CN101660277A - Novel PU printing waterproof and anti-crease fabric and preparation method thereof - Google Patents
Novel PU printing waterproof and anti-crease fabric and preparation method thereof Download PDFInfo
- Publication number
- CN101660277A CN101660277A CN200910034962A CN200910034962A CN101660277A CN 101660277 A CN101660277 A CN 101660277A CN 200910034962 A CN200910034962 A CN 200910034962A CN 200910034962 A CN200910034962 A CN 200910034962A CN 101660277 A CN101660277 A CN 101660277A
- Authority
- CN
- China
- Prior art keywords
- disperse dyes
- fabric
- printing
- leather
- wrinkle resistant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a novel PU printing waterproof and anti-crease new fabric, which comprises three layers: the first layer is PU surface layer mainly comprising PU polyurethane; the second layeris printing dyes; the third layer is a PU surface layer mainly comprising PU polyurethane. The printing dyes in the second layer are ink disperse dyes made of disperse dyes and water-soluble carrier,or ink disperse dyes made of the disperse dyes and alcohol-soluble carrier, or ink disperse dyes made of the disperse dyes and oil-soluble resin. The invention also discloses a method for preparing the novel PU printing waterproof and anti-crease fabric, comprising the following steps: firstly, preparing a shell fabric and a backing material; secondly, carrying out coating operation; thirdly, performing the backing lamination; fourthly, drying, rolling and stripping; fifthly, thermally transferring a printing film to base leather; and sixthly, performing the secondary coating on the printingbase leather. The novel PU printing waterproof, anti-crease fabric has advantages of terrific tensile strength and hydrostatic pressure, and is durable in use, fastness to washing, colorfast; and thepreparation method is easy to operate.
Description
Technical field
The invention belongs to PU printing technique field, particularly a kind of PU printing waterproof, wrinkle resistant novel fabric and preparation method thereof.
Background technology
PU (polyurethanes is called for short polyurethane) leather is a kind of lining that always is loved by the people in recent years.Along with the raising of people's living standard, under the abundant day by day situation of material life, people require the fashion of PU leather facing material and pursue also to the class of PU leather goods that Yu adds outstanding.It is perfect not only to require at aspects such as color, quality, also at aspects such as energy-saving and environmental protection higher requirement has been arranged also, and modern trend that Here it is combines with reality.So market is also increasing to the demand of PU leather stamp product.
The stamp mode adopts the special look stamp mode of several rollers of several color systems at present, because printing machine can be printed 16 chromatographys at most at present at home, limitation to the flower type is bigger, for the multi-level pattern of polychrome, just can not fully show the style of original copy as landscape, personage, animal, traditional Chinese Painting, oil painting etc., lack third dimension, stereovision.
Summary of the invention
The object of the present invention is to provide a kind of environmental protection, lifelike image, one-time formed PU printing waterproof, wrinkle resistant novel fabric and preparation method thereof.
The technical solution that realizes the object of the invention is: a kind of PU printing waterproof, wrinkle resistant novel fabric comprise three layers: ground floor is the PU surface layer, and main component is a PU polyurethane; The second layer is a thickening agent; The 3rd layer is the PU surface layer, and composition is a PU polyurethane.The thickening agent of the second layer is the distributes ink dyestuff that DISPERSE DYES and water-solubility carrier are made, or the distributes ink dyestuff made of DISPERSE DYES and pure solubleness carrier, or the distributes ink dyestuff made of DISPERSE DYES and oil-soluble resin.DISPERSE DYES is molecular weight 250-400, the DISPERSE DYES of particle diameter 0.2-2 micron.
