CN101624703A - Method for washing surface of metallic punched plate - Google Patents

Method for washing surface of metallic punched plate Download PDF

Info

Publication number
CN101624703A
CN101624703A CN200810029357A CN200810029357A CN101624703A CN 101624703 A CN101624703 A CN 101624703A CN 200810029357 A CN200810029357 A CN 200810029357A CN 200810029357 A CN200810029357 A CN 200810029357A CN 101624703 A CN101624703 A CN 101624703A
Authority
CN
China
Prior art keywords
metal
plate
punched plate
piercing
minutes
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN200810029357A
Other languages
Chinese (zh)
Inventor
曾胜祥
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
DONGGUAN DALINGSHAN ALPHA METAL PRODUCT FACTORY
Original Assignee
DONGGUAN DALINGSHAN ALPHA METAL PRODUCT FACTORY
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by DONGGUAN DALINGSHAN ALPHA METAL PRODUCT FACTORY filed Critical DONGGUAN DALINGSHAN ALPHA METAL PRODUCT FACTORY
Priority to CN200810029357A priority Critical patent/CN101624703A/en
Publication of CN101624703A publication Critical patent/CN101624703A/en
Pending legal-status Critical Current

Abstract

The invention discloses a method for washing the surface of a metallic punched plate, which is finished through steps of preparing cleanout fluid, dipping the metallic punched plate, washing the metallic punched plate and drying the metallic punched plate. The method for washing the surface of the metallic punched plate has the characteristics of low cost and easy realization. Through the washing method, greasy dirt, dust, rusty spots and other attachments on the surface of the punched plate are washed away; fade, lacquer drop and other flaws are repaired; and when glue spraying and splicing are performed, foam or heat insulating/soundproof materials are firmly adhered to the surface of the punched plate, so that the quality of roof slabs is improved.

