CN101747475A - Formulation of synthetic resin for alcohol-soluble printing ink and preparation method thereof - Google Patents
Formulation of synthetic resin for alcohol-soluble printing ink and preparation method thereof Download PDFInfo
- Publication number
- CN101747475A CN101747475A CN 200810188225 CN200810188225A CN101747475A CN 101747475 A CN101747475 A CN 101747475A CN 200810188225 CN200810188225 CN 200810188225 CN 200810188225 A CN200810188225 A CN 200810188225A CN 101747475 A CN101747475 A CN 101747475A
- Authority
- CN
- China
- Prior art keywords
- parts
- alcohol
- printing ink
- acrylate
- soluble
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a resin for alcohol-soluble printing ink and relates to the field of chemical synthesis. The current plastic gravure ink uses a benzene-soluble synthetic resin as a main part, so volatilization pollution of a benzene solvent exists in manufacturing and using processes of the printing ink and endangers the health of human body. The invention provides a formulation of the resin for the alcohol-soluble printing ink and a preparation method thereof. The preparation method comprises the following steps: using acrylic ester, ethylene carbonate, vinyl acetate and an active functional group monomer as raw materials; adding an initiator to the raw materials; dissolving the mixture in mixed solution; under a stirring condition, dripping mixture solution of the monomer and a solvent in an alcohol ester solvent to prepare an acrylic pre-polymer; using the solvent to fully dissolve a condensation polymer of cyclohexanone and formaldehyde; under the stirring condition, adding a catalyst and the acrylic pre-polymer; performing a reaction between the dissolved condensation polymer and the acrylic pre-polymer to an end point; lowering the temperature; and adjusting the viscosity to obtain a finished product. The resin is alcohol soluble and has little harm to the human body and the environment. Moreover, the resin has the characteristics of convenient and readily available raw materials, low preparation cost, good pigment-wetting dispersivity and high drying speed.
Description
Technical field
The present invention relates to the synthetic field of chemical industry, relate in particular to prescription of a kind of synthetic resin for alcohol-soluble printing ink and preparation method thereof.
Background technology
Plastic gravure printing ink is the coloured material that is used for the plastic wrapping printing.Be to be main component by resin, solvent, pigment and auxiliary agent, the liquid substance that processes through operations such as grindings, wherein the performance of resin determines the printing ink solvent type, and the printability, pigment-dispersing, attachment fastness etc. of decision printing ink, for a long time, the plastic gravure printing ink of China contains a large amount of benzene kind solvents based on the molten type synthetic resins of benzene in the printing ink, pollute the health that is endangering the producer and human consumer so all exist the volatilization of benzene solvent in the manufacturing of printing ink, the use.Even more serious is the benzene kind solvent that remains in the packing bag, is polluting article, food, very big to the people's lives Health hazard.In recent years, though occur the alcohol-soluble printing ink of water-based, alcohol-soluble polyurethane plastic gravure printing ink and other type in the market, but there is the price height, to the pigment wetting bad dispersibility, drying waits problem slowly, has influenced promoting the use of of this series products, at acrylic acid or the like associated resin and printing ink, still there are minority one or two tame products to be used with regard to white single kind is domestic, but present domestic this resinoid supply of still not having of the pure dissolubility plastic gravure printing ink of whole chromatogram.
Summary of the invention
The objective of the invention is a kind of ethanol-soluble type synthetic resins and synthetic method, satisfy ethanol-soluble type compound oil ink whole chromatogram and make requirement.
The technical scheme that realizes above-mentioned purpose is as follows:
A kind of synthetic resin for alcohol-soluble printing ink, it is as follows to fill a prescription:
75 parts of polycondensate 30-35 part, catalyzer 0.5-0.7 part, butylacetate 20-25 part, ethyl acetate 10-15 part, the dehydrated alcohols of acrylate 24-39 part, tertiary ethylene carbonate 5-10 part, vinyl-acetic ester 15-20 part, active function groups monomer 15-21 part, initiator 0.5-0.7 part, pimelinketone and formaldehyde.
Described acrylate is one or more in ethyl propenoate, butyl acrylate, the butyl methacrylate, described active function groups monomer is one or more the mixture in vinylformic acid, propenoic acid beta hydroxyl ethyl ester, Propylene glycol monoacrylate, glycidyl acrylate, the acrylamide, described initiator is an azobisisobutyronitrile, and described catalyzer is a tosic acid.
