CN101628646A - Composite packing material and manufacturing method thereof - Google Patents
Composite packing material and manufacturing method thereof Download PDFInfo
- Publication number
- CN101628646A CN101628646A CN200910109015A CN200910109015A CN101628646A CN 101628646 A CN101628646 A CN 101628646A CN 200910109015 A CN200910109015 A CN 200910109015A CN 200910109015 A CN200910109015 A CN 200910109015A CN 101628646 A CN101628646 A CN 101628646A
- Authority
- CN
- China
- Prior art keywords
- bubble cloth
- air bubble
- pearl wool
- temperature
- pearl
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a packing material, in particular to a composite packing material compounding pearl wool with air bubble cloth and a manufacturing method thereof. The composite packing material comprises a substrate which is made of the pearl wool, wherein the outer side part of the pearl wool is pasted with the air bubble cloth, and the pearl wool and the air bubble cloth are extruded and pasted after the surfaces of the pearl wool and the air bubble cloth are melted at high temperature. The composite packing material has the advantages that the pearl wool and the air bubble cloth are compounded to generate a new packing material, thereby improving the properties of the pearl wool and the air bubble cloth and deficiencies; the interior of a film coating machine is filled with heating oil, and the temperature of the heating oil can be controlled by adjusting the amount of heating current so as to control the temperature of a roller; after the pearl wool and the air bubble cloth pass through the roller, and the roller melts the surfaces of the pearl wool and the air bubble cloth at high temperature and then pastes the pearl wool and the air bubble cloth together by extruding. The invention enhances the appearance and the buffering performance of a product singly made of the pearl wool or the air bubble cloth, and the air bubble cloth improves the buffering performance of the packing material, thereby guaranteeing the safety factor of the product of a client in the process of transport. Meanwhile, the pearl wool at the inner side has the effect of heat and warm preservation.
Description
Technical field
The present invention relates to a kind of packing, refer more particularly to compound package material of the cotton compound bubble cloth of a kind of pearl and preparation method thereof.
Background technology
The polyethylene foam cotton is the non-crosslinked hole-closing structure, claims pearl cotton (EPE) again, is a kind of packing of novel environment friendly.It produces countless separated foams by low density polyethylene (LDPE) fat through physical blowing and constitutes.Overcome that common foamed glue is frangible, the shortcoming of distortion, recovery difference.Plurality of advantages such as have water proof protection against the tide, shockproof, sound insulation, insulation, plastic performance is good, toughness strong, reconstituted circularly, environmental protection, crashworthiness power are strong also has good chemical resistance.It is the ideal substitute of Traditional Packing material.The packing that is widely used in the multiple product such as inner packing, daily necessities of electronic apparatus, instrument and meter, computer, sound equipment, medicine equipment, industry control cabinet, lamp decoration, workmanship, glass, pottery, household electrical appliances, spraying, furniture, drinks and gift wrap, hardware, toy, melon and fruit, leather shoes.After adding antistatic agent and fire retardant, more apparent its remarkable performance.
The pearl cotton also is used for the cushions of handbag case and bag in a large number in addition, the floatation device of industrial sound insulation, thermal insulation material, agricultural warm material, aquaculture, the anti-protection pad of sports goods, the operation at sea buoyant apparatus, the floor finiss in family, hotel, liner or the like.Its tubing is used for industries such as air-conditioning, perambulator, toy for children, family property in a large number.
Existing machine construction of producing the pearl cotton comprises spice machine and extruder, the spice machine is used for regrown material and virgin material are evenly mixed, extruder comprises heat fused, foaming, qualitative, extrude and cool off several steps, the structure of extruder comprises material inlet, extruder inner chamber, is used for the heating cabinet that the extruder inner chamber is heated, the inner chamber that foams, and in the rear end of extruder cooling system is housed.
Bubble cloth also claims air-cushion film, gas pearl film, bubble chamber film, bubble paper, is to adopt the LDPE ldpe resin to process, as the current unique transparent a kind of flexible packaging padded coaming that generally uses.In the extruder raw material, add different additives in addition and more can produce various special-purpose bubble films such as electrostatic prevention, conduction and environmental protection.And can be processed into various composite materials according to customer requirement, compound as EPE, aluminum film compounded etc.
As packing, the cotton appearance looks elegant cushion characteristic of above single thin pearl deficiency, though and mono-bubble cloth cushion characteristic strong but aspect outward appearance with regard to some deficiency.
In order to remedy the weak point of above-mentioned existing pearl cotton and bubble cloth, the inventor has designed the present invention's " a kind of compound package material and preparation method thereof ".
Summary of the invention
The present invention is directed to above-mentioned the deficiencies in the prior art technical matters to be solved is: compound package material of a kind of cushion characteristic and appearance looks elegant and preparation method thereof is provided.
The technical solution adopted for the present invention to solve the technical problems is:
A kind of compound package material comprises matrix, and described matrix is the pearl cotton, is provided with bubble cloth in the outside portion of pearl cotton adhesion, pushes the phase adhesion again after melting with high temperature surface between bubble cloth and the pearl cotton.