A kind of method of making PU printing waterproof, wrinkle resistant novel fabric may further comprise the steps:
Step 1: lining and bed material are prepared, afterwards the slurry that configures is left standstill froth breaking, filtration;
Step 2: bottom is coated with operation: the slurry that will leave standstill is added on the release liners, dries afterwards;
Step 3: base fabric is fitted, and is specially: knitted cloth is covered on the bed material after step 2 oven dry is handled, add the gas roller afterwards on base fabric;
Step 4: the bed material that is coated with knitted cloth in the step 3 is dried once more;
Step 5: clot is peeled off, and is specially: release liners is separated clot respectively with the PU leather;
Step 6: printed film heat is transferred on the base leather by printing machine;
Step 7: stamp base leather is carried out secondary coating, the slurry that leaves standstill in the step 1 is added on the release liners;
Step 8: bed material is dried;
Step 9: base fabric is fitted, and is specially: the finished product after printed the spending is removed from office on the bed material that covers after step 8 oven dry is handled, add the gas roller afterwards on base fabric;
Step 10: the bed material that is coated with the finished product leather in the step 9 is dried once more;
Step 11: clot is peeled off; Release liners is separated with the PU leather, and PU printing waterproof, wrinkle resistant novel fabric are made in clot respectively.
The present invention compared with prior art, its remarkable advantage is: 1) the present invention puts into vavuum pump with the slurry that configures and is evacuated down to 0 atmospheric pressure 2 hours, effectively eliminate the tension of pulp surface, when coating, reduced base leather depression in the surface phenomenon, the leather good hand feeling that makes, smooth; 2) product lining of the present invention has and good tensile strength and water pressure resistance, and product is durable in use, and water-fast washing is colour-fast; 3) lining is wrinkle resistant, toughness is strong, does not ftracture, and does not influence the lines on leather surface after the transfer printing, and can provide transfer coated senior metal light sensation for the clothing leather; 4) main component of lining is the PU resin, and nontoxic, tasteless, environmental protection have no side effect to human body; 5) the colored type of lining accurately, levels are rich and clear, artistry is high, third dimension is strong, good visual effect.
Below in conjunction with accompanying drawing the present invention is described in further detail.
Description of drawings
Accompanying drawing is PU printing waterproof of the present invention, wrinkle resistant novel fabric manufacture method flow chart.
The specific embodiment
A kind of PU printing waterproof of the present invention, wrinkle resistant novel fabric comprise three layers: ground floor is the PU surface layer, and main component is a PU polyurethane; The second layer is a thickening agent; The 3rd layer is the PU surface layer, and composition is a PU polyurethane.The thickening agent of the second layer is the distributes ink dyestuff that DISPERSE DYES and water-solubility carrier are made, or the distributes ink dyestuff made of DISPERSE DYES and pure solubleness carrier, or the distributes ink dyestuff made of DISPERSE DYES and oil-soluble resin.Described DISPERSE DYES is molecular weight 250-400, the DISPERSE DYES of particle diameter 0.2-2 micron.
In conjunction with the accompanying drawings, a kind of method of making PU printing waterproof, wrinkle resistant novel fabric of the present invention may further comprise the steps:
Step 1: lining and bed material are prepared, afterwards the slurry that configures is left standstill froth breaking, filtration; The PU slurry of being prepared comprises 100 parts of the resins of 50 modulus, 10 parts of dimethyl formyl ammoniums, and 10 parts of butanone, 60～90 parts of toluene, the concentration of preparation is 3000cps;
Step 2: bottom is coated with operation: the slurry that will leave standstill is added on the release liners, and the thickness between cylinder and the release liners is 18, dries afterwards, and the temperature of oven dry is 65 degree, and drying time is 20s;
Step 3: base fabric is fitted, and is specially: knitted cloth is covered on the bed material after step 2 oven dry is handled, add 4KG gas roller afterwards on base fabric;
Step 4: the bed material that is coated with knitted cloth in the step 3 is dried once more, and the temperature of oven dry is 100～135 degree, and drying time is 50s～70s;
Step 5: clot is peeled off, and is specially: release liners is separated clot respectively with the PU leather;
Step 6: printed film heat is transferred on the base leather by printing machine; Printed film is that thickening agent forms, and this thickening agent is the distributes ink dyestuff that DISPERSE DYES and water-solubility carrier are made, or the distributes ink dyestuff made of DISPERSE DYES and pure solubleness carrier, or the distributes ink dyestuff made of DISPERSE DYES and oil-soluble resin; DISPERSE DYES is molecular weight 250--400, the DISPERSE DYES of particle diameter 0.2-2 micron; The transition temperature that printed film heat is transferred on the base leather is 110--120 ℃;
Step 7: stamp base leather is carried out secondary coating, the slurry that leaves standstill in the step 1 is added on the release liners, the thickness between cylinder and the release liners is 18;
Step 8: bed material is dried, and the temperature of oven dry is that temperature is 65 degree, and drying time is 20s;
Step 9: base fabric is fitted, and is specially: the finished product after printed the spending is removed from office on the bed material that covers after step 8 oven dry is handled, add 4KG gas roller afterwards on base fabric;
Step 10: the bed material that is coated with the finished product leather in the step 9 is dried once more, and the temperature of oven dry is 100～135 degree, and drying time is 50s～70s;
Step 11: clot is peeled off; Release liners is separated with the PU leather, and PU printing waterproof, wrinkle resistant novel fabric are made in clot respectively.
