CN101696279B - Method for preparing thermoplastic elastomer through dynamic vulcanization - Google Patents
Method for preparing thermoplastic elastomer through dynamic vulcanization Download PDFInfo
- Publication number
- CN101696279B CN101696279B CN2009101932248A CN200910193224A CN101696279B CN 101696279 B CN101696279 B CN 101696279B CN 2009101932248 A CN2009101932248 A CN 2009101932248A CN 200910193224 A CN200910193224 A CN 200910193224A CN 101696279 B CN101696279 B CN 101696279B
- Authority
- CN
- China
- Prior art keywords
- rubber
- master batch
- thermoplastic elastomer
- vulcanizing agent
- dynamic vulcanization
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention relates to a method for preparing a thermoplastic elastomer through dynamic vulcanization, which comprises the following operation steps: (1) preparation of a reactive first-step material, namely, fusing and blending raw materials comprising part of rubber, plastics, a stuffing, a softener, an aging agent and a processing aid except a vulcanizing agent and an accelerant for granulation; (2) preparation of vulcanizing agent master batch, namely, blending the vulcanizing agent and part of the rubber for granulation; (3) preparation of accelerant master batch, namely, blending the accelerant and part of the rubber for granulation; and (4) dynamic vulcanization, namely, mixing the reactive first-step material, the vulcanizing agent master batch and the accelerant master batch prepared by the three steps for dynamic vulcanization. The elastomer prepared by the method has the characteristics of high fluidity, high elasticity and low hardness; and the process has the advantages of wide equipment application, simple preparation processes, wide processing window and the like.
Description
Technical field
The present invention relates to a kind of process for preparation of thermoplastic elastomer, particularly a kind of method of utilizing dynamic vulcanization technology to prepare thermoplastic elastomer.
Background technology
Dynamic full vulcanization is meant in the mixing tank of high-temperature field and high shear field rubber and resin melt blending; The rubber original position is vulcanized the also trickle stable dispersion system of formation in the resin that is scattered under the effect of linking agent; Thereby the elastomerics of preparing of new generation, its elastomerics of preparing had both had the processing convenience of thermoplastics, had the snappiness of thermoset rubber again; Excellent combination property; Moulding process is simple, and can reclaim use repeatedly, is progressively replacing traditional rubber in a lot of fields.
In the dynamic vulcanization process, under high-temperature field and high shear forces, rubber is ground into the great quantity of micron particle; Be evenly dispersed in the thermoplastics matrix; The particle diameter of disperse phase rubber is more little, and the mechanical property of material is high more, for the rubber that guarantees disperse phase should tight cure have certain fineness again; Just need blending dispersion and sulfuration be united, promptly require velocity of shear and vulcanization rate to be complementary.Vulcanization rate and technology are closely related, therefore select suitable technology just to become the key point place of production dynamic vulcanization thermoplastic elastomer.
The method of existing preparation dynamic vulcanization thermoplastic elastomer comprises: earlier with rubber and thermoplastic plastic melt blending, after reaching thorough mixing, add vulcanizing agent, limit mixing this moment, limit sulfuration, granulation after sulfuration is accomplished, cooling.Chinese patent CN101445612A discloses a kind of method for preparing thermoplastic elastomer by supercritical fluid assisted dynamic vulcanization that utilizes; Its main points are, supercritical fluid delivery system pilot-gas is in supercritical state, and are injected in forcing machine or the injection moulding machine machine barrel; The supercutical fluid that is injected mixes with polymer melt and vulcanization system; Its advantage is, can promote the dispersion of vulcanized rubber in plastics and the minimizing of size, thus the mechanical property of enhance elasticity body; But its deficiency is, thereby to the higher narrow application range of equipment requirements; Chinese patent CN101440182A discloses a kind of dynamic vulcanization thermoplastic elastomer and preparation method, is included under the shear conditions, with plastics and EPDM rubber melt-processed under high shear forces; And adding at least a organo-peroxide solidifying agent and additional propylene class homopolymer, its benefit is to have the linking agent that can form radical; Help the rubber curing reaction more; But its deficiency is, the elastomerics illiquidity of preparing and seem harder, and deformability is bad.
