CN101665617A - Hydroxyl resin composition and solvent-free polyurethane putty containing same - Google Patents
Hydroxyl resin composition and solvent-free polyurethane putty containing same Download PDFInfo
- Publication number
- CN101665617A CN101665617A CN200910075548A CN200910075548A CN101665617A CN 101665617 A CN101665617 A CN 101665617A CN 200910075548 A CN200910075548 A CN 200910075548A CN 200910075548 A CN200910075548 A CN 200910075548A CN 101665617 A CN101665617 A CN 101665617A
- Authority
- CN
- China
- Prior art keywords
- component
- solvent
- resin composition
- agent
- formula
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a hydroxyl resin composition and a solvent-free polyurethane putty containing the same. The resin composition is prepared by mixing resins that have two molecular structures.The prepared solvent-free polyurethane putty consists of a component A and a component B, wherein the compositing ratio of the component A and the component B is 5-6:1; the component B is a curing agent; and the component A consists of an assistant and 30-40 parts by weight of the hydroxyl resin composition. The solvent-free polyurethane putty has properties of excellent adhesion and self polymerization; the drawing intensity of the dried putty reaches 4.0Mpa above which meets the requirement of a fan blade. The impact resistance of the solvent-free polyurethane putty reaches 50kg, and the flexibility reaches 10mm. The putty is resistant to temperature change in a range from -40 DEG C to 40 DEG C.
Description
Technical field
The solvent-free polyurethane putty that the present invention relates to a kind of hydroxy resin composition and contain this hydroxy resin composition.
Background technology
Along with the deterioration of world energy sources situation, wind-power electricity generation is developed rapidly as green energy resource.Wind-powered electricity generation is mainly caught wind energy and then is driven generator for electricity generation by fan blade.This facility need be installed in air port, plateau, mountain area part, and temperature variation is very big throughout the year, and has dust storm to impact, expose to the sun and rain, and is very high to the substrate surface performance requriements.Because fan blade adopts fiber glass epoxy to do base material more, and the weathering resistance of fiber glass epoxy is bad, need be coated with high performance paint outside the surface, again because the inevitable defective in manufacturing processed surface needs high performance putty to fill up defective again.This putty requires to have stronger bonding force, force of cohesion, and this just requires cross-linking density to want big and has quite high shock-resistance and snappiness, and physicals can not be burst apart in shrinkage strain under cold condition.
At present in the industry comparative maturity be atomic lime putty, solvent borne polyurethane putty and epoxy ester putty etc., fast drying, grinability are good, the advantage of strong adhesion though have, but snappiness variation and shrinkability are big at low temperatures, and bonding force, force of cohesion deficiency are not suitable for fan blade and use.
Summary of the invention
Technical problem to be solved by this invention is the defective that overcomes prior art, the solvent-free polyurethane putty that a kind of hydroxy resin composition is provided and contains this hydroxy resin composition.
Hydroxy resin composition of the present invention is the resin by formula (I) structure:
Form with the mixed with resin of formula (II) structure,
n=1、2、3、4……8;
(II)
The consumption mass ratio of the resin of the resin of described formula (I) structure and formula (II) structure is 1: 4~6.
The resin of described formula (I) structure makes by following approach,
The resin of described formula (II) structure makes by following approach,
n=1、2、3、4……8。
A kind of solvent-free polyurethane putty is made up of component A and B component, and the composition proportioning of described component A and B component is 5~6: 1; Described B component is a solidifying agent, and described component A is made up of the hydroxy resin composition of auxiliary agent and 30~40 mass parts; Described auxiliary agent is counted by mass parts:
Titanium dioxide 3~5; Organobentonite 1~2; White carbon black 1~2; Dispersion agent 1~2; Defoamer 2~3;
Flow agent 1~2; Talcum powder 40~50;
Described dispersion agent is selected from BYK-163 or BYK-161; Described defoamer is selected from BYK-141 or BYK-070; Described flow agent is selected from BYK-302 or BYK-331.