Below in conjunction with embodiment the present invention is done further detailed description:
Embodiment 1:
The method of making PU printing waterproof, wrinkle resistant novel fabric may further comprise the steps:
(1) lining and bed material are prepared, the PU slurry of preparation comprises 100 parts of the resins of 50 modulus, 10 parts of dimethyl formyl ammoniums, and 10 parts of butanone, 60 parts of toluene, the concentration of preparation is 3000cps;
(2) slurry that configures is left standstill froth breaking, filtration; Then the slurry that will leave standstill is added on the release liners, and the thickness between cylinder and the release liners is 18, dries afterwards, and the temperature of oven dry is 65 degree, and drying time is 20s;
(3) knitted cloth is covered on the bed material after step 2 oven dry is handled, on base fabric, add 4KG gas roller afterwards;
(4) bed material that is coated with knitted cloth is dried once more, the temperature of oven dry is 100 degree, and drying time is 50s;
(5) release liners is separated clot respectively with the PU leather;
(6) by printing machine printed film heat is transferred on the base leather; Printed film is that thickening agent forms, and this thickening agent is the distributes ink dyestuff that DISPERSE DYES and water-solubility carrier are made, or the distributes ink dyestuff made of DISPERSE DYES and pure solubleness carrier, or the distributes ink dyestuff made of DISPERSE DYES and oil-soluble resin; DISPERSE DYES is molecular weight 250--400, the DISPERSE DYES of particle diameter 0.2-2 micron; The transition temperature that printed film heat is transferred on the base leather is 110 ℃;
(7) stamp base leather is carried out secondary coating, the slurry that leaves standstill is added on the release liners, the thickness between cylinder and the release liners is 18;
(8) bed material is dried, the temperature of oven dry is that temperature is 65 degree, and drying time is 20s;
(9) base fabric is fitted, and is specially: the leather of the finished product after printed the spending is covered on the bed material, add 4KG gas roller afterwards on base fabric;
(10) bed material that is coated with the finished product leather in the step 9 is dried once more, the temperature of oven dry is 100 degree, and drying time is 50s;
(11) clot is peeled off; Release liners is separated with the PU leather, and PU printing waterproof, wrinkle resistant novel fabric are made in clot respectively.
