CN101696753A - White polytetrafluoroethylene pipe with colored sign line and manufacture method thereof - Google Patents
White polytetrafluoroethylene pipe with colored sign line and manufacture method thereof Download PDFInfo
- Publication number
- CN101696753A CN101696753A CN200910071024A CN200910071024A CN101696753A CN 101696753 A CN101696753 A CN 101696753A CN 200910071024 A CN200910071024 A CN 200910071024A CN 200910071024 A CN200910071024 A CN 200910071024A CN 101696753 A CN101696753 A CN 101696753A
- Authority
- CN
- China
- Prior art keywords
- white
- pipe
- colored
- mould
- manufacture method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a white polytetrafluoroethylene pipe with a colored sign line and a manufacture method thereof. For the white polytetrafluoroethylene pipe, the colored sign line is formed along the axial direction on the peripheral surface of the white pipe wall. With the white polytetrafluoroethylene pipe with the colored sign line and the manufacture method thereof, the white polytetrafluoroethylene pipes can be completely differentiated by using sign lines of different colors, when a plurality of white polytetrafluoroethylene pipes are centrally used for conveying different fluidized media, an operator can not only directly observe the change condition inside each pipe from the outside, but also can effectively differentiate different types of fluidized media according to the colored sign lines, therefore, the white polytetrafluoroethylene pipe is convenient and practical. In addition, the manufacture method can also be used for manufacturing the pipes of pipe walls and sign lines of different colors.
Description
Technical field
The present invention relates to a kind of tubing and processing technique thereof, particularly relate to a kind of white polytetrafluoroethylpipe pipe and manufacture method thereof that has colored sign line.
Background technique
Teflon is a kind of chemical raw material with excellent high and low temperature resistance and chemical stability, excellent electric insulating energy, non-adhesive, weatherability, flame retarding and good self lubricity, therefore obtains extensive use in fields such as chemical industry, oil, weaving, electric, medical treatment and machineries.Polyfluortetraethylene pipe is to adopt extruding method to make with teflon as raw material, and main three will be used for conveying gas or liquid medium.Polyfluortetraethylene pipe color commonly used at present is more single, even be pure white, or has different colors.Because the tube wall of white polytetrafluoroethylpipe pipe is transparent, therefore can be easy to from visual observation to its inner liquid or gas situation of change, and the polyfluortetraethylene pipe that has a color can't be accomplished.But under some occasion, when needs concentrate use to carry different flowing mediums many tubing, when also needing to observe directly from the outside situation of change of every tubing inside and active zone separate different types flowing medium simultaneously, existing polyfluortetraethylene pipe all can not satisfy this requirement.
Summary of the invention
In order to address the above problem, the object of the present invention is to provide a kind of situation of change that can either observe directly tubing inside, can concentrate the white polytetrafluoroethylpipe pipe that has colored sign line of effectively distinguishing different interior medias when using again.
Another object of the present invention is to provide a kind of above-mentioned manufacture method that has the white polytetrafluoroethylpipe pipe of colored sign line.
In order to achieve the above object, the white polytetrafluoroethylpipe pipe that has colored sign line provided by the invention is in axial direction to form the coloured markings of a band on its white tube wall outer peripheral surface.
The width of described markings is 0.5-1.5mm.
The manufacture method that has the white polytetrafluoroethylpipe pipe of colored sign line provided by the invention comprises the following step that carries out in order:
1) teflon is divided bulk cargo and as the gasoline of extrusion aid with 100: the weight ratio of 1-50 is mixed into white mixed ingredients, at room temperature places 5-48 hour then to carry out slaking;
2) teflon is divided bulk cargo, as the gasoline of extrusion aid and pigment with 100: the weight ratio of 1-50: 0.1-10 is mixed into colored mixed ingredients, at room temperature places 5-48 hour then to carry out slaking;
3) the inner side margin of the external mold in the blank mould is vertically put into a metal bar shaped mould isometric with the external mold internal height, then by external mold, pour above-mentioned white mixed ingredients in the space that core and mouthful mould constitute through overcuring, reach the height of metal bar shaped mould up to the piling height of white mixed ingredients, take out metal bar shaped mould afterwards, again above-mentioned colored mixed ingredients through overcuring is poured into and taken out in the space of being reserved behind the metal bar shaped mould, install top die at last, and under the pressure of 1-10MPa, pushed depanning and the tubulose hair made is bad 5-15 minute;
4) with the bad top, space that constitutes by external mold, centrum mould, mouthful mould and core on the extrusion die of putting into of tubulose hair, install top die then, afterwards at the pressure of 1-50MPa, the pushing speed of 1-20mm/min, and under the condition of the cooling section of the dryer section of the room temperature of associating-260 ℃, 260 ℃-380 ℃ sintering stage and 380 ℃-200 ℃, push and sintering 10-30 minute the tubulose hair is bad continuously, promptly can be made into the described white polytetrafluoroethylpipe pipe that has colored sign line behind depanning and the natural cooling.
