CN101844199A - Production method of aluminium alloy lock panel connecting column - Google Patents
Production method of aluminium alloy lock panel connecting column Download PDFInfo
- Publication number
- CN101844199A CN101844199A CN 201010158125 CN201010158125A CN101844199A CN 101844199 A CN101844199 A CN 101844199A CN 201010158125 CN201010158125 CN 201010158125 CN 201010158125 A CN201010158125 A CN 201010158125A CN 101844199 A CN101844199 A CN 101844199A
- Authority
- CN
- China
- Prior art keywords
- aluminium alloy
- lock panel
- panel
- connecting column
- production method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to the lock field and provides a production method of aluminium alloy lock panel connecting column. The production method includes the following steps: (1) aluminium alloy round bar or rectangular bar is punched or subject to lathe processing to be in the required size; (2) aluminium alloy panel is subject to blanking by a mould, is punched into the required size and then is stretched and moulded into the required shape; (3) the two parts are completed and then forging and stamping are carried out, the aluminium alloy panel is placed into a tunnel heating furnace, is subject to preheating and heat perseveration and then is taken out at 490-530 DEG C, the aluminium alloy panel is placed into the mould and pressure is adjusted according to requirement, and meanwhile the aluminium alloy connecting column is placed into the mould, and the lock panel and the connecting column are subject to one-step forging and stamping. The lock panel of the invention is subject to aluminium alloy forging, the produced aluminium alloy lock panel product is subject to further post treatment, the produced lock panel connecting column is stable in connection, high in rigidity, difficult to fade and anti-static, and post treatment is easy to be carried out on the lock panel.
Description
Technical field
The present invention relates to the lock field, relate in particular to a kind of production method of lock panel connecting column.
Background technology
Lock panel on the market adopts the kirsite manufacturing mostly at present, be to adopt zinc alloy diecasting, plating or injector surface etc., lock panel with this technology manufacturing, exist overlay coating easily to come off, color is single, use after about 1 year, special ugly, higher or the like the shortcoming and defect of antistatic, cost not just seems.
Make panel with aluminium alloy, also the someone developed in the past, but all failed, a kind of do not have intensity with aluminium die casting, product, the surface can not anode, can only electroplate or the oil spout effect does not have the good of kirsite, and a period of time does not just have market, two kinds have the people also the lock handle to be made of the forging mode, but can not do good intensity and surface of good effect.It more than is a great problem of lock industry.The no one can solve.
Present lock panel all is to adopt the mode of joint pin to be connected with base plate.
Summary of the invention
The technical problem to be solved in the present invention is the above-mentioned shortcoming that overcomes prior art, provides a kind of novel employing aluminium alloy to make the production method of lock panel connecting column.
The production method of aluminium alloy lock panel connecting column of the present invention, its scheme may further comprise the steps:
(1) prepares the aluminium alloy joint pin: become required size by punching press or machined into aluminium alloy pole or square bar;
(2) prepare aluminium alloy lock panel: aluminium alloy panel mould blanking, strike out required size, drawing and forming is to required shape then;
(3) forging and pressing: above two parts forge and press after finishing again, aluminium alloy panel is put into the tunnel heating furnace, by preheating, heating, being incubated tapping temperature is 490～530 ℃, put into mould and mix up the pressure size on demand, simultaneously the aluminium alloy joint pin is put into mould, with lock panel and forging forming of joint pin.
In order to make the present invention reach better effect, the tapping temperature of step (3) can be preferred 500～520 ℃.
Better for the surface property that makes lock panel, can carry out following processing to lock panel: again lock panel is heat-treated to HB37 after forging and pressing, the product after the heat treatment is removed rim charge earlier, then according to handle, turn-knob the position punching press is set, hole, tapping.
Also can further comprise the steps: the section of the side of manual polishing lock panel, vibrate the surface 2～4 hours of water mill polishing lock panel then.
Also can further comprise the steps: to do and throw: walnut grain and polishing agent with 20～40, slightly threw 5～7 hours, threw 3～5 hours with 60～100 walnut grains are smart again.
Also can further comprise the steps: the smart anode processing of throwing afterwards again.
Described aluminium alloy joint pin is preferably AL6061, AL6063.
When selecting Al6061 for use, before step (2) is heat-treated, also the aluminium alloy joint pin is carried out T4, T6 and handle, AL6061 carries out T5 to be handled.
Joint pin is used to connect the front and back panel (rear board is base plate again) of lock, be located at the back side of the front panel of lock, traditional method is one-body molded or be welded to connect post and make in the mode of back side of panel by the mode of cast molding and panel, and shortcoming is to be difficult for surface treatment, and is not attractive in appearance.The present invention adopts riveted way to make, and adopts aluminium alloy to make, and the intensity height is easy to surface treatment, attractive in appearance.
The aluminum alloy forged mode of lock panel, former no one did, because two of this products are high protruding, area is big, the wall book is very big, impossible in theory with forging mode difficulty.The application passes through process modification, a panel is disposable to process to adopt the riveted joint mode to combine with forging and pressing, the kirsite panel drawback that adopted aluminum alloy forged process improving, the colour stable of product, and color is various, can need collocation arbitrarily with the client, and antistatic, product strength is better than kirsite, and the produce market future is huge.
