CN101575169A - Jade white lighting glass - Google Patents
Jade white lighting glass Download PDFInfo
- Publication number
- CN101575169A CN101575169A CNA2009100160103A CN200910016010A CN101575169A CN 101575169 A CN101575169 A CN 101575169A CN A2009100160103 A CNA2009100160103 A CN A2009100160103A CN 200910016010 A CN200910016010 A CN 200910016010A CN 101575169 A CN101575169 A CN 101575169A
- Authority
- CN
- China
- Prior art keywords
- glass
- percent
- white lighting
- bao
- cao
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses jade white lighting glass, which consists of the following components by mass percentage: 65 to 72 percent of SiO2, 0 to 3 percent of B2O3, 2 to 6 percent of Al2O3, 10 to 15 percent of Na2O, 4.5 to 6.5 percent of K2O, 5 to 10 percent of CaO, 2 to 3 percent of BaO, 0 to 1 percent of ZnO, 4 to 8 percent of F <->, 0.1 to 0.8 percent of Er2O3 and 0 to 1 percent of Nd2O3. The jade white lighting glass has the characteristics of novel color varieties of crystal colored glass for the lighting industry, capabilities of meeting the requirements of customers on the colored glass diversification and being used for the various glass artcles, unchangeable color and low cost.
Description
Technical field
The invention belongs to the glass technology field, especially relate to a kind of beautiful white glass that is used for the lamp decoration industry.
Background technology
Present Chinese lamp decoration industry development is rapid, but lighting glass is of less types on the market, in order to increase the lighting glass kind, satisfy the client to the diversified requirement of coloured glass, generally be to adopt in flint glass surface applied color layers, to change the glass appearance color, though this mode has solved certain problem, because the temperature of lamp decoration is higher, long-time use can cause problems such as color change, decolouring, cause outward appearance to change, do not satisfy present needs.
Summary of the invention
The objective of the invention is to improve the deficiency of prior art and the new color variety of a kind of quartzy coloured glass that is used for the lamp decoration industry is provided, satisfy the client to the diversified requirement of coloured glass, can be applicable to various Glass Crafts, color does not change, cost is low jade white lighting glass.
The object of the present invention is achieved like this, and a kind of jade white lighting glass is characterized in by mass percent being: SiO
2: 65~72%, B
2O
3: 0~3%, Al
2O
3: 2~6%, Na
2O:10~15%, K
2O:4.5~6.5%, CaO:5~10%, BaO:2~3%, ZnO:0~1%, F
-: 4~8%, Er
2O
3: 0.1~0.8%, Nd
2O
3: 0~1% forms.
In order further to realize purpose of the present invention, can be to be by mass percent: SiO
2: 65~68%, B
2O
3: 0~2.5%, Al
2O
3: 4~5%, Na
2O:10~15%, K
2O:4.5~6.5%, CaO:5~10%, BaO:2~3%, ZnO:0~1%, F
-: 4~8%, Er
2O
3: 0.1~0.8%, Nd
2O
3: 0~1% forms.
Compared with the prior art the present invention has following distinguishing feature and good effect: the present invention adopts and by mass percent is: SiO
2: 65~72%, B
2O
3: 0~3%, Al
2O
3: 2~6%, Na
2O:10~15%, K
2O:4.5~6.5%, CaO:5~10%, BaO:2~3%, ZnO:0~1%, F
-: 4~8%, Er
2O
3: 0~0.3%, Nd
2O
3: 0~1% forms, wherein Er
2O
3And Nd
2O
3Be the tone stabilizing agent, it is variegated that other impurity that neutralizes causes, makes the color of glass be beautiful white.
SiO
2Be the main component that forms glass, melt temperature increases with the increase of content, and chemical stability is variation with the minimizing of content.SiO among the present invention
2Content (weight percent content, as follows) is 65~72%, is preferably 65~68%.
B
2O
3Be the glass flux, the melting situation improves with the increase of content, but content increases the erosion that can strengthen refractory material.B among the present invention
2O
3Content is 0~3%, is preferably 0~2.5%.
Al
2O
3Can improve glass devitrification and chemical stability, but too high levels can make the melting difficult, increase production difficulty.Al among the present invention
2O
3Content is 2~6%, is preferably 4~5%.
