CN101709186A - 防火涂料 - Google Patents
防火涂料 Download PDFInfo
- Publication number
- CN101709186A CN101709186A CN200910175265A CN200910175265A CN101709186A CN 101709186 A CN101709186 A CN 101709186A CN 200910175265 A CN200910175265 A CN 200910175265A CN 200910175265 A CN200910175265 A CN 200910175265A CN 101709186 A CN101709186 A CN 101709186A
- Authority
- CN
- China
- Prior art keywords
- coating
- parts
- water
- fire retardant
- present
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种防火涂料,该涂料由下述重量份的原料制成:水400-600份、柔性乳液250-350份、三聚氰胺100-200份、季戊四醇50-100份和适量水性增稠剂。本涂料以柔性乳液为基料;以三聚氰胺和季戊四醇为阻燃剂制成,具有阻燃时间长,拉伸粘结强度高,防火性能好的特点。
Description
技术领域
本发明涉及一种建筑涂料,尤其是一种用于建筑材料聚苯乙烯板的防火涂料。
背景技术
目前,防火涂料在世界上有两大类:一类是非发泡型的防火涂料,虽有很强的耐火与耐水性能,但隔热性不良,防火性能不高。另一类是发泡型防火涂料,尤其当遇火时能形成蜂窝微泡结构的隔热层,隔热性能好,这类涂料通常是以有机高分子作为成膜材料,这类涂料隔热性优异,防火性能良好,但发泡隔热层机械强度低,易掉落,致使防火性能降低或失效,此外成本较高,装饰性也不够理想。
发明内容
本发明要解决的技术问题是提供一种隔热性能和防火性能好的防火涂料。
为解决上述技术问题,本发明所采取的技术方案是:该涂料由下述重量份的原料制成:水400-600份、柔性乳液250-350份、三聚氰胺100-200份、季戊四醇50-100份和适量水性增稠剂。
优选的,所述原料的重量份为:水500份、柔性乳液300份、三聚氰胺150份、季戊四醇75份和适量增稠剂。
优选的,所述的柔性乳液选自氯丁胶乳、丁基胶乳、醋酸乙烯共聚乳液或VAE乳液。
优选的,所述增稠剂选自聚氨酯增稠剂(HEUR)、缔合型碱溶胀增稠剂(HASE)和羟乙基纤维素(HEC)。
采用上述技术方案所产生的有益效果在于:本发明以柔性乳液为基料;以三聚氰胺和季戊四醇为阻燃剂制成,具有阻燃时间长,拉伸粘结强度高,防火性能好的特点。
具体实施方式
下面结合具体实施例对本发明作进一步详细的说明。
实施例1:
采用下述重量的原料制备:水500kg、醋酸乙烯共聚乳液300kg、三聚氰胺150kg、季戊四醇75kg、聚氨酯(PU,属于HEUR系列)3kg。
制备方法:将上述各原料混合搅拌均匀即可得到本涂料。
本实施例得到的涂料性能检测:
PH值:在本涂料无结块、搅拌均匀的状态下检测;检测结果:PH=8。
施工性:分别在可发性聚苯乙烯板(EPS)和聚苯乙烯挤塑板(XPS)板上涂刷本涂料,使粉刷有涂料的EPS/XPS板的长边呈水平方向、短边与水平面呈约85°角竖放。放置0.5h后,再用同样方法涂刷第二道本涂料。在涂刷第二道时,刷子运行无困难,为“施工无障碍”。经试验,本实施例得到的涂料的施工性为:施工无障碍。
表干时间:分别在EPS/XPS板上涂刷两道本涂料,晾置,晾置过程中用手指触摸表面,当无涂料粘在手指上,即判定表面干燥,该时间即为表干时间/h。本实施例得到的涂料在≥15℃、通风干燥环境下的表干时间=37min。
拉伸粘结强度:按JC/T993-2006外墙外保温用膨胀聚苯乙烯板抹面胶浆中附录A的规定进行测定。经检测,涂刷有本涂料的聚苯板与胶粘剂的原强度=0.32MPa、耐水强度=0.26MPa;涂刷有本涂料的聚苯板与抹面胶浆的原强度=0.31MPa、耐水强度=0.27MPa、耐冻融强度=0.25MPa。
阻燃时间:在尺寸为150mm×150mm的EPS/XPS板上涂刷一道本涂料,形成试验板;用圆筒内径9.5mm±0.5mm的本生灯,以液化石油气为燃气,在试验板中心的下部炙烧实验板,本生灯喷嘴端面距离实验板13mm±1mm;炙烧过程中,取5个试验板无火焰及滴落物产生的平均时间,该平均时间即为阻燃时间。经试验,涂刷本实施例得到的涂料时的阻燃时间=25s。
实施例2:
