CN101786851B - Inorganic fireproofing insulation material and production process thereof - Google Patents

Inorganic fireproofing insulation material and production process thereof Download PDF

Info

Publication number
CN101786851B
CN101786851B CN2010100116387A CN201010011638A CN101786851B CN 101786851 B CN101786851 B CN 101786851B CN 2010100116387 A CN2010100116387 A CN 2010100116387A CN 201010011638 A CN201010011638 A CN 201010011638A CN 101786851 B CN101786851 B CN 101786851B
Authority
CN
China
Prior art keywords
insulation material
water
glass adhesive
solids content
water glass
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN2010100116387A
Other languages
Chinese (zh)
Other versions
CN101786851A (en
Inventor
金�畅
金同芳
Original Assignee
金同芳
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 金同芳 filed Critical 金同芳
Priority to CN2010100116387A priority Critical patent/CN101786851B/en
Publication of CN101786851A publication Critical patent/CN101786851A/en
Application granted granted Critical
Publication of CN101786851B publication Critical patent/CN101786851B/en
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention relates to an inorganic fireproofing insulation material, which is prepared with the following raw materials: water glass adhesive (with the solid content being 40-85 percent), calcium carbonate, alumina, zinc oxide, magnesium oxide, fine flint clay powder, titanium dioxide powder, ferricoxide, red mud, chopped glass fiber (or nylon fiber), a foaming agent and a water repellent. The preparation process comprises the following steps: mixing the raw materials, forming, foaming and drying at a high temperature of 180-350 DEG C, and stripping, thereby obtaining the inorganic fireproofing insulation material. For the inorganic fireproofing insulation material, the weight is light and the insulation effect is good; the combustion performance reaches Class A national standards for fireproofing materials, the inorganic fireproofing insulation material is a non-combustible material with high temperature resistance against the temperature of 800-2100 DEG C; the cost is low and the application scope is wide; and the strength is high with pressure resistance against the pressure of 0.2-12MPa, and the inorganic fireproofing insulation material has certain toughness simultaneously. The production process needs no coal combustion and generates no 'three wastes' emission, thereby belonging to clean production. Moreover, the production process can save energy and water, and the inorganic fireproofing insulation material is non-toxic and tasteless, has no harmful radiation, and belongs to the 'green fireproofing insulation material'.

