CN101619496A - Non-linear optical crystal N-methyl-1,3- propane-diammonium aluminum pentaborate, preparation method and application thereof - Google Patents
Non-linear optical crystal N-methyl-1,3- propane-diammonium aluminum pentaborate, preparation method and application thereof Download PDFInfo
- Publication number
- CN101619496A CN101619496A CN200810071330A CN200810071330A CN101619496A CN 101619496 A CN101619496 A CN 101619496A CN 200810071330 A CN200810071330 A CN 200810071330A CN 200810071330 A CN200810071330 A CN 200810071330A CN 101619496 A CN101619496 A CN 101619496A
- Authority
- CN
- China
- Prior art keywords
- diammonium
- propane
- preparation
- methyl
- aluminum
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to novel non-linear optical crystal N-methyl-1,3-propane-diammonium aluminum pentaborate, which has a chemical formula of Al(B5010.CH3NH2CH2CH2CH2NH3); and the chemical formula has molecular weight of 331.20 and belongs an orthorhombic system with a space group of P2(1)2(1)2(1), single cell parameters: a is equal to 10.332(6), b is equal to 9.447 (6), c is equal to 13.775 (8), alpha, beta and gamma are equal to 90 degrees, V is equal to 1344.5 (1)<3> and Z is equal to 4. The novel non-linear optical crystal N-methyl-1,3-propane-diammonium aluminum pentaborate is prepared by a water (agent) thermal method. The N-methyl-1,3-propane-diammonium aluminum pentaborate has excellent non-linear optical property, and the power SHG coefficient thereof is two times of KDP, which corresponds to LBO.
Description
Technical field
The present invention relates to a kind of nonlinear optical material N-methyl isophthalic acid, 3-propane-diammonium five aluminum borates (chemical formula: [Al (B
5O
10)] CH
3NH
2CH
2CH
2CH
2NH
3) preparation and application.
Background technology
(Nonlinear Optics is a frontier of contemporary optics NLO) to nonlinear optics, is the research response of material and science of the nonlinear relationship that field intensity presents under the high light effect.In numerous non-linear optical effects, frequency-doubled effect (SHG) be the most noticeable also be the non-linear effect of studying at most.Optical material with non-linear effect is in modern science and technology, in particularly some civilian and military high-tech areas, for example photoelectricity communication, optical information storage, unicircuit, photoswitch, light slicer, color laser printing, blinding laser weapons, the ocean locating fish etc. all have a series of important application.
Studies show that borate compound compares the non-centrosymmetrical structure of the easier formation of compound of other type, but not the structure of the heart is the precondition that produces non-linear optical effect.Therefore, for a long time, the borate crystal of nonlinear optics is people's a research focus always.The nonlinear optics borate crystal of practical application comprises LiB at present
3O
5(LBO), β-BaB
2O
4(BBO), BiB
3O
6(BIBO) etc.Though these nonlinear optical materials are widely used in all trades and professions, yet different fields is also different to the requirement of nonlinear optical material, therefore can not have single nonlinear optical material optimization to be applied to all fields.This has just proposed requirement to the diversity of nonlinear optical material, so that can the specific nonlinear optical material of optimized selection in specific field.So be necessary to continue to seek and develop new nonlinear optical material.We are by adopting the AlO of chirality
4The poly-boron anion bunch coordinated groups of the group and the non-heart is dressed up the strategy of the non-heart or chiral structure, thereby has obtained the novel non-linearity optical material of superior performance.
Summary of the invention
The objective of the invention is to prepare a kind of non-linear optic crystal N-methyl isophthalic acid, 3-propane-diammonium five aluminum borates (chemical formula: [Al (B
5O
10)] CH
3NH
2CH
2CH
2CH
2NH
3), its technical scheme is as follows:
We select aluminum isopropylate (Al (i-PrO)
3), boric acid (H
3BO
3), N, N-two (3-amine propyl group) methylamine (C
7H
19N
3) make raw material, its mol ratio is 1: 6: 9, adopts water and pyridine to make mixed solvent, the chirality AlO that utilizes aluminum isopropylate to be hydrolyzed into
4The non-the heart-yin ion cluster coordinated groups that group and boric acid aggregate into is dressed up skeleton, and by N, the N-methyl isophthalic acid of the diprotonization that N-two (3-amine propyl group) methylamine resolves into, 3-propylene diamine positively charged ion is made counter ion, under hydrothermal condition, obtain the N-methyl isophthalic acid, the crystalline material of 3-propane-diammonium five aluminum borates.
