CN101862468A - Aquasol self-adhesive elastic bandage and manufacturing method thereof - Google Patents
Aquasol self-adhesive elastic bandage and manufacturing method thereof Download PDFInfo
- Publication number
- CN101862468A CN101862468A CN 201010171978 CN201010171978A CN101862468A CN 101862468 A CN101862468 A CN 101862468A CN 201010171978 CN201010171978 CN 201010171978 CN 201010171978 A CN201010171978 A CN 201010171978A CN 101862468 A CN101862468 A CN 101862468A
- Authority
- CN
- China
- Prior art keywords
- aquasol
- fabric
- self
- adhesive
- elastic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to an aquasol self-adhesive elastic bandage which comprises aquasol and elastic fabric, and the formula of the aquasol is as follows: 62 to 90 percent of emulsion adhesive, 0.1 to 10 percent of tackifier, 0.5 to 20 percent of softener, 0.001 to 2 percent of age inhibitor, 0.1 to 5 percent of environmental-friendly additive and 0.1 to 1 percent of colorant; the elastic fabric is one type of elastic cotton fabric, elastic chemical fiber fabric, elastic chemical fiber/cotton blended fabric; the manufacturing process comprises the following steps that: first, mixing the aquasol by the component, then selecting one type of the elastic cotton fabric, the elastic chemical fiber fabric, the elastic chemical fiber/cotton blended fabric as the backup fabric, putting the mixed aquasol into gluing equipment, uniformly applying the aquasol onto the prepared elastic fabric through rolling, spray coating, roll coating, scrape coating and extrusion coating processes, and manufacturing aquasol self-adhesive elastic bandage products with various specifications through a rolling device. The products manufactured through the method have the advantages of good air permeability, comfortable feel, no mildew after long-termed storage, convenient use and the like.
Description
Technical field
The present invention relates to medical bandage, specifically it relates to a kind of Aquasol self-adhesive elastic bandage and production method thereof.
Background technology
Self-adhesive elastic bandage has two types: a kind of is the natural emulsion self-adhesive elastic bandage, mainly with natural emulsion for making in the two-sided gluing of Elastic bandage from adhesive, because natural emulsion contains protein substance, long-term storage can be gone mouldy, so that can cause skin allergy; Another kind is a self-adhesive elastic bandage made from rubber polymer, mainly be dissolved in gasoline as making in the two-sided gluing of Elastic bandage from adhesive with polyisoprene rubber, because its course of processing is used gasoline, has not only increased cost, but also has caused environmental pollution and energy waste.
Therefore, research and develop a kind of self-adhesive elastic bandage of making by the water solublity self-adhesive, have crucial technical meaning.
Summary of the invention
The purpose of this invention is to provide a kind of environment-friendly type, long-term storage do not go mouldy, not sensitization, good permeability, feel comfortable Aquasol self-adhesive elastic bandage and manufacture method thereof, be intended to overcome the technological deficiency that natural emulsion and synthetic rubber exist in the prior art.
Purpose of the present invention is achieved through the following technical solutions:
Aquasol self-adhesive elastic bandage, characteristics are: described binder is made up of the hydrosol and stockinette, the described hydrosol comprises following components in weight percentage: emulsion adhesive 62～90%, viscosifier 0.1～10%, softening agent 0.5～20%, age resistor 0.001～2%, environmental-protection additive 0.1～5%, coloring agent 0.1～1%; Described stockinette is a kind of in cotton stretch, elastic force chemical ﹠ blended fabric, the elastic force chemical fibre/cotton blended fabric.
Further, above-mentioned Aquasol self-adhesive elastic bandage, wherein, described hydrosol component has following percentage by weight: emulsion adhesive 83.3%, viscosifier 10%, softening agent 5%, age resistor 1%, environmental-protection additive 0.5%, coloring agent 0.2%.
Further, above-mentioned Aquasol self-adhesive elastic bandage, wherein, described emulsion adhesive is one or more the mixture in polyaminoester emulsion, polyacrylate dispersion, benzene emulsion, Silicone acrylic emulsion, pure-acrylic emulsion, the neoprene latex; Described viscosifier are one or more in butyl polyacrylate, Petropols, terpene resin, the 12 carbon alcohol esters; Described softening agent is one or more in white oil, tween, lanoline, silicone oil softener, glycerol, PEPA, dibutyl phthalate, the low molecular poly; Described age resistor is that 2,6 ditertiary butyl p cresol (also claiming antioxidant 264), styrenated phenol (also claiming age resistor sp), two (3,5-two-tertiary butyl-4-hydroxy benzyl) thioether (also claim a kind of in the age resistor methene-4426-S); Described environmental-protection additive is a nano silver antimicrobials; Described coloring agent is a kind of in zinc oxide, the titanium dioxide.
