CN101735738B - Oil and solvent-absorbing cleaning adhesive tape - Google Patents
Oil and solvent-absorbing cleaning adhesive tape Download PDFInfo
- Publication number
- CN101735738B CN101735738B CN 201010019580 CN201010019580A CN101735738B CN 101735738 B CN101735738 B CN 101735738B CN 201010019580 CN201010019580 CN 201010019580 CN 201010019580 A CN201010019580 A CN 201010019580A CN 101735738 B CN101735738 B CN 101735738B
- Authority
- CN
- China
- Prior art keywords
- solvent
- oil suction
- adhesive tape
- resin
- oil
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention provides an oil and solvent-absorbing cleaning adhesive tape, which is used in the photoelectric industry and the process of machining conductive glass and can avoid scratch and drying trace on a treated surface in the photoelectric engineering. A polyethylene glycol terephthalate polyester film coat is added on the upper surface of a non-silicone oil series anti-sticking layer, and an adhesive coat capable of absorbing the oil and the solvent is added on the upper surface of the polyethylene glycol terephthalate polyester film coat. The adhesive layer of the cleaning adhesive tape has micro viscosity and oil-adsorbing liquid, and can be fully adsorbed on the cleaned surface without producing bubbles during machining so as not to cause ghost-like pollution of a product to an adhered object. The cleaning adhesive tape can be widely used in the field of photoelectric industry.
Description
Technical field
The present invention relates to a kind of adhesive tape, relate in particular to a kind of adhesive tape that has the meeting oil suction and inhale the cleaning function of solvent.
Background technology
At present; in optoelectronics industry in the conductive glass work flow; the adhesive tape that needs various uses; scrape the vestige that injures drying to prevent that treated side in the photoelectric project from not having; the adhesive tape of prior art can't satisfy this requirement; having much room for improvement all has rapidly oil suction, inhales the adhesive tape of the specific function of cleaning solvent, and the plastics of special industry environment, the surface of metal are protected.
Summary of the invention
Problem for the prior art existence, technical problem to be solved by this invention is that a kind of cleaning efficacy that finishing coat has the meeting oil suction and inhales solvent in adhesive tape will be provided, in optoelectronics industry, in the conductive glass course of processing, use, can avoid treated side in the photoelectric project not have and scrape the vestige that injures drying.
For reaching above-mentioned purpose, the cleaning adhesive tape that the present invention understands oil suction and suction solvent is achieved by following technical proposals:
A kind of can oil suction and inhale the cleaning adhesive tape of solvent, non-silicone oil system anti-glutinous layer by layer on the additional polyethylene terephthalate polyester film coating in surface, the surface is additional on the polyethylene terephthalate polyester film coating can oil suction and the viscose coating of solvent.
Further, described can oil suction and the viscose of solvent itself, be that the thermoplastic rubber by the asynthetic rubber is matrix, each composition quality ratio is:
(a) hot plastic elastomer rubber matrix 100
(b) tackifier 1～15
(c) anti-aging agent 1～5
(d) solvent 150～300
(e) static inhibitor 0.005～0.05
(f) bridging agent 0.1～1;
Further, the plastic elastomer rubber of described heat, it mainly adopts:
Vinylbenzene-pentadiene-vinylbenzene
Or styrene-butadiene-styrene
Or vinylbenzene-(ethylene/butylene)-vinylbenzene;
Further, described tackifier are tackifying resin, and hot plastic rubber is the same with natural rubber, and itself does not have viscosity thermoplastic elastomer, therefore will be made into pressure sensitive adhesive, therefore the essential tackifying resin that adds, its tackifying resin is divided into two classes:
(a) nonpolar, its solubility parameter is generally all lower, as: aliphatics and alicyclic petroleum resin, rosin and staybelite fat, terpine resin, resol
(b) polarity, its solubility parameter are generally all higher, such as aromatic petroleum resin, and coumarone-indene resin, indenes alkene-phenol resins that softening temperature is higher.