Na
2O, K
2O plays strong fluxing action, to reduce temperature of fusion, reduces the volatilization of fluorochemical.While K
2O can improve the goods glossiness.Na among the present invention
2O content is 10~15%, K
2O content is 4.5~6.5%.
CaO, BaO, ZnO are conditioning agent, can improve the crystallization ability and the chemical stability of glass.CaO content is 5~10% among the present invention, and BaO content is 2~3%, and ZnO content is 0~1%.
Adopt prescription of the present invention, according to the accurate weighing frit of prescription, mix then to melt and make glass.Both improve fusing speed, prolonged furnace life again, reduced production cost.
Embodiment
Embodiment 1, and a kind of jade white lighting glass is to be by mass percent:
SiO
2: 65~72%, B
2O
3: 0~3%, Al
2O
3: 2~6%, Na
2O:10~15%, K
2O:4.5~6.5%, CaO:5~10%, BaO:2~3%, ZnO:0~1%, F
-: 4~8%, Er
2O
3: 0~0.3%, Nd
2O
3: 0~1% forms, and present embodiment adopts the SiO of 65.5kg
2, the Al of 4kg
2O
3, the Na of 10kg
2O, the K of 5.5kg
2O, the CaO of 8kg, the BaO of 3kg, the F of 4kg
-Mix according to a conventional method to melt and make glass.
Embodiment 2, and a kind of jade white lighting glass is the SiO by 72kg
2, the B of 0.4kg
2O
3, the Al of 2kg
2O
3, the Na of 10kg
2O, the K of 4.5kg
2O, the CaO of 5kg, the BaO of 2kg, the F of 4kg
-, the Er of 0.1kg
2O
3Mix according to a conventional method to melt and make glass.
Embodiment 3, and a kind of jade white lighting glass is the SiO by 70kg
2, the Al of 3kg
2O
3, the Na of 11kg
2O, the K of 4.6kg
2O, the CaO of 5kg, the BaO of 2kg, the ZnO of 0.1kg, the F of 4kg
-, the Er of 0.3kg
2O
3Mix according to a conventional method to melt and make glass.
Embodiment 4, and a kind of jade white lighting glass is the SiO by 69kg
2, the Al of 5kg
2O
3, the Na of 10kg
2O, the K of 4.5kg
2O, the CaO of 5kg, the BaO of 2kg, the F of 4kg
-, the Er of 0.3kg
2O
3, the Nd of 0.2kg
2O
3Mix according to a conventional method to melt and make glass.
Embodiment 5, and a kind of jade white lighting glass is the SiO by 65kg
2, the B of 1kg
2O
3, the Al of 2kg
2O
3, the Na of 10kg
2O, the K of 5kg
2O, the CaO of 6kg, the BaO of 2kg, the ZnO of 0.3kg, the F of 8kg
-, the Er of 0.2kg
2O
3, the Nd of 0.5kg
2O
3Mix according to a conventional method to melt and make glass.
Embodiment 6, and a kind of jade white lighting glass is the SiO by 65kg
2, the B of 0.5kg
2O
3, the Al of 2kg
2O
3, the Na of 15kg
2O, the K of 4.5kg
2O, the CaO of 5kg, the BaO of 2kg, the ZnO of 1kg, the F of 4kg
-, the Er of 0.1kg
2O
3, the Nd of 0.9kg
2O
3Mix according to a conventional method to melt and make glass.
Embodiment 7, and a kind of jade white lighting glass is the SiO by 65kg
2, the B of 0.8kg
2O
3, the Al of 6kg
2O
3, the Na of 10kg
2O, the K of 4.5kg
2O, the CaO of 7kg, the BaO of 2kg, the ZnO of 0.5kg, the F of 4kg
-, the Er of 0.1kg
2O
3, the Nd of 0.1kg
2O
3Mix according to a conventional method to melt and make glass.
Embodiment 8, and a kind of jade white lighting glass is the SiO by 65kg
2, the B of 0.2kg
2O
3, the Al of 2kg
2O
3, the Na of 12kg
2O, the K of 4.5kg
2O, the CaO of 10kg, the BaO of 2kg, the ZnO of 0.1kg, the F of 4kg
-, the Er of 0.1kg
2O
3, the Nd of 0.1kg
2O
3Mix according to a conventional method to melt and make glass.
