CN101637652A - Skateboard body and manufacture method thereof - Google Patents
Skateboard body and manufacture method thereof Download PDFInfo
- Publication number
- CN101637652A CN101637652A CN200810144357A CN200810144357A CN101637652A CN 101637652 A CN101637652 A CN 101637652A CN 200810144357 A CN200810144357 A CN 200810144357A CN 200810144357 A CN200810144357 A CN 200810144357A CN 101637652 A CN101637652 A CN 101637652A
- Authority
- CN
- China
- Prior art keywords
- composite fibre
- fibre layer
- board
- skateboard body
- glued membrane
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a skateboard body and a manufacture method thereof. The skateboard body comprises a combination board, a composite fiber layer and an adhesive film, wherein the lower surfaceof the composite fiber layer is combined on the upper surface of the combination board, the area of the composite fiber layer is slightly smaller than the area of the combination board, and the adhesive film is combined on the upper surface of the composite fiber layer in the mode of thermal fusion welding. The method for manufacturing the skateboard body comprises the following steps: the adhesive film is combined with the composite fiber layer by thermal fusion welding; the combined adhesive film and the composite fiber layer are cut, and the area thereof is slightly smaller than the combination board after cutting; and the cut composite fiber layer is combined on the combination board, and the edge of the composite fiber layer is not connected with the edge of the combination board. Therefore, the edge of the composite fiber layer can not crack, the adhesive film supported by the composite fiber layer can be conveniently combined on the combination board, and the adhesive film combination by thermal fusion welding is firm.
Description
Technical field
The present invention mainly is about a kind of skateboard body and method for making thereof, refers to a kind of skateboard body and method for making thereof of avoiding edge breakage and making easily especially.
Background technology
Slide plate is because its simple portable and the characteristic that can play everywhere become very popular CRUX equipment.Existing skateboard body is that the hard wood by majority overlaps fixing mutually and forms mostly.Because skateboard body is the body weight in order to the carrying user, the use that adds upper slide often makes skateboard body by the suitable height ground of dropping, so the intensity of skateboard body itself must reach certain degree, otherwise in use there is the doubt of fracture in regular meeting.
Existing skateboard body is in order to increase the intensity of plate body, avoiding plate body to break easily, is the end face in skateboard body mostly, and just trampling of user covers a composite fibre layer fully on the face, produce slight crack so as to the end face of avoiding skateboard body, and then prevent the fracture of skateboard body.Yet, because composite fibre layer is not good in the intensity of side direction, therefore when the skateboard body edge was subjected to clash into, the edge of composite fibre layer often split easily and produces the phenomenon that fork protrudes, so not only cause the not attractive in appearance of skateboard body edge, and also stab or hurt the slide plate user easily.
In addition,, composite fibre laminar surface on skateboard body is also arranged, yet, therefore be difficult for smooth and fully stick on the skateboard body, and also come off easily in the future because glued membrane is a soft materials further combined with a glued membrane in order to prevent splitting of composite fibre layer.
Summary of the invention
Be difficult for directly being combined on the skateboard body at glued membrane, the purpose of this invention is to provide a kind of skateboard body and method for making thereof, utilize this method for making can make glued membrane easily be combined on the skateboard body and difficult drop-off, and also cracky not of the edge of skateboard body.
For achieving the above object, the invention provides a kind of skateboard body, it includes:
One board;
One composite fibre layer, the lower surface of this composite fibre layer is combined in the upper surface of board, and the composite fibre layer area is slightly less than the area of board, and the edge that makes composite fibre layer not with the side edge of board; And
One glued membrane, this glued membrane is incorporated into the upper surface of composite fibre layer in the mode of thermal welding, and this glued membrane does not join with the upper surface of board.
Preferably, the spacing between the edge of the edge of composite fibre layer and board is not less than 2 centimeters.
Preferably, the thickness of this glued membrane is 0.1 to 0.2 centimeter.
The present invention provides a kind of skateboard body method for making in addition, and it comprises following steps:
The thermal welding step combines the upper surface of a glued membrane and the composite fibre layer mode with thermal welding;
Cutting step is cut the glued membrane and the composite fibre layer of combination, and the area after it is cut is slightly less than the area of a board; And
Integrating step is incorporated into the upper surface of above-mentioned board with the lower surface of the composite fibre layer that cut, and the edge that makes composite fibre layer not with the side edge of board.
Preferably, the lower surface of the composite fibre layer that has cut is incorporated into the upper surface of above-mentioned board in the mode of spray glue, forms a mucigel between composite fibre layer and board and make.
Preferably, this glued membrane is the thermoplastic poly amido formate.
Preferably, this glued membrane is incorporated into the upper surface of composite fibre layer in the mode of high frequency thermal welding.
By above-mentioned technological means, the producible concrete beneficial effect of the present invention comprises that the edge that can make composite fibre layer can not clashed into and splits, and can increase the attractive in appearance and security of skateboard body.In addition, the present invention combines the thermal welding of going ahead of the rest of glued membrane and composite fibre layer, be bonded on the board again, therefore the comparatively rigid composite fibre layer of glued membrane utilization is as support, can be bonded to easily on the board, and glued membrane combines also quite firmly with the thermal welding of composite fibre layer, the phenomenon that glued membrane comes off can not take place in the future.
Description of drawings
Fig. 1 is the stereogram of the preferred embodiment of skateboard body of the present invention;
Fig. 2 is the side view of the preferred embodiment of skateboard body of the present invention;
Fig. 3 is the schematic perspective view of the preferred embodiment of skateboard body method for making of the present invention when carrying out the thermal welding step;
Fig. 4 is the schematic side view of the preferred embodiment of skateboard body method for making of the present invention when carrying out the thermal welding step;
Fig. 5 is the schematic diagram of the preferred embodiment of skateboard body method for making of the present invention when carrying out cutting step.
