table 1.
The mixture that in LLDPE, adds silicon-dioxide and Sodium Benzoate, Sodium Benzoate content is 20~50%, and the stiction force of LLDPE film all has obvious decline, does not more add the comparative example 1 of opening agent as embodiment 1, stiction force is reduced to 0.06 newton from 0.82 newton, and the opening performance obviously improves.The tensile strength of the vertical and horizontal of film all has raising after having added the opening agent, for example compare the comparative example 1 that does not add the opening agent among the embodiment 4, longitudinal tensile strength has been brought up to 29MPa from 20.9MPa, transverse tensile strength is brought up to 24.4MPa from 22.9MPa, and dart impact strength also increases.And do not add Sodium Benzoate, directly use SiO
2As the comparative example 3 of opening agent, tensile strength has small size raising, but not as the effect of the mixture that adds silicon-dioxide and Sodium Benzoate obvious.
The mixture that spraying drying makes after adopting Sodium Benzoate to mix with silicon-dioxide adds the blown film product that makes among the LLDPE, the opening performance obviously improves, and the tensile strength at vertical and horizontal all improves to some extent, and obtains the LLDPE film article of high comprehensive performance.
The every performance of film * * of table 1.LLDPE prescription * and preparation
*During above LLDPE film granulation, oxidation inhibitor is 0.02phr1010,0.08phr168,0.1phr Zinic stearas.
*30 microns of film thickness average out to.
Claims (4)
1. composite anti-blocking agent that is used for linear low-density polyethylene film comprises following component: silicon-dioxide, Sodium Benzoate, and wherein the mass ratio of silicon-dioxide and Sodium Benzoate is 25: 75 to 90: 10,
And adopt following method preparation: at first Sodium Benzoate is dissolved in the deionized water, silicon sol and Sodium Benzoate solution stirring is even, again the solution that mixes is carried out spraying drying, obtain the mixture of silicon-dioxide and Sodium Benzoate.
2. opening agent according to claim 1, wherein the mass ratio of silicon-dioxide and Sodium Benzoate is 50: 50 to 80: 20.
3. claim 1 or 2 described opening agent are in the using method of preparation in the linear low-density polyethylene film, comprise the steps: to add described opening agent and oxidation inhibitor in the linear low density polyethylene together, through adding blown film in the inflation film manufacturing machine, the consumption 0.1-1phr of its split shed agent behind the extruding pelletization.
4. using method according to claim 3, its split shed agent consumption 0.2-0.5phr.