CN101723625B - Abrasion proof ground material - Google Patents
Abrasion proof ground material Download PDFInfo
- Publication number
- CN101723625B CN101723625B CN2008101974142A CN200810197414A CN101723625B CN 101723625 B CN101723625 B CN 101723625B CN 2008101974142 A CN2008101974142 A CN 2008101974142A CN 200810197414 A CN200810197414 A CN 200810197414A CN 101723625 B CN101723625 B CN 101723625B
- Authority
- CN
- China
- Prior art keywords
- ground material
- abrasion proof
- proof ground
- powder
- abrasion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention provides an abrasion proof ground material. The abrasion proof ground material comprises cement, extra hard alloy metallic aggregates, red alumina, dispersible gelatine powder, silicon micro powder, a water reducing agent, quartz sand, ferric hydroxide and a brightener. The preparation method comprises the following steps of: adding cement and extra hard alloy metallic aggregates in a double helix cone type mixer, starting the mixer, adding filling materials including the red alumina, dispersible gelatine powder, quartz sand, brightener, water reducing agent, ferric hydroxide, silicon micro powder and the like and continuously mixing the filling materials for 45 to 60 minutes until the color and interface are evenly mixed, weighing up the mixture and packaging. The abrasion proof ground material has the advantages of static electricity resistance, spark failure, high strength, high abrasion proof property, good luster, difficult oil impregnate and pollution resistance, and is particularly suitable for heavy machinery plants.
Description
Technical field
The present invention relates to a kind of earth material, specifically a kind of abrasion proof ground material.
Background technology
Abrasion-proof terrace is at the new joints cement concrete and the even curface that paves; Evenly spreading one deck abrasion-proof terrace material uses the finisher of specialty to carry slurry and receive the light operation, utilizes the slurry of substrate concrete that wetting back of high-abrasive material and substrate concrete are formed an integral body; And form an anti-skid wearable surface layer on the surface; Obviously improve concrete surface strength, strengthened wear resisting property, solved founding, a dirt problem on ground, reservoir area to greatest extent.
And at present common abrasion proof ground material is owing to adopt common silica sand or common metal slag; Have following shortcoming: be prone to oil impregnate, resistance to crocking is relatively poor, it is 15cm that oil oozes the degree of depth, and Mohs' hardness is 6～7; Wear-resisting shortcoming such as bad can not be applicable to Heavy Machinery Plant.
Summary of the invention
The purpose of this invention is to provide a kind of abrasion proof ground material, solve poor, the wear-resisting not enough problem of common abrasion proof ground material oil rub resistance.
Abrasion proof ground material provided by the invention is characterized in that the composition of each component and weight percent are following:
Cement 20%～35%
Superhard alloy metal aggregate 30%～55%
Arsenic soil 1%～3%
Can disperse rubber powder 1%～3%
Silicon powder 3%～5%
Water reducer 0.1%～0.3%
Silica sand 1%～33%
Ironic hydroxide 1%～3%
Brightening agent 1%～3%
Can disperse rubber powder is the vinylformic acid rubber powder, and water reducer is a polycarboxylate water-reducer, and brightening agent is a sulfonated melamine.
The invention provides a kind of preparation method of abrasion proof ground material, it is characterized in that:, earlier cement and superhard alloy metal aggregate are added the duplex cone-type mixer according to formula rate; Start machinery; Add arsenic soil then, can disperse stopping composition such as rubber powder, silica sand, brightening agent, water reducer, ironic hydroxide, silicon powder to continue to mix, mixed 45～60 minutes, mixed until color and interface; Weigh packing.
Superhard alloy metal aggregate anti-electrostatic, hardness that the present invention selects for use are big; Arsenic soil is misfired; Can disperse rubber powder is polymer powder, can improve cement rigidity, improve splitting resistance, improve cohesiveness, anti-soil etc.; Silicon powder can the intergranular hole of filling concrete, simultaneously and hydrated product generate gelinite, can significantly improve resistance to compression, anti-folding, impervious, anticorrosion, shock resistance and wear resisting property.