Embodiment 2:
The method of making PU printing waterproof, wrinkle resistant novel fabric may further comprise the steps:
(1) lining and bed material are prepared, the PU slurry of preparation comprises 100 parts of the resins of 50 modulus, 10 parts of dimethyl formyl ammoniums, and 10 parts of butanone, 70 parts of toluene, the concentration of preparation is 3000cps;
(2) slurry that configures is left standstill froth breaking, filtration; Then the slurry that will leave standstill is added on the release liners, and the thickness between cylinder and the release liners is 18, dries afterwards, and the temperature of oven dry is 65 degree, and drying time is 20s;
(3) knitted cloth is covered on the bed material after step 2 oven dry is handled, on base fabric, add 4KG gas roller afterwards;
(4) bed material that is coated with knitted cloth is dried once more, the temperature of oven dry is 110 degree, and drying time is 60s;
(5) release liners is separated clot respectively with the PU leather;
(6) by printing machine printed film heat is transferred on the base leather; Printed film is that thickening agent forms, and this thickening agent is the distributes ink dyestuff that DISPERSE DYES and water-solubility carrier are made, or the distributes ink dyestuff made of DISPERSE DYES and pure solubleness carrier, or the distributes ink dyestuff made of DISPERSE DYES and oil-soluble resin; DISPERSE DYES is molecular weight 250--400, the DISPERSE DYES of particle diameter 0.2-2 micron; The transition temperature that printed film heat is transferred on the base leather is 115 ℃;
(7) stamp base leather is carried out secondary coating, the slurry that leaves standstill is added on the release liners, the thickness between cylinder and the release liners is 18;
(8) bed material is dried, the temperature of oven dry is that temperature is 65 degree, and drying time is 20s;
(9) base fabric is fitted, and is specially: the leather of the finished product after printed the spending is covered on the bed material, add 4KG gas roller afterwards on base fabric;
(10) bed material that is coated with the finished product leather in the step 9 is dried once more, the temperature of oven dry is 110 degree, and drying time is 60s;
(11) clot is peeled off; Release liners is separated with the PU leather, and PU printing waterproof, wrinkle resistant novel fabric are made in clot respectively.
Embodiment 3:
The method of making PU printing waterproof, wrinkle resistant novel fabric may further comprise the steps:
(1) lining and bed material are prepared, the PU slurry of preparation comprises 100 parts of the resins of 50 modulus, 10 parts of dimethyl formyl ammoniums, and 10 parts of butanone, 90 parts of toluene, the concentration of preparation is 3000cps;
(2) slurry that configures is left standstill froth breaking, filtration; Then the slurry that will leave standstill is added on the release liners, and the thickness between cylinder and the release liners is 18, dries afterwards, and the temperature of oven dry is 65 degree, and drying time is 20s;
(3) knitted cloth is covered on the bed material after step 2 oven dry is handled, on base fabric, add 4KG gas roller afterwards;
(4) bed material that is coated with knitted cloth is dried once more, the temperature of oven dry is 135 degree, and drying time is 70s;
(5) release liners is separated clot respectively with the PU leather;
(6) by printing machine printed film heat is transferred on the base leather; Printed film is that thickening agent forms, and this thickening agent is the distributes ink dyestuff that DISPERSE DYES and water-solubility carrier are made, or the distributes ink dyestuff made of DISPERSE DYES and pure solubleness carrier, or the distributes ink dyestuff made of DISPERSE DYES and oil-soluble resin; DISPERSE DYES is molecular weight 250--400, the DISPERSE DYES of particle diameter 0.2-2 micron; The transition temperature that printed film heat is transferred on the base leather is 120 ℃;
(7) stamp base leather is carried out secondary coating, the slurry that leaves standstill is added on the release liners, the thickness between cylinder and the release liners is 18;
(8) bed material is dried, the temperature of oven dry is that temperature is 65 degree, and drying time is 20s;
(9) base fabric is fitted, and is specially: the leather of the finished product after printed the spending is covered on the bed material, add 4KG gas roller afterwards on base fabric;
(10) bed material that is coated with the finished product leather in the step 9 is dried once more, the temperature of oven dry is 135 degree, and drying time is 70s;
(11) clot is peeled off; Release liners is separated with the PU leather, and PU printing waterproof, wrinkle resistant novel fabric are made in clot respectively.
Claims (10)
1, a kind of PU printing waterproof, wrinkle resistant novel fabric is characterized in that, comprise three layers, and ground floor is the PU surface layer, and main component is a PU polyurethane; The second layer is a thickening agent; The 3rd layer is the PU surface layer, and composition is a PU polyurethane.