The manufacture method of Aquasol self-adhesive elastic bandage of the present invention comprises following processing step:
(1) the preparation hydrosol:
Press following set of dispense controlling the water circulation colloidal sol: emulsion adhesive 62～90%, viscosifier 0.1～10%, softening agent 0.5～20%, age resistor 0.001～2%, environmental-protection additive 0.1～5%, coloring agent 0.1～1%;
(2) stockinette is got the raw materials ready:
Choose a kind of conduct in cotton stretch, elastic force chemical ﹠ blended fabric, elastic force chemical fibre/cotton blended fabric fabric of getting the raw materials ready;
(3) stockinette gluing:
The hydrosol that step (1) prepares is put into glue application device, by calendering, spraying, roller coating, blade coating, coating tech the hydrosol is evenly distributed on the fabric that step (2) gets ready, makes the Aquasol self-adhesive elastic bandage product of different size again by volume device.
Substantive distinguishing features and obvious improvement that technical solution of the present invention is outstanding are mainly reflected in:
1. the present invention adopts the hydrosol, has overcome the natural emulsion product and has gone mouldy easily, wound is had dysgenic technological deficiency;
2. adopt the hydrosol, overcome that the rubber polymer product uses petrolic solvent in manufacture process and the defective that causes energy waste, contaminated environment;
3. the product of producing by process of the present invention reaches medical sanitary level quality, has good permeability, feels advantage such as comfortable, easy to use, and long-term storage do not go mouldy, sensitization not.
The specific embodiment
Aquasol self-adhesive elastic bandage of the present invention, form by the hydrosol and stockinette, the hydrosol comprises following components in weight percentage: emulsion adhesive 62～90%, viscosifier 0.1～10%, softening agent 0.5～20%, age resistor 0.001～2%, environmental-protection additive 0.1～5%, coloring agent 0.1～1%; Stockinette is a kind of in cotton stretch, elastic force chemical ﹠ blended fabric, the elastic force chemical fibre/cotton blended fabric.The ideal formulations of the hydrosol is: emulsion adhesive 83.3%, viscosifier 10%, softening agent 5%, age resistor 1%, environmental-protection additive 0.5%, coloring agent 0.2%.
Wherein, emulsion adhesive is one or more the mixture in polyaminoester emulsion, polyacrylate dispersion, benzene emulsion, Silicone acrylic emulsion, pure-acrylic emulsion, the neoprene latex; Viscosifier are one or more in butyl polyacrylate, Petropols, terpene resin, the 12 carbon alcohol esters; Softening agent is one or more in white oil, tween, lanoline, silicone oil softener, glycerol, PEPA, dibutyl phthalate, the low molecular poly; Age resistor is that 2,6 ditertiary butyl p cresol (also claiming antioxidant 264), styrenated phenol (also claiming age resistor sp), two (3,5-two-tertiary butyl-4-hydroxy benzyl) thioether (also claim a kind of in the age resistor methene-4426-S); Environmental-protection additive is a nano silver antimicrobials; Coloring agent is a kind of in zinc oxide, the titanium dioxide.
The manufacture method of Aquasol self-adhesive elastic bandage of the present invention comprises following processing step:
(1) the preparation hydrosol: press following set of dispense controlling the water circulation colloidal sol: emulsion adhesive 62～90%, viscosifier 0.1～10%, softening agent 0.5～20%, age resistor 0.001～2%, environmental-protection additive 0.1～5%, coloring agent 0.1～1%;
(2) stockinette is got the raw materials ready: choose a kind of conduct in cotton stretch, elastic force chemical ﹠ blended fabric, elastic force chemical fibre/cotton blended fabric fabric of getting the raw materials ready;
(3) stockinette gluing: the hydrosol that step (1) prepares is put into glue application device, by calendering, spraying, roller coating, blade coating, coating tech the hydrosol is evenly distributed on the fabric that step (2) gets ready, makes the Aquasol self-adhesive elastic bandage product of different size again by volume device.