Solvent-free polyurethane putty of the present invention, described B component be by MDI solidifying agent and HDI solidifying agent with 16~19: the mixture that 4~1 usage ratio is formed;
Described MDI solidifying agent is the mixture of material with different polymerization degree of following molecular structure:
Wherein, n is the polymerization degree, and value is 0,1,2,3 or 4;
Described HDI solidifying agent has OCN-[CH
2]
6-NCO structural formula.
Above-mentioned solvent-free polyurethane putty, the composition proportioning of described component A and described B component is 5~6: 1.
A kind of method for preparing above-mentioned solvent-free polyurethane putty, it may further comprise the steps:
A. roll 1~2 time after stirring in hydroxy resin composition and the unclassified stores adding jar, being uniformly dispersed is component A;
B. with MDI solidifying agent and HDI solidifying agent with 16~19: 4~1 usage ratio mixes and is B component;
C. get component A and B component and mix at 5~6: 1 in proportion, be solvent-free polyurethane putty.
For research and development sticking power, autohemagglutination power are strong, shock-resistant and snappiness good, the putty of excellent performance under the low temperature, the contriver has selected multiple hydroxy polyethers to make putty, flexibility, the good but pull-out strength deficiency of shock resistance; Synthesize multiple polyester polyol with the acid of polyvalent alcohol polyprotonic acid fat, found the snappiness good impact resistance but the pull-out strength deficiency, good but the product that snappiness and shock resistance are poor slightly of pull-out strength found simultaneously.Utilize interpenetrating(polymer)networks theoretical invention people independent research a kind of molecular weight moderate, the hydroxy resin composition that hydroxy radical content is suitable.The putty and the epoxy glass laminate ground that are made by component A that contains this hydroxy resin composition and B component have extremely strong sticking power, autohemagglutination power, after the putty drying, pull-out strength can reach more than the 4.0Mpa, reach the requirement of fan blade fully, its shock-resistant 50kg.cm that reaches, snappiness can reach 10mm, and can anti--40~40 ℃ temperature variation.
Embodiment
Below in conjunction with specific embodiment the present invention is described in further detail.
Preparation hydroxy resin composition
The preparation of the resin of formula (I) structure:
The preparation of the resin of formula (II) structure:
n=1、2、3、4……8
With the resin of the resin of formula (I) structure and formula (II) structure, mix according to 1: 4~6 usage ratio, hydroxy resin composition of the present invention, standby.
Embodiment 1
A. get and roll 1~2 time after stirring in the adding jar according to 1: 4 usage ratio blended mixture 30g and titanium dioxide 3g, organobentonite 1g, white carbon black 1g, dispersion agent 1g, defoamer 2g, flow agent 1g, talcum powder 40g of resin of the resin of above-mentioned formula (I) structure and formula (II) structure, being uniformly dispersed is component A;
B. MDI solidifying agent 16g and HDI solidifying agent 4g are mixed and be B component;
C. get component A and B component and mix at 5: 1 in proportion, be solvent-free polyurethane putty.
Described dispersion agent is selected from BYK-163 or the BYK-161 that German Bi Ke company produces; Described defoamer and flow agent also are selected from the series product that German Bi Ke company produces.
Embodiment 2
A. get and roll 1~2 time after stirring in the adding jar according to 1: 6 usage ratio blended mixture 40g and titanium dioxide 5g, organobentonite 2g, white carbon black 2g, dispersion agent 2g, defoamer 3g, flow agent 2g, talcum powder 50g of resin of the resin of above-mentioned formula (I) structure and formula (II) structure, being uniformly dispersed is component A;
