CN101734719A - Firing process of watertight high temperature carbon cup - Google Patents
Firing process of watertight high temperature carbon cup Download PDFInfo
- Publication number
- CN101734719A CN101734719A CN200810171857A CN200810171857A CN101734719A CN 101734719 A CN101734719 A CN 101734719A CN 200810171857 A CN200810171857 A CN 200810171857A CN 200810171857 A CN200810171857 A CN 200810171857A CN 101734719 A CN101734719 A CN 101734719A
- Authority
- CN
- China
- Prior art keywords
- high temperature
- firing process
- temperature
- carbon cup
- watertight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a firing process of a watertight high temperature carbon cup. Wooden bamboo material is subject to forming so that the wooden bamboo material is made into a containing vessel with containing function; then the containing vessel is put in a sealed steel drum; during the heat processing to the wooden bamboo material, a preset temperature is required to be raised in a preset time within each temperature range, and kilning can not be stopped until tar produced after the burning of the organic substance of the wooden bamboo material in a kiln body in a high temperature carbonization stage is volatilized, therefore, paint vehicle is not required to be brushed, and the radiation rate of the far infrared ray generated by the wooden bamboo material after the high temperature kilning at normal temperature can reach 94.1 percent.
Description
Technical field
The present invention refers to a kind of firing process of watertight high temperature carbon cup that utilizes the high temperature klining and need not to brush any paint vehicle especially for a kind of impermeable charcoal cup is provided.
Background technology
Press,, bamboo wood gas must be done three to five months when making in general commercially available bamboo charcoal beaker, the bamboo wood of finishing afterwards after gas is done carries out sawing and puts into the kiln body, and can pass through many stages in the process of klining respectively, and is as described below:
The hot smoking stage: with 150 ℃ bamboo charcoal is carried out continuous 10 hours klining earlier.
The low-temperature carbonization stage: the bamboo charcoal of finishing the hot smoking stage carries out continuous 30 hours klining with 450 ℃ temperature again, and this stage can be collected the flue gas that klining produces, and becomes bamboo vinegar stoste after cooling.
In the warm charing stage: finish the flue gas that collection produces by bamboo charcoal and after the bamboo vinegar of making, again bamboo charcoal carried out 30 hours klining with 600 ℃ to 700 ℃ high temperature.
Can be different via above-mentioned time of burning till and temperature control point because of the quantity of the structure of kiln, size, bamboo wood or the like factor.
The goods that right above-mentioned klining bamboo wood process is produced, not only far-infrared effect can't effectively promote, and must produce the situation of infiltration with charcoal cup after avoiding by the brushing paint vehicle when using when klining.
Summary of the invention
Main purpose of the present invention is: a kind of firing process of watertight high temperature carbon cup, wooden bamboo wood material is formed processing, make it become ccontaining vessel with ccontaining function, again ccontaining vessel are inserted in the dead front type steel drum and put into the dead front type steel drum and put into, when wooden bamboo wood material carries out heat treated, must be in the scheduled time of each temperature range, promote a preset temperature, up to the intravital wooden bamboo wood material of kiln because of the high temperature carbonization stage, the tar that makes organic substance burning back be produced volatilizees totally, can stop klining, finish wooden bamboo wood material after the klining under normal temperature, can produce the far infrared rays of high emissivity, so, not only need not brushing and prevent the paint vehicle that seeps water, more can produce the far infrared rays of high emissivity.
Secondary objective of the present invention is: as mentioned above, the charcoal cup after the high temperature klining need not be brushed any paint vehicle and promptly have impermeable characteristics, differs from the bamboo charcoal cup that the existing middle low temperature klining in market forms.
Secondary objective of the present invention is: by this kind klining process, and the far infrared irradiation rate that can effectively promote bamboo charcoal cup and produced.
Description of drawings
Fig. 1 is a flow process block schematic diagram of the present invention;
Fig. 2 is a shaping processing block schematic diagram of the present invention;
Fig. 3 is a processing procedure action synoptic diagram one of the present invention;
Fig. 4 is a processing procedure action synoptic diagram two of the present invention;
Fig. 5 is the profile status synoptic diagram of bamboo wood putting position of the present invention.
[figure number explanation]
Bamboo wood ... 1
Dead front type steel drum ... 2
Engine firewall ... 20
Kiln body ... 3
Lid ... 30
Well heater ... 4
Embodiment
Seeing also shown in Figure 1ly, is flow process block schematic diagram of the present invention, by can know among the figure find out the present invention by following flow process to reach impermeable charcoal cup:
A) wooden bamboo wood material is formed processing, make it become ccontaining vessel with ccontaining function;
B) these ccontaining vessel that will have ccontaining function are again inserted in the dead front type steel drum;
C) utilize this dead front type steel drum that is equipped with these ccontaining vessel to put into a kiln body;
When d) in this kiln body, this wood bamboo wood material being carried out heat treated, in the scheduled time of each temperature range, promote a preset temperature, up to kiln is intravital should wood bamboo wood material, the tar that makes the organic substance burning be produced because of the high temperature carbonization stage volatilizees totally, and stops klining; And
E) finish this wood bamboo wood material after the klining under normal temperature, produce the far infrared rays of high emissivity.