采用下述重量的原料制备:水400kg、氯丁胶乳320kg、三聚氰胺200kg、季戊四醇60kg、增稠剂ASE-60(属于HASE系列)5kg。
制备方法:将上述各原料混合搅拌均匀即可得到本涂料。
本实施例得到的涂料性能检测:
PH值:在本涂料无结块、搅拌均匀的状态下检测;检测结果:PH=8.6。
施工性:施工性试验方法同实施例1。经试验,本实施例得到的涂料的施工性为:施工无障碍。
表干时间:表干时间试验方法同实施例1。本实施例得到的涂料在≥15℃、通风干燥环境下的表干时间=42min。
拉伸粘结强度:按JC/T993-2006外墙外保温用膨胀聚苯乙烯板抹面胶浆中附录A的规定进行测定。经检测,涂刷有本涂料的聚苯板与胶粘剂的原强度=0.28MPa、耐水强度=0.22MPa;涂刷有本涂料的聚苯板与抹面胶浆的原强度=0.27MPa、耐水强度=0.23MPa、耐冻融强度=0.23MPa。
阻燃时间:阻燃时间试验方法同实施例1。经试验,涂刷本实施例得到的涂料时的阻燃时间=18s。
实施例3:
采用下述重量的原料制备:水450kg、丁基胶乳250kg、三聚氰胺180kg、季戊四醇50kg、甲基羟乙基纤维素(HMEC,属于HEC系列)4kg。
制备方法:将上述各原料混合搅拌均匀即可得到本涂料。
本实施例得到的涂料性能检测:
PH值:在本涂料无结块、搅拌均匀的状态下检测;检测结果:PH=9.0。
施工性:施工性试验方法同实施例1。经试验,本实施例得到的涂料的施工性为:施工无障碍。
表干时间:表干时间试验方法同实施例1。本实施例得到的涂料在≥15℃、通风干燥环境下的表干时间=52min。
拉伸粘结强度:按JC/T993-2006外墙外保温用膨胀聚苯乙烯板抹面胶浆中附录A的规定进行测定。经检测,涂刷有本涂料的聚苯板与胶粘剂的原强度=0.25MPa、耐水强度=0.21MPa;涂刷有本涂料的聚苯板与抹面胶浆的原强度=0.26MPa、耐水强度=0.22MPa、耐冻融强度=0.21MPa。
阻燃时间:阻燃时间试验方法同实施例1。经试验,涂刷本实施例得到的涂料时的阻燃时间=19s。
实施例4:
采用下述重量的原料制备:水600kg、VAE乳液270kg、三聚氰胺100kg、季戊四醇100kg、HEUR-C 5kg。
制备方法:将上述各原料混合搅拌均匀即可得到本涂料。
本实施例得到的涂料性能检测:
PH值:在本涂料无结块、搅拌均匀的状态下检测;检测结果:PH=8.5。
施工性:施工性试验方法同实施例1。经试验,本实施例得到的涂料的施工性为:施工无障碍。
表干时间:表干时间试验方法同实施例1。本实施例得到的涂料在≥15℃、通风干燥环境下的表干时间=47min。
拉伸粘结强度:按JC/T993-2006外墙外保温用膨胀聚苯乙烯板抹面胶浆中附录A的规定进行测定。经检测,涂刷有本涂料的聚苯板与胶粘剂的原强度=0.28MPa、耐水强度=0.23MPa;涂刷有本涂料的聚苯板与抹面胶浆的原强度=0.28MPa、耐水强度=0.22MPa、耐冻融强度=0.22MPa。
阻燃时间:阻燃时间试验方法同实施例1。经试验,涂刷本实施例得到的涂料时的阻燃时间=21s。
实施例5:
1.采用下述重量的原料制备:水550kg、醋酸乙烯共聚乳液270kg、三聚氰胺120kg、季戊四醇90kg、疏水缔合羟乙基纤维素(HMHEC)4.5kg。
制备方法:将上述各原料混合搅拌均匀即可得到本涂料。
本实施例得到的涂料性能检测:
PH值:在本涂料无结块、搅拌均匀的状态下检测;检测结果:PH=8.3。
施工性:施工性试验方法同实施例1。经试验,本实施例得到的涂料的施工性为:施工无障碍。
表干时间:表干时间试验方法同实施例1。本实施例得到的涂料在≥15℃、通风干燥环境下的表干时间=46min。
拉伸粘结强度:按JC/T993-2006外墙外保温用膨胀聚苯乙烯板抹面胶浆中附录A的规定进行测定。经检测,涂刷有本涂料的聚苯板与胶粘剂的原强度=0.30MPa、耐水强度=0.25MPa;涂刷有本涂料的聚苯板与抹面胶浆的原强度=0.29MPa、耐水强度=0.26MPa、耐冻融强度=0.24MPa。
阻燃时间:阻燃时间试验方法同实施例1。经试验,涂刷本实施例得到的涂料时的阻燃时间=18s。
Claims (4)
1.一种防火涂料,其特征在于该涂料由下述重量份的原料制成:水400-600份、柔性乳液250-350份、三聚氰胺100-200份、季戊四醇50-100份和适量水性增稠剂。
2.根据权利要求1所述的防火涂料,其特征在于所述原料的重量份为:水500份、柔性乳液300份、三聚氰胺150份、季戊四醇75份和适量增稠剂。
3.根据权利要求1所述的防火涂料,其特征在于:所述的柔性乳液选自氯丁胶乳、丁基胶乳、醋酸乙烯共聚乳液或VAE乳液。
4.根据权利要求1、2或3所述的防火涂料,其特征在于:所述增稠剂选自HEUR类、HASE类和HEC类。