Technology contents
The technical problem that the utility model will solve is to provide a kind of method for preparing dynamic vulcanization thermoplastic elastomer; So that prepare the dynamic vulcanization thermoplastic elastomer of high workability, low compression set, soft, improve its equipment scope of application, production efficiency and reduce production costs.
The method for preparing thermoplastic elastomer through dynamic vulcanization that the present invention proposes is following:
(1) preparation of a reactive step material: part rubber, plastics, filler, tenderizer, aging agent and processing aid are carried out the melt blending granulation, and wherein rubber accounts for the 10-70% of rubber gross weight in the prepared thermoplastic elastomer;
(2) preparation of vulcanizing agent rubber master batch: with vulcanizing agent and the granulation of part blend rubber, wherein rubber accounts for the 20-60% of rubber gross weight in the prepared thermoplastic elastomer;
(3) preparation of promotor rubber master batch: with promotor and the granulation of part blend rubber, wherein promotor accounts for the 5-30% of rubber gross weight in the prepared thermoplastic elastomer;
(4) dynamic vulcanization: one step of reactivity material, vulcanizing agent rubber master batch, the promotor rubber master batch of above-mentioned three steps preparation are mixed into the sulfuration of action attitude.
Except that vulcanizing agent rubber master batch and promotor rubber master batch, prescription used in the present invention is the prescription of the dynamic vulcanization thermoplastic elastomer of routine, and the raw material that uses is the known raw material that can be used for dynamic vulcanization thermoplastic elastomer.Wherein rubber can be selected X 050, tree elastomer, trans-isoprene, terpolymer EP rubber, cis-1,4-polybutadiene rubber, Injecatable EVA Copolymer, chlorinated polyethylene rubber, acrylic elastomer, paracril, styrene-butadiene rubber(SBR) or their mixture; Plastics comprise Vilaterm, PS, SE, Vestolen PP 7052, polymeric amide, acrylonitrile-butadiene-styrene copolymer, styrene-acrylonitrile copolymer, polycarbonate, polymethylmethacrylate, polybutylene terephthalate or their mixture; Filler has WHITE CARBON BLACK, carbon black, lime carbonate, talcum powder, potter's clay; Tenderizer comprises NO, Yellow Protopet 2A, white mineral oil, Vaseline; Aging agent comprises 1010 (Hinered phenols), 168 (phosphorous acid esters); Processing aid comprises Triple Pressed Stearic Acid, polyethylene wax.
Described vulcanizing agent comprises organo-peroxide, sulphur, resol, brominated phenolic resin or their mixture.
Vulcanizing agent component concentration per-cent in the vulcanizing agent rubber master batch is 5-90%, wherein preferred 20-80%.
Described promotor comprises dithiocarbamate(s), xanthogenic acid salt, thiazole salt, Thiourea, guanidine class, sulfenamide, thiurams, aldehyde amines, metal halide class or their mixture, wherein preferred ziram, zinc n butylxanthate, dibenzothiazole disulfide, thiocarbamyl sulfenamide, vulkacit D, N cyclohexyl 2 benzothiazole sulfenamide, tetramethyl-thiuram disulfide, hexamethylenetetramine or 2-benzothiazolyl mercaptan.
Promoter component percentage composition in the promotor rubber master batch is 2-85%, wherein preferred 10-80%.
In formula system; The usage quantity of vulcanizing agent is fewer; Therefore direct adding then is difficult in the system and mixes, and causes the rubber phase state of vulcanization in the system uneven easily, part rubber phase over cure; And another part rubber phase is undervulcanization, makes that prepared dynamic vulcanization thermoplastic elastomer quality is inhomogeneous; Same, because the promotor usage quantity is seldom, directly adding is difficult in the system and mixes, and causes the rubber phase vulcanization rate in the system different easily.
