CN101701118A - Metal antiseptic silicon fluoride paint and preparation method thereof - Google Patents
Metal antiseptic silicon fluoride paint and preparation method thereof Download PDFInfo
- Publication number
- CN101701118A CN101701118A CN200910075899A CN200910075899A CN101701118A CN 101701118 A CN101701118 A CN 101701118A CN 200910075899 A CN200910075899 A CN 200910075899A CN 200910075899 A CN200910075899 A CN 200910075899A CN 101701118 A CN101701118 A CN 101701118A
- Authority
- CN
- China
- Prior art keywords
- paint
- silicon fluoride
- preparation
- corrosion
- metal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a metal antiseptic silicon fluoride paint and preparation method thereof. The paint is characterized by comprising the follow components by weight percent: 40-70% of modified high chlorinated polyethylene resin, 15-20% of organic silicon fluoride resin, 20-25% of solvent dimethylbenzene, 3-5% of organic tin dibutyltin dilaurate and 3-5% of phenyl silicone resin. The metal antiseptic silicon fluoride paint of the invention is applicable to power equipment metal elements such as iron tower and the like and has the long-term effective anti-corrosion protection function on the iron tower and other metal elements. The invention has the characteristic that: 1. the paint is resistant to chemical corrosion and electrochemical corrosion and is capable of resisting various strong corrosion mediums; 2. plyadhesion of film is strong, reliability is high, thus being capable of preventing destroy of water, oxygen and other corrosion mediums; 3. the paint has super weather fastness and is uvioresistant and resistant to temperature change, and period of maintenance and use is long, thus the paint is applicable to adverse weather condition and various strong corrosion environments.
Description
Technical field
The present invention relates to a kind of preparation method of coating, relate in particular to a kind of metal antiseptic silicon fluoride paint and preparation method thereof.
Background technology
Electric power transmission line is an important transportation passage of the energy, has brought into play enormous function in national economic development process.Under filthy conditions such as high height above sea level, many thunders and lightnings and coastal salt fog, sand and dust, water smoke, chemical mediator, corrosion phenomenon usually appears in metal component surface for a long time for line steel tower and other all kinds of hardwares.Gently then influence equipment appearance, heavy then threaten the equipment operating safety, make transmitting line exist potential safety hazard, can cause the direct massive losses that influences production and construction and people's lives that is difficult to remedy.
At present, the protective system that is used for operation power equipment in a large number mainly is " cold-applied zinc ", though this protective system can effectively be removed the rusty stain of power equipment hardware, weak point is that the anticorrosion life-span is short partially.
Summary of the invention
The objective of the invention is in order to solve the deficiencies in the prior art, for the long-time effectively anti-corrosion protection of iron tower and other hardware designs a kind of metal antiseptic silicon fluoride paint of invention and preparation method thereof.
The present invention for the technical scheme that remedies the deficiencies in the prior art and adopt is:
1, the quality percentage composition of metal antiseptic silicon fluoride paint component is: the HCPE 40～70% of modification, organic fluorinated silicone resin 15～20%, solvent xylene 20～25%, organotin dibutyl tin laurate 3～5%, phenyl polysiloxane 3～5%.
2, the present invention for the technical scheme that remedies the deficiencies in the prior art and adopt also can be: the HCPE with modification is a base-material, add the organic fluorinated silicone resin in the preparation protective system, and with 70～150 ℃ of temperature, under pressure 0.1～0.3Mpa condition, react after 1～3 hour, add volatile solvent and solidifying agent, protective agent and make metal antiseptic silicon fluoride paint.
3, the solidifying agent of the above-mentioned described component of the present invention is the organotin dibutyl tin laurate, and described protective agent is a phenyl polysiloxane.
The invention has the beneficial effects as follows:
1. metal antiseptic silicon fluoride paint and preparation method thereof has had the ability of various strong corrosive mediums such as corrosion of opposing chemicals-resistant and galvanic corrosion.
2. strong adhesion, reliability height between paint film layer have water, oxygen and other corrosive medium destructive ability of prevention; Super weather resisteant, uvioresistant, temp. variation resistant ability are strong.
3. be applicable to heavy weather condition and various strong corrosive environment, played effective corrosionproof protection effect for iron tower and other hardware extend working time.
Embodiment
1, a kind of metal antiseptic silicon fluoride paint and preparation method thereof, the quality percentage composition of its metal antiseptic silicon fluoride paint component is: the HCPE 40～70% of modification, organic fluorinated silicone resin 15～20%, solvent xylene 20～25%, organotin dibutyl tin laurate 3～5%, phenyl polysiloxane 3～5%.
2, described a kind of metal antiseptic silicon fluoride paint and preparation method thereof, its preparation method is: the HCPE with modification is a base-material, add the organic fluorinated silicone resin in the preparation protective system, and with 70～150 ℃ of temperature, under pressure 0.1～0.3Mpa condition, react after 1～3 hour, add volatile solvent and solidifying agent, protective agent and make metal antiseptic silicon fluoride paint.
3, the metal antiseptic silicon fluoride paint of making according to above-mentioned preparation method, the solidifying agent of described component are the organotin dibutyl tin laurates, and described protective agent is a phenyl polysiloxane.
4, hardware is taked sandblast or technologies such as rubberization, metallic brush carry out zone of oxidation cleaning after, again described metal antiseptic silicon fluoride paint spraying or the brushing for preparing formed corrosion protection coating on hardware, its thickness is 0.3～0.5 millimeter, and coating evenly, pore-free, nothing pile up.Metal antiseptic silicon fluoride paint has obtained ideal corrosion protection coating effect on hardware.
Claims (3)
1. metal antiseptic silicon fluoride paint and preparation method thereof, it is characterized in that: the quality percentage composition of metal antiseptic silicon fluoride paint component is: the HCPE 40～70% of modification, organic fluorinated silicone resin 15～20%, solvent xylene 20～25%, organotin dibutyl tin laurate 3～5%, phenyl polysiloxane 3～5%.
2. a kind of metal antiseptic silicon fluoride paint according to claim 1 and preparation method thereof, it is characterized in that: the HCPE with modification is a base-material, add the organic fluorinated silicone resin in the preparation protective system, and with 70～150 ℃ of temperature, under pressure 0.1～0.3Mpa condition, react after 1～3 hour, add volatile solvent and solidifying agent, protective agent and make metal antiseptic silicon fluoride paint.
3. the metal antiseptic silicon fluoride paint of making according to the preparation method of claim 1 or 2, the solidifying agent of described component is the organotin dibutyl tin laurate, described protective agent is a phenyl polysiloxane.