Background technology
Nano silica powder is a kind of Performances of Novel Nano-Porous meter level amorphous solid material, is a kind of nontoxic, tasteless, free of contamination ceramic, at aspects such as construction industry, chemical industry, space flight and aviation industry, agriculturals important use is arranged all.Nano silica powder demonstrates unusual characteristic at aspects such as sound, light, electricity, magnetic and thermodynamics, is widely used in aspects such as microelectronics, information material, coating, rubber, plastics, crop seeds treatment agent, rumbling compound, high grade refractory and papermaking.Development nanometer grade silica material is produced high purity, high-tech product is one of current research focus.
The method for preparing at present nano silica powder is a lot, but no matter is vapor phase process, or liquid-phase precipitation method, all has problems such as conversion unit requirement height, complex process, cost height.Additive method also has combustion method, sol-gel method, carburizing reagent method, reverse micelle sol method etc.Methods such as wherein carburizing reagent method, inverse micellar solution method prepare superfine silicon dioxide, and it exists ME loaded down with trivial details, the not high defective of resultant purity.And the combustion method complex process; The grain diameter that obtains with the precipitator method is big, short texture; High with traditional sol-gel method thermal treatment temp, the Si-OH silanol on the silica sphere is removed by high temperature, and easy reunion of progenitor grows up.
Summary of the invention
The technical problem that the present invention solves is to provide a kind of preparation method of preparing spherical SiO 2 nano-powder, and this method technology is simple, with short production cycle, required equipment is simple, can prepare the spherical nano-silicon dioxide powder of regular shape, good dispersivity.
The present invention realizes through following technical scheme:
A kind of preparation method of preparing spherical SiO 2 nano-powder may further comprise the steps:
1) Hydrocerol A being dissolved in volumetric concentration is that the amount of ammoniacal liquor is as the criterion can dissolve Hydrocerol A in 25~28% the ammoniacal liquor, and then according to tetraethoxy: the mol ratio of Hydrocerol A=1: 1~1.5 adds tetraethoxy, stirs to make the tetraethoxy dissolving; Add absolute ethyl alcohol and terepthaloyl moietie more successively, the absolute ethyl alcohol consumption is 1/3~1/2 of an ammoniacal liquor volume, and the mol ratio of terepthaloyl moietie and Hydrocerol A is 1: 1.5~2, is heated to 50~60 ℃ of stirrings it is dissolved fully; Behind ammoniacal liquor accent pH value to 7.0~8.0,80~90 ℃ of water-baths evaporations are until obtaining wet gel;
2) wet gel is carried out the drying foaming under 130~140 ℃ of conditions and obtain xerogel;
3) xerogel is carried out calcining at constant temperature at 600~850 ℃, take out behind calcining 3~5h, obtain nano silica powder.
Described wet gel carries out the drying foaming under air atmosphere.
Described xerogel carries out calcining at constant temperature under air atmosphere.
Described nano silica powder is a kind of preparing spherical SiO 2 nano-powder, and its particle size is 20~100nm.
Compared with prior art, the present invention has following beneficial technical effects:
The preparation method of a kind of preparing spherical SiO 2 nano-powder provided by the invention; Because tetraethoxy will all be converted into silicon-dioxide; In this preparation process, do not introduce impurity such as cl ions, need not the suction filtration cleaning, can shorten preparation cycle to remove impurity; And ammoniacal liquor, organic substance Hydrocerol A and polyoxyethylene glycol bring into play through water-bath and remove, and all the other remain in and can be carbonized in the calcination process and remove, and the purity of prepared nano silica powder is high, good dispersivity.
The preparation method of preparing spherical SiO 2 nano-powder provided by the invention, it is simple also to have production technique, easy to operate, and preparation cycle is short, and productive rate is higher, and facility investment is few, the advantage that cost is low.
Embodiment
Embodiment 1
The preparation method of preparing spherical SiO 2 nano-powder may further comprise the steps:
1) Hydrocerol A 192.14g (1mol) being dissolved in volumetric concentration is in 25% the 200ml ammoniacal liquor, then according to tetraethoxy: the mol ratio of Hydrocerol A=1: 1 adds tetraethoxy, stirs and makes the tetraethoxy dissolving; Add the absolute ethyl alcohol of 100ml and the terepthaloyl moietie of 0.5mol more successively, be heated to 50 ℃ of stirrings it is dissolved fully; With being made into precursor behind the ammoniacal liquor accent pH value to 7.0, evaporate until the wet gel that obtains white 80 ℃ of water-baths;
2) wet gel is carried out the drying foaming in 130 ℃ stove, under the air atmosphere condition, obtain xerogel;
3) xerogel is carried out calcining at constant temperature putting into kiln under 600 ℃, air atmosphere condition, take out the spherical nano-silicon dioxide powder that obtains loosening behind the calcining 5h.