Vulcanizing agent and part rubber are prepared into the vulcanizing agent rubber master batch, owing to do not have promotor in the vulcanizing agent rubber master batch, and temperature is a normal temperature during preparation vulcanizing agent rubber master batch; Therefore can avoid vulcanizing agent and rubber phase generation prevulcanized, as previously mentioned, vulcanizing agent rubber master batch and promotor rubber master batch joined after the system; Along with beginning of shearing carries out; Vulcanizing agent rubber master batch and promotor rubber master batch begin to disperse in a reactive step material, and vulcanizing agent contacts with promotor beginning also and simultaneously carries out vulcanization reaction with rubber phase, owing to adopt vulcanizing agent and promotor to adopt the mode of rubber master batch rather than directly adding; Thereby more even, thereby improve the uniformity coefficient of its sulfidation with contacting of rubber phase.Equally; Vulcanizing agent and promotor contact with rubber gradually along with the carrying out of shearing and carry out vulcanization reaction; Thereby the danger of having avoided the rubber phase overcuring and can not having continued to be sheared, and the island structure that rubber phase is sheared into certain fineness more easily is dispersed in the plastic substrate.
Of the present invention pair of rubber master batch legal system is equipped with the method for thermoplastic elastomer, and its advantage is following:
Owing to adopt the mode of rubber master batch rather than directly add vulcanizing agent and promotor; Thereby it is more even with contacting of rubber phase; Thereby improve the uniformity coefficient of its sulfidation; Equally, vulcanizing agent and promotor contact with rubber gradually along with the carrying out of shearing and carry out vulcanization reaction, thereby have avoided the problem that excessively causes rubber phase to be difficult to shear because of prevulcanized.
Use the promotor rubber master batch to make usage quantity promotor seldom in system, mix more easily; On the other hand; After promotor is scattered in rubber master batch, no dust, pollution-free, be suitable for automatic weighing operation, for the processing of dynamic vulcanization thermoplastic elastomer brings convenience.
In a word, the rubber that adopts two rubber master batch technology to solve disperse phase should tight cure has the difficult point of certain fineness again, and prepared dynamic vulcanization thermoplastic elastomer has advantages such as high workability, low compression set, soft, and quality is more even.And, adopt two rubber master batch technology to associate velocity of shear and vulcanization rate, thereby reduce dependency equipment and technology, have equipment and be suitable for advantages such as wide, that preparation technology is simple, process window is wide.
Embodiment
Below in conjunction with specific embodiment, the present invention is done further explain, but the present invention is confined to scope of embodiments.
In following embodiment, aging agent can be selected 1010 (Hinered phenols) or 168 (phosphorous acid esters) for use, and processing aid comprises Triple Pressed Stearic Acid or polyethylene wax.
Embodiment 1
A kind of method for preparing thermoplastic elastomer through dynamic vulcanization, step is following:
1) preparation of a reactive step material: 30 parts of terpolymer EP rubbers (EPDM), 40 parts of Vestolen PP 7052 (PP), 10 parts of filler WHITE CARBON BLACKs, 30 parts of tenderizer white mineral oils, 0.5 part of aging agent, 0.5 part of processing aid are mixed in 180 ℃ of mixing tanks; Carry out granulation then, obtain a reactive step material.
2) preparation of vulcanizing agent rubber master batch: 3 parts of vulcanizing agent resol and 20 parts of EPDM are mixed in 120 ℃ of mixing tanks, carry out granulation then, obtain the vulcanizing agent rubber master batch.
3) preparation of promotor rubber master batch: 0.6 part of promotor ziram and 10 parts of EPDM are mixed in 120 ℃ of mixing tanks, carry out granulation then, obtain the promotor rubber master batch.
4) dynamic vulcanization: one step of reactivity material, vulcanizing agent rubber master batch, the promotor rubber master batch of above-mentioned three step preparations joined carry out dynamic vulcanization in 180 ℃ the mixing tank cocurrent and parallel twin screw extruder and obtain rubber and plastic than EPT rubber (EPDM/PP) dynamic vulcanization thermoplastic elastomer that is 60/40.