The preparation method of synthetic resin for alcohol-soluble printing ink is made up of following steps:
(1) ethyl acetate 5-10 part and dehydrated alcohol are mixed in the adding reactor for 45 parts, make pure ester solvent, standby;
(2) acrylate 24-39 part, tertiary ethylene carbonate 5-10 part, vinyl-acetic ester 15-20 part, active function groups monomer 15-21 part, initiator 0.5-0.7 part are dissolved in the mixing solutions of 10 parts of ethyl acetate 5-10 parts, dehydrated alcohol, make monomer mixed solution, and place header tank standby;
(3) under agitation condition, the monomer mixed solution that step (2) is made is added drop-wise in the pure ester solvent that step (1) makes, and the dropping time is 3-4 hour, drips to finish back backflow 1-2 hour, and temperature of reaction is 72-78 ℃, makes the acrylic acid multielement performed polymer, and is standby;
(4) in another reactor, add butylacetate 20-25 part, under agitation condition, add polycondensate 30-35 part of pimelinketone and formaldehyde, being warming up to 65 ℃ dissolves it fully, add the acrylic acid multielement performed polymer that catalyzer 0.5-0.7 part and step (3) make while stirring, temperature is controlled at 95-98 ℃, react to terminal with acrylate prepolymer, be cooled to 65 ℃, add 20 parts of dehydrated alcohols and adjust viscosity, discharging makes finished product.
The synthetic resin for alcohol-soluble printing ink that the present invention makes is pure dissolubility, does not use benzene kind solvent, and is little to human body, environmental hazard.
Raw material of the present invention conveniently is easy to get, and preparation cost is low.
The present invention also has the pigment wetting good dispersity, the characteristics of fast drying.
Embodiment
With embodiment the present invention is further explained below, but the present invention is not restricted to following embodiment.
Embodiment 1
Prescription is:
10 parts of 20 parts of 0.5 part of 30 parts of polycondensates, tosic acid, butylacetates, the ethyl acetate of 15 parts of methacrylic acid ester methyl esters, 16 parts of ethyl propenoates, 8 parts of butyl methacrylate, 5 parts of tertiary ethylene carbonates, 15 parts of vinyl-acetic esters, 2 parts in vinylformic acid, 5 parts of Propylene glycol monoacrylates, 8 parts of acrylamides, 0.5 part of azobisisobutyronitrile, pimelinketone and formaldehyde, 75 parts of dehydrated alcohols.
The preparation method is made up of following steps:
(1) 5 parts of ethyl acetate and dehydrated alcohol are mixed in the adding reactor for 45 parts, make 50 parts of pure ester solvents, standby;
(2) 0.5 part of 15 parts of methacrylic acid ester methyl ester, 16 parts of ethyl propenoates, butyl methacrylate .8 part, 5 parts of tertiary ethylene carbonates, 15 parts of vinyl-acetic esters, 2 parts in vinylformic acid, 5 parts of Propylene glycol monoacrylates, 8 parts of acrylamides, azobisisobutyronitrile is dissolved in the mixing solutions of 5 parts of ethyl acetate, 10 parts of dehydrated alcohols, make monomer mixed solution, and place header tank standby;
(3) under agitation condition, the monomer mixed solution that step (2) is made is added drop-wise in the pure ester solvent that step (1) makes, and the dropping time is 3 hours, drips to finish the back and refluxed 1 hour, and temperature of reaction is 72 ℃, makes the acrylic acid multielement performed polymer, and is standby;
(4) in another reactor, add 20 parts of butylacetates, under agitation condition, add 30 parts of the polycondensates of pimelinketone and formaldehyde, being warming up to 65 ℃ dissolves it fully, add the acrylic acid multielement performed polymer that 0.5 part of benzene methanesulfonic acid and step (3) are made while stirring, temperature is controlled at 95 ℃, react to terminal with acrylate prepolymer, be cooled to 65 ℃, add 20 parts of dehydrated alcohols and adjust viscosity, discharging makes finished product.
Embodiment 2
Prescription is: 10 parts of 20 parts of 0.5 part of 0.7 part of 30 parts of polycondensates, azobisisobutyronitrile, tosic acid, butylacetates, the ethyl acetate of 5 parts of methacrylic acid ester methyl esters, 19 parts of butyl methacrylate, 20 parts of vinyl-acetic esters, 10 parts of tertiary ethylene carbonates, 3 parts in vinylformic acid, 4 parts of propenoic acid beta hydroxyl ethyl esters, 2 parts of glycidyl acrylates, 11 parts of acrylamides, pimelinketone and formaldehyde, 75 parts of dehydrated alcohols
The preparation method is made up of following steps:
(1) 5 parts of ethyl acetate and dehydrated alcohol are mixed in the adding reactor for 45 parts, make 50 parts of pure ester solvents, standby;
(2) 0.7 part of 5 parts of methacrylic acid ester methyl ester, 19 parts of butyl methacrylate, 20 parts of vinyl-acetic esters, 10 parts of tertiary ethylene carbonates, 3 parts in vinylformic acid, 4 parts of propenoic acid beta hydroxyl ethyl esters, 2 parts of glycidyl acrylates, 11 parts of acrylamides, azobisisobutyronitrile is dissolved in the mixing solutions of 5 parts of ethyl acetate, 10 parts of dehydrated alcohols, make monomer mixed solution, and place header tank standby;
(3) under agitation condition, the monomer mixed solution that step (2) is made is added drop-wise in the pure ester solvent that step (1) makes, and the dropping time is 3.5 hours, drips to finish the back and refluxed 1.5 hours, and temperature of reaction is 75 ℃, makes the acrylic acid multielement performed polymer, and is standby;
(4) in another reactor, add 30 parts of the polycondensates of 20 parts of butylacetates, pimelinketone and formaldehyde, 30 parts of polycondensates that under agitation condition, add pimelinketone and formaldehyde, being warming up to 65 ℃ dissolves it fully, agitation condition adds the acrylic acid multielement performed polymer that 0.5 part of tosic acid and step (3) make down, temperature is controlled at 96 ℃, reacts to terminal with acrylate prepolymer, is cooled to 65 ℃, add 20 parts of dehydrated alcohols, discharging makes finished product.