Description

A kind of inorganic fireproofing insulation material and manufacture craft thereof
Technical field
The invention belongs to building materials field, particularly a kind of inorganics that utilizes is made fire-retardant heat-insulation material technology.
Background technology
The common lagging material in lagging material market has following several both at home and abroad at present: 1) organic class lagging material: EPS polystyrene foamed material, XPS extrusion molding ethylene foam material, polyurethane foamed material etc.; 2) mineral-type lagging material: rock wool, slag wool, glass wool, pure aluminium silicate, cement (or flyash, magnesium oxide) foam material etc.; 3) organism and inorganics mixing lagging material: cement (or flyash) granular polystyrene concrete thermal-insulating material etc.There is following problem in above-mentioned lagging material.1) though organic class lagging material high insulating effect is in light weight, easy firing.Along with the attention of country to fire safety problem, and the building field fire safety rules widely popularize enforcement, its use range is more and more littler.2) though rock wool, mineral wool, glass wool fire resistance reach the requirement of A grade standard, production process power consumption, contaminate environment, its material itself has certain injury to human skin, and simultaneously, material cost is also high.Cement (or flyash) foam material, fire resistance reaches the requirement of A level, but unit weight is big, and every cubic metre more than 450 kilograms, and heat insulation effect is not good enough, only limits to body of wall and fills and use; The aluminosilicate material fire resistance also is the A level, and heat insulation effect is also fine, but the cost height costs an arm and a leg, and marketing is subjected to very big influence.3) cement (or flyash) granular polystyrene concrete material, though reach fire prevention, insulation requirement, unit weight is big, use range is being greatly limited property equally.
Summary of the invention
Technical problem to be solved by this invention provides a kind of inorganic fireproofing insulation material and manufacture craft thereof, and is in light weight, high insulating effect, and cost is low, and performance is good.
A kind of inorganic fireproofing insulation material technology of the present invention, it is characterized in that constitutive material is 40%~85% water glass adhesive by solids content, lime carbonate, aluminum oxide, zinc oxide, magnesium oxide, the flint clay fine powder, titanium dioxide, ferric oxide, red mud, short glass fiber (or nylon fiber) and whipping agent and water-resisting agent are formed, with the water glass adhesive solid contents is benchmark, according to the weight percentage meter, lime carbonate is 30%~50% of water glass adhesive solids content, aluminum oxide be its 3%~30%, zinc oxide be its 3%~20%, magnesium oxide be its 20%~60%, the flint clay fine powder be its 10%~50%, whipping agent be its 1.5%~8%, water-resisting agent be its 1.5%~6%, short glass fiber be its 2%~10% or nylon fiber for its 2%~5%, titanium dioxide be its 4%~9%, ferric oxide be its 7%~12%, red mud be its 12%~27%.
Manufacture craft is: each constitutive material is mixed in proportion stirring, through moulding (as tabular, bulk etc.), in 180 ℃~350 ℃ following high temperature foaming oven dry, the demoulding, can obtain the fireproof heat insulating foam materials.
Wherein the high temperature foaming can be undertaken by microwave, light wave or high temperature drying room mode after each constitutive material moulding, makes production process need not coal combustion, does not have " three wastes " discharging, belongs to cleaner production, energy-conservation, water saving.
Whipping agent of the present invention and water-resisting agent can adopt the general raw material of building material industry, and preferred whipping agent adopts animal protein foaming agent, and water-resisting agent adopts waterproofing agent of organosilicon or stearic acid water-resisting agent.
Advantage of the present invention:
1, in light weight, high insulating effect.Every cubic metre of unit weight only is 10 kilograms to 300 kilograms, and thermal conductivity is 0.020~0.095W/ (m.k).
2, combustionproperty reaches the requirement of national fire-retardant material A grade standard, is non-fire material, high temperature resistantly reaches 800 ℃~2100 ℃.
3, cost is low, profitable.Than other lagging materials, cost can reduce by 1/3rd to 2/3rds, helps wide popularization and application.
4, of many uses.Unit weight is at every cubic metre below 60 kilograms, can be used for the sandwich material of metal skinned sandwich panel, concrete composite lightweight wall plate and building roof heat insulation and external-wall heat-insulation material and uses, and also can be used for pipeline, boats and ships, freezer insulation; Unit weight can directly use as light cellular partition board at 280 kilograms to 300 kilograms; Because its outstanding high temperature resistance also can be used as refractory brick and uses.
5, make inorganics fireproof heat insulating foam materials owing to add short glass fiber (or nylon fiber), have higher intensity, resistance to compression 0.2~12MPa has certain toughness simultaneously.
6, production process need not coal combustion, does not have " three wastes " discharging, belongs to cleaner production, energy-conservation, water saving.
7, nontoxic, tasteless, no harmful radiation, genus " green fire-retardant heat-insulation material ".
Embodiment
Illustrate below in conjunction with embodiment.Be not specifically noted, described percentage ratio is weight percentage.
Embodiment 1:
Constitutive material is 60% water glass adhesive by solids content, lime carbonate, aluminum oxide, zinc oxide, magnesium oxide, the flint clay fine powder, titanium dioxide, ferric oxide, red mud, short glass fiber and whipping agent and water-resisting agent are formed, with the water glass adhesive solid contents is benchmark, according to the weight percentage meter, lime carbonate is 30% of water glass adhesive solids content, aluminum oxide is a water glass adhesive solids content 10%, zinc oxide is water glass adhesive solids content 15%, magnesium oxide (the order number is more than 180) is water glass adhesive solids content 60%, flint clay fine powder (the order number is more than 200) is a water glass adhesive solids content 10%, whipping agent (animal protein foaming agent, Shandong section Thailand builds construction equipment factory and produces) be 3% of water glass adhesive solids content, water-resisting agent (waterproofing agent of organosilicon, Jinan chemical industry company limited of state nation produces) be water glass adhesive solids content 6%, short glass fiber is a water glass adhesive solids content 10%, titanium dioxide is a water glass adhesive solids content 6%, ferric oxide is a water glass adhesive solids content 10%, red mud is a water glass adhesive solids content 20%, each constitutive material is mixed in proportion stirring, through moulding, 300 ℃ of following high temperature foaming oven dry, the demoulding can obtain the fireproof heat insulating foam materials.
Embodiment 2:
Constitutive material is 40% water glass adhesive by solids content, lime carbonate, aluminum oxide, zinc oxide, magnesium oxide, the flint clay fine powder, titanium dioxide, ferric oxide, red mud, short glass fiber and whipping agent and water-resisting agent are formed, with the water glass adhesive solid contents is benchmark, according to the weight percentage meter, lime carbonate is 50% of water glass adhesive solids content, aluminum oxide is a water glass adhesive solids content 20%, zinc oxide is water glass adhesive solids content 5%, magnesium oxide (the order number is more than 180) is water glass adhesive solids content 40%, flint clay fine powder (the order number is more than 200) is a water glass adhesive solids content 30%, whipping agent (animal protein foaming agent) is a water glass adhesive solids content 8%, water-resisting agent (waterproofing agent of organosilicon) is a water glass adhesive solids content 4%, short glass fiber is a water glass adhesive solids content 6%, titanium dioxide is a water glass adhesive solids content 9%, ferric oxide is a water glass adhesive solids content 12%, red mud is a water glass adhesive solids content 27%, each constitutive material is mixed in proportion stirring, through moulding, 350 ℃ of following high temperature foaming oven dry, the demoulding can obtain the fireproof heat insulating foam materials.
Embodiment 3:
Constitutive material is 85% water glass adhesive by solids content, lime carbonate, aluminum oxide, zinc oxide, magnesium oxide, the flint clay fine powder, titanium dioxide, ferric oxide, red mud, nylon fiber and whipping agent and water-resisting agent are formed, with the water glass adhesive solid contents is benchmark, according to the weight percentage meter, lime carbonate is 30% of water glass adhesive solids content, aluminum oxide is a water glass adhesive solids content 5%, zinc oxide is water glass adhesive solids content 20%, magnesium oxide (the order number is more than 180) is water glass adhesive solids content 20%, flint clay fine powder (the order number is more than 200) is a water glass adhesive solids content 10%, whipping agent (animal protein foaming agent) is a water glass adhesive solids content 1.5%, water-resisting agent (stearic acid water-resisting agent, the Hunan produces with fortune building materials Science and Technology Ltd.) be water glass adhesive solids content 1.5%, nylon fiber is a water glass adhesive solids content 2%, titanium dioxide is a water glass adhesive solids content 4%, ferric oxide is a water glass adhesive solids content 7%, red mud is a water glass adhesive solids content 12%, each constitutive material is mixed in proportion stirring, through moulding, 200 ℃ of following high temperature foaming oven dry, the demoulding can obtain the fireproof heat insulating foam materials.
Embodiment 4:
Constitutive material is 50% water glass adhesive by solids content, lime carbonate, aluminum oxide, zinc oxide, magnesium oxide, the flint clay fine powder, titanium dioxide, ferric oxide, red mud, nylon fiber and whipping agent and water-resisting agent are formed, with the water glass adhesive solid contents is benchmark, according to the weight percentage meter, lime carbonate is 40% of water glass adhesive solids content, aluminum oxide is a water glass adhesive solids content 20%, zinc oxide is water glass adhesive solids content 15%, magnesium oxide (the order number is more than 180) is water glass adhesive solids content 30%, flint clay fine powder (the order number is more than 200) is a water glass adhesive solids content 45%, whipping agent (animal protein foaming agent) is a water glass adhesive solids content 5%, water-resisting agent (stearic acid water-resisting agent) is a water glass adhesive solids content 4%, nylon fiber is a water glass adhesive solids content 5%, titanium dioxide is a water glass adhesive solids content 6%, ferric oxide is a water glass adhesive solids content 10%, red mud is a water glass adhesive solids content 18%, each constitutive material is mixed in proportion stirring, through moulding, 300 ℃ of following high temperature foaming oven dry, the demoulding can obtain the fireproof heat insulating foam materials.
The technical indicator of the fireproof heat insulating foam materials that obtains of embodiment 1 ~ 4 is after testing:
Technical indicator Embodiment 1 Embodiment 2 Embodiment 3 Embodiment 4
Unit weight, (kg/m 3) 40 60 25 120
Thermal conductivity W/ (m.k) 0.046 0.049 0.035 0.057
Combustionproperty The A level is not fired The A level is not fired The A level is not fired The A level is not fired
High temperature resistant, ℃ 1200 1200 1200 1200
Ultimate compression strength, Mpa (lagging material thickness is 100mm) 1.7 2.2 0.97 5.6

