CN101911935B - Bamboo fiber coiled mosquito-repellent incense and preparation method thereof - Google Patents
Bamboo fiber coiled mosquito-repellent incense and preparation method thereof Download PDFInfo
- Publication number
- CN101911935B CN101911935B CN 201010246151 CN201010246151A CN101911935B CN 101911935 B CN101911935 B CN 101911935B CN 201010246151 CN201010246151 CN 201010246151 CN 201010246151 A CN201010246151 A CN 201010246151A CN 101911935 B CN101911935 B CN 101911935B
- Authority
- CN
- China
- Prior art keywords
- bamboo fiber
- bamboo
- fiber coiled
- mosquito
- repellent incense
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention relates to a coiled mosquito-repellent incense, in particular to a bamboo fiber coiled mosquito-repellent incense prepared from bamboo pulp as the main raw material and a preparation method thereof. The coiled mosquito-repellent incense comprises bamboo fiber coiled blank and a mosquito-repellent medicament, wherein the bamboo fiber coiled blank comprises the following components in percentage by weight: 70 to 90 percent of bamboo fiber, 3 to 20 percent of charcoal powder and 3 t 15 percent of light calcium carbonate. The preparation method comprises the following steps of: 1) defibering the bamboo pulp serving as the raw material, thoroughly washing and concentrating the bamboo pulp and putting the concentrated bamboo pulp into a fiberizer for defibrination to obtain the bamboo fiber pulp; 2) mixing the bamboo fiber pulp, the charcoal powder and the light calcium carbonate, stirring the mixture, manufacturing a flaky substrate with the pulp and performing cold pressing and punch forming on the flaky substrate to obtain the bamboo fiber coiled blank; and 3) spraying the mosquito-repellent medicament on the bamboo fiber coiled blank to obtain the bamboo fiber coiled incense. The coiled mosquito-repellent incense and the preparation method have the characteristics of safety, environmental-protection, low cost, high combustion performance, lighter weight, high strength and high tearing resistance.
Description
Technical field
The present invention relates to a kind of coiled mosquito-repellent incense, relate in particular to and adopt bamboo pulp as a kind of bamboo fiber coiled mosquito-repellent incense of primary raw material and preparation method thereof.
Background technology
At present, the manufacturing of traditional coiled mosquito-repellent incense all is that primary raw material adds a large amount of chemical binder compression mouldings with the charcoal powder, because the charcoal powder light weight causes dust from flying in the workshop, has a strong impact on production environment and operating personnel are healthy.In addition, the charcoal resource shortage of China own uses charcoal powder to strengthen the consumption of timber in a large number, and timber burns till charcoal powder influences environment equally.
For addressing the above problem, people begin to develop the papery mosquito-repellent incense, as the disclosed a kind of paper special for mosquito coil of Chinese invention patent notification number CN100590256 and production technology thereof, all be to utilize waste paper and charcoal powder to make, but have foreign material such as a large amount of printing ink, plastics in the waste paper.If foreign material such as the printing ink in the waste paper, plastics are removed, these foreign material itself just pollute the environment; Make mosquito-repellent incense as not removing, have a large amount of toxic smogs and smell to produce so in burning, the consumer can smell niff, and these toxic smogs also can influence the healthy of consumer.Therefore, how to make more environmental protection of coiled mosquito-repellent incense, safer and reduce its manufacturing cost, become the problem that relevant enterprise is needed solution badly.
Summary of the invention
The object of the present invention is to provide a kind of safety, environmental protection, bamboo fiber coiled mosquito-repellent incense cheaply, it has good combustibility, weight is lighter, and has intensity height, characteristics that degree of resistance to demolition is high.Another object of the present invention provides the preparation method of above-mentioned bamboo fiber coiled mosquito-repellent incense, but this method has large-scale production, and production cost is low, the characteristics little to environmental influence.
The present invention solves the problems of the technologies described above by following technical proposals: a kind of bamboo fiber coiled mosquito-repellent incense, comprise bamboo fiber coiled blank and anophelifuge, described bamboo fiber coiled blank comprises following component by weight percentage: bamboo fibre 70%-90%, charcoal powder 3%-20%, precipitated calcium carbonate 3%-15%.
As preferably, described bamboo fiber coiled blank comprises following component by weight percentage: bamboo fibre 70%-80%, charcoal powder 10%-20%, precipitated calcium carbonate 10%-15%.