Embodiment 2
A kind of method for preparing thermoplastic elastomer through dynamic vulcanization, step is following:
1) preparation of a reactive step material: 40 parts of paracrils (NBR), 30 parts of polyamide (PA)s, 5 parts of filler carbon blacks, 10 parts of tenderizer Vaseline, 0.4 part of aging agent, 0.6 part of processing aid are mixed in 200 ℃ of mixing tanks; Carry out granulation then, obtain a reactive step material.
2) preparation of vulcanizing agent rubber master batch: 4 parts of vulcanizing agent sulphur and 20 parts of NBR are mixed in 120 ℃ of mixing tanks, carry out granulation then, obtain the vulcanizing agent rubber master batch.
3) preparation of promotor rubber master batch: 0.7 part of promotor zinc n butylxanthate and 10 parts of NBR are mixed in 120 ℃ of mixing tanks, carry out granulation then, obtain the promotor rubber master batch.
4) dynamic vulcanization: one step of reactivity material, vulcanizing agent rubber master batch, the promotor rubber master batch of above-mentioned three step preparations joined carry out dynamic vulcanization in 200 ℃ the mixing tank and obtain rubber and plastic than paracril/polymeric amide (NBR/PA) dynamic vulcanization thermoplastic elastomer that is 70/30.
Embodiment 3
A kind of method for preparing thermoplastic elastomer through dynamic vulcanization, step is following:
1) preparation of a reactive step material: 10 parts of X 050s (CR), 40 parts of Vilaterm (PE), 25 parts of filler-calcium carbonates, 24 parts of tenderizer NOs, 0.5 part of aging agent, 0.5 part of processing aid are mixed in 180 ℃ of mixing tanks; Carry out granulation then, obtain a reactive step material.
2) preparation of vulcanizing agent rubber master batch: 6 parts of vulcanizing agent brominated phenolic resins and 60 parts of X 050s are mixed in 120 ℃ of mixing tanks, carry out granulation then, obtain the vulcanizing agent rubber master batch.
3) preparation of promotor rubber master batch: 0.7 part of accelerator dibenzothiazyl disulfide and 30 parts of X 050s are mixed in 120 ℃ of mixing tanks, carry out granulation then, obtain the promotor rubber master batch.
4) dynamic vulcanization: one step of reactivity material, vulcanizing agent rubber master batch, the promotor rubber master batch of above-mentioned three step preparations joined carry out dynamic vulcanization in 180 ℃ the mixing tank and obtain rubber and plastic than X 050/Vilaterm (CR/PE) dynamic vulcanization thermoplastic elastomer that is 100/40.
Embodiment 4
A kind of method for preparing thermoplastic elastomer through dynamic vulcanization, step is following:
1) preparation of a reactive step material: 20 parts of trans-isoprenes (TPI), 40 parts of PS (PS), 20 parts of filler talcum powder, 25 parts of tenderizer Vaseline, 0.5 part of aging agent, 0.5 part of processing aid are mixed in 180 ℃ of mixing tanks; Carry out granulation then, obtain a reactive step material.
2) preparation of vulcanizing agent rubber master batch: 8 parts of vulcanizing agent sulphur and 12 parts of trans-isoprenes are mixed in 120 ℃ of mixing tanks, carry out granulation then, obtain the vulcanizing agent rubber master batch.
3) preparation of promotor rubber master batch: 1.2 parts of promotor thiocarbamyl sulfenamides and 8 parts of trans-isoprenes are mixed in 120 ℃ of mixing tanks, carry out granulation then, obtain the promotor rubber master batch.
4) dynamic vulcanization: one step of reactivity material, vulcanizing agent rubber master batch, the promotor rubber master batch of above-mentioned three step preparations joined carry out dynamic vulcanization in 180 ℃ the mixing tank and obtain rubber and plastic than trans-isoprene/PS (TPI/PS) dynamic vulcanization thermoplastic elastomer that is 40/40.
Embodiment 5
A kind of method for preparing thermoplastic elastomer through dynamic vulcanization, step is following:
1) preparation of a reactive step material: 35 parts of cis-1,4-polybutadiene rubbers (BR), 40 parts of SE (PVC), 10 parts of filler potter's clay, 30 parts of tenderizer Yellow Protopet 2As, 0.4 part of aging agent, 0.8 part of processing aid are mixed in 180 ℃ of mixing tanks; Carry out granulation then, obtain a reactive step material.