Embodiment 1
Hydrosol preparation:
According to following set of dispense controlling the water circulation colloidal sol: polyacrylate dispersion 70%, ten two carbon alcohol ester 10%, white oil 16%, 2,6 ditertiary butyl p cresol 1%, nanometer silver is received antibacterial 2%, zinc oxide 1.0%;
Fabric is got the raw materials ready:
Select for use the burr cotton to add elastic filament, 21 cottons of warp, 16 cottons of parallel, elastic filament 280 Denier (denir), thread count 120～150; Perhaps select for use cotton creppella to add elastic filament, 32 cottons of warp, 16 cottons of parallel, elastic filament 210 Denier (denir), thread count 120～150;
The fabric gluing:
The hydrosol for preparing is put into glue application device, the hydrosol is evenly coated on the fabric of getting ready, make the hydrosol self-adhering fascia product of different size again by volume device, the packing warehouse-in by calendering, spraying, roller coating, blade coating, coating tech.
Embodiment 2
Hydrosol preparation:
According to following set of dispense controlling the water circulation colloidal sol: polyaminoester emulsion 80%, terpene resin 8%, glycerol 4.2%, styrenated phenol 2%, nano silver antimicrobials 5%, titanium dioxide 0.8%;
Fabric is got the raw materials ready:
Select the novel elastic chemical ﹠ blended fabric for use, this fabric adds elastic filament for the pp non-woven fabrics, elastic filament 70 Denier (denir), density 28g/m
2
The fabric gluing:
The hydrosol for preparing is put into glue application device, the hydrosol is evenly coated on the fabric of getting ready, make the hydrosol self-adhering fascia product of different size again by volume device, the packing warehouse-in by calendering, spraying, roller coating, blade coating, coating tech.
Embodiment 3
Hydrosol preparation:
According to following set of dispense controlling the water circulation colloidal sol: neoprene latex 86%, terpene resin 9.9%, lanoline 0.5%, 2,6 ditertiary butyl p cresol 1.5%, nano silver antimicrobials 2%, titanium dioxide 0.1%;
Fabric is got the raw materials ready:
Select novel elastic chemical fibre/cotton blended fabric for use, this fabric adds elastic filament for the pp tearable non-woven fabric, elastic filament 70 Denier (denir), density 28g/m
2
The fabric gluing:
The hydrosol for preparing is put into glue application device, the hydrosol is evenly coated on the fabric of getting ready, make the hydrosol self-adhering fascia product of different size again by volume device, the packing warehouse-in by calendering, spraying, roller coating, blade coating, coating tech.
Embodiment 4
Hydrosol preparation:
According to following set of dispense controlling the water circulation colloidal sol: benzene emulsion 90%, butyl polyacrylate 0.1%, tween 8.799%, two (3,5-two-tertiary butyl-4-hydroxy benzyl) thioether 0.001%, nano silver antimicrobials 0.1%, titanium dioxide 1%;
Fabric is got the raw materials ready:
Select novel elastic chemical fibre/cotton blended fabric for use, this fabric adds elastic filament for the pp tearable non-woven fabric, elastic filament 70 Denier (denir), density 28g/m
2
The fabric gluing:
The hydrosol for preparing is put into glue application device, the hydrosol is evenly coated on the fabric of getting ready, make the hydrosol self-adhering fascia product of different size again by volume device, the packing warehouse-in by calendering, spraying, roller coating, blade coating, coating tech.
Embodiment 5
Hydrosol preparation:
According to following set of dispense controlling the water circulation colloidal sol: pure-acrylic emulsion 62%, ten two carbon alcohol ester 10%, PEPA 20%, two (3,5-two-tertiary butyl-4-hydroxy benzyl) thioether 2%, nano silver antimicrobials 5%, titanium dioxide 1.0%;
Fabric is got the raw materials ready:
Select novel elastic chemical fibre/cotton blended fabric for use, this fabric adds elastic filament for the pp tearable non-woven fabric, elastic filament 70 Denier (denir), density 28g/m
2
The fabric gluing:
The hydrosol for preparing is put into glue application device, the hydrosol is evenly coated on the fabric of getting ready, make the hydrosol self-adhering fascia product of different size again by volume device, the packing warehouse-in by calendering, spraying, roller coating, blade coating, coating tech.
Embodiment 6
Hydrosol preparation:
According to following set of dispense controlling the water circulation colloidal sol: Silicone acrylic emulsion 83.3%, Petropols 10%, dibutyl phthalate 5%, styrenated phenol 1%, nano silver antimicrobials 0.5%, titanium dioxide 0.2%;
Fabric is got the raw materials ready:
Select novel elastic chemical fibre/cotton blended fabric for use, this fabric adds elastic filament for the pp tearable non-woven fabric, elastic filament 70 Denier (denir), density 28g/m
2
The fabric gluing:
The hydrosol for preparing is put into glue application device, the hydrosol is evenly coated on the fabric of getting ready, make the hydrosol self-adhering fascia product of different size again by volume device, the packing warehouse-in by calendering, spraying, roller coating, blade coating, coating tech.
