CN101581059B - Method for producing matte super-sensitive paper - Google Patents
Method for producing matte super-sensitive paper Download PDFInfo
- Publication number
- CN101581059B CN101581059B CN200910016138XA CN200910016138A CN101581059B CN 101581059 B CN101581059 B CN 101581059B CN 200910016138X A CN200910016138X A CN 200910016138XA CN 200910016138 A CN200910016138 A CN 200910016138A CN 101581059 B CN101581059 B CN 101581059B
- Authority
- CN
- China
- Prior art keywords
- paper
- matte
- coating
- percent
- super
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention relates to a method for producing matte super-sensitive paper. The base paper of the matte super-sensitive paper is made of 100 percent of wood pulp, which comprises 40 percent of needlepulp and 60 percent of kargeleaf pulp; the degree of beating is between 40 and 45 degrees of SR, the pulping concentration of the pulp is between 0.5 and 1.0 percent, and the quantitation of the basepaper is between 80 and 200g/m<2>; the base paper is subjected to double-sided coating processing and bundling treatment, wherein the double-sided coating processing adopts roller-type feeding and air knife coating forming for one time, a finished product is double coated paper, and the single coating quantity is between 10 and 15g/m<2>; and the coating comprises main pigment and a matte additive, wherein the main pigment is prepared by mixing kaoline and calcium carbonate according to the ratio of 1:1, the matte additive is G-365 commonly sold on markets, and the dosage of the matte additiveaccounts for 5 to 10 percent of the coating. The coating paper surface and the printed coating paper surface have no bright luster, and the paper surface touches slippery and smooth like floss and has visual effect of elegant printing matte; and the method has easy production and low production cost, and reduces processing steps under the condition of ensuring the printing effect.
Description
Technical field
The present invention relates to a kind of manufacture craft of speciality paper, specifically a kind of method for producing matte super-sensitive paper.
Background technology
We know that coated paper in the market can be divided into two classes: a class is low quantitative coated printing paper, and its quality is between art paper and offset paper; Another kind of is art paper.Coated printing paper is handled by copper coin body paper superpressure after being coated with and is formed.Its paper glossiness height prints Well-recovered characteristics, once is being subjected to printing the welcome on boundary.But along with development of market economy, people's aesthetic standard is also in continuous variation, and magnificent high glaze sense is not accepted gradually, and on this basis, people begin to carry out the exploitation of high-grade coating ultra-sense paper.Coating ultra-sense paper has been abandoned the theory of art paper high glaze, makes full use of the texture of body paper nature, in light weight coating back paper, used the special coating prescription during coating, become that the paper printing color is Well-recovered, printing texture nature.It is with low coating weight, high surface strength, high printability, high color reducibility with without the natural texture of press polish, ornamenting, primary surface effect, the nature cubic appearance is more arranged after the printing, be widely used in high-grade books and periodicals, magazine, poster, fine arts picture, label, advertisement, building and say on the printed matters such as a name book, household design, decoration.Subsequently, external matte super-sensitive paper enters the domestic market, but method for producing matte super-sensitive paper is not seen bibliographical information as yet.
Summary of the invention
Technical problem to be solved by this invention is to overcome above-mentioned the deficiencies in the prior art, provide a kind of processing and fabricating easy, production cost is low, under the preceding topic that guarantees printing effect, reduce manufacturing procedure, both had the feel as the fine hair, had the method for producing matte super-sensitive paper of the mute gloss visual effect of graceful printing again.
The technical solution adopted for the present invention to solve the technical problems is: a kind of method for producing matte super-sensitive paper, its body paper are made and are adopted 100% wood pulp to manufacture paper with pulp, and wherein the needle slurry 40%, broad-leaved slurry 60%, beating degree 40-45 ° of SR, slurry sizing concentration 0.5-1.0%, the quantitative 80-200g/m of body paper
2, it is characterized in that: described body paper is carried out double spread processing and the bundling arrangement obtains matte super-sensitive paper, double spread processing employing roll-type material loading, coated and molded of air knife, finished product is a two side coated paper, single face coating weight 10-15g/m
2Comprise body pigment and matte additive in the used coating, body pigment is that kaolin and calcium carbonate are mixed, and the two ratio is 1: 1, and the matte additive is commercial commodity nanometer materials G-365, and consumption accounts for the 5-10% of coating.
