CN101769427A - Continuous forming process for bamboo fabric folding honeycomb plate - Google Patents
Continuous forming process for bamboo fabric folding honeycomb plate Download PDFInfo
- Publication number
- CN101769427A CN101769427A CN200810242542A CN200810242542A CN101769427A CN 101769427 A CN101769427 A CN 101769427A CN 200810242542 A CN200810242542 A CN 200810242542A CN 200810242542 A CN200810242542 A CN 200810242542A CN 101769427 A CN101769427 A CN 101769427A
- Authority
- CN
- China
- Prior art keywords
- bamboo
- fabric
- honeycomb
- folding
- plate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a continuous forming process for a bamboo fabric folding honeycomb plate, which cuts a bamboo fabric into a bamboo honeycomb core by folding. The bamboo honeycomb core is unfolded into a bamboo honeycomb by being stretched. The bamboo honeycomb together with the bamboo fabric and other cladding materials is matched with a sandwich or a binding layer to be compounded into various bamboo honeycomb composite plate products. The products can be widely used in various fields of ornament, decoration, furniture, building materials, packaging, construction and the like.
Description
The invention belongs to the composite honeycomb sandwich structures technical field, particularly the folding continuous forming process of making cellular board of Weft-wise bamboo fabric.
Technique known is at present: the honeycomb structure composite material is rational in infrastructure because of having, lightweight, high-strength, series of advantages such as materials province and always be the emphasis of composite material application and development area research, the covering and the sandwich material kind that develop sandwich structure so far are a lot, skin material commonly used has aluminum alloy book plate, titanium-alloy thin-plate, glass fibre reinforced plastics book version, bamboo plywood, wad, the inorganic composite materials plate, plastic board, glass fiber cloth, aramid fiber cloth, cotton and paper or the like, honeycomb core commonly used has paper honeycomb core, the frp honeycomb core, plastic honeycomb core, aluminum alloy honeycomb core, aramid fiber honeycomb core or the like, just can develop many kinds of honeycomb composite sandwich construction materials with every kind of covering and different comb cores are compound, most widely used product mainly is the paper paper honeycomb core now, various man-made board facial tissue honeycomb cores, glass fibre reinforced plastics and frp honeycomb core and aluminium and aluminium honeycomb core sandwich structure etc.
Various paper wasp nest sandwich material waterproof, humidity resistance are limited, and it is limited to expose intensity, and application area is restricted.Sandwich materials such as frp honeycomb, aluminium honeycomb, aramid fiber honeycomb are because of the price height, and application area neither be very wide.Sandwich materials such as paper paper wasp nest, frp honeycomb and aluminium honeycomb can be realized the continuous automation compound molding, and various man-made board cellular material can only be by unit intermittent type compound molding, and labor intensity is big, efficient is low.How can find the advantage of the continuous compound molding of the existing paper of a kind of material, good performance is arranged again, price is not high yet simultaneously.
The objective of the invention is: make skin material and the compound a kind of forming method of Weft-wise bamboo fabric folded honeycomb core by utilizing bamboo matter fabric, the bamboo fabric honeycomb interlayer made from it or wrap up in the composite sheet structure of layer, have and to realize extensive continuous automatic production, be that aboundresources, renewable are reached cheap bamboo material by force as raw material, raw material sources are extensive, renewable is strong, big along bamboo line compressive strength, be with warp, the latitude bamboo band is weaved or the non-woven different disadvantage of mechanical property of having eliminated the bamboo silver together with flexible fiber.
