CN101555536B - 一种冶炼低锰生铁的生产工艺 - Google Patents

一种冶炼低锰生铁的生产工艺 Download PDF

Info

Publication number
CN101555536B
CN101555536B CN2009101361114A CN200910136111A CN101555536B CN 101555536 B CN101555536 B CN 101555536B CN 2009101361114 A CN2009101361114 A CN 2009101361114A CN 200910136111 A CN200910136111 A CN 200910136111A CN 101555536 B CN101555536 B CN 101555536B
Authority
CN
China
Prior art keywords
percent
manganese
cao
pig iron
iron
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN2009101361114A
Other languages
English (en)
Other versions
CN101555536A (zh
Inventor
渠天盛
成国光
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Baotou Shenrun High New Material Co ltd
Original Assignee
BAOTOU SHENRUN ADVANCED MATERIALS Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by BAOTOU SHENRUN ADVANCED MATERIALS Co Ltd filed Critical BAOTOU SHENRUN ADVANCED MATERIALS Co Ltd
Priority to CN2009101361114A priority Critical patent/CN101555536B/zh
Publication of CN101555536A publication Critical patent/CN101555536A/zh
Application granted granted Critical
Publication of CN101555536B publication Critical patent/CN101555536B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种冶炼低锰生铁的生产工艺，在熔炼装置中以生铁为主要原料，在熔炼过程中向铁水中吹入氧气，在吹炼的过程中逐步加入含有下列成分的造渣剂、CaO、SiO2、CaF2、MgO，使合成造渣剂碱度为：B(％CaO/％SiO2)0.35～1.0；使合成造渣剂成分满足下列重量百分比：(CaO+SiO2)43～97％，(FeO+MnO)0～30％，CaF2 3～15％，MgO 0～8％，其它残余成分总和0～4％；冶炼温度为1280～1350℃，吹炼时间为25～35min。本发明可以利用较低的冶炼成本将高锰铁水中的锰脱除到0.02％以下，脱锰率达到85％以上。满足汽车、风力发电等行业对其性能优异的球墨铸铁提出的严格要求。