B. MDI solidifying agent 19g and HDI solidifying agent 1g are mixed and be B component;
C. get component A and B component and mix at 6: 1 in proportion, be solvent-free polyurethane putty.
Embodiment 3
A. get and roll 1~2 time after stirring in the adding jar according to 1: 5 usage ratio blended mixture 35g and titanium dioxide 4g, organobentonite 1.5g, white carbon black 1.5g, dispersion agent 1.5g, defoamer 2.5g, flow agent 1.5g, talcum powder 45g of resin of the resin of above-mentioned formula (I) structure and formula (II) structure, being uniformly dispersed is component A;
B. MDI solidifying agent 17g and HDI solidifying agent 3g are mixed and be B component;
C. get component A and B component and mix at 5.5: 1 in proportion, be solvent-free polyurethane putty.
Embodiment 4
A. get and roll 1~2 time after stirring in the adding jar according to 1: 4 usage ratio blended mixture 30g and titanium dioxide 5g, organobentonite 1.5g, white carbon black 1.5g, dispersion agent 1.5g, defoamer 2.5g, flow agent 1.5g, talcum powder 45g of resin of the resin of above-mentioned formula (I) structure and formula (II) structure, being uniformly dispersed is component A;
B. MDI solidifying agent 18g and HDI solidifying agent 2g are mixed and be B component;
C. get component A and B component and mix at 6: 1 in proportion, be solvent-free polyurethane putty.
Embodiment 5
A. get and roll 1~2 time after stirring in the adding jar according to 1: 6 usage ratio blended mixture 300g and titanium dioxide 50g, organobentonite 15g, white carbon black 15g, dispersion agent 15g, defoamer 25g, flow agent 15g, talcum powder 450g of resin of the resin of above-mentioned formula (I) structure and formula (II) structure, being uniformly dispersed is component A;
B. MDI solidifying agent 80g and HDI solidifying agent 20g are mixed and be B component;
C. get component A and B component and mix at 5: 1 in proportion, be solvent-free polyurethane putty.
Embodiment 6
A. get and roll 1~2 time after stirring in the adding jar according to 1: 5 usage ratio blended mixture 400g and titanium dioxide 50g, organobentonite 20g, white carbon black 20g, dispersion agent 20g, defoamer 30g, flow agent 20g, talcum powder 500g of resin of the resin of above-mentioned formula (I) structure and formula (II) structure, being uniformly dispersed is component A;
B. MDI solidifying agent 95g and HDI solidifying agent 5g are mixed and be B component;
C. get component A and B component and mix at 6: 1 in proportion, be solvent-free polyurethane putty.
Claims (6)
4, a kind of solvent-free polyurethane putty is made up of component A and B component, it is characterized in that, the composition proportioning of described component A and B component is 5~6: 1; Described B component is a solidifying agent, and described component A is made up of the hydroxy resin composition of auxiliary agent and 30~40 mass parts; Described auxiliary agent is counted by mass parts:
Titanium dioxide 3~5; Organobentonite 1~2; White carbon black 1~2; Dispersion agent 1~2; Defoamer 2~3;
Flow agent 1~2; Talcum powder 40~50;
Described dispersion agent is selected from BYK-163 or BYK-161; Described defoamer is selected from BYK-141 or BYK-070; Described flow agent is selected from BYK-302 or BYK-331.
5, solvent-free polyurethane putty according to claim 4 is characterized in that, described B component be by MDI solidifying agent and HDI solidifying agent with 16~19: the mixture that 4~1 mass parts ratio is formed;
Wherein, the MDI solidifying agent is the mixture of material with different polymerization degree of following molecular structure:
Wherein, n is the polymerization degree, and value is 0,1,2,3 or 4;
Described HDI solidifying agent has OCN-[CH
2]
6-NCO structural formula.
6, a kind of preparation is characterized in that as the method for solvent-free polyurethane putty as described in claim 4 or 5 it carries out according to the following steps:
A. roll 1~2 time after stirring in hydroxy resin composition and the auxiliary agent adding jar, being uniformly dispersed is component A;
B. with MDI solidifying agent and HDI solidifying agent with 16~19: 4~1 mixed evenly is a B component;
C. get component A and B component and mix in proportion, be solvent-free polyurethane putty.