The aluminium alloy lock panel products of being produced is carried out further post processing, solved the defective that aluminium alloy is difficult to make high-quality surface; Improved the hardness of aluminium alloy panel and joint pin by heat treatment; Improve glossing (prior art all adopts manual polishing, throws technology with mechanical dry now), also adopt anode processing technique then, make aluminum alloy surface reach preferable effect, solved the problem that kirsite panel of the prior art fades easily.
The specific embodiment
Below provide preferred embodiments more of the present invention, to help further to understand technical scheme of the present invention.
The production method of embodiment 1 aluminium alloy lock panel connecting column
(1) prepares the aluminium alloy joint pin: become required size by punching press or machined into aluminium alloy pole or square bar;
(2) prepare aluminium alloy lock panel: aluminium alloy panel mould blanking, strike out required size, drawing and forming is to required shape then;
(3) forging and pressing: above two parts forge and press after finishing again, aluminium alloy panel is put into the tunnel heating furnace, by preheating, heating, being incubated tapping temperature is 490～530 ℃, put into mould and mix up the pressure size on demand, simultaneously the aluminium alloy joint pin is put into mould, with lock panel and forging forming of joint pin.
The production method of embodiment 2 aluminium alloy lock panel connecting columns
(1) prepares the aluminium alloy joint pin: become required size by punching press or machined into the aluminium alloy pole;
(2) prepare aluminium alloy lock panel: aluminium alloy panel mould blanking, strike out required size, drawing and forming is to required shape then;
(3) forging and pressing: above two parts forge and press after finishing again, aluminium alloy panel is put into the tunnel heating furnace, by preheating, heating, being incubated tapping temperature is 500～520 ℃, put into mould and mix up the pressure size on demand, simultaneously the aluminium alloy joint pin is put into mould, with lock panel and forging forming of joint pin.
The further surface treatment of 3 couples of embodiment 1 of embodiment and embodiment 2 products obtained therefroms
(4) lock panel is heat-treated to about HB37 after forging and pressing, the product after the heat treatment is removed rim charge earlier again, then according to handle, turn-knob the position punching press is set, hole, tapping.
(5) section of the side of manual polishing lock panel vibrates the surface 2～4 hours of water mill polishing lock panel then.
(6) do to throw: remove earlier batch cutting edge of a knife or a sword and burr and big surperficial bad with vibropolish earlier, use dry-fine then: walnut grain and polishing agent with 20～40, slightly threw 5～7 hours, again with 80～100 walnut grains essence throwing 3～5 hours.
(7) anode processing again after smart the throwing.
Embodiment 4 is assembled into lock
Lock panel connecting column after embodiment 3 processing and other accessory of lock are assembled into lock.
The preparation of embodiment 5 aluminium alloy lock panel connecting columns
(1) become required size with the aluminium alloy pole by punching press or machined into, if AL6061 handles about HB90-95 through T4, T6, AL6063T5 handles about HB37.
(2) aluminium alloy panel mould blanking strikes out required size, then drawing and forming to required definite shape so that forging forming goes out high-quality product.
(3) above two parts forge and press after finishing again, aluminium alloy panel are put into the tunnel heating furnace, by preheating, heating, be incubated about 500 ℃ of tapping temperatures, put into mould and mix up the pressure size, simultaneously the aluminium alloy joint pin is put into forging forming of mould.
The foregoing description is a preferred implementation of the present invention; but embodiments of the present invention are not restricted to the described embodiments; other any do not deviate from change, the modification done under spiritual essence of the present invention and the principle, substitutes, combination, simplify; all should be the substitute mode of equivalence, be included within protection scope of the present invention.
Claims (4)
1. the production method of aluminium alloy lock panel connecting column is characterized in that, may further comprise the steps:
(1) prepares the aluminium alloy joint pin: become required size by punching press or machined into aluminium alloy pole or square bar;
(2) prepare aluminium alloy lock panel: aluminium alloy panel mould blanking, strike out required size, drawing and forming is to required shape then;
(3) forging and pressing: above two parts forge and press after finishing again, aluminium alloy panel is put into the tunnel heating furnace, heat by preheating, being incubated tapping temperature is 490～530 ℃, put into mould and mix up the pressure size on demand, simultaneously the aluminium alloy joint pin is put into mould, with lock panel and forging forming of joint pin.
2. the production method of aluminium alloy lock panel connecting column according to claim 1 is characterized in that, the tapping temperature in the step (3) is 500～520 ℃.
3. according to the production method of claim 1 or 2 described aluminium alloy lock panel connecting columns, it is characterized in that described aluminium alloy joint pin is AL6061, AL6063.
4. the production method of aluminium alloy lock panel connecting column according to claim 3 is characterized in that, before step (2) is heat-treated, the AL6061 joint pin is carried out T4, T6 handle, AL6063 carries out T5 and handles.