Description

一种冶炼低锰生铁的生产工艺
技术领域
本发明涉及钢铁冶金生产工艺领域，尤其涉及到一种低锰生铁的冶金新工艺。
背景技术
随着我国汽车、风力发电等行业的迅猛发展，对其所用铸件的强度、延伸率、韧性及耐磨性等提出了越来越严格的要求。这些铸件主要是性能优异的球墨铸铁(以下简称：球铁)。国内外研究表明：要获得优良的球铁使用性能，严格控制其杂质元素中锰含量非常重要。高纯度球铁中要求锰含量低于0.05％，甚至要求达到0.02％以下。
我国铁矿石资源种类多、成分复杂，其中许多铁矿中含有较高的锰含量，因此导致铁液中锰含量较高，有的铁液中锰含量达到0.4％以上。
文献(闫晓峰：氧化法超纯生铁的生产工艺，专利公开号CN101157962A)提出了一种氧化法生产高纯生铁工艺。其冶炼工艺以高炉炼铁和转炉吹炼为主，生产出杂质元素很低的高纯生铁，可以将铁水中锰含量从初始的(0.04～0.10)％降低到0.021％以下。但该专利中没有提及当铁液中初始锰含量大于0.1％时的转炉脱锰效果。
发明内容
本发明的目的在于针对上述现有的技术问题提供一种冶炼低锰生铁的生产工艺。在熔炼装置中以生铁为主要原料，在熔炼过程中向铁液中吹入氧气，在吹炼的过程中逐步加入含有下列原料的造渣剂：CaO、SiO2、CaF2、MgO，使合成造渣剂碱度为：B(％CaO/％SiO2)0.35～1.0；使合成造渣剂成分满足下列重量百分比：(CaO+SiO2)43～97％，(FeO+MnO)0～30％，CaF2 3～15％，MgO 0～8％，其它残余成分总和0～4％；冶炼温度为1280～1350℃，吹炼时间为25～35min。
本发明可以继续转入下道工序再进行脱磷、脱硫等其它操作。
本发明：(1)通过向感应炉(也可是电弧炉、铁水罐)中吹入氧气，起到同时脱硅、脱锰的目的，减少了对高炉铁水预脱硅工序，简化了流程。(2)脱硅所生成的(SiO2)在炉渣中起到了稳定(MnO)作用，有利于铁水脱锰。(3)由于在吹炼过程中硅、锰等元素的氧化会放出较多化学热，这部分热恰好可以用来加热和熔化冶炼过程所添加的造渣剂，使得热量得到了有效利用。(4)可以将高锰铁水(锰含量达到0.4％以上)脱除到0.02％以下，脱锰率达到85％以上(脱锰率＝(初始锰含量-终点锰含量)/初始锰含量×100％)。(5)工序紧凑，冶炼成本低。
本发明的脱锰工艺原理为：当铁液中吹入氧气时，铁液中硅、锰和氧结合生成(MnO)和(SiO2)，这些氧化物上浮到铁液表面成为熔渣。众所周知，(MnO)是碱性氧化物，而渣中的脱硅产物(SiO2)是强酸性氧化物，因此，渣中一定量的(SiO2)有利于渣中(MnO)的稳定存在，有利于铁液深度脱锰。但仅仅依靠铁液中生成的(SiO2)、(MnO)来调节炉渣成分是远远不够的，主要原因是渣中(SiO2)的生成量是由铁液中硅含量来决定，如果渣中(SiO2)量太高，炉渣粘度显著增加，不利于脱锰生成的(MnO)均匀进入渣相，反之，如果(SiO2)太低，就会使得炉渣中(MnO)稳定性降低，不利于铁液中锰含量的进一步降低。为此，为铁液快速脱锰，需要对炉渣成分进行严格控制。添加CaO、CaF2可以调节炉渣的流动性和碱度；由于(MgO)会显著增加炉渣粘度，所以炉渣中(MgO)不能超过8％；渣中(MnO)过高，会明显增加渣中(MnO)的不稳定性，对脱锰不利；同时，在吹炼过程中会导致部分金属铁的氧化，生成(FeO)进入炉渣，渣中过高的(FeO)表明铁液金属烧损严重，降低了金属收得率。
附图说明
图1是本发明实施例中不同炉渣成分对脱锰效果的影响图
具体实施方式
下面通过实施例进一步描述本发明。
选定10公斤感应炉为熔炼装置，以低磷、低硫生铁为原料，并用添加合金的办法来调节铁液中硅含量为0.5～0.8％，锰含量0.40～0.55％。然后用氧枪从感应炉上部向铁液中吹入氧气，在吹炼过程中逐步加入成分含有CaO、SiO2、CaF2、MgO的造渣剂，控制冶炼温度1280至1350℃，吹炼时间25至35min。表1为不同的炉渣成分对脱锰效果的影响，并进一步用图1表示。从表1和图1中的对比实验结果可以看出，当炉渣碱度控制在本发明的成分范围，可以获得85％以上的脱锰率，最低锰含量可以脱除到0.02％。
表1  采用不同炉渣成分工艺对脱锰效果的对比结果
Figure GSB00000364423000031

Claims (1)

1.一种冶炼低锰生铁的生产工艺，其特征在于，在熔炼装置中以生铁为主要原料，在熔炼过程中向铁水中吹入氧气，在吹炼的过程中逐步加入含有下列原料的造渣剂：CaO、SiO2、CaF2、MgO，使合成造渣剂碱度为：％CaO/％SiO20.35～1.0；使合成造渣剂成分满足下列重量百分比：CaO+SiO2 43～97％，FeO+MnO 0～30％，CaF2 3～15％，MgO 0～8％，其它残余成分总和0～4％；冶炼温度为1280～1350℃，吹炼时间为25～35min。
CN2009101361114A 2009-04-30 2009-04-30 一种冶炼低锰生铁的生产工艺 Expired - Fee Related CN101555536B (zh)