2) preparation of vulcanizing agent rubber master batch: 9 parts of vulcanizing agent Lucidols and 1 part of cis-1,4-polybutadiene rubber are mixed in 120 ℃ of mixing tanks, carry out granulation then, obtain the vulcanizing agent rubber master batch.
3) preparation of promotor rubber master batch: 6 parts of promotor vulkacit D and 14 parts of cis-1,4-polybutadiene rubbers are mixed in 120 ℃ of mixing tanks, carry out granulation then, obtain the promotor rubber master batch.
4) dynamic vulcanization: one step of reactivity material, vulcanizing agent rubber master batch, the promotor rubber master batch of above-mentioned three step preparations joined carry out dynamic vulcanization in 180 ℃ the mixing tank and obtain rubber and plastic than cis-1,4-polybutadiene rubber/vinylchlorid (BR/PVC) dynamic vulcanization thermoplastic elastomer that is 50/40.
Embodiment 6
A kind of method for preparing thermoplastic elastomer through dynamic vulcanization, step is following:
1) preparation of a reactive step material: 40 parts of Injecatable EVA Copolymers (EVA), 40 parts of polycarbonate (PC), 10 parts of filler-calcium carbonates, 35 parts of tenderizer NOs, 0.8 part of aging agent, 0.6 part of processing aid are mixed in 180 ℃ of mixing tanks; Carry out granulation then, obtain a reactive step material.
2) preparation of vulcanizing agent rubber master batch: 10 parts of vulcanizing agent resol and 13.5 parts of Injecatable EVA Copolymers are mixed in 120 ℃ of mixing tanks, carry out granulation then, obtain the vulcanizing agent rubber master batch.
3) preparation of promotor rubber master batch: 8.5 parts of accelerant N-cyclohexyl-2-[4-morpholinodithio sulphenamide and 1.5 parts of Injecatable EVA Copolymers are mixed in 120 ℃ of mixing tanks, carry out granulation then, obtain the promotor rubber master batch.
4) dynamic vulcanization: one step of reactivity material, vulcanizing agent rubber master batch, the promotor rubber master batch of above-mentioned three step preparations joined carry out dynamic vulcanization in 180 ℃ the mixing tank and obtain rubber and plastic than Injecatable EVA Copolymer/polycarbonate (EVA/PC) dynamic vulcanization thermoplastic elastomer that is 55/40.
Embodiment 7
A kind of method for preparing thermoplastic elastomer through dynamic vulcanization, step is following:
1) preparation of a reactive step material: 60 parts of chlorinated polyethylene rubbers (CM), 20 parts of polymethylmethacrylates (PMMA), 9 parts of filler carbon blacks, 30 parts of tenderizer Yellow Protopet 2As, 0.7 part of aging agent, 0.4 part of processing aid are mixed in 180 ℃ of mixing tanks; Carry out granulation then, obtain a reactive step material.
2) preparation of vulcanizing agent rubber master batch: 0.3 part of vulcanizing agent sulphur and 15 parts of chlorinated polyethylene rubbers are mixed in 120 ℃ of mixing tanks, carry out granulation then, obtain the vulcanizing agent rubber master batch.
3) preparation of promotor rubber master batch: 2 parts of accelerant disulfide tetra methylthiurams and 10 parts of chlorinated polyethylene rubbers are mixed in 120 ℃ of mixing tanks, carry out granulation then, obtain the promotor rubber master batch.
4) dynamic vulcanization: one step of reactivity material, vulcanizing agent rubber master batch, the promotor rubber master batch of above-mentioned three step preparations joined carry out dynamic vulcanization in 180 ℃ the mixing tank and obtain rubber and plastic than chlorinated polyethylene rubber/polymethylmethacrylate (CM/PMMA) dynamic vulcanization thermoplastic elastomer that is 85/40.