Embodiment 9, and a kind of jade white lighting glass is the SiO by 65kg
2, the B of 0.1kg
2O
3, the Al of 2kg
2O
3, the Na of 13kg
2O, the K of 4.5kg
2O, the CaO of 9kg, the BaO of 2kg, the ZnO of 0.2kg, the F of 4kg
-, the Er of 0.1kg
2O
3, the Nd of 0.1kg
2O
3Mix according to a conventional method to melt and make glass.
Embodiment 10, and a kind of jade white lighting glass is the SiO by 65kg
2, the B of 1.3kg
2O
3, the Al of 2kg
2O
3, the Na of 14kg
2O, the K of 4.5kg
2O, the CaO of 5kg, the BaO of 2.5kg, the ZnO of 0.6kg, the F of 4kg
-, the Er of 0.1kg
2O
3, the Nd of 1kg
2O
3Mix according to a conventional method to melt and make glass.
Embodiment 11, and a kind of jade white lighting glass is the SiO by 65kg
2, the B of 3kg
2O
3, the Al of 2kg
2O
3, the Na of 10kg
2O, the K of 6.5kg
2O, the CaO of 5kg, the BaO of 2kg, the ZnO of 0.3kg, the F of 6kg
-, the Er of 0.1kg
2O
3, the Nd of 0.1kg
2O
3Mix according to a conventional method to melt and make glass.
Embodiment 12, and a kind of jade white lighting glass is the SiO by 65kg
2, the B of 2kg
2O
3, the Al of 2kg
2O
3, the Na of 10kg
2O, the K of 5.2kg
2O, the CaO of 5kg, the BaO of 2kg, the ZnO of 0.9kg, the F of 7kg
-, the Er of 0.1kg
2O
3, the Nd of 0.8kg
2O
3Mix according to a conventional method to melt and make glass.
Embodiment 13, and a kind of jade white lighting glass is the SiO by 67kg
2, the B of 1.4kg
2O
3, the Al of 2kg
2O
3, the Na of 10kg
2O, the K of 6kg
2O, the CaO of 5kg, the BaO of 2kg, the ZnO of 0.8kg, the F of 5kg
-, the Er of 0.1kg
2O
3, the Nd of 0.7kg
2O
3Mix according to a conventional method to melt and make glass.
Embodiment 14, and a kind of jade white lighting glass is the SiO by 71kg
2, the B of 0.3kg
2O
3, the Al of 2kg
2O
3, the Na of 10kg
2O, the K of 4.5kg
2O, the CaO of 5kg, the BaO of 2kg, the ZnO of 0.7kg, the F of 4kg
-, the Er of 0.1kg
2O
3, the Nd of 0.4kg
2O
3Mix according to a conventional method to melt and make glass.
Embodiment 15, and a kind of jade white lighting glass is the SiO by 68kg
2, the B of 2.2kg
2O
3, the Al of 2kg
2O
3, the Na of 10kg
2O, the K of 4.9kg
2O, the CaO of 5kg, the BaO of 2.8kg, the ZnO of 0.4kg, the F of 4kg
-, the Er of 0.1kg
2O
3, the Nd of 0.6kg
2O
3Mix according to a conventional method to melt and make glass.
Embodiment 16, and a kind of jade white lighting glass is the SiO by 66kg
2, the B of 2.8kg
2O
3, the Al of 2kg
2O
3, the Na of 10kg
2O, the K of 6.2kg
2O, the CaO of 5kg, the BaO of 3kg, the ZnO of 0.6kg, the F of 4kg
-, the Er of 0.1kg
2O
3, the Nd of 0.3kg
2O
3Mix according to a conventional method to melt and make glass.
Claims (2)
1, a kind of jade white lighting glass is characterized in that by mass percent being: SiO
2: 65~72%, B
2O
3: 0~3%, Al
2O
3: 2~6%, Na
2O:10~15%, K
2O:4.5~6.5%, CaO:5~10%, BaO:2~3%, ZnO:0~1%, F
-: 4~8%, Er
2O
3: 0.1~0.8%, Nd
2O
3: 0~1% forms.
2, a kind of jade white lighting glass according to claim 1 is characterized in that by mass percent being: SiO
2: 65~68%, B
2O
3: 0~2.5%, Al
2O
3: 4~5%, Na
2O:10~15%, K
2O:4.5~6.5%, CaO:5~10%, BaO:2~3%, ZnO:0~1%, F
-: 4~8%, Er
2O
3: 0.1~0.8%, Nd
2O
3: 0~1% forms.