We record the single crystal structure of this compound, and its structural parameter are as follows:
Chemical formula is [Al (B
5O
10)] CH
3NH
2CH
2CH
2CH
2NH
3, molecular weight is 331.20, belongs to rhombic system, spacer P2
12
12
1, cell parameter is a=10.332 (6), b=9.447 (6),
α=β=γ=90 °,
Z=4.
The N-methyl isophthalic acid, the structure of 3-propane-diammonium five aluminum borates is by AlO
4With B
5O
10Bunch alternately be connected to three-dimensional spacious skeleton structure by summit altogether.[100], [010] and [001] direction in this structure have 8 yuan of ring foraminous spiral tracts, and direction has 11 membered ring channels in [110] and [110], the N-methyl isophthalic acid of diprotonization, and the 3-propylene diamine is filled in 11 membered ring channels as counter cation.
The nonlinear optics measurement shows, the N-methyl isophthalic acid, and 3-propane-diammonium five aluminum borates have good non-linear optical property, the very strong 532nm green glow of output under the 1064nm laser radiation, its powder SHG coefficient is 2 times of KDP, and is suitable with LBO.
N-methyl isophthalic acid provided by the invention, 3-propane-diammonium five aluminum borates are the crystal that grow by water (agent) process for thermosynthesizing.Material preparation method of the present invention has that technology is simple, productive rate is high and advantage such as good reproducibility.The advantage of this material is not to be soluble in general solvent, and heat decomposition temperature point high (can be stabilized to 360 ℃ in the air atmosphere), photoabsorption is low, transparency range is big.
The prepared nonlinear optical material of this invention can be applicable to laser frequency conversion, Electro-optical Modulation, light and sells off high-tech areas such as information processing.
Embodiment
1, the preparation of compound
At first Al (i-PrO)
3(204mg) and H
3BO
3Mixture (372mg) joins 1.0mL water (H is housed
2O) and in the tetrafluoroethylene reactor of 3.0mL pyridine (pyridine) mixing solutions, use magnetic stirrer.After the question response thing dissolves fully, stop to stir the N of adding 1.3mL in the mixing solutions, N-two (3-amine propyl group) methylamine (C
7H
19N
3), make Al in the reactor (i-PrO)
3/ H
3BO
3/ C
7H
19N
3/ pyridine/H
2The mol ratio of O is 1/6/9/37/56, and the tetrafluoroethylene reactor is packed into seals in the stainless steel high-pressure reactor then, 170 ℃ of reactions 7 days down.Final N, N-two (3-amine propyl group) methylamine is decomposed into the N-methyl isophthalic acid, 3-propylene diamine and further diprotonization, and then obtain water white bulk crystals.
2, performance test
Our N-methyl isophthalic acid to obtaining, 3-propane-diammonium five aluminum borates carry out optical performance test, and its second order nonlinear optical effect is about 2 times of KDP.
Claims (4)
1. non-linear optic crystal N-methyl isophthalic acid, 3-propane-diammonium five aluminum borates is characterized in that: its chemical formula is [Al (B
5O
10)] CH
3NH
2CH
2CH
2CH
2NH
3, molecular weight is: 331.20, belong to rhombic system, and spacer P212121 (No.19), cell parameter are a=10.332 (6), b=9.447 (6), c=13.775 (8)
α=β=γ=90 °, V=1344.5 (1)
Z=4.
2. the N-methyl isophthalic acid of a claim 1, the preparation method of 3-propane-diammonium five aluminum borates is characterized in that: adopt the hot method preparation of water (agent).
3. preparation method as claimed in claim 2 is characterized in that: the hot method of described water (agent) comprises the steps: reactant A l (i-PrO)
3, H
3BO
3, N, the mol ratio of N-two (3-amine propyl group) methylamine is 1: 6: 9, adopts water and pyridine to make mixed solvent, and temperature of reaction is 170 ℃, and the reaction times is 7 days.
4. the N-methyl isophthalic acid of a claim 1, the purposes of 3-propane-diammonium five aluminum borates is characterized in that: this crystal is used for photoelectricity communication, optical information storage, unicircuit, photoswitch, light slicer, color laser printing, blinding laser weapons, the ocean locating fish.