CN101644358B - Novel energy-saving pouring gate pipe - Google Patents
Novel energy-saving pouring gate pipe Download PDFInfo
- Publication number
- CN101644358B CN101644358B CN2009100420435A CN200910042043A CN101644358B CN 101644358 B CN101644358 B CN 101644358B CN 2009100420435 A CN2009100420435 A CN 2009100420435A CN 200910042043 A CN200910042043 A CN 200910042043A CN 101644358 B CN101644358 B CN 101644358B
- Authority
- CN
- China
- Prior art keywords
- clay
- pouring gate
- content
- gate pipe
- sand
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses a novel energy-saving pouring gate pipe cast by mixing clay, argil and bauxite. The pouring gate pipe has the advantages of light weight, favorable wear resistance, corrosion resistance, high integrated intensity and favorable integrated performance and can meet the requirements of industrial use. The pouring gate pipe greatly saves resources and energy, effectively avoids casting defects such as adhering sand, sand inclusions, sand cuts, sand holes and the like, and enhances the cost and the quality of the casting.
Description
Technical field
The present invention relates to the tubing field, the tubing that material such as specifically a kind of liquid medium that is used for containing solid particle and powder transmits at kiln.
Background technique
Runner brick is a kind ofly be communicated with to divide the hollow refractory brick of steel brick and steel ingot mould in the groove of base plate at ingot casting, is commonly called as runner brick, and runner brick is generally the cuboid shape hollow clay brick of plurality of specifications.For reducing the resistance in the Molten Steel Flow process and preventing bleed-out, require the runner brick endoporus smooth, neat appearance, seam is tight.Owing to be the hollow clay brick, so the runner brick of existing technology exists defectives such as foundry goods scab, burning into sand, sand washing, make that product impurity is many, influence quality of product, defect rate is high.
Summary of the invention
Be to solve the problem that existing technology exists, the invention provides gate pin a kind of alternative runner brick, that be used for carrying at kiln materials such as the liquid medium that contains solid particle and powder, its preparation is more energy-conservation.
The present invention is achieved in that
A kind of novel energy-saving pouring gate pipe, said gate pin adopt clay, potter's clay, alum earth to mix casting and form, said clay content be 50%～70%, the content of said potter's clay is 10%～20%, the content of said alum earth is 20%～30%.
Preferably, said clay content be 60%, the content of said potter's clay is 15%, the content of said alum earth is 25%.
As another preferred version of the present invention, said gate pin in a tubular form.
Gate pin provided by the invention has the following advantages:
Brought into play the wear-resisting and/or corrosion resistance characteristic of china clay material; Utilized the intensity of alum earth material high again, proportion is little, process advantage such as large scale goods easily; The gate pin of manufacturing is in light weight, wear resistance good, anticorrosive, bulk strength is big, overall performance good, can satisfy industrial usage requirement;
Need 4 tons of runner bricks that raw material makes in the conventional art, only need 1 ton raw material can be cast as the gate pin of same length and size now, practiced thrift resource greatly, energy-conservation;
Can be made into any large-sized gate pin pipe, and long service life, mainly be adapted to contain the transmission of the material such as liquid medium and powder of solid particle;
Effectively avoid defectives such as foundry goods scab, burning into sand, sand washing, sand holes in the transmission course of materials such as the liquid medium of solid particle and powder in gate pin, improved casting cost and casting quality.
Description of drawings
Accompanying drawing described herein is used to provide further understanding of the present invention, constitutes the application's a part, does not constitute to improper qualification of the present invention, in the accompanying drawings:
The structural representation of the gate pin that Fig. 1 provides for the embodiment of the invention 1;
The structural representation of the gate pin that Fig. 2 provides for the embodiment of the invention 2;
The structural representation of the gate pin that Fig. 3 provides for the embodiment of the invention 3.
Embodiment
To combine accompanying drawing and specific embodiment to specify the present invention below, be used for explaining the present invention in this illustrative examples of the present invention and explanation, but not as to qualification of the present invention.
Embodiment 1:
Novel energy-saving pouring gate pipe that present embodiment provides adopts clay, potter's clay, alum earth to mix casting and forms, its medium clay soil content be 50%, the content of potter's clay is 20%, the content of alum earth is 30%.Said gate pin is circle straight tube shape (as shown in Figure 1).
Embodiment 2:
Novel energy-saving pouring gate pipe that present embodiment provides adopts clay, potter's clay, alum earth to mix casting and forms, its medium clay soil content be 70%, the content of potter's clay is 10%, the content of alum earth is 20%.Said gate pin is reducing bend pipe (as shown in Figure 2).
Embodiment 3:
Novel energy-saving pouring gate pipe that present embodiment provides adopts clay, potter's clay, alum earth to mix casting and forms, its medium clay soil content be 60%, the content of potter's clay is 15%, the content of alum earth is 25%.Said gate pin is reducing cross shape pipe (as shown in Figure 3).
Gate pin provided by the invention can be according to the required Any shape that is cast as of reality.
More than the technological scheme that the embodiment of the invention provided has been carried out detailed introduction; Used concrete example among this paper the principle and the mode of execution of the embodiment of the invention are set forth, above embodiment's explanation only is applicable to the principle that helps to understand the embodiment of the invention; Simultaneously, for one of ordinary skill in the art, according to the embodiment of the invention, the part that on embodiment and application area, all can change, in sum, this description should not be construed as limitation of the present invention.
Claims (3)
1. novel energy-saving pouring gate pipe; It is characterized in that: said gate pin adopts clay, potter's clay, alum earth to mix casting and forms; The content of said clay is 50%～70%, and the content of said potter's clay is 10%～20%, and the content of said alum earth is 20%～30%.
2. novel energy-saving pouring gate pipe as claimed in claim 1 is characterized in that: said clay content be 60%, the content of said potter's clay is 15%, the content of said alum earth is 25%.
3. like the described novel energy-saving pouring gate pipe of one of claim 1～2, it is characterized in that: said gate pin in a tubular form.