As preferably, described bamboo fiber coiled blank comprises following component by weight percentage: bamboo fibre 80%-90%, charcoal powder 3%-10%, precipitated calcium carbonate 3%-10%.
As preferably, described bamboo fiber coiled blank comprises following component by weight percentage: bamboo fibre 85%, charcoal powder 10%, precipitated calcium carbonate 5%.
As preferably, described bamboo fiber coiled blank comprises following component by weight percentage: bamboo fibre 90%, charcoal powder 3%, precipitated calcium carbonate 7%.
As preferably, described bamboo fiber coiled blank comprises following component by weight percentage: bamboo fibre 80%, charcoal powder 15%, precipitated calcium carbonate 5%.
A kind of preparation method of bamboo fiber coiled mosquito-repellent incense comprises the steps:
1), the bamboo pulp raw material discongested and fully washing, concentrate, put into paste mill grinding then, make the bamboo fibre slurry;
2), with bamboo fibre slurry and charcoal powder, precipitated calcium carbonate mixing stirring is manufactured paper with pulp and is made the base material of sheet, by colding pressing, punch forming makes bamboo fiber coiled blank;
3), spray anophelifuge at above-mentioned bamboo fiber coiled blank, make bamboo fiber coiled mosquito-repellent incense.
As preferably, the concentration of the slurry that concentrates in the step 1 is 5%-6%.
As preferably, to make the degree of beating of slurry be 40 ° of SR-50 ° of SR to paste mill grinding in the step 1.
As preferably, the thickness 2mm-3.5mm of the bamboo fiber coiled blank that makes in the step 2, fragrant bar length 1400mm-1800mm.Certainly, can also print various patterns on the bamboo fibre base material in step 2.
Adopt its beneficial effect of invention of the technical program as follows:
The present invention uses the content 70%-90% of bamboo fibre, and the smog that product burning back is produced significantly reduces, and also can send bamboo class special delicate fragrance after the bamboo fibre burning; Adopted the 3%-20% charcoal powder to use as combustion adjuvant simultaneously, mosquito-repellent incense can not stopped working, yield rate improves greatly.The present invention has improved mosquito incense burning by reasonably filling a prescription, the mosquito-repellent incense that makes (double plate 15 grams ~ 25 grams) in light weight, and traditional mosquito-repellent incense is 32 ~ 45 grams.
Because it is raw material that the present invention adopts clean bamboo pulp, so water can be recycling, sewage does not outflow, and can not impact environment.By squeezing process, make the product burning very slow, can save big content of starting materials.The mosquito-repellent incense cardboard that makes also has other some characteristic, as the deformable of shape except the characteristic with mosquito-repellent incense application, can print etc., thereby can be made into differently, the coiled mosquito-repellent incense with different decorative patterns, literal etc. has been broken the single shortcoming of traditional mosquito-repellent incense outward appearance.
The present invention selects for use bamboo pulp as primary raw material, and its reason is that also bamboo can be for the manufacture of the plant of mosquito-repellent incense with respect to other, and its growth cycle is shorter, more is conducive to environmental protection.And at present domestic have a large amount of bamboo groves to distribute, bamboo product is being accepted by the consumer more and more widely also, one band in the Jiangsu and Zhejiang Provinces particularly, bamboo product manufacturing firm can produce a large amount of discarded bamboo material in process of production, and bamboo pulp can be purchased and manufacture to these bamboo material by bamboo pulp factory.At present, the market price of bamboo pulp per ton only has only 1/5th of waste paper, therefore can reduce production costs greatly.
Embodiment
Embodiment 1
A kind of preparation method of bamboo fiber coiled mosquito-repellent incense comprises the steps:
1), the bamboo pulp raw material discongested and fully washing, concentrate, wherein the concentration of the slurry of Nong Suoing is 5%, puts into paste mill grinding then, degree of beating is 45 ° of SR, makes the bamboo fibre slurry;
2), with bamboo fibre slurry and charcoal powder, precipitated calcium carbonate mixing stirring, be equivalent to bamboo fibre 85%, charcoal powder 10%, precipitated calcium carbonate 5% by weight percentage, manufacture paper with pulp and make the base material of sheet, by the dehydration of colding pressing, make bamboo fiber coiled blank with the mould punch forming again, the thickness 2.5mm of bamboo fiber coiled blank, fragrant bar length 1500mm.
3), spray anophelifuge at above-mentioned bamboo fiber coiled blank, make bamboo fiber coiled mosquito-repellent incense.