White polytetrafluoroethylpipe pipe and the manufacture method thereof that has colored sign line provided by the invention can utilize the markings of different colours that white polytetrafluoroethylpipe pipe is distinguished fully, when carrying different flowing mediums when concentrating many white polytetrafluoroethylpipe pipes of use like this, operator not only can observe directly the situation of change of every tubing inside from the outside, and it is, therefore convenient, practical according to all right active zone separate different types flowing medium of colored sign line.In addition, this manufacture method can also be used to make the tubing that tube wall and markings have different colours.
Description of drawings
Fig. 1 is the white polytetrafluoroethylpipe pipe structural perspective that has colored sign line provided by the invention.
Fig. 2 is the blank mould that manufacture method the adopted extruding mixed ingredients process schematic representation that has the white polytetrafluoroethylpipe pipe of colored sign line provided by the invention.
The tubulose hair bad structural representation of Fig. 3 for squeezing out by the blank mould shown in Fig. 2.
Fig. 4 is the bad process schematic representation of extrusion die extruded tubular hair that manufacture method adopted that has the white polytetrafluoroethylpipe pipe of colored sign line provided by the invention.
Embodiment
Below in conjunction with the drawings and specific embodiments white polytetrafluoroethylpipe pipe and the manufacture method thereof that has colored sign line provided by the invention is elaborated.
As shown in Figure 1, the white polytetrafluoroethylpipe pipe 1 that has colored sign line provided by the invention is in axial direction to form the coloured markings 2 of a band on its white tube wall outer peripheral surface.
The width of described markings 2 is 0.5-1.5mm.
Embodiment 1: the manufacture method that has the white polytetrafluoroethylpipe pipe of blue markings
The manufacture method of the white polytetrafluoroethylpipe pipe that has blue markings that present embodiment provides comprises the following step that carries out in order:
1) teflon is divided bulk cargo and be mixed into white mixed ingredients with 100: 17 weight ratio, at room temperature place 24 hours then, make extrusion aid mix teflon fully and divide in the bulk cargo to carry out slaking as the gasoline of extrusion aid;
2) teflon is divided bulk cargo, mix the au bleu mixed ingredients as the gasoline of extrusion aid and blue pigment with 100: 17: 0.5 weight ratio, at room temperature place 24 hours then to carry out slaking;
3) the 3 inner side margin of the external mold in blank mould are as shown in Figure 2 vertically put into a metal bar shaped mould 4 isometric with external mold 3 internal height, then by external mold 3, pour above-mentioned white mixed ingredients in the space that core 5 and mouthful mould 6 constitute through overcuring, reach the height of metal bar shaped mould 4 up to the piling height of white mixed ingredients, take out metal bar shaped mould 4 afterwards, again above-mentioned blue mixed ingredients through overcuring is poured into and taken out in the space of being reserved behind the metal bar shaped mould 4, install top die 7 at last, and under the pressure of 3Mpa, pushed depanning and make tubulose hair shown in Figure 3 bad 85 minutes;
4) with the top, space that constitutes by external mold 10, centrum mould 11, mouthful mould 12 and core 13 on bad 8 extrusion dies of putting into as shown in Figure 49 of tubulose hair, install top die 14 then, afterwards at the pressure of 20Mpa, the pushing speed of 5mm/min, and under the condition of the cooling section of the dryer section of the room temperature of associating-260 ℃, 260 ℃-380 ℃ sintering stage and 380 ℃-200 ℃, tubulose hair bad 8 pushed continuously and sintering 10 minutes, promptly can be made into the white polytetrafluoroethylpipe pipe that has blue markings 1 as shown in Figure 1 behind depanning and the natural cooling.
The width of described metal bar shaped mould 4 is 1mm, and thickness is 1/4 of external mold 3 internal diameters.
Embodiment 2: the manufacture method that has the white polytetrafluoroethylpipe pipe of red marker line
The manufacture method of the white polytetrafluoroethylpipe pipe that has the red marker line that present embodiment provides comprises the following step that carries out in order:
1) teflon is divided bulk cargo and be mixed into white mixed ingredients with 100: 19 weight ratio, at room temperature place 20 hours then to carry out slaking as the gasoline of extrusion aid;
2) teflon is divided bulk cargo, be mixed into red mixed ingredients as the gasoline of extrusion aid and red pigment with 100: 19: 2 weight ratio, at room temperature place 20 hours then to carry out slaking;
3) the 3 inner side margin of the external mold in blank mould are as shown in Figure 2 vertically put into a metal bar shaped mould 4 isometric with external mold 3 internal height, then by external mold 3, pour above-mentioned white mixed ingredients in the space that core 5 and mouthful mould 6 constitute through overcuring, reach the height of metal bar shaped mould 4 up to the piling height of white mixed ingredients, take out metal bar shaped mould 4 afterwards, again above-mentioned red mixed ingredients through overcuring is poured into and taken out in the space of being reserved behind the metal bar shaped mould 4, install top die 7 at last, and under the pressure of 2MPa, pushed depanning and make tubulose hair shown in Figure 3 bad 86 minutes;
4) with the top, space that constitutes by external mold 10, centrum mould 11, mouthful mould 12 and core 13 on bad 8 extrusion dies of putting into as shown in Figure 49 of tubulose hair, install top die 14 then, afterwards at the pressure of 25MPa, the pushing speed of 3mm/min, and under the condition of the cooling section of the dryer section of the room temperature of associating-260 ℃, 260 ℃-380 ℃ sintering stage and 380 ℃-200 ℃, tubulose hair bad 8 pushed continuously and sintering 12 minutes, promptly can be made into the white polytetrafluoroethylpipe pipe that has the red marker line 1 as shown in Figure 1 behind depanning and the natural cooling.
