CN101669879B - Method for preparing a series of matching color dental titanium porcelain powders - Google Patents
Method for preparing a series of matching color dental titanium porcelain powders Download PDFInfo
- Publication number
- CN101669879B CN101669879B CN2009100242207A CN200910024220A CN101669879B CN 101669879 B CN101669879 B CN 101669879B CN 2009100242207 A CN2009100242207 A CN 2009100242207A CN 200910024220 A CN200910024220 A CN 200910024220A CN 101669879 B CN101669879 B CN 101669879B
- Authority
- CN
- China
- Prior art keywords
- porcelain
- color
- powder
- porcelain powder
- zirconium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses a method for preparing a series of matching color dental titanium porcelain powders, which comprises the steps of color masking porcelain powder color matching and body porcelain powder color matching, wherein in the color masking porcelain powder color matching, at least three kinds of commercial ceramic pigments, such as vanadium-zirconium yellow, zirconium-praseodymium yellow, iron-zirconium pink and nickel-chromium gray are added by adopting color masking porcelain powder as the quality base number; in the body porcelain powder color matching, at least two kinds of commercial ceramic pigments, such as vanadium-zirconium yellow, zirconium-praseodymium yellow, iron-zirconium pink, iron-chromium yellow and nickel-chromium gray are added by adopting body porcelain powder as the quality base number; the color masking porcelain powder and the body porcelain powder after the pigments are added are respectively ball-milled for 20-30 hours; and after being dried, the ball-milled color masking porcelain powder and the ball-milled body porcelain powder are respectively charged into bottles for porcelain-baking on the surface of a pure-titanium substrate. The color masking porcelain powder and the body porcelain powder are respectively modulated into coloring porcelain powders in 16 colors in four series of A, B, C and D according to the currently general vita porcelain color card standard, and the coloring porcelain powders can be respectively selected according to different colors of natural teeth, thereby achieving the vivid and attractive effect.
Description
Technical field
The present invention relates to the preparation method of biomaterial, be specifically related to a kind of preparation method of dental titanium porcelain powders of the series of matching color that is used to satisfy different patients, different colours demand.
Background technology
Pfm (porcelain-fused-metal, PFM) complete crown has been widely used in clinically, but billon substrate ceramic crown costs an arm and a leg, and is difficult to apply; Nichrome often has genotoxic potentials such as allergy, gingiva black line, bans use of in the world.Compare with it, the biocompatibility excellence of pure titanium, safe in utilization, and also cheap, research titanium ceramic crown is current pressing for, and has the project of bright prospects again.
Domestic literature [practical stomatology magazine, 1996,12 (4): 275-278.] has been developed the special-purpose porcelain powders of titanium material, but its porcelain powders of developing only contains screening color porcelain, two kinds of powder body of body porcelain.Foreign patent (US5176747, US5288232, JP10094550, US5314334) composition and the preparation method of titanium porcelain powders have been introduced, its porcelain powders sintering temperature of developing is lower than 800 ℃, thermal coefficient of expansion and titanio body coupling, but its porcelain powders of developing is the bique powder of single white equally.More than research does not all relate to the configuration of color.Application number is the manufacture method that 200410015585.0 Chinese patent has been introduced the leucite ceramic material that is applicable to noble metal and nichrome, and prepared porcelain powders has been carried out series of matching color.
Abroad constitute by bonding porcelain, screening color porcelain and body porcelain about the titanium porcelain powders that company produced at present, and considered the color of different patient's teeth, mainly represent as VITATITANKERAMIK (VITA company, Germany), TiBond (Dentsply company, the U.S.), Surper porcerain (NORITAKE company, Japan), but the not announcement of relevant production technology, and have the problem that collapses porcelain, light discolouration after the clinical use.
Summary of the invention
When the present invention installs titanium porcelain corona for satisfying different odontopathy patients,, provide a kind of preparation method of dental titanium porcelain powders of series of matching color to the different demands of color.This method hides color porcelain, body porcelain porcelain powder by the fusion preparation, adding different colorants respectively in hiding color porcelain, body porcelain porcelain powder matches colors, make the screening color porcelain pigment and the body porcelain pigment of A, B, 16 color codes of four series of C, D according to present general ceramic prosthesis colour atla standard, the patient can select for use according to the creamy white of self, makes the porcelain corona true to nature, attractive in appearance.
For reaching above purpose, the present invention takes following technical scheme to be achieved:
A kind of preparation method of dental titanium porcelain powders of series of matching color, it is characterized in that, comprise and hide color matching of color porcelain powder and the color matching of body porcelain powder, the color matching of described screening color porcelain powder is to be the quality radix to hide color porcelain powder, add commercial ceramic pigment vanadium zirconium Huang, praseodymium zirconium Huang, ferrozirconium is red and nickel chromium triangle is grey at least three kinds, wherein the percentage composition of each component adding is: the yellow 0-10% of vanadium zirconium, the yellow 0-4% of praseodymium zirconium, the red 0.05-1% of ferrozirconium, nickel chromium triangle ash 0.1-1.5%;
Described body porcelain powder color matching, be to be the quality radix with body porcelain powder, add commercial ceramic pigment vanadium zirconium Huang, praseodymium zirconium Huang, ferrozirconium is red, siderochrome is yellow and nickel chromium triangle is grey at least two kinds, wherein the percentage composition of each component adding is: the yellow 0-1% of vanadium zirconium,, the yellow 0-1.5% of praseodymium zirconium, the red 0-0.5% of ferrozirconium, the yellow 0-0.5% of siderochrome, nickel chromium triangle ash 0-0.2%;
Screening color porcelain powder behind the adding colorant and body porcelain powder difference ball milling 20~30 hours; Bottling respectively after screening color porcelain porcelain powder behind the ball milling and body porcelain porcelain dried bean noodles are dry is in order at pure titanio basal surface porcelain.