After testing, the Aquasol self-adhesive elastic bandage that adopts technical solution of the present invention to obtain, its main performance index sees Table 1.
Table 1
| Test item | Embodiment 1 | Embodiment 2 | Embodiment 3 | Embodiment 4 | Embodiment 5 | Embodiment 6 |
| Shearing force (N) | ??37.4 | ??24.3 | ??27.9 | ??25.2 | ??30.7 | ??31.9 |
| Peeling force (N) | ??2.51 | ??1.83 | ??2.02 | ??1.87 | ??1.94 | ??2.23 |
In sum, the present invention adopts the hydrosol, has overcome the natural emulsion product and has gone mouldy easily, wound is had dysgenic technological deficiency; Adopt the hydrosol, overcome that the rubber polymer product uses petrolic solvent in manufacture process and the defective that causes energy waste, contaminated environment; Product by process of the present invention is produced reaches medical sanitary level quality, has good permeability, feels advantage such as comfortable, easy to use, and long-term storage do not go mouldy, sensitization not.
What need understand is: the above only is a preferred implementation of the present invention; for those skilled in the art; under the prerequisite that does not break away from the principle of the invention, can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (9)
1. Aquasol self-adhesive elastic bandage, it is characterized in that: described binder is made up of the hydrosol and stockinette, the described hydrosol comprises following components in weight percentage: emulsion adhesive 62～90%, viscosifier 0.1～10%, softening agent 0.5～20%, age resistor 0.001～2%, environmental-protection additive 0.1～5%, coloring agent 0.1～1%; Described stockinette is a kind of in cotton stretch, elastic force chemical ﹠ blended fabric, the elastic force chemical fibre/cotton blended fabric.
2. Aquasol self-adhesive elastic bandage according to claim 1 is characterized in that: described hydrosol component has following percentage by weight: emulsion adhesive 83.3%, viscosifier 10%, softening agent 5%, age resistor 1%, environmental-protection additive 0.5%, coloring agent 0.2%.
3. Aquasol self-adhesive elastic bandage according to claim 1 and 2 is characterized in that: described emulsion adhesive is one or more the mixture in polyaminoester emulsion, polyacrylate dispersion, benzene emulsion, Silicone acrylic emulsion, pure-acrylic emulsion, the neoprene latex.
4. Aquasol self-adhesive elastic bandage according to claim 1 and 2 is characterized in that: described viscosifier are one or more in butyl polyacrylate, Petropols, terpene resin, the 12 carbon alcohol esters.
5. Aquasol self-adhesive elastic bandage according to claim 1 and 2 is characterized in that: described softening agent is one or more in white oil, tween, lanoline, silicone oil softener, glycerol, PEPA, dibutyl phthalate, the low molecular poly.
6. Aquasol self-adhesive elastic bandage according to claim 1 and 2 is characterized in that: described age resistor is a kind of in 2,6 ditertiary butyl p cresol, styrenated phenol, two (3,5-two-tertiary butyl-4-hydroxy benzyl) thioether.
7. Aquasol self-adhesive elastic bandage according to claim 1 and 2 is characterized in that: described environmental-protection additive is a nano silver antimicrobials.
8. Aquasol self-adhesive elastic bandage according to claim 1 and 2 is characterized in that: described coloring agent is a kind of in zinc oxide, the titanium dioxide.
9. the manufacture method of the described Aquasol self-adhesive elastic bandage of claim 1 is characterized in that comprising following processing step:
(1) the preparation hydrosol:
Press following set of dispense controlling the water circulation colloidal sol: emulsion adhesive 62～90%, viscosifier 0.1～10%, softening agent 0.5～20%, age resistor 0.001～2%, environmental-protection additive 0.1～5%, coloring agent 0.1～1%;
(2) stockinette is got the raw materials ready:
Choose a kind of conduct in cotton stretch, elastic force chemical ﹠ blended fabric, elastic force chemical fibre/cotton blended fabric fabric of getting the raw materials ready;
(3) stockinette gluing:
The hydrosol that step (1) prepares is put into glue application device, by calendering, spraying, roller coating, blade coating, coating tech the hydrosol is evenly distributed on the stockinette that step (2) gets ready, makes the Aquasol self-adhesive elastic bandage product of different size again by volume device.