CN101684346A - Composition of 10PB 5.25/9 pigment and technical method for preparing color characterization objects by using same - Google Patents

Abstract

The invention discloses a composition of a 10PB 5.25/9 pigment, which comprises the following components in parts by weight: 995-1005 parts of CSC-B base material, 17.32-17.65 parts of PV23 with the pigment content of 30 percent, 1.32-1.46 parts of PB15:3 with the pigment content of 27 percent and 0.46 part of PBK7 with the pigment content of 9 percent. The main component of the CSC-B base material is acrylic copolymer the content of which is 30-40 percent and the average molecular weight range of which is 150,000-200,000. TiO2 is selected as the main white pigment and has the content of 8-12percent. For the base material, the contrast ratio is 0.78-0.82, the Stormer viscosity is 90-100 KU, and when an incident angle is 85 degrees, the glossiness is 5-10. The composition has high weatherresistance and stability and good proportioning reproducibility; the adopted raw materials and the technology process both meet the low-VOC and zero-VOC environment protection requirement and standard; and compared with a standard value in a theoretical model of Chinese Color System, the real object color block of the composition has the advantages of very little chromatism, very high accurate degree of color realization, concise manufacture process and very high practical value.

Description

The composition of 10PB 5.25/9 pigment and with the technological method of this preparation of compositions characterization substance

[technical field]

The present invention relates to composition, particularly be the composition of pigment, and with the technological method of this preparation of compositions characterization substance.

[background technology]

A kind of color comprises form and aspect, lightness and chroma, as long as determined form and aspect, lightness and chroma, just can determine unique a kind of color.Stipulate among the Chinese colour system GB/T 15608-1995 that in the Chinese colour system theoretical model, any color can be demarcated with the tone on the color solid, lightness and chroma, and gives certain label.Scaling method is to write out tone H earlier, writes lightness V then, writes chroma C behind oblique line, represent with H V/C, and be example with color 10BG 5.5/6,10BG represents tone, 5.5 expression lightness, 6 expression chromas.

Theoretical value from theoretical model can relate to multinomial important steps such as aberration Δ E, raw material, prescription and technology to the production process of physical color lump.Wherein, Difference Control is to weigh the unalterable quota of a national colours reproducing technology ability, and the degree of approach that aberration is more little, the color theory value is reduced into the color matter sample is high more, and technical difficulty is big more, the scientific research strength that indicates this state simultaneously is strong more, and state of the art is high more.Therefore the research and development technology of physical color lump and research and development achievement in the Chinese colour system theoretical model, embodied the sci-tech innovation ability of China, all had extremely profound significance in the status in color field, the world for development that promotes whole country color science technical field and raising country in the color field.

Coating pigment obtains physical color lump in accordance with regulations, and physical color lump is widely applied to the national life every aspect, radiation with have influence on each field relevant with color.For example, coloured manufacturing, electronic imaging, colored record, multi-media storage and transmission, liquid-crystal display, the practical sample of having contained the national standard under the method for expressing of color, relevant industries comprise: modern architecture and finishing material, clothes, textile materials, dissemination of news medium and printing industry, industries such as multimedia display color.

At present, domesticly also be in the stage of accurately to control to the technical elements that reproduces physical color lump, and this is only the core of color theory using value in the theoretical value from theoretical model.

[summary of the invention]

The composition that the purpose of this invention is to provide a kind of 10PB 5.25/9 pigment reaches the physical color lump of realizing with this composition, the fast light sex change and the favorable reproducibility of this physical color lump coating, and glossiness is moderate, and environmental protection.

A kind of composition of 10PB 5.25/9 pigment consists of by weight:

995～1005 parts of CSC-B base-materials;

PV23, pigment content are 30%, 17.32～17.65 parts;

PB15:3, pigment content are 27%, 1.32～1.46 parts;

PBK7, pigment content are 9%, 0.46 part.

Above-mentioned CSC-B base-material main component is an acrylic copolymer, and content is 30～40%, and its average molecular weight range is 15～200,000, median size is 0.1～0.2m, and minimum film-forming temperature is 10～22 ℃, 25～35 ℃ of second-order transition temperature sides, anionic, pH value are 8.5～10.0.Select TiO for use ₂Content 〉=95%, oil number＜20g/100g, the reducing power Reynolds is several now 1800, and ISO 591 R2 types are as main white pigment, and content is 8～12%.The contrast ratio of this base-material is 0.78～0.82, and stormer viscosity is 90～100KU, and incident angle is 85 o'clock, glossiness 5～10.