Claims (3)

1. inorganic fireproofing insulation material, it is characterized in that constitutive material is 40%~85% water glass adhesive by solids content, lime carbonate, aluminum oxide, zinc oxide, magnesium oxide, the flint clay fine powder, titanium dioxide, ferric oxide, red mud, short glass fiber or nylon fiber and whipping agent and water-resisting agent are formed, with the water glass adhesive solid contents is benchmark, according to the weight percentage meter, lime carbonate is 30%~50% of water glass adhesive solids content, aluminum oxide be its 3%~30%, zinc oxide be its 3%~20%, magnesium oxide be its 20%~60%, the flint clay fine powder be its 10%~50%, whipping agent be its 1.5%~8%, water-resisting agent be its 1.5%~6%, short glass fiber be its 2%~10% or nylon fiber for its 2%~5%, titanium dioxide be its 4%~9%, ferric oxide be its 7%~12%, red mud be its 12%~27%.
2. inorganic fireproofing insulation material according to claim 1 is characterized in that described whipping agent adopts animal protein foaming agent, and water-resisting agent adopts waterproofing agent of organosilicon or stearic acid water-resisting agent.
3. a technology of making the described inorganic fireproofing insulation material of claim 1 is characterized in that each constitutive material is mixed in proportion stirring, through moulding, in 180 ℃~350 ℃ following high temperature foaming oven dry, the demoulding, can obtain the fireproof heat insulating foam materials.
CN2010100116387A 2010-01-17 2010-01-17 Inorganic fireproofing insulation material and production process thereof Expired - Fee Related CN101786851B (en)