In the such scheme, the preparation method of described screening color porcelain powder comprises the steps:
(1) by mass percentage, with the SiO of following component: 50-60%
2, 3-10% Al
2O
3, the CaO of 0.5-1%, the SnO of 20-30%
2, 0.5-1% TiO
2, 0.5-1% ZrO
2, 7-10% Na
2The K of O, 5-8%
2The BaO batching of O and 0.5-4%, mixing and ball milling 10-20 hour; Component S nO wherein
2Separately and exclusively shelve and do not participate in mixing and ball milling;
(2) compound behind the ball milling is packed in the crucible,, be incubated 2~4 hours, pour the vitreous humour after the fusion in water quenching in 1400~1500 ℃ of fusions;
(3) with the quenching solid wet ball grinding after the shrend 24~40 hours; Must hide the middle powder body of color porcelain after the drying;
(4) in the middle of hiding the color porcelain, add the SnO that has neither part nor lot in mixing and ball milling that step (1) is separately and exclusively shelved in the powder body
2Component, mixing and ball milling 20~30 hours;
(5) powder after step (4) mixing and ball milling is packed in the crucible, in 800~900 ℃ synthetic, be incubated 2~3 hours, furnace cooling;
(6) with synthesis material wet ball grinding 24~40 hours, must hide color porcelain powder after the drying.
Described body porcelain powder comprises the SiO of following component: 60-70% by mass percentage
2, 4-10% Al
2O
3, the CaO of 0.5-1%, the B of 1-5%
2O
3, 5-10% Na
2The K of O, 5-10%
2The Li of O, 0.5-1%
2The BaO of O and 5-8%.
The present invention respectively modulates the coloring ceramic powder of A, B, 16 color codes of four series of C, D hiding color porcelain powder and body porcelain powder according to general vita porcelain colour atla standard at present, can select for use respectively according to the different color and lusters of natural tooth, and color and luster is true to nature attractive in appearance.In the painted porcelain of synthetic A, B, 16 color codes of four series of C, D,, can satisfy clinical instructions for use with presenting from shallow to deep graded with the saturation different colours in a series of.Reflectance spectrum the analysis showed that, adopts the reflectance spectrum curve and the general porcelain basically identical of the painted porcelain powders that color matching method of the present invention obtains.In addition, the present invention hides color porcelain powder and adopts middle material technology adding crystal to carry out the secondary synthesis technique mutually, has both regulated the ceramic material thermal coefficient of expansion, helps reducing the porcelain temperature again, helps improving titanium/porcelain bond strength simultaneously.
The specific embodiment
Hide the preparation method of color porcelain powder:
(1) presses table 1 and hide the weighing of color porcelain powder recipe calculation, must hide color porcelain batching and be designated as screening 1, respectively mixing and ball milling t to hiding 6
0Hour; Component S nO wherein
2Separately and exclusively shelve and do not participate in mixing and ball milling; B component wherein
2O
3Introduce component Na with boric acid
2O, K
2O, Li
2O, BaO introduce with corresponding carbonate, and component F introduces with corresponding fluoride.
(2) compound behind each ball milling is packed in the crucible, in T
1℃ fusion, insulation t
1Hour, pour the vitreous humour after the fusion in water quenching.
(3) with the quenching solid wet ball grinding t after the shrend
2Hour; Must hide the middle powder body of color porcelain after the drying.
(4) in the middle of hiding the color porcelain, add the SnO that has neither part nor lot in mixing and ball milling that step (1) is separately and exclusively shelved in the powder body
2Component, mixing and ball milling t
3Hour.
(5) powder after step (4) mixing and ball milling is packed in the crucible, in T
2℃ synthetic, insulation t
4Hour, furnace cooling.
(6) with synthesis material wet ball grinding t
5Hour, must hide color porcelain powder after the drying.
Hide color porcelain powder preparation technique parameter and see Table 2.