A kind of physical color lump of 10PB 5.25/9 color, press above-mentioned raw materials and proportioning, incident angle is 85 o'clock, its glossiness 4～6, and aberration Δ E≤3.0 between the standard value, the Chromatic color that satisfies GB/T 15608-1995 " Chinese colour system " national Specification are the requirement of sample aberration latitude Δ E≤3.

The preparation method of the physical color lump of above-mentioned 10PB 5.25/9 color comprises the steps:

1) raw material blending: the proportioning by above-mentioned 10PB 5.25/9 color takes by weighing raw material, mixes.

2) coating: in envrionment conditions is relative humidity 50% ± 5%, in 23 ± 2 ℃ of the room temperatures, adopts mechanical coating method, and composition evenly entirely is coated on the White Board, and the coating wet-film thickness is 250m.

3) drying: place 50 ± 2 ℃ of dry 3～4h of accurate baking oven to constant weight composition coating, take out, be cooled to room temperature, obtain physical color lump.

Advantage of the present invention: said composition weathering resistance and stability are high, and good proportion repeatability, raw materials used and technological process meet low VOC and zero VOC environmental protection requirement and standard; It is very little that this physical color lump and the standard value in " Chinese colour system " theoretical model are compared aberration, and the order of accuarcy that color realizes is very high, and manufacture craft is concise, has extremely strong practical value.

[embodiment]

Pigment preferred for this invention comprises that international pigment index codes is PV23 (pigment content is 30%), PB15:3 (pigment content is 27%) and PBK7 (pigment content is 9%).Wherein, PV23 (pigment content is 30%) dioxazine violet, it is present the most frequently used heterocyclic violet pigment, be the blue light purple, bright-colored pure, outstanding tinctorial strength and luminance brightness and excellent heat-resisting, anti-oozing property and good light fastness are arranged, stronger opacifying power is arranged, even usage quantity can keep excellent weathering resistance seldom equally, be mainly used in the painted of automobile, motorcycle, bike one class flawless finish coating; PB15:3 (pigment content is 27%) is a phthalocyanine blue, because phthalocyanine pigment has excellent sun-proof and resistance toheat, is insoluble to any solvent, and has extremely bright-coloured form and aspect, belongs to best performance in the current senior pigment, a class that cost is minimum; PBK7 (pigment content is 9%) is a kind of high-carbon black pigment, particle size range 10～15nm, be used for trace adjustment and water down and reduce the saturation ratio and the lightness of color, play the colour killing effect, not causing simultaneously the bigger deviation of generations on the form and aspect, is that a kind of security is higher and improve the very tangible pigment of effect for the fine setting of color.

Adopting contrast ratio is 0.78～0.82, and stormer viscosity is 90～100KU, and the CSC-B base-material of glossiness (85) 5～10 is realized the underlying carrier of color as us, and the CSC-B base-material is provided by the Hiachuan Industry Co., Ltd., Shenzhen.

We are called CSC3352509 with the physical color lump that generates, and its standard L* value, standard A * value, standard B* value are respectively 55.00,11.45 ,-30.82, the observed value of this physical color lump and aberration Δ E≤3.0 between the standard value.

Embodiment 1:

Take by weighing 17.48 gram PV23 by weight, 1.39 gram PB15:3,0.46 gram PBK7, CSC-B base-material 1000 grams.With above-mentioned raw materials mixing mixing, then with the composition behind the mixing, in envrionment conditions is relative humidity 50% ± 5%, in 23 ± 2 ℃ of the room temperatures, adopts mechanical coating method, evenly entirely be coated on the White Board, the coating wet-film thickness is 250m, places 50 ± 2 ℃ of dry 3～4h of accurate baking oven to constant weight then, takes out, be cooled to room temperature, obtain physical color lump.

Embodiment 2:

Take by weighing 17.32 gram PV23 by weight, 1.46 gram PB15:3,0.46 gram PBK7, CSC-B base-material 1000 grams.Making processes is with embodiment 1.

Embodiment 3:

Take by weighing 17.48 gram PV23 by weight, 1.32 gram PB15:3,0.46 gram PBK7, CSC-B base-material 1005 grams.Making processes is with embodiment 1.