The present invention solves technology side that its technical problem adopts by being: at first a reel Weft-wise bamboo fabric is contained on the reel on the cloth holder, Weft-wise bamboo fabric selects Weft bamboo glass fabric; Weft bamboo glass fabric is imported the horizontal gluing of horizontal glue applicator of rubber-coated mechanism by preceding guide reel, it is to utilize vertical reticulate pattern bar of glue applicator or longitudinal groove corresponding bamboo band on Weft bamboo glass fabric to be coated with lateral separation bar shaped glue, respectively there is a cover rubber-coated mechanism to realize that the Weft bamboo glass fabric both sides replace gluing in the both sides of gummed cloth, length alternately equals following folding length, alternately point equals folding point, the speed and the switching between the rubber-coated mechanism of Weft bamboo glass fabric and glue applicator need realize synchronization control, should guarantee to fold the back adjacent surface is laterally coated bamboo latitude bar width integral multiple along bamboo latitude bar adhesive tape, width between the adhesive tape is to be coated with 4 times of adhesive tape width, gummed cloth adjacent surface adhesive tape staggers, and the one side adhesive tape is in the centre of two adhesive tape of adjacent surface exactly; The Weft bamboo glass fabric that was coated with glue through after Guide roller enter the heating cabinet heating as required, again through one or more Guide roller guiding, make its length back and forth folding on folding platform by the drive of fabric folded mechanism by design, be to cooperate with the tight mechanism of an intussusception head-clamp each side by band cloth mechanism to realize accurate folding, the location, the folded tight mechanism of head-clamp is a pair of cooperation in front and back, to guarantee is to clamp same bamboo silver simultaneously to make it press to folding platform in front and back, and keep-up pressure until another tight mechanism of folded head-clamp unclamps after depressing again, start following one deck cloth that execution is brought by band cloth mechanism, opposite side is in clamped condition always and unclamps after this side is depressed again again, start execution by band cloth mechanism's band following one deck cloth in the past, start and carry out next work cycle, so alternate cycles is folding; Fold mechanism removes and includes the folded tight mechanism of head-clamp, band cloth mechanism, and folding platform comprises that also other guarantees that each mechanism effectively is connected the assisting agency of cooperating; Folding into needs thickness Weft bamboo glass fabric end socket to cut into the honeycomb core folded piece, by folding platform move or fold on the platform the line belt band from, abdicate folding platform simultaneously and continue folding next piece honeycomb core folded piece, the honeycomb core folded piece is delivered to pressurization or is pressurizeed, is heated and cured into broadwise honeycomb core raw sheet as required; The honeycomb core raw sheet is through cutting into the bamboo honeycomb core bar perpendicular to bamboo latitude bar by the length of honeycomb height, and the width of honeycomb core strip just equals folded length; The bamboo honeycomb core bar is through splicing the bonding continuous honeycomb pellet that becomes continuously; Continous way honeycomb pellet drawn is launched into bamboo honeycomb core, and this honeycomb core is vertically stood bamboo silver rift grain, sprays glue dipping and fixing as required typing as required and is heated to be continous way bamboo honeycomb core plate as required; Continuously the bamboo honeycomb core plate as required upper and lower surface or up and down the four sides as required gluing not gluing and upper and lower surface or up and down four sides bamboo fabric face layer be not coated with (soaking) glue or be coated with (soaking) glue and heat as required, pressurize or heat the composite curing that pressurizes and become continous way bamboo matter fabric honeycomb plate; Directly length is cut off on demand, and this plate is without the blank bamboo honeycomb batten of covering with paint, lacquer, colour wash, etc., and is called for short the bamboo cellular board, can be used for partition panel, floor, roofer, concrete shuttering panel, various facing base boards or the like; If what the top layer was used is to decorate bamboo glass fabric, cover with paint, lacquer, colour wash, etc. the sanding working procedure processing through the multiple tracks resin as required, cut off as required, gained is a bamboo honeycomb facing plate, this plate can be directly as decorative sheet, furniture-plates, floor, the floor, partition panel, the many aspects of door-plate or the like are used; Continous way bamboo cellular board is through coating, and length is cut off as required, and gained is a coating bamboo cellular board, and this plate can be widely used as decorative sheet, furniture-plates, and floor, the floor, partition panel, door-plate, the many aspects of wallboard or the like are used; Continous way bamboo cellular board can be processed through overlay film, and length is cut off as required, and gained is an overlay film bamboo cellular board, and this plate can be widely used as decorative sheet, furniture-plates, and floor, the floor, partition panel, door-plate, the many aspects of wallboard or the like are used; Honeycomb core strip satisfies usage requirement and can be used as the use of honeycomb pellet, otherwise sticks into the honeycomb pellet through assembly, uses as modular honeycomb core; Honeycomb core strip can satisfy the demand of the honeycomb pellet of width increasing through horizontal butt joint; Honeycomb core strip can be through piecing together the demand that foot is produced cellular board continuously that sticks continuously; The honeycomb pellet can satisfy the demand of concave-convex curved surface interlayer mechanism through processing.
The invention has the beneficial effects as follows, the bamboo fabric honeycomb plate greatly reduces the use amount of bamboo wood, and can realize easily decorating with various finish materials, and can be the decorative layer of realizing carrying the bamboo line through the warp that mills special processing such as shape, sanding, bamboo fabric that latitude bamboo silver is made into as the restricting material of composite intermediate layer cellular board, realized the maximization of material use efficient, realize the manufacturing efficiency maximization, had extraordinary economic benefit and social benefit.