Embodiment 8
A kind of method for preparing thermoplastic elastomer through dynamic vulcanization, step is following:
1) preparation of a reactive step material: 40 parts of acrylic elastomers (ACM), 40 parts of polybutylene terephthalates (PBT), 10 parts of filler WHITE CARBON BLACKs, 26 parts of tenderizer Vaseline, 0.7 part of aging agent, 0.5 part of processing aid are mixed in 180 ℃ of mixing tanks; Carry out granulation then, obtain a reactive step material.
2) preparation of vulcanizing agent rubber master batch: 3 parts of vulcanizing agent resol and 22 parts of acrylic elastomers are mixed in 120 ℃ of mixing tanks, carry out granulation then, obtain the vulcanizing agent rubber master batch.
3) preparation of promotor rubber master batch: 2 parts of promotor hexamethylenetetramines and 8 parts of acrylic elastomers are mixed in 120 ℃ of mixing tanks, carry out granulation then, obtain the promotor rubber master batch.
4) dynamic vulcanization: one step of reactivity material, vulcanizing agent rubber master batch, the promotor rubber master batch of above-mentioned three step preparations joined carry out dynamic vulcanization in 180 ℃ the mixing tank and obtain rubber and plastic than acrylic elastomer/polybutylene terephthalate (ACM/PBT) dynamic vulcanization thermoplastic elastomer that is 70/40.
Embodiment 9
A kind of method for preparing thermoplastic elastomer through dynamic vulcanization, step is following:
1) preparation of a reactive step material: 30 parts of styrene-butadiene rubber(SBR) (SBR), 30 parts of acrylonitrile-butadiene-styrene copolymers (ABS), 10 parts of filler talcum powder, 22 parts of tenderizer white mineral oils, 0.5 part of aging agent, 0.7 part of processing aid are mixed in 180 ℃ of mixing tanks; Carry out granulation then, obtain a reactive step material.
2) preparation of vulcanizing agent rubber master batch: 5 parts of vulcanizing agent brominated phenolic resins and 20 parts of styrene-butadiene rubber(SBR) are mixed in 120 ℃ of mixing tanks, carry out granulation then, obtain the vulcanizing agent rubber master batch.
3) preparation of promotor rubber master batch: 1 part of promotor 2-benzothiazolyl mercaptan and 10 parts of styrene-butadiene rubber(SBR) are mixed in 120 ℃ of mixing tanks, carry out granulation then, obtain the promotor rubber master batch.
4) dynamic vulcanization: one step of reactivity material, vulcanizing agent rubber master batch, the promotor rubber master batch of above-mentioned three step preparations joined carry out dynamic vulcanization in 180 ℃ the mixing tank and obtain rubber and plastic than styrene-butadiene rubber(SBR)/acrylonitrile-butadiene-styrene copolymer (SBR/ABS) dynamic vulcanization thermoplastic elastomer that is 60/40.
Comparative Examples 1
Adopt conventional art to prepare rubber and plastic than EPT rubber (EPDM/PP) dynamic vulcanization thermoplastic elastomer that is 60/40.Operation steps is following:
60 parts of terpolymer EP rubbers (EPDM), 40 parts of Vestolen PP 7052 (PP), 10 parts of fillers, 30 parts of tenderizers, 0.5 part of aging agent, 0.5 part of processing aid are mixed in 180 ℃ of mixing tanks, add 3 parts of vulcanizing agents and 0.6 part of promotor then and carry out dynamic vulcanization and obtain rubber and plastic than EPT rubber (EPDM/PP) dynamic vulcanization thermoplastic elastomer that is 60/40.
Comparative Examples 2
Adopt conventional art to prepare rubber and plastic than nitrile rubber/polypropylene (NBR/PA) dynamic vulcanization thermoplastic elastomer that is 70/30.Operation steps is following:
70 parts of paracrils (NBR), 30 parts of Vestolen PP 7052 (PA), 5 parts of fillers, 10 parts of tenderizers, 0.5 part of aging agent, 0.5 part of processing aid are mixed in 200 ℃ of mixing tanks, add 4 parts of vulcanizing agents and 0.7 part of promotor then and carry out dynamic vulcanization and obtain rubber and plastic than EPT rubber (NBR/PA) dynamic vulcanization thermoplastic elastomer that is 70/30.
