CN101819856A - Anti-explosion dehumidifying solvent for transformer and manufacturing method thereof - Google Patents
Anti-explosion dehumidifying solvent for transformer and manufacturing method thereof Download PDFInfo
- Publication number
- CN101819856A CN101819856A CN 201010147221 CN201010147221A CN101819856A CN 101819856 A CN101819856 A CN 101819856A CN 201010147221 CN201010147221 CN 201010147221 CN 201010147221 A CN201010147221 A CN 201010147221A CN 101819856 A CN101819856 A CN 101819856A
- Authority
- CN
- China
- Prior art keywords
- transformer
- solvent
- dehumidifying
- explosion
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides an anti-explosion dehumidifying solvent for a transformer, aiming at the defects of easy kerosene volatilization and accident occurrence of a dewatering medium, i.e. kerosene used for large-size oil transformer, in operation. The anti-explosion dehumidifying solvent for the transformer is prepared by a plurality of chemical raw materials according to a certain process. The invention has few raw materials, simple production process, production without three wastes discharge and low boiling point of produced mixed solvent, can greatly enhance the production safety factor of the large-size oil cooling transformer, prevents the accidents, can be repeatedly used for multiple times and reduces the production cost.
Description
Affiliated technical field
The invention discloses a kind of anti-explosion dehumidifying solvent for transformer and manufacture method thereof, belong to the chemical products production technical field, the product that this method is produced is mainly used in the large-scale oil cooled transformer of ultra-high voltage transformer station.
Background technology
The high-power transformer that ultra-high voltage transformer station is used needs oil cooling but, in the cooling transformer process that produces oil, before perfusion transformer heat conduction cold oil operation, the high-power transformer integrated member must be carried out the dehumidifying processed, make the moisture content of high-power transformer integrated member drop to ten thousand/below, during processing integrated member is flooded kerosene in the vacuum impregnation jar, allow kerosene be penetrated in the capillary micropore of insulating material, utilize the dissolution of kerosene to micro-moisture, micro-moisture in the transformer integrated member and kerosene are thoroughly removed totally, in the horizontal degassing tank of high vacuum, heat then and carry out secondary vacuum and handle, the lamination wood that uses in the particularly large-scale oil cooled transformer, cable paper, hydrophilic insulants such as fiberglass products, all need handle, to guarantee its insulativity through this operation.But there is following defective in this treatment process: this is because kerosene can volatilization gas when handling, the gas that kerosene volatilizes is flammable explosive gas, though the operation of this link requirement is very strict, potential risks still exist, in case misoperation will set off an explosion, consequence is very serious.
Summary of the invention
Volatile at the kerosene that this dehydration medium of kerosene of large-scale oil change use is in operation, as to cause the accident easily defective, the invention provides a kind of anti-explosion dehumidifying solvent for transformer, it is not only simple to operate but also be safe from danger to utilize this anti-explosion dehumidifying solvent for transformer that transformer is carried out the deep dehydration of integrated member.
Taked following technical scheme for realizing purpose of the present invention:
A kind of anti-explosion dehumidifying solvent for transformer, this anti-explosion dehumidifying solvent for transformer are that the feedstock production by following weight portion forms: industry anhydrous ethanol, acetone, toluene, ethyl acetate, carbon dichloride, inorganic dehydrating agent; The consumption of each raw material is respectively by weight:
Industry anhydrous ethanol 5-70 part, acetone 5-90 part, toluene 5-30 part, ethyl acetate, 5-30 part, carbon dichloride 5-20 part, inorganic dehydrating agent 5-15 part.
The present invention also provides the preparation method of this anti-explosion dehumidifying solvent for transformer simultaneously, and its preparation method is:
Raw material → add inorganic dehydrating agent → stirring → filtration → finished product.
Whipping temp among the preparation technology of the present invention is 20 ℃-30 ℃, and mixing time is 1-2 hour.
Raw material of the present invention can be one or more in ethanol, acetone, toluene, ethyl acetate, the carbon dichloride.
Remarkable advantage of the present invention is raw materials used few, and production technology is simple, three-waste free discharge in the production; The mixed solvent boiling point of producing is low, can greatly improve the production safety coefficient of large-scale oil cooled transformer, and the accident of stopping takes place; Can repeatedly use repeatedly, reduce production costs.
Specific embodiments
Further specify technical characterictic of the present invention below in conjunction with embodiment:
Embodiment 1
Get industry anhydrous ethanol 70kg, acetone 80kg, toluene 30kg joins in the mixing tank, adds inorganic dehydrating agent 15kg part, mixes under 25 ℃ 1.5 hours, filters finished product through plate and frame filter press.
Embodiment 2
Get industrial alcohol 60kg, ethyl acetate 30kg, carbon dichloride 10kg, toluene 20kg join in the mixing tank, add inorganic dehydrating agent 10kg, mix under 20 ℃ 2 hours, filter finished product through plate and frame filter press.
Embodiment 3
Get ethyl acetate 50kg, carbon dichloride 20kg, toluene 60kg joins in the mixing tank, adds inorganic dehydrating agent 15kg, mixes under 30 ℃ 1 hour, filters finished product through plate and frame filter press.
Wherein: inorganic dehydrating agent can be one or both a mixture of anhydrous calcium chloride, calcium oxide etc.
Claims (4)
1. anti-explosion dehumidifying solvent for transformer is characterized in that this anti-explosion dehumidifying solvent for transformer is that feedstock production by following weight portion forms:
Industry anhydrous ethanol 5-70 part, acetone 5-90 part, toluene 5-30 part, ethyl acetate, 5-30 part, carbon dichloride 5-20 part, inorganic dehydrating agent 5-15 part.
2. by the preparation method of the described anti-explosion dehumidifying solvent for transformer of claim 1, it is characterized in that described preparation method is:
Raw material → add inorganic dehydrating agent → stirring → filtration → finished product.
3. by the preparation method of the described anti-explosion dehumidifying solvent for transformer of claim 2, it is characterized in that the whipping temp among the described preparation technology is 20 ℃-30 ℃, mixing time is 1-2 hour.
4. by the preparation method of the described anti-explosion dehumidifying solvent for transformer of claim 2, it is characterized in that described raw material can be one or more in ethanol, acetone, toluene, ethyl acetate, the carbon dichloride.