Further, three layers of total thickness of viscose of the anti-glutinous layer of described non-silicone oil system, polyethylene terephthalate polyester film, meeting oil suction and solvent are 0.07～0.10mm, polyethylene terephtalate polyester film (2) layer thickness is 0.05～0.055mm, and the viscose coat-thickness of meeting oil suction and solvent is 0.02～0.025mm.
Further, described solvent adopts toluene: gasoline is that mix (50: 50), and bridging agent mainly is:
(a) sulphur and sulfur-donor
(b) organo-peroxide
(c) active phenolphthalein resin
The invention solves above-mentioned existing technical problem, and have the following advantages than prior art:
1., its mucigel all has microviscosity, all adsorbs again the specific function of oleaginous fluid;
2., viscose itself, be to be matrix by asynthetic rubber (TPR) thermoplastic rubber;
3., colloid itself can chemical resistant properties, and again can be with adsorption;
4., colloid has anlistatig performance to make to prevent in its course of processing foreign matter from bringing into again;
5., the selecting of glue, must have neither too hard, nor too soft, make its work in-process can be adsorbed on cleaned surface fully and do not produce bubble, and cause product to stay the contaminative of similar ghost at affixed object.
The present invention can be widely used in the optoelectronics industry field.
Description of drawings
Fig. 1 is structural representation of the present invention.
Embodiment
For further understanding feature of the present invention, technique means and the specific purposes that reach, function, below in conjunction with accompanying drawing and embodiment the present invention is described in further detail.
The present invention is additional polyethylene terephtalate polyester film 2 coatings in surface on 1 layer on the anti-glutinous layer of non-silicone oil system, and the surface is additional on polyethylene terephtalate polyester film 2 coatings can oil suction and viscose 3 coatings of solvent.
Can oil suction and the viscose 3 of solvent itself, be to be matrix by asynthetic rubber (TPR), thermoplastic rubber, each composition quality ratio is:
(a) hot plastic elastomer rubber matrix 100
(b) tackifier 1～15
(c) anti-aging agent 1～5
(d) solvent 150～300
(e) static inhibitor 0.005～0.05
(f) bridging agent 0.1～1
The hot plastic elastomer rubber of the viscose 3 of meeting oil suction and solvent, it mainly contains:
(1) SIS vinylbenzene-pentadiene-vinylbenzene
(2) SBS styrene-butadiene-styrene
(3) SEBS vinylbenzene-(ethylene/butylene)-vinylbenzene,
Its soft durometer of SIS and molecular weight are fit to be applied to Pressuresensitive Tape, with the tool thermotolerance of SEBS.
Because hot plastic rubber is the same with natural rubber, itself does not have viscosity thermoplastic elastomer, therefore be made into pressure sensitive adhesive, therefore the essential tackifying resin that adds, above-mentioned tackifier are tackifying resin, and hot plastic rubber is the same with natural rubber, itself does not have viscosity thermoplastic elastomer, therefore be made into pressure sensitive adhesive, therefore the essential tackifying resin that adds, its tackifying resin is divided into two classes:
(a) nonpolar, its solubility parameter is generally all lower, as: aliphatics and alicyclic petroleum resin, rosin and staybelite fat, terpine resin, resol;
(b) polarity, its solubility parameter are generally all higher, such as aromatic petroleum resin, and coumarone-indene resin, indenes alkene-phenol resins that softening temperature is higher.
The solvent of the viscose 3 of meeting oil suction and solvent adopts toluene, and bridging agent mainly is:
(1), sulphur and sulfur-donor
(2), organo-peroxide
(3), active phenolphthalein resin.
3 three layers of total thickness of viscose of the anti-glutinous layer 1 of non-silicone oil system, polyethylene terephtalate polyester film 2, meeting oil suction and solvent are 0.07～0.10mm, polyethylene terephtalate polyester film (2) layer thickness is 0.05～0.055mm, and viscose 3 coat-thicknesses of meeting oil suction and solvent are 0.02～0.025mm.
