CN101760151A - Corrugated carton glue and preparing method thereof - Google Patents
Corrugated carton glue and preparing method thereof Download PDFInfo
- Publication number
- CN101760151A CN101760151A CN200810228309A CN200810228309A CN101760151A CN 101760151 A CN101760151 A CN 101760151A CN 200810228309 A CN200810228309 A CN 200810228309A CN 200810228309 A CN200810228309 A CN 200810228309A CN 101760151 A CN101760151 A CN 101760151A
- Authority
- CN
- China
- Prior art keywords
- corrugated carton
- organic solvent
- portions
- glue
- polystyrene foam
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to one glue to prepare cartons, in particular to one glue and preparing method thereof used for corrugated paperboards and cartons. The glue is prepared by the components with the weight portions as follows: 15-35 portions of waste polystyrene foam, 20-40 portions of organic solvent, 2-8 portions of plasticizer, 40-60 portions of water, 0.5-1.5 portions of emulsifier, 0.5-1.5 portions of assistant, 0.5-1.5 portions of thickener as well as 0.01-0.02 portion of defoamer. The invention uses the waste polystyrene foam in the packaging industry to prepare glue and finishing agent used in the packaging box industry, which changes the environment and reduces white pollution. Compared with the current glue, the production cost is reduced and the quality of the corrugated carton is guaranteed to reach national standard GB5033-85.
Description
Technical field
The present invention relates to a kind of glue of making carton, particularly be used for glue of corrugated cardboard, packing case carton and preparation method thereof.
Background technology
The quality test of corrugated cardboard and Corrugated Box is divided into three major types.Visual testing, the performance test of corrugated cardboard and Corrugated Box and the type approval test of Corrugated Box of Here it is Corrugated Box.At present, the application of Corrugated Box more and more widely.Also more and more higher to using Corrugated Box to make the specification of quality that packing beautifies commodity, protection commodity as commodity, equipment, technology and the technology of producing Corrugated Box is also corresponding to have obtained significant progress.For the quality of the quality of the corrugated cardboard that guarantees to produce and the Corrugated Box produced complies with the national standard requirements, both be fit to use, the U.S. valency of thing is modest again, and prior should be the quality of stupefied carton also, want to guarantee stupefied carton quality-critical be the glue of stupefied carton.
Summary of the invention
The present invention is proposed by the problems referred to above, and a kind of quality that guarantees stupefied carton is provided, the glue that utilizes the waste polystyrene foam preparation to use as the Packaging Box industry.
In order to realize above purpose, technical scheme of the present invention is: corrugated carton glue is characterized in that it being to count ratio by following raw materials in parts by weight to be prepared from: waste polystyrene foam: organic solvent: softening agent: water: emulsifying agent: auxiliary agent: thickening material: defoamer=15～35: 20～40: 2～8: 40～60: 0.5～1.5: 0.5～1.5: 0.5～1.5: 0.01～0.02.
Corrugated carton glue is counted ratio by following raw materials in parts by weight and is prepared from: waste polystyrene foam: organic solvent: softening agent: water: emulsifying agent: auxiliary agent: thickening material: defoamer=30: 30: 5: 50: 1: 1: 1: 0.015.
Described organic solvent is to be mixed by a certain percentage by benzene class and alcohols material.
Softening agent is made up of dibutyl phthalate or dioctyl phthalate (DOP).
Emulsifying agent is mixed by a certain percentage by anion surfactant and nonionogenic tenside and forms.
Thickening material is made up of carboxymethyl cellulose or Natvosol.
Defoamer is made up of tbp or water-soluble methyl-silicone oil.
The method for preparing corrugated carton glue is:
Earlier by formula ratio take by weighing cleaned, dry and pulverizes after waste polystyrene foam adding reaction flask in, when add total amount 1/5 the time, the organic solvent and the softening agent that add formula ratio again, and under agitation continue to add 4/5 remaining waste polystyrene foam until being dissolved into uniform organic phase fully;
The water, emulsifying agent, auxiliary agent, thickening material, the defoamer that in another reaction flask, add formula ratio more successively, be stirred to into uniform inorganic phase after the adding, suitably heat in the whipping process to accelerate dissolution rate, stir and slowly be added dropwise in the organic phase mutually down inorganic, adding heats up, and to be stirred to a bottle interior temperature be 70-80 ℃, this moment, organic solvent distilled, and amount to be recycled accounts for 80% o'clock of adding the organic solvent amount can stop heated and stirred;
At last reactant in the bottle is carried out checking after the filtering and impurity removing matter, be finished product.
Advantageous effect of the present invention is that this product of the present invention utilizes the waste polystyrene foam preparation of packaging industry as Packaging Box industry glue and finishing agent, has improved environment, has reduced white pollution.It is compared with existing glue and has reduced production cost, guarantees that the quality of demonstrate,proving stupefied carton reaches national GB5033-85 standard.