The present invention is applied to the substrate concrete surface in initial set stage soon as the dried material that spreads; Through processing, make itself and basic unit concrete to form an integral body specially, thereby the concrete surface wear resistance is significantly improved, extruding, anti-folding, tension, shock resistance, fuel tolerance capability are enhanced; And cleaning does not play ash; Have wear-resisting, dustproof and advantage attractive in appearance, improve operating environment greatly, will become current ideal concrete surface strengthening material.
The volume resistance of abrasion proof ground material of the present invention and surface resistivity are 1 * 10
6～1 * 10
9, meeting GB GB50209-95, it is 1.3～2.7cm that oil oozes the degree of depth, the Mohs' hardness of aggregate is more than 9.Therefore, abrasion proof ground material of the present invention has anti-electrostatic, misfires, and intensity is high, and wear resistance is high, and good luster is difficult for oil impregnate, resistant to pollution function, is particularly suitable for Heavy Machinery Plant.
Embodiment
Below in conjunction with embodiment the present invention is done further detailed description, following examples are to explanation of the present invention and the present invention is not limited to following examples.
Embodiment 1:
Earlier portland cement 30%, superhard alloy metal aggregate (20～60 order) 30% are added the duplex cone-type mixer; Start machinery; Add arsenic soil (350 order) 1%, vinylformic acid rubber powder 3%, silicon powder (3000 order) 3%, polycarboxylate water-reducer 0.1%, silica sand (20～60 order) 30.4%, ironic hydroxide 1.5%, sulfonated melamine 1% etc. then and continue to mix, mixed 55 minutes, mixed until color and interface; Weigh packing.Through test, the volume resistance of this abrasion proof ground material and surface resistivity are 1 * 10
6～1 * 10
9, meeting GB GB50209-95, it is 1.3～2.7cm that oil oozes the degree of depth, the Mohs' hardness of aggregate is more than 9.
Embodiment 2:
Earlier portland cement 35%, superhard alloy metal aggregate (20～60 order) 40% are added the duplex cone-type mixer; Start machinery; Add arsenic soil (350 order) 2%, vinylformic acid rubber powder 3%, silicon powder (3000 order) 4%, polycarboxylate water-reducer 0.2%, silica sand (20～60 order) 10.8%, ironic hydroxide 2%, sulfonated melamine 1% etc. then and continue to mix, mixed 60 minutes, mixed until color and interface; Weigh packing.Through test, the volume resistance of this abrasion proof ground material and surface resistivity are 1 * 10
6～1 * 10
9, meeting GB GB50209-95, it is 1.3～2.7cm that oil oozes the degree of depth, the Mohs' hardness of aggregate is more than 9.
Embodiment 3:
Earlier portland cement 31.7%, superhard alloy metal aggregate (20～60 order) 55% are added the duplex cone-type mixer; Start machinery; Add arsenic soil (350 order) 3%, vinylformic acid rubber powder 1%, silicon powder (3000 order) 5%, polycarboxylate water-reducer 0.3%, silica sand (20～60 order) 1%, ironic hydroxide 2%, sulfonated melamine 1% etc. then and continue to mix, mixed 50 minutes, mixed until color and interface; Weigh packing.Through test, the volume resistance of this abrasion proof ground material and surface resistivity are 1 * 10
6～1 * 10
9, meeting GB GB50209-95, it is 1.3～2.7cm that oil oozes the degree of depth, the Mohs' hardness of aggregate is more than 9.
Claims (3)
1. abrasion proof ground material is characterized in that the composition of each component and weight percent are following:
2. abrasion proof ground material according to claim 1 is characterized in that: can disperse rubber powder is the vinylformic acid rubber powder, and water reducer is a polycarboxylate water-reducer, and brightening agent is a sulfonated melamine.
3. the preparation method of an abrasion proof ground material is characterized in that: according to the described formula rate of claim 1, earlier cement and superhard alloy metal aggregate are added the duplex cone-type mixer; Start machinery; Add arsenic soil then, can disperse rubber powder, silica sand, brightening agent, water reducer, ironic hydroxide, silicon powder stopping composition continues to mix, and mixes 45～60 minutes, mix until color and interface; Weigh packing.