Claims (10)
1. continuous forming process for bamboo fabric folding honeycomb plate of the present invention is characterized in that: at first a reel Weft-wise bamboo fabric is contained on the reel on the cloth holder, Weft-wise bamboo fabric selects Weft bamboo glass fabric; Weft bamboo glass fabric is imported the horizontal gluing of horizontal glue applicator of rubber-coated mechanism by preceding guide reel, it is to utilize vertical reticulate pattern bar of glue applicator or longitudinal groove corresponding bamboo band on Weft bamboo glass fabric to be coated with lateral separation bar shaped glue, respectively there is a cover rubber-coated mechanism to realize that the Weft bamboo glass fabric both sides replace gluing in the both sides of gummed cloth, length alternately equals following folding length, alternately point equals folding point, the speed and the switching between the rubber-coated mechanism of Weft bamboo glass fabric and glue applicator need realize synchronization control, should guarantee to fold the back adjacent surface is laterally coated bamboo latitude bar width integral multiple along bamboo latitude bar adhesive tape, width between the adhesive tape is to be coated with 4 times of adhesive tape width, gummed cloth adjacent surface adhesive tape staggers, and the one side adhesive tape is in the centre of two adhesive tape of adjacent surface exactly; The Weft bamboo glass fabric that was coated with glue through after Guide roller enter the heating cabinet heating as required, again through one or more Guide roller guiding, make its length back and forth folding on folding platform by the drive of fabric folded mechanism by design, be to cooperate with the tight mechanism of an intussusception head-clamp each side by band cloth mechanism to realize accurate folding, the location, the folded tight mechanism of head-clamp is a pair of cooperation in front and back, to guarantee is to clamp same bamboo silver simultaneously to make it press to folding platform in front and back, and keep-up pressure until another tight mechanism of folded head-clamp unclamps after depressing again, start following one deck cloth that execution is brought by band cloth mechanism, opposite side is in clamped condition always and unclamps after this side is depressed again again, start execution by band cloth mechanism's band following one deck cloth in the past, so alternate cycles is folding; Fold mechanism removes and includes the folded tight mechanism of head-clamp, band cloth mechanism, and folding platform comprises that also other guarantees that each mechanism effectively is connected the assisting agency of cooperating; Folding into needs thickness Weft bamboo glass fabric end socket to cut into the honeycomb core folded piece, by folding platform move or fold on the platform the line belt band from, abdicate folding platform simultaneously and continue folding next piece honeycomb core folded piece, the honeycomb core folded piece is delivered to pressurization or is pressurizeed, is heated and cured into broadwise honeycomb core raw sheet as required; The honeycomb core raw sheet is through cutting into the bamboo honeycomb core bar perpendicular to bamboo latitude bar by the length of honeycomb height, and the width of honeycomb core strip just equals folded length; The bamboo honeycomb core bar is through splicing the bonding continuous honeycomb pellet that becomes continuously; Continous way honeycomb pellet drawn is launched into bamboo honeycomb core, and this honeycomb core is vertically stood bamboo silver rift grain, sprays glue dipping and fixing as required typing as required and is heated to be continous way bamboo honeycomb core plate as required; Continuously the bamboo honeycomb core plate as required upper and lower surface or up and down the four sides as required gluing not gluing and upper and lower surface or up and down four sides bamboo fabric face layer be not coated with (soaking) glue or be coated with (soaking) glue and heat as required, pressurize or heat the composite curing that pressurizes and become continous way bamboo matter fabric honeycomb plate; Directly length is cut off on demand, and this plate is without the blank bamboo honeycomb batten of covering with paint, lacquer, colour wash, etc., and is called for short the bamboo cellular board, can be used for partition panel, floor, roofer, concrete shuttering panel, various facing base boards or the like; If what the top layer was used is to decorate bamboo glass fabric, cover with paint, lacquer, colour wash, etc. the sanding working procedure processing through the multiple tracks resin as required, cut off as required, gained is a bamboo honeycomb facing plate, this plate can be directly as decorative sheet, furniture-plates, floor, the floor, partition panel, the many aspects of door-plate or the like are used; Continous way bamboo cellular board is through coating, and length is cut off as required, and gained is a coating bamboo cellular board, and this plate can be widely used as decorative sheet, furniture-plates, and floor, the floor, partition panel, door-plate, the many aspects of wallboard or the like are used; Continous way bamboo cellular board can be processed through overlay film, and length is cut off as required, and gained is an overlay film bamboo cellular board, and this plate can be widely used as decorative sheet, furniture-plates, and floor, the floor, partition panel, door-plate, the many aspects of wallboard or the like are used; Honeycomb core strip satisfies usage requirement and can be used as the use of honeycomb pellet, otherwise sticks into the honeycomb pellet through assembly, uses as modular honeycomb core; Honeycomb core strip can satisfy the demand of the honeycomb pellet of width increasing through horizontal butt joint; Honeycomb core strip can be through piecing together the demand that foot is produced cellular board continuously that sticks continuously; The honeycomb pellet can satisfy the demand of concave-convex curved surface interlayer mechanism through processing.