Please cooperate simultaneously and consult Fig. 2, Fig. 3 and shown in Figure 4, it is shaping processing block schematic diagram of the present invention, heat treated block schematic diagram one and figure two, find out by knowing among the figure, learn by above-mentioned, the charcoal cup adds in shaping and comprises cutting man-hour, peeling, grind, cutting, light, chamfering, various combinations such as boring, finishing base substrate after the processing then sends in the kiln body (as: gas kiln or electrical kiln) and carries out heat treated, heat treated then can be passed through dry epoch, temperature raising period, the charing initial stage, stages such as main charing phase and refining period, and all must in the scheduled time, reach a temperature range in each stage, and promote a preset temperature, required demand of its each stage is as described below:
1, dry epoch, this temperature raising period and this charing initial stage, its temperature is progressively finished in 200 ℃, and heats up gradually with 2 ℃ to 6 ℃ in each hour.
2, charing initial stage and this main charing phase, its temperature is progressively finished in 400 ℃ in 200 ℃, and heats up gradually with 2 ℃ to 10 ℃ in each hour.
3, the main charing phase, its temperature is progressively finished in 900 ℃ in 400 ℃, and heats up gradually with 10 ℃ to 40 ℃ in each hour.
4, refining period, its temperature is progressively finished in 1000 ℃ in 900 ℃, and heats up gradually with 30 ℃ to 50 ℃ in each hour, and keeps 2 to 3 hours.
By above-mentioned processing procedure, can allow the emissivity of far infrared rays of wooden bamboo wood material be promoted to 94.1%, and the wavelength of its far infrared rays is 3.9um to 16um, make heat insulation effect originally better.
As shown in Figure 5, it is the profile status synoptic diagram of bamboo wood putting position of the present invention, find out by knowing among the figure, the bamboo wood 1 for the treatment of klining is put in dead front type steel drum 2, again dead front type steel drum 2 is put in the kiln body 3, again lid 30 is covered the inlet of kiln body 3, and the bottom in dead front type steel drum 2 is provided with engine firewall 20, carry out temperature controlling by external heated device 4 at engine firewall 20 again, so, operator can utilize well heater 4 to reach effective controlled temperature and klining to go out need not the brushing paint vehicle then can prevent the charcoal cup that seeps water.
Be with, firing process of watertight high temperature carbon cup of the present invention is for improving the key problem in technology of commonly using:
One, as mentioned above, the charcoal cup after the high temperature klining need not be brushed any paint vehicle and promptly have impermeable characteristics, differs from the bamboo charcoal cup that the existing low temperature klining in market forms.
Two, by this kind klining process, the far infrared irradiation rate that can effectively promote bamboo charcoal cup and produced.
In sum, the present invention utilizes the interior method that promotes a preset temperature of the scheduled time of a temperature range, and then make generation of the present invention can more progressive, more practical, more meet institute's palpus that the human consumer uses, and really having met the important document of application for a patent for invention, the whence proposes patent application in accordance with the law.
Yet the above person only is preferred embodiment of the present invention, when not limiting scope of the invention process with this; So all simple equivalent of being done according to the present patent application claim and description of the invention content change and modify, all should still belong in the scope that patent of the present invention contains.
Claims (10)
1. firing process of watertight high temperature carbon cup comprises:
A) wooden bamboo wood material is formed processing, makes it become ccontaining vessel with ccontaining function:
B) these ccontaining vessel that will have ccontaining function are again inserted in the dead front type steel drum;
C) utilize this dead front type steel drum that is equipped with these ccontaining vessel to put into a kiln body;
When d) in this kiln body, this wood bamboo wood material being carried out heat treated, in the scheduled time of each temperature range, promote a preset temperature, up to kiln is intravital should wood bamboo wood material, the tar that makes the organic substance burning be produced because of the high temperature carbonization stage volatilizees totally, and stops klining; And
E) finish this wood bamboo wood material after the klining under normal temperature, produce the far infrared rays of high emissivity.
2. firing process of watertight high temperature carbon cup as claimed in claim 1, wherein this shaping processing comprises following combination: cutting, peeling, grinding, cutting, light, chamfering, boring.
3. firing process of watertight high temperature carbon cup as claimed in claim 1, wherein this kiln body be a gas kiln or electrical kiln one of them.
4. firing process of watertight high temperature carbon cup as claimed in claim 1, wherein this heat treated comprises: dry epoch, temperature raising period, charing initial stage, main charing phase and refining period.
5. firing process of watertight high temperature carbon cup as claimed in claim 4, wherein this dry epoch, this temperature raising period and this charing initial stage, its temperature is progressively finished in 200 ℃, and heats up gradually with 2 ℃ to 6 ℃ in each hour.
6. firing process of watertight high temperature carbon cup as claimed in claim 4, wherein this charing initial stage and this main charing phase, its temperature is progressively finished in 400 ℃ in 200 ℃, and heats up gradually with 2 ℃ to 10 ℃ in each hour.
7. firing process of watertight high temperature carbon cup as claimed in claim 4, wherein this main charing phase, its temperature is progressively finished in 900 ℃ in 400 ℃, and heats up gradually with 10 ℃ to 40 ℃ in each hour.
8. firing process of watertight high temperature carbon cup as claimed in claim 4, wherein should refining period its temperature progressively finish in 1000 ℃ in 900 ℃, and heat up gradually with 30 ℃ to 50 ℃, and kept 2 to 3 hours in each hour.
9. firing process of watertight high temperature carbon cup as claimed in claim 1, the emissivity of this far infrared rays that wherein should wood bamboo wood material is 94.1%.
10. firing process of watertight high temperature carbon cup as claimed in claim 1, wherein the wavelength of this far infrared rays is 3.9um to 16um.