Described method for making comprises:
1) adjust coating machine direct heating oil temperature, earlier, oily temperature setting range value is 120～170 ℃, and coating machine inside is heated oil, is used to control the oil temperature by the magnitude of current that changes load resistor adjusting heating coating machine;
2), pass through the temperature of control oil temperature and then control roller bearing at 110 ℃～165 ℃, cotton and bubble cloth is by the roller bearing of coating machine with pearl, roller bearing carries out high temperature melt with bubble cloth and the cotton surface of pearl, originally the cotton surface of bubble cloth and pearl is a solid-state form, make bubble cloth and pearl cotton material surface moment melt by high temperature conduction, rotate extruding by roller bearing when melting in material surface moment then and be sticked together.
The oil temperature of described coating machine direct heating oil is 130 ℃.
Described heated oil is a transformer oil.
The cotton high temperature of described bubble cloth and pearl surface melt temperature is 125 ℃
The beneficial effect of a kind of compound package material of the present invention and preparation method thereof is:
At existing technical deficiency part, the present invention carries out the new packing of compound generation with bubble cloth and pearl cotton, thereby improved the character of bubble cloth and pearl cotton, improved the weak point of existing packing, bubble cloth with the mutually compound technological principle of pearl cotton is: pearl cotton and bubble cloth raw MAT'L all are polyethylene, have identical fusing point, coating machine inside is heated oil, can control the oil temperature of heated oil by adjusting the heating current amount, thereby the temperature of control roller bearing, pearl cotton and bubble cloth melt bubble cloth and the cotton high temperature of pearl surface through out-of-date, are sticked together by extruding then.
Strengthen the outward appearance and the cushion characteristic of single pearl cotton and bubble cloth and product, the bubble cloth in the outside improves the cushion characteristic of material, and the product that has guaranteed the client is safety factor in transit, and inboard simultaneously pearl cotton has and is incubated warming effect.
Description of drawings
The present invention is further described below in conjunction with drawings and Examples.
Fig. 1 is the integral structure front schematic view of compound package material;
Fig. 2 is the A-A cross-sectional view among Fig. 1.
Description of reference numerals:
10, bubble cloth 20, pearl cotton
The specific embodiment
Referring to figs. 1 through Fig. 2, the present invention implements like this:
A kind of compound package material comprises matrix, and described matrix is a pearl cotton 20, is provided with bubble cloth 10 in the outside portion of pearl cotton 20 adhesion, pushes the phase adhesion again after melting with high temperature surface between bubble cloth 10 and the pearl cotton 20.
The method for making of above-mentioned compound package material may further comprise the steps:
1, adjust coating machine direct heating oil temperature earlier, oily temperature setting range value is 120～170 ℃, and coating machine inside is heated oil, is used to control the oil temperature by the magnitude of current that changes load resistor adjusting heating coating machine;
2, pass through the temperature of control oil temperature and then control roller bearing at 110 ℃～165 ℃, cotton and bubble cloth is by the roller bearing of coating machine with pearl, roller bearing carries out high temperature melt with bubble cloth 10 and cotton 20 surfaces of pearl, originally cotton 20 surfaces of bubble cloth 10 and pearl are solid-state forms, make bubble cloth 10 and pearl cotton 20 material surface moments melt by high temperature conduction, rotate extruding by roller bearing when melting in material surface moment then and be sticked together.
In the present embodiment, the oil temperature of coating machine direct heating oil is 130 ℃.Heated oil is a transformer oil.Cotton 20 high temperature of bubble cloth 10 and pearl surface melt temperature is 125 ℃.
The above, it only is the preferred embodiment of a kind of compound package material of the present invention and preparation method thereof, be not that technical scope of the present invention is imposed any restrictions, every foundation technical spirit of the present invention all still belongs in the scope of technical solution of the present invention above any trickle modification, equivalent variations and modification that embodiment did.
Claims (5)
1, a kind of compound package material, comprise matrix, it is characterized in that: described matrix is pearl cotton (20), is provided with bubble cloth (10) in the outside portion adhesion of pearl cotton (20), pushes the phase adhesion again after melting with the high temperature surface between bubble cloth (10) and the pearl cotton (20).
2, a kind of method for making of above-mentioned compound package material is characterized in that described method for making comprises:
1) adjust coating machine direct heating oil temperature, earlier, oily temperature setting range value is 120～170 ℃, and coating machine inside is heated oil, is used to control the oil temperature by the magnitude of current that changes load resistor adjusting heating coating machine;
2), pass through the temperature of control oil temperature and then control roller bearing at 110 ℃～165 ℃, cotton and bubble cloth is by the roller bearing of coating machine with pearl, roller bearing carries out high temperature melt with bubble cloth (10) and pearl cotton (20) surface, originally bubble cloth (10) and pearl cotton (20) surface are solid-state forms, make bubble cloth (10) and pearl cotton (20) material surface moment melt by high temperature conduction, rotate to push by roller bearing when melting in material surface moment then and be sticked together.
3, method for making according to claim 2, the oil temperature that it is characterized in that described coating machine direct heating oil is 130 ℃.
4, method for making according to claim 2 is characterized in that described heated oil is a transformer oil.
5, method for making according to claim 2 is characterized in that described bubble cloth (10) and pearl cotton (20) high temperature surface melt temperature is 125 ℃.