CN101735731A - Nano-ceramic self-cleaning type leather shoe brightener - Google Patents
Nano-ceramic self-cleaning type leather shoe brightener Download PDFInfo
- Publication number
- CN101735731A CN101735731A CN200910231566A CN200910231566A CN101735731A CN 101735731 A CN101735731 A CN 101735731A CN 200910231566 A CN200910231566 A CN 200910231566A CN 200910231566 A CN200910231566 A CN 200910231566A CN 101735731 A CN101735731 A CN 101735731A
- Authority
- CN
- China
- Prior art keywords
- nano
- self
- ceramic
- brightener
- leather shoe
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses nano-ceramic self-cleaning type leather shoe brightener comprising the following raw materials: 30-60 g by weight of film forming matrix, 5-9 g by weight of nano-ceramic material, 1-2 g by weight of nano self-cleaning material, 0.1-0.2 g by weight of emulsifier and 100 ml of water. Compared with the prior art, the nano-ceramic self-cleaning type leather shoe brightener has long leather shoe brightness duration, good wear-resisting performance, good water-resisting effect and photochemical reaction characteristic and can effectively decompose the organic contaminants on the surfaces of the leather shoes under the photocatalysis and make the organic contaminants naturally fall off the surfaces of the leather shoes, thus the labor intensity and the cost of people maintaining the leather shoes are reduced effectively, and the service lives of the leather shoes are prolonged.
Description
Technical field
The present invention relates to the footwear material technical field, specifically a kind of nano-ceramic self-cleaning type leather shoe brightener.
Background technology
At present, the brightening agent that the leather shoes vamp uses mainly contains two kinds of lotion and liquid, and lotion mainly is to be made of wax, after the vamp obliterating, increases gloss to vamp, and the bright time length of this brightening agent is short, and intensity is low, and wears no resistance, and does not have self-cleaning ability; The liquid brightening agent is in the leather shoes production process, be sprayed onto on the vamp, mainly be that several resins are made, the relative paste brightening agent of this brightening agent has improved the bright time length, but exists intensity low equally, and wear resisting property is poor, waterproof effect is poor, the defective that does not have self-cleaning ability can not effectively remove the organic dirt of vamp, increased labour intensity and cost that people maintain leather shoes.
Summary of the invention
Technical assignment of the present invention provides a kind of nano-ceramic self-cleaning type leather shoe brightener.
Technical assignment of the present invention realizes that in the following manner this brightening agent is by becoming membrane matrix, nano ceramic material, Nano self-cleaning material, emulsifying agent and water to constitute, and the weight proportion relation of each raw material is as follows:
Water 100ml becomes membrane matrix 30g~60g, nano ceramic material 5g~9g, Nano self-cleaning material 1g~2g, emulsifying agent 0.1g~0.2g.
Described one-tenth membrane matrix is the mixture of palm wax, Microcrystalline Wax, methyl-silicone oil, amido silicon oil and polysiloxane.
Described nano ceramic material is one or more mixtures in aluminum oxide, silicon carbide and the silicon nitride of particle diameter 0.1~100nm.
Described Nano self-cleaning material is the silicon-dioxide of particle diameter 0.1~100nm and the mixture of titanium dioxide.
Described emulsifying agent is a kind of in tween 20 or the Arlacel-80.
The manufacture craft of this leather shoe brightener is as follows: earlier nano ceramic material and Nano self-cleaning material mixing are put into water, splash into emulsifying agent again, disperse with clarifixator, nano ceramic material and Nano self-cleaning material are dispersed in uniformly form dispersion liquid in the water; The film forming substrate material is added heated and stirred in the reactor, and Heating temperature is 70 ℃~85 ℃ melts it, is to stir in 100~300 stirrers that change at rotating speed, add above-mentioned dispersion liquid while stirring slowly, mix, be cooled to normal temperature afterwards, make the lotion finished product, the packing warehouse-in gets final product.
A kind of nano-ceramic self-cleaning type leather shoe brightener of the present invention is compared with prior art, has bright longer duration, wear resisting property is good, and good water-proof effect has the photochemical reaction characteristic, can be by photocatalysis, effectively decompose the organic dirt of vamp, make dirt to come off naturally, effectively reduced the labour intensity that people maintain leather shoes, reduce cost of upkeep, prolonged the work-ing life of leather shoes.