2, PU printing waterproof according to claim 1, wrinkle resistant novel fabric, it is characterized in that, the thickening agent of the second layer is the distributes ink dyestuff that DISPERSE DYES and water-solubility carrier are made, or the distributes ink dyestuff made of DISPERSE DYES and pure solubleness carrier, or the distributes ink dyestuff made of DISPERSE DYES and oil-soluble resin.
3, PU printing waterproof according to claim 1 and 2, wrinkle resistant novel fabric is characterized in that, described DISPERSE DYES is molecular weight 250-400, the DISPERSE DYES of particle diameter 0.2-2 micron.
4, a kind of method of making the described PU printing waterproof of claim 1, wrinkle resistant novel fabric is characterized in that, may further comprise the steps:
Step 1: lining and bed material are prepared, afterwards the slurry that configures is left standstill froth breaking, filtration;
Step 2: bottom is coated with operation: the slurry that will leave standstill is added on the release liners, dries afterwards;
Step 3: base fabric is fitted, and is specially: knitted cloth is covered on the bed material after step 2 oven dry is handled, add the gas roller afterwards on base fabric;
Step 4: the bed material that is coated with knitted cloth in the step 3 is dried once more;
Step 5: clot is peeled off, and is specially: release liners is separated clot respectively with the PU leather;
Step 6: printed film heat is transferred on the base leather by printing machine;
Step 7: stamp base leather is carried out secondary coating, the slurry that leaves standstill in the step 1 is added on the release liners;
Step 8: bed material is dried;
Step 9: base fabric is fitted, and is specially: the finished product after printed the spending is removed from office on the bed material that covers after step 8 oven dry is handled, add the gas roller afterwards on base fabric;
Step 10: the bed material that is coated with the finished product leather in the step 9 is dried once more;
Step 11: clot is peeled off; Release liners is separated with the PU leather, and PU printing waterproof, wrinkle resistant novel fabric are made in clot respectively.
5, the method for manufacturing according to claim 4 PU printing waterproof, wrinkle resistant novel fabric is characterized in that, the PU slurry of preparation comprises 100 parts of the resins of 50 modulus in the step 1,10 parts of dimethyl formyl ammoniums, 10 parts of butanone, 60～90 parts of toluene, the concentration of preparation is 3000cps.
6, the method for manufacturing PU printing waterproof according to claim 4, wrinkle resistant novel fabric is characterized in that the thickness between step 2 intermediate roll and the release liners is 18, and the temperature that bed material is dried is 65 degree, and drying time is 20s.
7, the method for manufacturing PU printing waterproof according to claim 4, wrinkle resistant novel fabric is characterized in that the gas roller that step 3 adds is 4KG on base fabric.
8, the method for manufacturing PU printing waterproof according to claim 4, wrinkle resistant novel fabric is characterized in that the temperature that step 4 is dried once more is 100～135 degree, and drying time is 50s～70s.
9, the method for manufacturing PU printing waterproof according to claim 4, wrinkle resistant novel fabric, it is characterized in that, printed film in the step 6 is that thickening agent forms, this thickening agent is the distributes ink dyestuff that DISPERSE DYES and water-solubility carrier are made, or the distributes ink dyestuff made of DISPERSE DYES and pure solubleness carrier, or the distributes ink dyestuff made of DISPERSE DYES and oil-soluble resin; DISPERSE DYES is molecular weight 250--400, the DISPERSE DYES of particle diameter 0.2-2 micron; The transition temperature that printed film heat is transferred on the base leather is 110--120 ℃.
10, the method for manufacturing PU printing waterproof according to claim 4, wrinkle resistant novel fabric is characterized in that when step 7 was carried out secondary coating, the thickness between cylinder and the release liners was 18; The temperature that step 8 pair bed material is dried is that temperature is 65 degree, and drying time is 20s; The gas roller that step 9 adds on base fabric is 4KG; The temperature of step 10 oven dry is 100～135 degree, and drying time is 50s～70s.