Embodiment 3
Prescription is:
15 parts of 25 parts of 0.7 part of 1 part of 35 parts of polycondensates, initiator, catalyzer, butylacetates, the ethyl acetate of 6 parts of ethyl propenoates, 25 parts of butyl methacrylate, 5 parts of tertiary ethylene carbonates, 20 parts of vinyl-acetic esters, 3 parts in vinylformic acid, 5 parts of propenoic acid beta hydroxyl ethyl esters, 3 parts of glycidyl acrylates, 10 parts of acrylamides, pimelinketone and formaldehyde, 75 parts of dehydrated alcohols.
(1) 8 parts of ethyl acetate and dehydrated alcohol are mixed in the adding reactor for 45 parts, make 53 parts of pure ester solvents, standby;
(2) 1 part of 6 parts of ethyl propenoate, 25 parts of butyl methacrylate, 5 parts of tertiary ethylene carbonates, 20 parts of vinyl-acetic esters, 3 parts in vinylformic acid, 5 parts of propenoic acid beta hydroxyl ethyl esters, 3 parts of glycidyl acrylates, 10 parts of acrylamides, azobisisobutyronitrile is dissolved in the mixing solutions of 7 parts of ethyl acetate, 10 parts of dehydrated alcohols, make monomer mixed solution, and place header tank standby;
(3) under agitation condition, the monomer mixed solution that step (2) is made is added drop-wise in the pure ester solvent that step (1) makes, and the dropping time is 4 hours, drips to finish the back and refluxed 2 hours, and temperature of reaction is 78 ℃, makes the acrylic acid multielement performed polymer, and is standby;
(4) in another reactor, add 35 parts of the polycondensates of 25 parts of butylacetates, pimelinketone and formaldehyde, 30 parts of polycondensates that under agitation condition, add pimelinketone and formaldehyde, being warming up to 65 ℃ dissolves it fully, add the acrylic acid multielement performed polymer that 0.7 part of tosic acid and step (3) make while stirring, temperature is controlled at 98 ℃, reacts to terminal with acrylate prepolymer, is cooled to 65 ℃, add 20 parts of dehydrated alcohols, discharging makes finished product.
Claims (3)
1. synthetic resin for alcohol-soluble printing ink, it is as follows to it is characterized by prescription: 75 parts of polycondensate 30-35 part, catalyzer 0.5-0.7 part, butylacetate 20-25 part, ethyl acetate 10-15 part, the dehydrated alcohols of acrylate 24-39 part, tertiary ethylene carbonate 5-10 part, vinyl-acetic ester 15-20 part, active function groups monomer 15-21 part, initiator 0.5-0.7 part, pimelinketone and formaldehyde.
2. a kind of synthetic resin for alcohol-soluble printing ink according to claim 1, it is characterized in that described acrylate is one or more in ethyl propenoate, butyl acrylate, the butyl methacrylate, described active function groups monomer is one or more the mixture in vinylformic acid, propenoic acid beta hydroxyl ethyl ester, Propylene glycol monoacrylate, glycidyl acrylate, the acrylamide, described initiator is an azobisisobutyronitrile, and described catalyzer is a tosic acid.
3. a kind of synthetic resin for alcohol-soluble printing ink according to claim 1 and 2 is characterized by the preparation method and is made up of following steps:
(1) ethyl acetate 5-10 part and dehydrated alcohol are mixed in the adding reactor for 45 parts, make pure ester solvent, standby;
(2) acrylate 24-39 part, tertiary ethylene carbonate 5-10 part, vinyl-acetic ester 15-20 part, active function groups monomer 15-21 part, initiator 0.5-0.7 part are dissolved in the mixing solutions of 10 parts of ethyl acetate 5-10 parts, dehydrated alcohol, make monomer mixed solution, and place header tank standby;
(3) under agitation condition, the monomer mixed solution that step (2) is made is added drop-wise in the pure ester solvent that step (1) makes, and the dropping time is 3-4 hour, drips to finish back backflow 1-2 hour, and temperature of reaction is 72-78 ℃, makes the acrylic acid multielement performed polymer, and is standby;
(4) in another reactor, add butylacetate 20-25 part, under agitation condition, add polycondensate 30-35 part of pimelinketone and formaldehyde, being warming up to 65 ℃ dissolves it fully, add the acrylic acid multielement performed polymer that catalyzer 0.5-0.7 part and step (3) make while stirring, temperature is controlled at 95-98 ℃, react to terminal with acrylate prepolymer, be cooled to 65 ℃, add 20 parts of dehydrated alcohols and adjust viscosity, discharging makes finished product.