Embodiment 3: the manufacture method that has the white polytetrafluoroethylpipe pipe of green mark line
The manufacture method of the white polytetrafluoroethylpipe pipe that has the green mark line that present embodiment provides comprises the following step that carries out in order:
1) teflon is divided bulk cargo and be mixed into white mixed ingredients with 100: 20 weight ratio, at room temperature place 26 hours then to carry out slaking as the gasoline of extrusion aid;
2) teflon is divided bulk cargo, be mixed into green mixed ingredients as the gasoline of extrusion aid and viridine green with 100: 20: 1 weight ratio, at room temperature place 26 hours then to carry out slaking;
3) the 3 inner side margin of the external mold in blank mould are as shown in Figure 2 vertically put into a metal bar shaped mould 4 isometric with external mold 3 internal height, then by external mold 3, pour above-mentioned white mixed ingredients in the space that core 5 and mouthful mould 6 constitute through overcuring, reach the height of metal bar shaped mould 4 up to the piling height of white mixed ingredients, take out metal bar shaped mould 4 afterwards, again above-mentioned green mixed ingredients through overcuring is poured into and taken out in the space of being reserved behind the metal bar shaped mould 4, install top die 7 at last, and under the pressure of 4Mpa, pushed depanning and make tubulose hair shown in Figure 3 bad 89 minutes;
4) with the top, space that constitutes by external mold 10, centrum mould 11, mouthful mould 12 and core 13 on bad 8 extrusion dies of putting into as shown in Figure 49 of tubulose hair, install top die 14 then, afterwards at the pressure of 23Mpa, the pushing speed of 7mm/min, and under the condition of the cooling section of the dryer section of the room temperature of associating-260 ℃, 260 ℃-380 ℃ sintering stage and 380 ℃-200 ℃, tubulose hair bad 8 pushed continuously and sintering 14 minutes, promptly can be made into the white polytetrafluoroethylpipe pipe that has the green mark line 1 as shown in Figure 1 behind depanning and the natural cooling.
Claims (4)
1. white polytetrafluoroethylpipe pipe that has colored sign line, it is characterized in that: the white polytetrafluoroethylpipe pipe of described colored sign line (1) is in axial direction to form the coloured markings of a band (2) on its white tube wall outer peripheral surface.
2. the white polytetrafluoroethylpipe pipe that has colored sign line according to claim 1 is characterized in that: the width of described markings (2) is 0.5-1.5mm.
3. manufacture method that has the white polytetrafluoroethylpipe pipe of colored sign line as claimed in claim 1, it is characterized in that: described manufacture method comprises the following step that carries out in order:
1) teflon is divided bulk cargo and as the gasoline of extrusion aid with 100: the weight ratio of 1-50 is mixed into white mixed ingredients, at room temperature places 5-48 hour then to carry out slaking;
2) teflon is divided bulk cargo, as the gasoline of extrusion aid and pigment with 100: the weight ratio of 1-50: 0.1-10 is mixed into colored mixed ingredients, at room temperature places 5-48 hour then to carry out slaking;
3) the inner side margin of the external mold in the blank mould (3) is vertically put into a metal bar shaped mould (4) isometric with external mold (3) internal height, then by external mold (3), pour above-mentioned white mixed ingredients in core (5) and mouthful space that mould (6) constitutes through overcuring, reach the height of metal bar shaped mould (4) up to the piling height of white mixed ingredients, take out metal bar shaped mould (4) afterwards, again above-mentioned colored mixed ingredients through overcuring is poured into and taken out in the space of being reserved behind the metal bar shaped mould (4), install top die (7) at last, and under the pressure of 1-10MPa, pushed depanning and make tubulose hair bad (8) 5-15 minute;
4) tubulose hair bad (8) is put into extrusion die (9) and gone up the top, space that constitutes by external mold (10), centrum mould (11), mouthful mould (12) and core (13), install top die (14) then, afterwards at the pressure of 1-50MPa, the pushing speed of 1-20mm/min, and under the cooling section condition of the dryer section of the room temperature of associating-260 ℃, 260 ℃-380 ℃ sintering stage and 380 ℃-200 ℃, tubulose hair bad (8) is pushed and sintering 10-30 minute continuously, promptly can be made into the described white polytetrafluoroethylpipe pipe (1) that has colored sign line behind depanning and the natural cooling.
4. the manufacture method that has the white polytetrafluoroethylpipe pipe of colored sign line according to claim 3 is characterized in that: the width of described metal bar shaped mould (4) is 1mm, and thickness is 1/4 of external mold (3) internal diameter.