The present invention uses rational roll-type material loading and air knife finished coated mode because the body paper paper has good fine and smooth flatness, obtains the coated face of homogeneous.Against existing technologies, in formulation for coating material, add special material G-365, its main feature is that printing is Well-recovered, the no magnificent gloss of coating paper and printing back, paper had both had the feel of smooth exquisiteness as the fine hair, has the mute gloss visual effect of graceful printing again, the characteristics of having given prominence to matte super-sensitive paper.Its processing and fabricating is easy, and production cost is low, under the preceding topic that guarantees printing effect, has reduced manufacturing procedure.
The specific embodiment
The present invention will be further described below in conjunction with embodiment.
A kind of method for producing matte super-sensitive paper, it comprises basic steps such as body paper production, double spread processing, bundling arrangement:
(1) making of body paper: the production of matte super-sensitive paper at first guarantees internal bond strength and surface strength and smoothness from body paper, requires the thickness uniformity of body paper view picture, and the smooth exquisiteness of paper is for following process production lays the foundation.Adopt 100% wood pulp to manufacture paper with pulp, wherein the needle slurry 40%, broad-leaved slurry 60%, beating degree 40-45 ° of SR, slurry sizing concentration 0.5-1.0%, the quantitative 80-200g/m of body paper
2, surface strength 〉=12 grade, the surface absorbs 20-30g/m
2, become paper smoothness 〉=30S;
(2) double spread processing: described body paper is carried out double spread processing obtain matte super-sensitive paper, roll-type material loading, coated and molded of air knife are adopted in double spread processing, and finished product is a two side coated paper, single face coating weight 10-15g/m
2, become paper surface nature like this, effect and good hand touch.Comprise body pigment and matte additive in the used coating composition, body pigment is that kaolin and calcium carbonate are mixed, and the two ratio is 1: 1, and the matte additive is commercial commodity nanometer materials G-365, and consumption accounts for the 5-10% of coating.At the feel and the print request that are coated with the back paper, on body pigment, select kaolin and winnofil to be mixed, the two ratio is about 1: 1, can satisfy the opacity, whiteness height of coated paper, the requirement that ink absorption is good simultaneously.In order to be different from conventional coated paper, allow fine and smooth feel as the paper villous, printing back clear patterns, third dimension is strong and gloss is soft, add the matte additive, it is the special nanometer materials G-365 of commercial commodity, handles through high speed dispersion, evenly sneak into coating and use the about 5-10% of consumption.
Coating flow is: matte super-sensitive body paper → material loading → metering → air knife → drying → rolling.Require when coating prepares to be uniformly dispersed, mix fully, viscosity is reasonable, is suitable for the air knife ornamenting.The coating feeding system requires metering accurately, paper defects such as no windrow, streak, shrinkage cavity.
Carry out the bundling arrangement at last, finish the production of matte super-sensitive paper.Become paper both to have the feel of smooth exquisiteness as the fine hair, have the mute gloss visual effect of graceful printing again, the characteristics of having given prominence to matte super-sensitive paper.Its processing and fabricating is easy, and production cost is low, under the preceding topic that guarantees printing effect, has reduced manufacturing procedure.
Claims (1)
1. method for producing matte super-sensitive paper, its body paper are made and are adopted 100% wood pulp to manufacture paper with pulp, and wherein the needle slurry 40%, broad-leaved slurry 60%, beating degree 40-45 ° of SR, slurry sizing concentration 0.5-1.0%, the quantitative 80-200g/m of body paper
2, it is characterized in that: described body paper is carried out double spread processing and the bundling arrangement obtains matte super-sensitive paper, double spread processing employing roll-type material loading, coated and molded of air knife, finished product is a two side coated paper, single face coating weight 10-15g/m
2Comprise body pigment and matte additive in the used coating, body pigment is that kaolin and calcium carbonate are mixed, and the two ratio is 1: 1, and the matte additive is nanometer materials G-365, and consumption accounts for the 5-10% of coating.