The anti-aging agent of the viscose 3 of meeting oil suction and solvent adopts:
Vinylbenzene-pentadiene-vinylbenzene, the unsaturated rubber of vinylbenzene-(ethylene/butylene)-thermoplastic elastomers such as vinylbenzene also can be subject to oxygen, ozone and ultraviolet effect in air, therefore the essential anti-aging agent that adds.
The solvent of understanding the viscose 3 of oil suction and solvent adopts toluene: gasoline (50: 50) mixes, and solvent pressure-sensitive adhesive is not avoided the residual solvent in the glue-line after drying, therefore the slower solvent of solvent evaporates is understood the character of influential the finished product.Toluene all has good intermiscibility, and is residual little to performance impact.Toluene: gasoline (50: 50) mixes, and can obtain minimum soltion viscosity to the ideal solvent system, drying efficiency and the most cheap price.
The static inhibitor (WETTING AGENT) (wetting agent) of the viscose 3 of meeting oil suction and solvent, it mainly provides when the solution colloid, coats meeting generation agglomeration effect on the PET film, adds therefore must be coated with.
Can oil suction and the bridging agent of the viscose 3 of solvent: purpose be to provide the crosslinked of its glue, and it is heat-resisting to promote, chemical resistant properties, resistance to crocking.It mainly adopts as follows:
(1), sulphur and sulfur-donor,
(2), organo-peroxide,
(3), active phenolphthalein resin.
The thermotolerance that has the meeting oil suction and inhale the cleaning adhesive tape of solvent of the present invention :-70 ℃+250 ℃.
Above illustrated embodiment is only with for conveniently illustrating the present invention, be not that the present invention is done any pro forma restriction, have in the technical field under any and usually know the knowledgeable, if in the scope that does not break away from technical characterictic that the present invention carries, utilize disclosed technology contents to do the local equivalent embodiment that changes or modify, and do not break away from technical characterictic content of the present invention, all still belong in the scope of the technology of the present invention feature.
Claims (5)
- One kind can oil suction and inhale the cleaning adhesive tape of solvent, it is characterized in that: additional polyethylene terephtalate polyester film (2) coating in surface on the non-silicone oil anti-glutinous layer of system (1) layer, the surface is additional on polyethylene terephtalate polyester film (2) coating can oil suction and viscose (3) coating of solvent;Described can oil suction and the viscose (3) of solvent itself, be that the thermoplastic rubber by the asynthetic rubber is matrix, each composition quality ratio is:
- 2. according to claim 1 can oil suction and inhale the cleaning adhesive tape of solvent, it is characterized in that: the plastic elastomer rubber of described heat, it mainly adopts:Vinylbenzene-pentadiene-vinylbenzeneOr styrene-butadiene-styreneOr styrene-ethylene/butylene-styrene.
- 3. according to claim 1 can oil suction and inhale the cleaning adhesive tape of solvent, it is characterized in that: described tackifier are tackifying resin, its tackifying resin adopts:Nonpolar tackifying resin divides: aliphatics or alicyclic petroleum resin, or rosin and staybelite fat, or terpine resin, or resol;Or the polarity tackifying resin divides: aromatic petroleum resin, or coumarone-indene resin.
- 4. according to claim 1 can oil suction and inhale the cleaning adhesive tape of solvent, it is characterized in that: (3) three layers of total thickness of viscose of described non-silicone oil system anti-glutinous layer (1), polyethylene terephtalate polyester film (2), meeting oil suction and solvent are 0.07～0.10mm, polyethylene terephthalate polyester film (2) layer thickness is 0.05～0.055mm, and viscose (3) coat-thickness of meeting oil suction and solvent is 0.02～0.025mm.
- 5. according to claim 1 can oil suction and inhale the cleaning adhesive tape of solvent, it is characterized in that: the ratio of described toluene, gasoline mixture is toluene: gasoline is 50: 50; Described bridging agent adopts: sulphur and sulfur-donor or organo-peroxide or active phenolphthalein resin.