Embodiment 4:

Take by weighing 17.65 gram PV23 by weight, 1.39 gram PB15:3,0.46 gram PBK7, CSC-B base-material 995 grams.Making processes is with embodiment 1.

Physical color lump detected result tabulation with embodiment 1 to 4:

Table 1

Circulation ratio: 0.01	Measure the L value	Measure the A value	Measure the B value	Measure aberration Δ E	Glossiness (85)
						Embodiment 1	??54.65	??10.94	??-30.90	??0.62	??5
Embodiment 2	??55.60	??11.45	??-30.42	??0.72	??5
						Embodiment 3	??55.30	??12.15	??-30.42	??0.86	??5
Embodiment 4	??56.00	??11.55	??-30.32	??1.12	??5

Remarks: in CIE1976 LAB uniform colour space, L represents brightness value; Red/green value that A represents; B represents Huang/indigo plant value; Δ E represents total color difference, is used for the degree of closeness of judgement sample and standard, Δ E=[(L-L*) ²+ (A-A*) ²+ (B-B*) ²] ^1/2Glossiness refers to the gloss intensity with the body surface of data statement.

Detect through DATACOLOR 600 spectrophotometers, in the embodiment of table 1, aberration Δ E≤3.0 between average value measured and the standard value, the Chromatic color that satisfies GB/T 15608-1995 Chinese colour system national Specification are the requirement of sample aberration latitude Δ E≤3.

Composition does not have the disadvantages of filming such as loose colour, layering and flocculation in put procedure, volatile organic compounds in technology making processes (VOC) burst size＜200g/L, free formaldehyde≤0.1g/kg, dissoluble lead≤90mg/kg, soluble cadmium≤75mg/kg, soluble chromium≤60mg/kg, soluble mercury≤60mg/kg, LD50/ per os/mouse:＞7000 milligrams/kilogram.The physical color lump color reproducibility is good.

Other some test performances are as shown in the table:

Table 2

	Composition weathering resistance (GB/T1865-1997)	Composition heat storage stability (GB 6753.3-86)
			Embodiment 1	700h is no abnormal	??ΔE≤0.30
Embodiment 2	700h is no abnormal	??ΔE≤0.30
			Embodiment 3	700h is no abnormal	??ΔE≤0.30
Embodiment 4	700h is no abnormal	??ΔE≤0.30

Can clearly be seen that by last table 2, the composition coating weathering resistance that selected embodiment obtains detects the prescribed value of data fit national standard, and detect by the heat storage stability experiment, colour-change is lower than 0.30, has guaranteed to realize the accuracy and the permanent stability of color in kind.

Claims (4)

1, a kind of composition of 10PB 5.25/9 pigment consists of by weight:

995～1005 parts of CSC-B base-materials;

PV23, pigment content are 30%, 17.32～17.65 parts;

PB15:3, pigment content are 27%, 1.32～1.46 parts;

PBK7, pigment content are 9%, 0.46 part;

Above-mentioned CSC-B base-material main component is an acrylic copolymer, and content is 30～40%, and its average molecular weight range is 15～200,000, median size is 0.1～0.2m, and minimum film-forming temperature is 10～22 ℃, and second-order transition temperature is 25～35 ℃, anionic, pH value are 8.5～10.0; Select TiO for use ₂Content 〉=95%, oil number＜20g/100g, the reducing power Reynolds is several now 1800, and ISO 591 R2 types are as main white pigment, and content is 8～12%; The contrast ratio of this base-material is 0.78～0.82, and stormer viscosity is 90～100KU, and incident angle is 85 o'clock, glossiness 5～10.

2, a kind of physical color lump of 10PB 5.25/9 color is characterized in that: by the raw material and the proportioning preparation of claim 1.

3, the physical color lump of 10PB 5.25/9 color according to claim 2 is characterized in that: incident angle is 85 o'clock, its glossiness 4～6, and aberration Δ E≤3.0 between the standard value.

4, the method for practicality color block of preparation claim 2 or 3 described 10PB 5.25/9 colors comprises the steps:

1) raw material blending: take by weighing raw material by proportioning, mix;

2) coating: in envrionment conditions is relative humidity 50% ± 5%, in 23 ± 2 ℃ of the room temperatures, adopts mechanical coating method, and composition evenly entirely is coated on the White Board, and the coating wet-film thickness is 250m;

3) drying: place 50 ± 2 ℃ of dry 3～4h of accurate baking oven to constant weight composition coating, take out, be cooled to room temperature, obtain physical color lump.