From embodiment, choose embodiment 1 and embodiment 2 as determination object, the performance data of corresponding Comparative Examples is as a reference with it again.See shown in the table 1 that testing standard all adopts national standard, test condition is 23 ℃.
Table 1
Wherein, the condition of measuring compression set be the condition of 70 ℃ * 22h, melt flow rate(MFR) be g/10min (230 ℃/5kg).Can find out that from table 1 hardness of embodiment 1, tensile set, compression set are less than Comparative Examples 1, tensile strength, 100% tensile modulus, elongation and melt flow rate(MFR) then are greater than Comparative Examples 1; Same; The hardness of embodiment 2, tensile set, compression set are less than Comparative Examples 1; Tensile strength, 100% tensile modulus and melt flow rate(MFR) then are greater than Comparative Examples 1 this explain that the prepared elastomerics that goes out of method for preparing thermoplastic elastomer through dynamic vulcanization of the present invention has higher flowability, low compression set, soft, thereby its overall performance is better than the prepared elastomerics that goes out of traditional technology.And the elastomerics of preparing when being 50/32,62/36,68/35 when rubber and plastic is mobile, low compression set and soft are optimum.
Claims (7)
1. method for preparing thermoplastic elastomer through dynamic vulcanization, step is following:
(1) preparation of a reactive step material: part rubber, plastics, filler, tenderizer, aging agent and processing aid are carried out the melt blending granulation, and wherein rubber accounts for the 10-70% of rubber gross weight in the prepared thermoplastic elastomer;
(2) preparation of vulcanizing agent rubber master batch: with vulcanizing agent and the granulation of part blend rubber, wherein rubber accounts for the 20-60% of rubber gross weight in the prepared thermoplastic elastomer;
(3) preparation of promotor rubber master batch: with promotor and the granulation of part blend rubber, wherein promotor accounts for the 5-30% of rubber gross weight in the prepared thermoplastic elastomer;
(4) dynamic vulcanization: one step of reactivity material, vulcanizing agent rubber master batch, the promotor rubber master batch of above-mentioned three steps preparation are mixed into the sulfuration of action attitude.
2. a kind of method for preparing thermoplastic elastomer through dynamic vulcanization according to claim 1, it is characterized in that: rubber comprises: X 050, tree elastomer, trans-isoprene, terpolymer EP rubber, cis-1,4-polybutadiene rubber, Injecatable EVA Copolymer, chlorinated polyethylene rubber, acrylic elastomer, paracril, styrene-butadiene rubber(SBR) or their mixture.
3. a kind of method for preparing thermoplastic elastomer through dynamic vulcanization according to claim 1, it is characterized in that: plastics comprise: Vilaterm, PS, SE, Vestolen PP 7052, polymeric amide, acrylonitrile-butadiene-styrene copolymer, styrene-acrylonitrile copolymer, polycarbonate, polymethylmethacrylate, polybutylene terephthalate or their mixture.
4. a kind of method for preparing thermoplastic elastomer through dynamic vulcanization according to claim 1 is characterized in that: vulcanizing agent comprises organo-peroxide, sulphur, brominated phenolic resin or their mixture.
5. a kind of method for preparing thermoplastic elastomer through dynamic vulcanization according to claim 1 is characterized in that: the vulcanizing agent component concentration per-cent in the vulcanizing agent rubber master batch is 2-90%.
6. a kind of method for preparing thermoplastic elastomer through dynamic vulcanization according to claim 5 is characterized in that: the preferred ingredient percentage composition of the vulcanizing agent in the vulcanizing agent rubber master batch is 20-80%.
7. a kind of method for preparing thermoplastic elastomer through dynamic vulcanization according to claim 1 is characterized in that: promotor comprises dithiocarbamate(s), xanthogenic acid salt, thiazole salt, Thiourea, guanidine class, sulfenamide, thiurams, aldehyde amines, metal halide class or their mixture.