Its burning-point time was greater than 8 hours, and is not flame-out, and smog is little.
Embodiment 2
Difference from Example 1 is, wherein bamboo fibre 90%, charcoal powder 7%, precipitated calcium carbonate 3%.The thickness of bamboo fiber coiled blank is 2.6mm, fragrant bar length 1500mm.Use the burning-point time greater than 8 hours 20 minutes, not flame-out, smog is little.
Embodiment 3
Difference from Example 1 is, wherein bamboo fibre 90%, charcoal powder 5%, precipitated calcium carbonate 5%.The thickness of bamboo fiber coiled blank is 2.9mm, fragrant bar length 1700mm.Use the burning-point time greater than 8 hours 40 minutes, not flame-out, smog is little.
Embodiment 4
Difference from Example 1 is, wherein 90%, charcoal powder 3%, precipitated calcium carbonate 7%.The thickness of bamboo fiber coiled blank is 3.1mm, fragrant bar length 1700mm.Use the burning-point time greater than 9 hours, not flame-out, smog is little.
Embodiment 5
Difference from Example 1 is, wherein bamboo fibre 80%, charcoal powder 15%, precipitated calcium carbonate 5%.The thickness of bamboo fiber coiled blank is 2mm, fragrant bar length 1400mm.Use the burning-point time greater than 7 hours 20 minutes, flame-out and smog is little.
Embodiment 6
Difference from Example 1 is, wherein bamboo fibre 70%, charcoal powder 15%, precipitated calcium carbonate 15%.The thickness of bamboo fiber coiled blank is 3.5mm, fragrant bar length 1700mm.Use the burning-point time greater than 7 hours, flame-out and smog is little.
The above only is preferred embodiment of the present invention, and all equalizations of doing according to the present patent application claim change and modify, and all should belong to the covering scope of patent of the present invention.
Claims (6)
1. bamboo fiber coiled mosquito-repellent incense, comprise bamboo fiber coiled blank and anophelifuge, it is characterized in that described bamboo fiber coiled blank is composed of the following components by weight percentage: bamboo fibre 70%-90%, charcoal powder 3%-20%, precipitated calcium carbonate 3%-15%; The preparation method of bamboo fiber coiled mosquito-repellent incense may further comprise the steps:
1), the bamboo pulp raw material discongested and fully washing, concentrate, the concentration of the slurry that concentrates is 5%-6%, puts into paste mill grinding then, it is 40 ° of SR-50 ° of SR that paste mill grinding makes the degree of beating of slurry, makes the bamboo fibre slurry;
2), with bamboo fibre slurry and charcoal powder, precipitated calcium carbonate mixing stirring is manufactured paper with pulp and is made the base material of sheet, by colding pressing, punch forming makes bamboo fiber coiled blank, and the thickness of bamboo fiber coiled blank is 2mm-3.5mm, and fragrant bar length is 1400mm-1800mm;
3), spray anophelifuge at above-mentioned bamboo fiber coiled blank, make bamboo fiber coiled mosquito-repellent incense.
2. a kind of bamboo fiber coiled mosquito-repellent incense according to claim 1 is characterized in that, described bamboo fiber coiled blank is composed of the following components by weight percentage: bamboo fibre 70%-80%, charcoal powder 10%-20%, precipitated calcium carbonate 10%-15%.
3. a kind of bamboo fiber coiled mosquito-repellent incense according to claim 1 is characterized in that, described bamboo fiber coiled blank is composed of the following components by weight percentage: bamboo fibre 80%-90%, charcoal powder 3%-10%, precipitated calcium carbonate 3%-10%.
4. a kind of bamboo fiber coiled mosquito-repellent incense according to claim 1 is characterized in that, described bamboo fiber coiled blank is composed of the following components by weight percentage: bamboo fibre 85%, charcoal powder 10%, precipitated calcium carbonate 5%.
5. a kind of bamboo fiber coiled mosquito-repellent incense according to claim 1 is characterized in that, described bamboo fiber coiled blank is composed of the following components by weight percentage: bamboo fibre 90%, charcoal powder 3%, precipitated calcium carbonate 7%.
6. a kind of bamboo fiber coiled mosquito-repellent incense according to claim 1 is characterized in that, described bamboo fiber coiled blank is composed of the following components by weight percentage: bamboo fibre 80%, charcoal powder 15%, precipitated calcium carbonate 5%.