2. continuous forming process for bamboo fabric folding honeycomb plate according to claim 1 is characterized in that: be bamboo latitude bar that bamboo processing is become, bamboo through bar, weave or non-wovenly become broadwise, bamboo fabric radially through the bar cooperation with flexible fiber and bamboo latitude bar, bamboo; Broadwise, radially the bamboo fabric can be interweave broadwise, radially bamboo fabric, knitting broadwise, radially bamboo fabric, braiding broadwise, radially bamboo fabric, loop bonding broadwise, radially bamboo fabric and lining yarn, lining felt, lining fabric, lining paper, lining form etc. bonding all are weaved and non-woven broadwise, bamboo fabric radially with becoming felt etc.
3. continuous forming process for bamboo fabric folding honeycomb plate according to claim 1, it is characterized in that: restricting bamboo fabric can be that one or more bamboo fabric wraps or clamp two sides, three or four sides bamboo honeycomb core, and longitudinal seam can be that to dock also can be overlap joint; Can be that individual layer also can be that multilayer bamboo fabric wraps or clamp bamboo honeycomb core; Can be that the bamboo fabric cooperates with Weft-wise bamboo fabric, also can be to cooperate with other fabric or other facing material; Two width of cloth Weft-wise bamboo fabrics can only be that bamboo honeycomb core is clamped on the two sides; Can be that common bamboo fabric also can be to decorate the bamboo fabric.
4. according to claim 1,3 described continuous forming process for bamboo fabric folding honeycomb plate, it is characterized in that: the bamboo fabric can be used other panel material, fabric and film covering substitute, promptly, it is used sheet metal, aluminium sheet, titanium alloy sheet, the glass fibre reinforced plastics thin plate, the bamboo veneer, bamboo plywood, the bamboo fiber plate, plastic board, various surface layer sheets such as inorganic composite materials plate are compound, also available itself and glass cloth, aramid fiber cloth, the bamboo fabric, the bamboo fabric, various web materials of cotton or the like and various film and stationery are made skin material and are substituted, just can produce the different various sandwich structure composite materials of cost performance, these interlayer composite materials can satisfy the demand in many fields; The honeycomb pellet can satisfy the demand of concave-convex curved surface sandwich structure through processing
5. continuous forming process for bamboo fabric folding honeycomb plate according to claim 1, it is characterized in that: decorate the bamboo fabric and be bamboo latitude bar, bamboo through bar after processing such as sanding polishing covering with paint and the bamboo glass fabric that is made into such as glass fibre, have the kind fabric that transparent resin glue just can demonstrate the bamboo grain effect through invading again.
6. according to claim 1,2 described continuous forming process for bamboo fabric folding honeycomb plate, it is characterized in that: flexible fiber can be all spendable fibers such as inorfil, organic fiber, artificial fiber, natural plant fibre, animal fibre, steel fiber, non-metallic fiber, mainly based on glass fibre.
7. continuous forming process for bamboo fabric folding honeycomb plate according to claim 1, it is characterized in that: can be the horizontal gluing of horizontal glue applicator, also can be vertically to spray glue, vertically playback, realized and so forth continuous spray glue operation with the horizontal return feeding of moved further with moved further traverse feed spray glue, vertical playback, continuation once the glue spraying head of arranging interval adhesive tape width, it is to utilize glue spraying head corresponding bamboo band spray lateral separation bar shaped glue on Weft bamboo glass fabric, and vertical and playback, the horizontal reciprocating feed speed of Weft bamboo glass fabric and spraying colloid system need be carried out synchronization control; In like manner also can use the vertical same moved further of hoop glue applicator, traverse feed roller coat, vertically playback, continue just to have realized with the horizontal return feeding of moved further roller coat, vertically playback, and so forth continuous roller coat operation, it is to utilize the hoop reticulate pattern bar of glue applicator or hoop groove corresponding bamboo band on Weft bamboo glass fabric to be coated with lateral separation bar shaped glue, and vertical and playback, the horizontal reciprocating feed speed of Weft bamboo glass fabric and roller colloid system need be carried out synchronization control; Need not can directly be used in the folding process with this coating method of moved further, realize intermittently spraying on the folding platform glue or gluing; This folding system also can be to finish the gluing operation with other gluing mode.
8. Weft-wise bamboo fabric honeycomb core moulding process according to claim 1 is characterized in that: moulding process determines by selected adhesive and adjusts that the different corresponding moulding process of adhesive kind also can be different.
9. continuous forming process for bamboo fabric folding honeycomb plate according to claim 1 is characterized in that: bamboo honeycomb facing plate, coating bamboo fabric honeycomb plate, overlay film bamboo cellular board, and this plate can be widely used as decorative sheet, furniture-plates, floor, floor, partition panel, door-plate, the many aspects of wallboard or the like are used.
10. Weft-wise bamboo fabric honeycomb core moulding process according to claim 1 is characterized in that: can be dull and stereotyped, also can be the linear product of any horizontal curve forms such as with groove and boss.