The SEM photo of gained preparing spherical SiO 2 powder is as shown in Figure 1, and the gained silicon-dioxide powdery is complete spherical, good dispersivity, and even particle size distribution, particle size is about 20~50nm.
Embodiment 2
The preparation method of preparing spherical SiO 2 nano-powder may further comprise the steps:
1) Hydrocerol A 192.14g (1mol) being dissolved in volumetric concentration is in 25% the 200ml ammoniacal liquor, then according to tetraethoxy: the mol ratio of Hydrocerol A=1: 2 adds tetraethoxy, stirs and makes the tetraethoxy dissolving; The absolute ethyl alcohol and the 0.67mol terepthaloyl moietie that add 66ml more successively are heated to 60 ℃ of stirrings it are dissolved fully; With being made into precursor behind the ammoniacal liquor accent pH value to 8.0, evaporate until the wet gel that obtains white 90 ℃ of water-baths;
2) wet gel is carried out the drying foaming in 140 ℃ stove, under the air atmosphere condition, obtain xerogel;
3) xerogel is carried out calcining at constant temperature putting into kiln under 750 ℃, air atmosphere condition, take out behind the calcining 5h, the spherical nano-silicon dioxide powder that obtains loosening, its particle size is 50~100nm.
Embodiment 3
The preparation method of preparing spherical SiO 2 nano-powder may further comprise the steps:
1) Hydrocerol A 192.14g (1mol) being dissolved in volumetric concentration is in 28% the 200ml ammoniacal liquor, then according to tetraethoxy: the mol ratio of Hydrocerol A=1: 1.2 adds tetraethoxy, stirs and makes the tetraethoxy dissolving; Add 80ml absolute ethyl alcohol and 0.6mol terepthaloyl moietie more successively, be heated to 55 ℃ of stirrings it is dissolved fully; With being made into precursor behind the ammoniacal liquor accent pH value to 8.0, evaporate until the wet gel that obtains white 85 ℃ of water-baths;
2) wet gel is carried out the drying foaming in 145 ℃ stove, under the air atmosphere condition, obtain xerogel;
3) xerogel is carried out calcining at constant temperature putting into kiln under 700 ℃, air atmosphere condition, take out behind the calcining 4h, the spherical nano-silicon dioxide powder that obtains loosening, its particle size is 50~100nm.
Embodiment 4
The preparation method of preparing spherical SiO 2 nano-powder may further comprise the steps:
1) Hydrocerol A 192.14g (1mol) being dissolved in volumetric concentration is in 28% the 200ml ammoniacal liquor, then according to tetraethoxy: the mol ratio of Hydrocerol A=1: 1.8 adds tetraethoxy, stirs and makes the tetraethoxy dissolving; Add 90ml absolute ethyl alcohol and 0.6mol terepthaloyl moietie more successively, be heated to 58 ℃ of stirrings it is dissolved fully; With being made into precursor behind the ammoniacal liquor accent pH value to 7.5, evaporate until the wet gel that obtains white 83 ℃ of water-baths;
2) wet gel is carried out the drying foaming in 138 ℃ stove, under the air atmosphere condition, obtain xerogel;
3) xerogel is carried out calcining at constant temperature putting into kiln under 650 ℃, air atmosphere condition, take out behind the calcining 2.5h, the spherical nano-silicon dioxide powder that obtains loosening, its particle size is 20~100nm.
Embodiment 5
The preparation method of preparing spherical SiO 2 nano-powder may further comprise the steps:
1) Hydrocerol A 192.14g (1mol) being dissolved in volumetric concentration is in 25% the 200ml ammoniacal liquor, then according to tetraethoxy: the mol ratio of Hydrocerol A=1: 1.6 adds tetraethoxy, stirs and makes the tetraethoxy dissolving; Add 100ml absolute ethyl alcohol and 0.55mol terepthaloyl moietie more successively, be heated to 58 ℃ of stirrings it is dissolved fully; With being made into precursor behind the ammoniacal liquor accent pH value to 7.2, evaporate until the wet gel that obtains white 90 ℃ of water-baths;
2) wet gel is carried out the drying foaming in 136 ℃ stove, under the air atmosphere condition, obtain xerogel;
3) xerogel is carried out calcining at constant temperature putting into kiln under 720 ℃, air atmosphere condition, take out behind the calcining 3h, the spherical nano-silicon dioxide powder that obtains loosening, its particle size is 20~80nm.