The main element label declaration
10: board
20: composite fibre layer
30: glued membrane
40: hot cylinder
The specific embodiment
Please refer to Fig. 1 and shown in Figure 2, the preferred embodiment of skateboard body of the present invention comprises that a board 10, is combined in composite fibre layer 20 and on the board 10 and is combined in glued membrane 30 on the composite fibre layer 20, wherein:
This board 10 can be laminated by the skin-deep alternating layers of most layer lignum vitae and close institute and forms, generally can comprise seven layers of lignum vitae skin and forms seven laminates, and the wood grain of the wooden skin of each layer is moved towards can interlaced intensity with raising board 10;
The lower surface of this composite fibre layer 20 is combined in the upper surface of board 10, and composite fibre layer 20 areas are slightly less than the area of board 10, and the edge that makes composite fibre layer 20 not with the side edge of board 10, the setting of composite fibre layer 20 can be strengthened the intensity on board 10 surfaces whereby, and when the edge of board 10 is collided, the edge of composite fibre layer 20 can be by bump and impaired splitting, in this preferred embodiment, spacing between the edge of the edge of composite fibre layer 20 and board 10 is not less than 2 centimeters, and composite fibre layer 20 can be formed with a mucigel and both are combined with 10 of boards;
This glued membrane 30 is incorporated into the upper surface of composite fibre layer 20 in the mode of thermal welding, the mode of this thermal welding can be utilized high frequency, and this glued membrane 30 does not join with the upper surface of board 10, the setting of glued membrane 30 can reduce the probability that composite fibre layer 20 splits whereby, in this preferred embodiment, the thickness of this glued membrane 30 is 0.1 to 0.2 centimeter, this glued membrane 30 can be the thermoplastic poly amido formate (ThermoplasticPolyurethane, TPU).
The preferred embodiment of skateboard body method for making of the present invention comprises thermal welding step, cutting step and integrating step.
See also Fig. 3 and shown in Figure 4, in the thermal welding step, the upper surface of one glued membrane 30 and a composite fibre layer 20 mode with thermal welding is combined, and in this preferred embodiment, this thermal welding step is with two hot cylinder 40 pressings this composite fibre layer 20 and this glued membrane 30;
See also Fig. 1 and shown in Figure 5, in cutting step, the glued membrane that engaged 30 and composite fibre layer 20 are cut, the glued membrane 30 after it is cut and the area of composite fibre layer 20 are slightly less than the area of a board 10;
In integrating step, the lower surface of the composite fibre layer 20 that cut is incorporated into the upper surface of above-mentioned board 10, and the edge that makes composite fibre layer 20 not with the side edge of board 10, in this preferred embodiment, the lower surface of the composite fibre layer 20 that has cut is incorporated into the upper surface of above-mentioned board 10 in the mode of spray glue, and makes composite fibre layer 20 and 10 of boards form a mucigel.
Because the embodiment of above-mentioned method for making combines the thermal welding of going ahead of the rest of glued membrane 30 and composite fibre layer 20, the general is bonded on the board 10 in conjunction with the composite fibre layer 20 of glued membrane 30 again, therefore by the support of comparatively rigid composite fibre layer 20, glued membrane 30 can be bonded on the board 10 easily, can avoid when if glued membrane 30 is bonded on the board 10 respectively with composite fibre layer 20, be difficult for fixation phenomenon because of what the soft materials of glued membrane 30 caused.In addition, glued membrane 30 combines also quite firm with the thermal welding of composite fibre layer 20, the phenomenon that glued membrane 30 comes off can not take place in the future.
Claims (10)
1. a skateboard body is characterized in that, described skateboard body includes:
One board;
One composite fibre layer, the lower surface of this composite fibre layer is combined in the upper surface of board, and the composite fibre layer area is slightly less than the area of board, and the edge that makes composite fibre layer not with the side edge of board; And
One glued membrane, this glued membrane is incorporated into the upper surface of composite fibre layer in the mode of thermal welding, and this glued membrane does not join with the upper surface of board.
2. skateboard body according to claim 1 is characterized in that, the spacing between the edge of composite fibre layer and the edge of board is not less than 2 centimeters.
3. skateboard body according to claim 1 and 2 is characterized in that, this glued membrane is the thermoplastic poly amido formate.
4. skateboard body according to claim 3 is characterized in that, the thickness of this glued membrane is 0.1 to 0.2 centimeter.
5. skateboard body according to claim 4 is characterized in that, is formed with a mucigel between composite fibre layer and board.
6. skateboard body according to claim 1 and 2 is characterized in that, is formed with a mucigel between composite fibre layer and board.
7. a skateboard body method for making is characterized in that, described skateboard body method for making comprises following steps:
The thermal welding step combines the upper surface of a glued membrane and the composite fibre layer mode with thermal welding;
Cutting step is cut the glued membrane and the composite fibre layer of combination, and the area after it is cut is slightly less than the area of a board; And
Integrating step is incorporated into the upper surface of above-mentioned board with the lower surface of the composite fibre layer that cut, and the edge that makes composite fibre layer not with the side edge of board.
8. skateboard body method for making according to claim 7 is characterized in that, the lower surface of the composite fibre layer that has cut is incorporated into the upper surface of above-mentioned board in the mode that the spray gluing closes, and forms a mucigel between composite fibre layer and board and make.
9. according to claim 7 or 8 described skateboard body method for makings, it is characterized in that this glued membrane is the thermoplastic poly amido formate.
10. skateboard body method for making according to claim 9 is characterized in that, this glued membrane is incorporated into the upper surface of composite fibre layer in the mode of high frequency thermal welding.