Embodiment
Embodiment 1
Corrugated carton glue, the raw materials by weight portion ratio is prepared from: waste polystyrene foam: organic solvent: softening agent: water: emulsifying agent: auxiliary agent: thickening material: defoamer=15: 20: 2: 40: 0.5: 0.5: 0.5: 0.01.
Described organic solvent is to be mixed by a certain percentage by benzene class and alcohols material.
Softening agent is made up of dibutyl phthalate or dioctyl phthalate (DOP).
Emulsifying agent is mixed by a certain percentage by anion surfactant and nonionogenic tenside and forms.
Thickening material is made up of carboxymethyl cellulose or Natvosol.
Defoamer is made up of tbp or water-soluble methyl-silicone oil.
The method for preparing corrugated carton glue is:
Earlier by formula ratio take by weighing cleaned, dry and pulverizes after waste polystyrene foam adding reaction flask in, when add total amount 1/5 the time, the organic solvent and the softening agent that add formula ratio again, and under agitation continue to add 4/5 remaining waste polystyrene foam until being dissolved into uniform organic phase fully;
The water, emulsifying agent, auxiliary agent, thickening material, the defoamer that in another reaction flask, add formula ratio more successively, be stirred to into uniform inorganic phase after the adding, suitably heat in the whipping process to accelerate dissolution rate, stir and slowly be added dropwise in the organic phase mutually down inorganic, adding heats up, and to be stirred to a bottle interior temperature be 70-80 ℃, this moment, organic solvent distilled, and amount to be recycled accounts for 80% o'clock of adding the organic solvent amount can stop heated and stirred; At last reactant in the bottle is carried out checking after the filtering and impurity removing matter, be finished product.
Embodiment 2
Corrugated carton glue, the raw materials by weight portion ratio is prepared from: waste polystyrene foam: organic solvent: softening agent: water: emulsifying agent: auxiliary agent: thickening material: defoamer=35: 40: 8: 60: 1.5: 1.5: 1.5: 0.02.Other is with embodiment 1.
Embodiment 3
Corrugated carton glue, the raw materials by weight portion ratio is prepared from: waste polystyrene foam: organic solvent: softening agent: water: emulsifying agent: auxiliary agent: thickening material: defoamer=30: 30: 5: 50: 1: 1: 1: 0.015.Other is with embodiment 1.
Claims (8)
1. corrugated carton glue is characterized in that it being to count ratio by following raw materials in parts by weight to be prepared from: waste polystyrene foam: organic solvent: softening agent: water: emulsifying agent: auxiliary agent: thickening material: defoamer=15～35: 20～40: 2～8: 40～60: 0.5～1.5: 0.5～1.5: 0.5～1.5: 0.01～0.02.
2. corrugated carton glue according to claim 1 is characterized in that counting ratio by following raw materials in parts by weight is prepared from: waste polystyrene foam: organic solvent: softening agent: water: emulsifying agent: auxiliary agent: thickening material: defoamer=30: 30: 5: 50: 1: 1: 1: 0.015.
3. corrugated carton glue according to claim 1 is characterized in that organic solvent is to be mixed by a certain percentage by benzene class and alcohols material.
4. corrugated carton glue according to claim 1 is characterized in that softening agent is made up of dibutyl phthalate or dioctyl phthalate (DOP).
5. corrugated carton glue according to claim 1 is characterized in that emulsifying agent is mixed by a certain percentage by anion surfactant and nonionogenic tenside to form.
6. corrugated carton glue according to claim 1 is characterized in that thickening material is made up of carboxymethyl cellulose or Natvosol.
7. corrugated carton glue according to claim 1 is characterized in that defoamer is made up of tbp or water-soluble methyl-silicone oil.
8. the method for preparing claim 1 or 2 described corrugated carton glues is characterized in that being made up of following step:
Earlier by formula ratio take by weighing cleaned, dry and pulverizes after waste polystyrene foam adding reaction flask in, when add total amount 1/5 the time, the organic solvent and the softening agent that add formula ratio again, and under agitation continue to add 4/5 remaining waste polystyrene foam until being dissolved into uniform organic phase fully;
The water, emulsifying agent, auxiliary agent, thickening material, the defoamer that in another reaction flask, add formula ratio more successively, be stirred to into uniform inorganic phase after the adding, suitably heat in the whipping process to accelerate dissolution rate, stir and slowly be added dropwise in the organic phase mutually down inorganic, adding heats up, and to be stirred to a bottle interior temperature be 70-80 ℃, this moment, organic solvent distilled, and amount to be recycled accounts for 80% o'clock of adding the organic solvent amount can stop heated and stirred;
At last reactant in the bottle is carried out checking after the filtering and impurity removing matter, be finished product.