Table 1 hides color porcelain powder prescription
Table 2 hides color porcelain powder preparation technique parameter
Numbering | ?t 0/ hour | T 1/℃ | t 1/ hour | t 2/ hour | t 3/ hour | T 2/℃ | ?t 4/ hour | t 5Hour |
Hide 1 | ?10 | 1400 | 4 | 24 | 30 | 900 | ?3 | 24 |
Hide 2 | ?12 | 1450 | 3 | 28 | 28 | 800 | ?3 | 40 |
Hide 3 | ?14 | 1500 | 2 | 32 | 30 | 800 | ?2 | 30 |
Hide 4 | ?16 | 1400 | 4 | 26 | 26 | 900 | ?3 | 36 |
Hide 5 | ?18 | 1450 | 3 | 30 | 20 | 850 | ?3 | 28 |
Hide 6 | ?20 | 1500 | 2 | 24 | 24 | 850 | ?2 | 40 |
By mass percentage, the prescription of the body porcelain powder of the present invention body 1 to 4 four embodiment of body that prepared altogether as shown in table 3.Body porcelain powder can adopt traditional fusion method once synthetic.
Table 3 body porcelain powder prescription
Table 4 hides color porcelain powder series of matching color prescription
Add screening color porcelain powder behind the colorant and use the ball grinder and the abrasive body of Achates medium, ball milling did not wait (table 4) in 20~30 hours respectively, and the dry back bottling of the screening color porcelain dried bean noodles behind the ball milling is prepared against at pure titanio basal surface porcelain.The color code that obtains behind the corresponding screening color porcelain powder porcelain uses spectrophotometric color measurement instrument to measure according to general vita porcelain colour atla standard respectively as shown in Table, and value of chromatism<1.0UBS meets the requirement of color matching to aberration.
The color matching of body porcelain powder, the commercial ceramic pigment mass fraction of adding is as shown in table 5 in 100 parts of body porcelain powder.
Table 5 body porcelain powder series of matching color prescription
Add body porcelain powder behind the colorant and use the ball grinder and the abrasive body of Achates medium, ball milling did not wait (table 5) in 20~30 hours respectively, and the dry back bottling of the body porcelain dried bean noodles behind the ball milling is prepared against at pure titanio basal surface porcelain.The color code that obtains behind the corresponding body porcelain powder porcelain uses spectrophotometric color measurement instrument to measure according to general vita porcelain colour atla standard respectively as shown in Table, and value of chromatism<1.0UBS meets the requirement of color matching to aberration.
Claims (1)
1. the preparation method of the dental titanium porcelain powders of a series of matching color, it is characterized in that, comprise and hide color matching of color porcelain powder and the color matching of body porcelain powder, the color matching of described screening color porcelain powder is to be the quality radix to hide color porcelain powder, add commercial ceramic pigment vanadium zirconium Huang, praseodymium zirconium Huang, ferrozirconium is red and nickel chromium triangle is grey at least three kinds, wherein the percentage composition of each component adding is: the yellow 0-10% of vanadium zirconium, the yellow 0-4% of praseodymium zirconium, the red 0.05-1% of ferrozirconium, nickel chromium triangle ash 0.1-1.5%;
Described body porcelain powder color matching, be to be the quality radix with body porcelain powder, add commercial ceramic pigment vanadium zirconium Huang, praseodymium zirconium Huang, ferrozirconium is red, siderochrome is yellow and nickel chromium triangle is grey at least two kinds, wherein the percentage composition of each component adding is: the yellow 0-1% of vanadium zirconium, the yellow 0-1.5% of praseodymium zirconium, the red 0-0.5% of ferrozirconium, the yellow 0-0.5 of siderochrome, nickel chromium triangle ash 0-0.2%;
Screening color porcelain powder behind the adding colorant and body porcelain powder difference ball milling 20~30 hours; Bottling respectively after screening color porcelain porcelain powder behind the ball milling and body porcelain porcelain dried bean noodles are dry is in order at pure titanio basal surface porcelain;
The preparation method of described screening color porcelain powder comprises the steps:
(1) by mass percentage, with the SiO of following component: 50-60%
2, 3-10% Al
2O
3, the CaO of 0.5-1%, the SnO of 20-30%
2, 0.5-1% TiO
2, 0.5-1% ZrO
2, 7-10% Na
2The K of O, 5-8%
2The BaO batching of O and 0.5-4%, mixing and ball milling 10~20 hours; Component S nO wherein
2Separately and exclusively shelve and do not participate in mixing and ball milling, component Na
2O, K
2O, BaO introduce with corresponding carbonate;
(2) compound behind the ball milling is packed in the crucible,, be incubated 2~4 hours, pour the vitreous humour after the fusion in water quenching in 1400~1500 ℃ of fusions;
(3) with the quenching solid wet ball grinding after the shrend 24~40 hours; Must hide the middle powder body of color porcelain after the drying;
(4) in the middle of hiding the color porcelain, add the SnO that has neither part nor lot in mixing and ball milling that step (1) is separately and exclusively shelved in the powder body
2Component, mixing and ball milling 20~30 hours;
(5) powder after step (4) mixing and ball milling is packed in the crucible, in 800~900 ℃ synthetic, be incubated 2~3 hours, furnace cooling;
(6) with synthesis material wet ball grinding 24~40 hours, must hide color porcelain powder after the drying;
Described body porcelain powder is made of following component: the SiO of 60-70% by mass percentage
2, 4-10% Al
2O
3, the CaO of 0.5-1%, the B of 1-5%
2O
3, 5-10% Na
2The K of O, 5-10%
2The Li of O, 0.5-1%
2The BaO of O and 5-8%.