Embodiment
Embodiment 1:
Get the aluminum oxide of 5g particle diameter 100nm, the silicon-dioxide of 1g particle diameter 100nm and the mixture of titanium dioxide and put into water, splash into the 0.1g tween 20 again, in clarifixator, disperse, aluminum oxide, silicon-dioxide and titanium dioxide are dispersed in uniformly form dispersion liquid in the water; The mixture of getting 30g palm wax, Microcrystalline Wax, methyl-silicone oil, amido silicon oil and polysiloxane adds heated and stirred in the reactor, Heating temperature is 70 ℃ makes its thawing, at rotating speed is to stir in 100 stirrers that change, add above-mentioned dispersion liquid while stirring slowly, mix, be cooled to normal temperature afterwards, make the lotion finished product, the packing warehouse-in gets final product.
Embodiment 2:
Get silicon carbide and the mixture of silicon nitride, the silicon-dioxide of 2g particle diameter 0.1nm and the mixture of titanium dioxide of 9g particle diameter 0.1nm and put into water, splash into the 0.2g Arlacel-80 again, in clarifixator, disperse, silicon carbide, silicon nitride, silicon-dioxide and titanium dioxide are dispersed in uniformly form dispersion liquid in the water; The mixture of getting 60g palm wax, Microcrystalline Wax, methyl-silicone oil, amido silicon oil and polysiloxane adds heated and stirred in the reactor, Heating temperature is 85 ℃ makes its thawing, at rotating speed is to stir in 300 stirrers that change, add above-mentioned dispersion liquid while stirring slowly, mix, be cooled to normal temperature afterwards, make the lotion finished product, the packing warehouse-in gets final product.
Embodiment 3:
Get the mixture of aluminum oxide, silicon carbide and the silicon nitride of 7g particle diameter 50nm, the silicon-dioxide of 1.5g particle diameter 50nm and the mixture of titanium dioxide and put into water, splash into the 0.15g Arlacel-80 again, in clarifixator, disperse, aluminum oxide, silicon carbide, silicon nitride, silicon-dioxide and titanium dioxide are dispersed in uniformly form dispersion liquid in the water; The mixture of getting 45g palm wax, Microcrystalline Wax, methyl-silicone oil, amido silicon oil and polysiloxane adds heated and stirred in the reactor, Heating temperature is 80 ℃ makes its thawing, at rotating speed is to stir in 200 stirrers that change, add above-mentioned dispersion liquid while stirring slowly, mix, be cooled to normal temperature afterwards, make the lotion finished product, the packing warehouse-in gets final product.
Claims (6)
1. a nano-ceramic self-cleaning type leather shoe brightener is characterized in that this brightening agent by becoming membrane matrix, nano ceramic material, Nano self-cleaning material, emulsifying agent and water to constitute, and the weight proportion relation of each raw material is as follows:
Water 100ml becomes membrane matrix 30g~60g, nano ceramic material 5g~9g, Nano self-cleaning material 1g~2g, emulsifying agent 0.1g~0.2g.
2. nano-ceramic self-cleaning type leather shoe brightener according to claim 1 is characterized in that described one-tenth membrane matrix is the mixture of palm wax, Microcrystalline Wax, methyl-silicone oil, amido silicon oil and polysiloxane.
3. nano-ceramic self-cleaning type leather shoe brightener according to claim 1 is characterized in that described nano ceramic material is one or more mixtures in aluminum oxide, silicon carbide and the silicon nitride of particle diameter 0.1~100nm.
4. nano-ceramic self-cleaning type leather shoe brightener according to claim 1 is characterized in that described Nano self-cleaning material is the silicon-dioxide of particle diameter 0.1~100nm and the mixture of titanium dioxide.
5. nano-ceramic self-cleaning type leather shoe brightener according to claim 1 is characterized in that described emulsifying agent is a kind of in tween 20 or the Arlacel-80.
6. nano-ceramic self-cleaning type leather shoe brightener according to claim 1, the manufacture craft that it is characterized in that this leather shoe brightener is as follows: earlier nano ceramic material and Nano self-cleaning material mixing are put into water, splash into emulsifying agent again, disperse with clarifixator, nano ceramic material and Nano self-cleaning material are dispersed in uniformly form dispersion liquid in the water; The film forming substrate material is added heated and stirred in the reactor, and Heating temperature is 70 ℃~85 ℃ melts it, is to stir in 100~300 stirrers that change at rotating speed, add above-mentioned dispersion liquid while stirring slowly, mix, be cooled to normal temperature afterwards, make the lotion finished product.