Description

A kind of method for cleaning surface of Metal-Piercing plate
Technical field
The present invention relates to the metal sheet treatment process, particularly a kind of method for cleaning surface of Metal-Piercing plate.
Background technology
Heat insulation, waterproof is the characteristic of roofing board indispensability, a kind of roofing board commonly used at present, constitute by metal sheet that offers venting hole and the foam or the heat insulation/Sound-proof material that are bonded at metal sheet surface, this roofing board can be isolated solar radiation summer, can preserve room temp winter, also possess waterproof sound damping function, favored by the human consumer.
This roofing board is by color steel, galvanized sheet, the titanium zine plate, the Al-Mg-Mn plate, aluminium alloy plate, metal sheet cuttings such as color aluminium sheet, punching, spray glue is stained with foam then or heat insulation/Sound-proof material is made, in the actual production, mostly punching is to finish by stamping machine to metal sheet, fading and depainting phenomenon appears in metal sheet that punching finishes easily, the surface adheres to greasy dirt easily, dust and rust staining or the like, and the punched-plate surface is not if clean up, then can produce fatal influence to ensuing spray glue process, therefore the punched-plate surface cleaning becomes the most key step in the roofing board processing, existing all multiple method for cleaning surface all can not satisfy demand of practical production.
Summary of the invention
In order to overcome the deficiencies in the prior art, the invention provides a kind of method of effective cleaning punched-plate surface residue.
In order to solve the problems of the technologies described above, the present invention is achieved by the following technical solutions:
A kind of method for cleaning surface of Metal-Piercing plate, it is realized by following steps:
A), press row compositions in weight portion configuration scavenging solution and remove oil-bound distemper, 75 parts of grease-removing agents and 1080~1320 parts of water thorough mixing for 100 parts;
B), immersion places above-mentioned scavenging solution immersion to take out after 30 seconds~6 minutes the Metal-Piercing plate;
C), clear water clean metal punched-plate 20 seconds~3 minutes are used in flushing;
D), the dry baking box of using toasted the Metal-Piercing plates 30 seconds~10 minutes at 60~150 ℃.
Described purging method is particularly realized by following steps:
A), press row compositions in weight portion configuration scavenging solution
100 parts are removed oil-bound distemper, 75 parts of grease-removing agents and 1200 parts of water thorough mixing;
B), soak
Place above-mentioned scavenging solution immersion to take out after 2 minutes the Metal-Piercing plate;
C), flushing
With clear water clean metal punched-plate 1 minute;
D), drying
Toasted the Metal-Piercing plates 4 minutes with baking box at 90 ℃.
Described step c) is specially: the Metal-Piercing plate is placed Rinsing Area, scrub with brush and form.
The invention has the beneficial effects as follows: purging method of the present invention is with low cost, realize easily, by this purging method, dirt settlings such as the greasy dirt on punched-plate surface, dust and rust staining are eliminated, fade and fall flaws such as lacquer and be repaired, when spraying glue and when bonding, foam or heat insulation/sound-proof material are firm sticks to the punched-plate surface, thereby the roofing board quality gets a promotion.
Embodiment
Below in conjunction with specific embodiment the present invention is described in further detail.
Embodiment 1
The present invention is realized by following steps:
Select for use 100 kilograms to remove oil-bound distemper and 75 kilograms of grease-removing agents are put into 1.08 cubic metres water thorough mixing, be configured to scavenging solution, scavenging solution is placed degreasing tank, allow Metal-Piercing plate current waterline pass through degreasing tank successively then, guarantee that punched-plate soaked 30 seconds in the scavenging solution the inside, enter Rinsing Area with streamline then, scrubbed 20 seconds with brush in the clear water the inside, enter baking box with streamline then, baking is 10 minutes under 60 ℃ of environment, leave baking box then, carry out next step packaging process.
By above purging method, dirt settlings such as the greasy dirt on punched-plate surface, dust and rust staining are eliminated, and fade and fall flaws such as lacquer to be repaired, when spraying glue and when bonding, foam or heat insulation/sound-proof material are firm sticks to the punched-plate surface, thereby the roofing board quality gets a promotion.
Embodiment 2
The present invention is realized by following steps:
Select for use 100 kilograms to remove oil-bound distemper and 75 kilograms of grease-removing agents are put into 1.32 cubic metres water thorough mixing, be configured to scavenging solution, scavenging solution is placed degreasing tank, allow Metal-Piercing plate current waterline pass through degreasing tank successively then, guarantee that punched-plate soaked 6 minutes in the scavenging solution the inside, enter Rinsing Area with streamline then, scrubbed 3 minutes with brush in the clear water the inside, enter baking box with streamline then, baking is 30 seconds under 150 ℃ of environment, leave baking box then, carry out next step packaging process.
Embodiment 3
The present invention is realized by following steps:
Select for use 100 kilograms to remove oil-bound distemper and 75 kilograms of grease-removing agents are put into 1.2 cubic metres water thorough mixing, be configured to scavenging solution, scavenging solution is placed degreasing tank, allow Metal-Piercing plate current waterline pass through degreasing tank successively then, guarantee that punched-plate soaked 2 minutes in the scavenging solution the inside, enter Rinsing Area with streamline then, scrubbed 1 minute with brush in the clear water the inside, enter baking box with streamline then, baking is 4 minutes under 90 ℃ of environment, leave baking box then, carry out next step packaging process.
Above-described only is preferred implementation of the present invention, should be pointed out that for the person of ordinary skill of the art, under the prerequisite that does not break away from the invention design, can also make some distortion and improvement, and these all belong to protection scope of the present invention.

Claims (3)

1, a kind of method for cleaning surface of Metal-Piercing plate is characterized in that, it is realized by following steps:
A), press row compositions in weight portion configuration scavenging solution
100 parts are removed oil-bound distemper, 75 parts of grease-removing agents and 1080~1320 parts of water thorough mixing;
B), soak
Place above-mentioned scavenging solution immersion to take out after 30 seconds~6 minutes the Metal-Piercing plate;
C), flushing
With clear water clean metal punched-plate 20 seconds~3 minutes;
D), drying
Toasted the Metal-Piercing plates 30 seconds~10 minutes with baking box at 60~150 ℃.
2, the method for cleaning surface of a kind of Metal-Piercing plate according to claim 1 is characterized in that, it is realized by following steps:
A), press row compositions in weight portion configuration scavenging solution
100 parts are removed oil-bound distemper, 75 parts of grease-removing agents and 1200 parts of water thorough mixing;
B), soak
Place above-mentioned scavenging solution immersion to take out after 2 minutes the Metal-Piercing plate;
C), flushing
With clear water clean metal punched-plate 1 minute;
D), drying
Toasted the Metal-Piercing plates 4 minutes with baking box at 90 ℃.
3, the method for cleaning surface of a kind of Metal-Piercing plate according to claim 1 and 2 is characterized in that, described step c) is specially: the Metal-Piercing plate is placed Rinsing Area, scrub with brush and form.
CN200810029357A 2008-07-09 2008-07-09 Method for washing surface of metallic punched plate Pending CN101624703A (en)