CN101845168A - Environment-friendly, antiflaming and antistatic foaming material and preparation method thereof - Google Patents
Environment-friendly, antiflaming and antistatic foaming material and preparation method thereof Download PDFInfo
- Publication number
- CN101845168A CN101845168A CN 201010163872 CN201010163872A CN101845168A CN 101845168 A CN101845168 A CN 101845168A CN 201010163872 CN201010163872 CN 201010163872 CN 201010163872 A CN201010163872 A CN 201010163872A CN 101845168 A CN101845168 A CN 101845168A
- Authority
- CN
- China
- Prior art keywords
- environment
- mentioned
- weight part
- foam material
- environmental protection
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an environment-friendly, antiflaming and antistatic foaming material and a preparation method thereof. The foaming material is mainly prepared by blending the following ingredients in parts by weight: 100 parts of foaming-level EVA or LDPE, 27 to 49.5 parts of environment-friendly fire retardant and 6 to 20 parts of antistatic agent. Prepared by blending the foaming-level EVA or LDPE, the environment-friendly fire retardant and the antistatic agent, the invention has environment-friendly, antiflaming and antistatic properties.
Description
Technical field
The present invention relates to a kind of foam material, especially a kind of foam material with environment-protection flame-proof electrostatic resistance performance.
Background technology
In industrial production, some use occasions require foamed products to have antistatic property, as antistatic shoes, antistatic packaging, antistatic ground cushion, antistatic work top etc., some use occasions require foamed products to have flame retardant properties, then require foamed products to have antistatic property and flame retardant properties simultaneously in some special use occasions.The foam material of existing foaming technique production has flame-retardant foam material, antistatic foaming material is also arranged, but do not have the foam material of the two function concurrently.
Summary of the invention
The purpose of this invention is to provide a kind of environment-protection flame-proof electrostatic resistance foam material, the performance of its existing environmental protection flame retardant has anlistatig performance again.
Another object of the present invention provides a kind of method for preparing above-mentioned environment-protection flame-proof electrostatic resistance foam material.
Technical scheme of the present invention is such: the environment-protection flame-proof electrostatic resistance foam material, mainly form by following weight part component:
Foaming other EVA of level or LDPE 100
Environmental protection fire retarding agent 27-49.5
Static inhibitor 6-20.
Above-mentioned environmental protection fire retarding agent comprises TDE and antimonous oxide, and wherein, the consumption of TDE is the 18-30 weight part, and the consumption of antimonous oxide is the 9-19.5 weight part.
Above-mentioned static inhibitor is the conductive carbon black with excellent conductive capability.
The preparation method of environment-protection flame-proof electrostatic resistance foam material, be achieved by the following scheme: environmental protection fire retarding agent and the 6-20 weight part static inhibitor of preparing 100 weight parts foaming other EVA of level or LDPE, 27-49.5 weight part earlier, together drop into mixing according to the mixing mode of routine above-mentioned EVA or LDPE and above-mentioned environmental protection fire retarding agent then, treating above-mentioned EVA or LDPE and above-mentioned environmental protection fire retarding agent, mixing to drop into above-mentioned static inhibitor again after evenly mixing once more, until mixing fully evenly till.
Above-mentioned environmental protection fire retarding agent comprises TDE and antimonous oxide, and wherein, the consumption of TDE is the 18-30 weight part, and the consumption of antimonous oxide is the 9-19.5 weight part.
Above-mentioned static inhibitor is the conductive carbon black with excellent conductive capability.
After adopting such scheme, environment-protection flame-proof electrostatic resistance foam material of the present invention adopts foaming other EVA of level or LDPE, environmental protection fire retarding agent and static inhibitor blend to form, and has environmental protection flame retardant performance and antistatic property simultaneously.And, selected fire retardant of the present invention and anti-quiet dose of fire retardant that belongs to filled-type and anti-quiet dose, molecular structure stabilized own has permanently, makes to have nonvolatil environment-protection flame-proof electrostatic resistance performance by foam material of the present invention.
Embodiment
Environment-protection flame-proof electrostatic resistance foam material of the present invention, mainly form by following weight part component:
Foaming other EVA of level or LDPE 100
Environmental protection fire retarding agent 27-49.5
Static inhibitor 6-20.
The preparation method of environment-protection flame-proof electrostatic resistance foam material of the present invention, be achieved by the following scheme: environmental protection fire retarding agent and the 6-20 weight part static inhibitor of preparing other EVA of 100 weight parts foaming level (the molten 2.0-5.0 of finger) or LDPE (the molten 1.5-2.2 of finger), 27-49.5 weight part earlier, together drop into mixing according to the mixing mode of routine above-mentioned EVA or LDPE and above-mentioned environmental protection fire retarding agent then, treating above-mentioned EVA or LDPE and above-mentioned environmental protection fire retarding agent, mixing to drop into above-mentioned static inhibitor again after evenly mixing once more, until mixing fully evenly till.
In the present embodiment: environmental protection fire retarding agent is selected TDE and antimonous oxide for use, and wherein, the consumption of TDE is the 18-30 weight part, and concrete consumption can be 24 weight parts; The consumption of antimonous oxide is the 9-19.5 weight part, and concrete consumption can be 14 weight parts; Static inhibitor is selected the conductive carbon black with excellent conductive capability for use, and the concrete consumption of conductive carbon black can be 13 weight parts.
Claims (6)
1. environment-protection flame-proof electrostatic resistance foam material is characterized in that: mainly be made up of following weight part component:
Foaming other EVA of level or LDPE 100
Environmental protection fire retarding agent 27-49.5
Static inhibitor 6-20.
2. environment-protection flame-proof electrostatic resistance foam material according to claim 1, it is characterized in that: above-mentioned environmental protection fire retarding agent comprises TDE and antimonous oxide, wherein, the consumption of TDE is the 18-30 weight part, and the consumption of antimonous oxide is the 9-19.5 weight part.
3. environment-protection flame-proof electrostatic resistance foam material according to claim 1 is characterized in that: above-mentioned static inhibitor is the conductive carbon black with excellent conductive capability.
4. the preparation method of environment-protection flame-proof electrostatic resistance foam material, it is characterized in that: be achieved by the following scheme: environmental protection fire retarding agent and the 6-20 weight part static inhibitor of preparing 100 weight parts foaming other EVA of level or LDPE, 27-49.5 weight part earlier, together drop into mixing according to the mixing mode of routine above-mentioned EVA or LDPE and above-mentioned environmental protection fire retarding agent then, treating above-mentioned EVA or LDPE and above-mentioned environmental protection fire retarding agent, mixing to drop into above-mentioned static inhibitor again after evenly mixing once more, until mixing fully evenly till.
5. the preparation method of environment-protection flame-proof electrostatic resistance foam material according to claim 4, it is characterized in that: above-mentioned environmental protection fire retarding agent comprises TDE and antimonous oxide, wherein, the consumption of TDE is the 18-30 weight part, and the consumption of antimonous oxide is the 9-19.5 weight part.
6. the preparation method of environment-protection flame-proof electrostatic resistance foam material according to claim 4 is characterized in that: above-mentioned static inhibitor is the conductive carbon black with excellent conductive capability.