CN101565770A - Fluorite powder pressing block and preparation method thereof - Google Patents
Fluorite powder pressing block and preparation method thereof Download PDFInfo
- Publication number
- CN101565770A CN101565770A CNA2009100510179A CN200910051017A CN101565770A CN 101565770 A CN101565770 A CN 101565770A CN A2009100510179 A CNA2009100510179 A CN A2009100510179A CN 200910051017 A CN200910051017 A CN 200910051017A CN 101565770 A CN101565770 A CN 101565770A
- Authority
- CN
- China
- Prior art keywords
- fluorite
- pressing block
- powder pressing
- content
- fluorite powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention particularly relates to a fluorite powder pressing block as well as a preparation method and applications thereof in AOD converter steelmaking. The method for preparing the fluorite powder pressing block is characterized in that the fluorite fine powder, the fluorite powder and a sodium silicate adhesive accounting for 10% of the total weight are added by proportion, mixed uniformly, pressurized, formed and dried. The content of the calcium fluoride in the fluorite fine powder is more than 90%. The weight ratio of the water to silicon dioxide in the sodium silicate adhesive is 1:1. The fluorite powder pressing block and the preparation method have the beneficial effects that the fluorite powder pressing block prepared by the method has the CaF2 with the content of 91.4%, belongs to the specification of 90 degree fluorite and is slightly higher than the fluorite purchase standard (85 degree) of the stainless steel smelting plant; furthermore, the content of the SiO2 is only 4.00% and is lower about 8.0% than the normal fluorite content; and according to 30 batches of site tests of steelmaking AOD furnace, compared results of fluorite powder pressing block with the normal fluorite results, the fluorite powder pressing block is slightly better than the normal fluorite and the usage amount is lowered, which indicates that the fluorite powder pressing block completely meets the stainless steel smelting requirement of the AOD furnace.
Description
Technical field
The invention belongs to the STEELMAKING PRODUCTION technical field, be specifically related to a kind of fluorite powder pressing block and preparation method thereof and the application in the AOD converter steelmaking.
Background technology
Fluorite has important application in Steel industry is produced, as adding natural fluorite in the STEELMAKING PRODUCTION, can reduce fusing point, the dissolving of acceleration lime of lime, improve the flowability of basic slag, improve desulfurization, dephosphorization efficient simultaneously, strengthen the interface reflection ability between the slag steel, play help, flux, fluxing effect.But owing to exploit for a long time, need the natural fluorite of higher-grade of usefulness in the steel-making, quite in short supply on the market, mine resources is overexploitation, and turnout can not satisfy the smelting industry needs; And a large amount of low-grade fluorites ore deposit can't be used again in STEELMAKING PRODUCTION, causes a large amount of low-grade fluorite ore resources wastes.
Summary of the invention
The objective of the invention is: substitute---fluorite powder pressing block and preparation method thereof that the natural fluorite of using in a kind of Steel industry of higher-grade is provided.
For achieving the above object, the technical scheme of employing is: the preparation method of fluorite powder pressing block is characterized in that: add the smart powder of fluorite, fluorite powder by proportioning, and the bubble flower alkali tackiness agent that accounts for gross weight 10%, stir, extrusion forming, oven dry.
The content of Calcium Fluoride (Fluorspan) reaches more than 90% in the smart powder of described fluorite.
The weight ratio of water and silicon-dioxide is 1: 1 in the described bubble flower alkali tackiness agent.
The invention has the beneficial effects as follows: by the fluorite powder pressing block that present method makes, CaF
2Content is high and stable, reaches 90 ° of fluorite specifications, a little more than stainless steel smelting factory fluorite buying standard (85 °), and SiO
2Content only 4.00%, about 8% level of more common fluorite is low.The test of AOD smelting furnace 30 heats shows that fluorite powder pressing block meets the requirement of AOD stove smelting stainless steel fully.
Embodiment
Embodiment 1
Add in the container and fluoridize the smart powder 93.24kg of calcium contents 97% fluorite, Calcium Fluoride (Fluorspan) content 60% fluorite powder 6.8kg, bubble flower alkali tamanori 10kg YJ150 disk stirrer stirring 15min, ZZXM-4 four roller secondary adding pressure type ball press compression mouldings, it is spherical to be 50-60mm, at temperature 180-200 ℃ of oven dry 1h, make fluorite powder pressing block CaF
2Content reaches more than 90%.
Embodiment 2
Add the smart powder 64.87kg of fluorite of Calcium Fluoride (Fluorspan) content 97%, the fluorite powder 35.13kg and the bubble flower alkali tamanori 10kg of Calcium Fluoride (Fluorspan) content 60% in the container, by embodiment 1 identical method stir, extrusion forming, oven dry, make fluorite powder pressing block CaF
2Content is more than 80%.
Described bubble flower alkali tamanori composition is water 50%, silicon-dioxide 50%.
Because natural fluorite quality fluctuation, it is unstable to cause stainless steel to be produced, and the content of Calcium Fluoride (Fluorspan) can require preparation as required according to client's difference in the fluorite powder pressing block.The fluorite powder pressing block that makes as stated above on probation in the stainless steel AOD converter, fluorite powder pressing block composition (weight %) analytical results on probation is: CaF
291.40%; S 0.157%; P 0.012%; SiO
24.00%.Through smelting AOD stove 30 heat test in places, steel grade is austenite and ferrite, facts have proved that using behind the fluorite powder pressing block AOD stove to smelt relevant index all slightly is better than using common fluorite.30 heat terminal point compositions all hit, and terminal point sulphur composition can reach 0.001%, and fluorite powder pressing block meets the requirement of AOD stove smelting stainless steel.
Claims (3)
1. the preparation method of a fluorite powder pressing block is characterized in that: add the smart powder of fluorite, fluorite powder by proportioning, and the bubble flower alkali tackiness agent that accounts for gross weight 10%, stir, extrusion forming, oven dry.
2. according to the preparation method of the described a kind of fluorite powder pressing block of claim 1, it is characterized in that: the content of Calcium Fluoride (Fluorspan) reaches more than 90% in the smart powder of described fluorite.
3. according to the preparation method of the described a kind of fluorite powder pressing block of claim 1, it is characterized in that: the weight ratio of water and silicon-dioxide is 1: 1 in the described bubble flower alkali tackiness agent.