CN101550752A - External wall decorative material and technique for producing the same - Google Patents
External wall decorative material and technique for producing the same Download PDFInfo
- Publication number
- CN101550752A CN101550752A CNA2009101365774A CN200910136577A CN101550752A CN 101550752 A CN101550752 A CN 101550752A CN A2009101365774 A CNA2009101365774 A CN A2009101365774A CN 200910136577 A CN200910136577 A CN 200910136577A CN 101550752 A CN101550752 A CN 101550752A
- Authority
- CN
- China
- Prior art keywords
- parts
- decorative material
- external wall
- wall decorative
- waste
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to decorative material, especially to external wall decorative material and a technique for producing the same, comprising: 100 parts of waste PVC powder; 150-200 parts of waste tail sand; and 8-12 parts of additive. The production technique comprises: mixing raw material based on recipe demand, after extrusion of the mixture by an extruding machine, cooling and forming by a vacuum forming die, cutting into floor blank after dragging, processing and surface coating, and forming finished goods. The main componnets of the decorative material of the invention are waste PVC powder, mineral powder and a certain amount of additive, and the decorative material is fromed by plasticization and extrusion molding, and has light specific gravity and low price; because of addition of ultraviolet light absorber, service life of the products is greatly enlonged; because of extrusion molding, color adjustable products of different surface forms can be produced, the products have strong three-dimensional apparence, are suitable for plastering and hanging, has strong combination with the wall and eliminates unsafe hidden trouble; waste material and waste sheet material processed by the products of the invention can be recoverably utilized and implement pollution-free discharge.
Description
Technical field:
The present invention relates to ornament materials, especially a kind of external wall decorative material and production technology thereof.
Background technology:
At present, external wall decorative material mostly is ceramic tile, marble and aluminum-pinch, and ceramic tile, marble are because weight is bigger, and there is serious potential safety hazard in outer the decoration, and the aluminum-pinch price is higher, and a large amount of the use is subjected to certain restriction.
Summary of the invention:
The present invention is intended to solve defective and the deficiency that present external wall decorative material exists, and provide CHARACTERISTICS OF TAILINGS SAND that a kind of utilization causes environment pollution and the useless PVC powder of trade waste to make, have the texture of enriching and color and luster, easy for installation, cheap, long-lived external wall decorative material and production technology thereof.
The technical scheme that the present invention addresses the above problem employing is:
A kind of external wall decorative material, make by following materials based on weight:
(1) useless PVC powder is 100 parts;
(2) useless CHARACTERISTICS OF TAILINGS SAND 150-200 part;
(3) auxiliary agent 8-12 part.
In the described CHARACTERISTICS OF TAILINGS SAND,, contain: the iron of 50-60 part silica, 2-3 part alundum (Al, 3.5-4 part manganese oxide, 3-3.5 part magnesia, 5.5-6 part, the sulphur and the phosphorus of trace in parts by weight.
Described auxiliary agent is made up of following materials based on weight: 0.8 part in plasticizing agent, 3.8 parts of heat stabilizers, 1 part of sliding agent, 1.2 parts of fire retardants, 0.5 part of stearic acid, 2.1 parts of ultra-violet absorbers.
The production technology of above-mentioned external wall decorative material, its step is as follows:
(1) presses the composition of raw materials batching;
(2) by behind useless PVC powder for preparing and the useless CHARACTERISTICS OF TAILINGS SAND adding batch mixer, carry out low-speed running, and add heat stabilizer, batch mixer is mentioned at a high speed;
(3), add plasticizing agent and fire retardant, stearic acid below 60 ℃;
(4) adding sliding agent, ultra-violet absorber below 75 ℃;
(5) in the time of 135 ℃, material put into discharging after 35 ℃ of the cold mixer coolings;
(6) extruder is preheated to starts main frame and material loading after the set point of temperature, adjust and determine technological parameter: 178 ℃ in a. barrel temperature one district, 182 ℃ in two districts, 188 ℃ in three districts, 189 ℃ in four districts; B. the merging core temperature is 180 ℃; C. die temperature is 190 ℃; D. engine speed 8.2r/min; E. feeding rotating speed 13.6r/min;
(7) sheet material by Vacuum shaping mould cooling and shaping, cuts into blank after the traction again after the extruder die cavity is extruded, and cooling water should be controlled at 25 ℃.
Compared with prior art, outstanding feature of the present invention is:
(1) Main Ingredients and Appearance of the present invention is useless PVC powder and breeze, and other adds a certain amount of auxiliary agent, through the plasticizing extrusion modling, and light specific gravity, price is honest and clean.
(2) the present invention is owing to added ultra-violet absorber, the application life of having improved product greatly in prescription.
(3) owing to adopt extrusion molding, can produce the product of different surfaces shape, color tunable, three-dimensional sense organ is strong, the back side applicable to paste, card hangs, and combines byer force with body of wall, eliminated hidden danger.
(4) waste material of product processing of the present invention and the discarded recyclable utilization of sheet material, non-pollution discharge.
The specific embodiment:
Below in conjunction with implementing cancer in detail the present invention is described in detail.
The external wall decorative material that present embodiment provides, make by following materials based on weight:
(1) useless PVC powder is 100 parts;
(2) useless CHARACTERISTICS OF TAILINGS SAND is 150 parts;
(3) auxiliary agent is 9.4 parts, and wherein plasticizing agent is 0.8 part, 3.8 parts of heat stabilizers, 1 part of sliding agent, 1.2 parts of fire retardants, 0.5 part of stearic acid, 2.1 parts of ultra-violet absorbers.
In the described CHARACTERISTICS OF TAILINGS SAND, in parts by weight, the iron that contains 50-60 part silica, 2-3 part alundum (Al, 3.5-4 part manganese oxide, 3-3.5 part magnesia, 5.5-6 part, the sulphur and the phosphorus of trace, the addition of useless CHARACTERISTICS OF TAILINGS SAND should be controlled within the limits prescribed, too high levels, difficult forming, low excessively, base material hardness is lower, and it is ground to 400-600 order powder with micropowder grinding, this routine addition is 150 parts.
Described useless PVC powder is a waste polyvinyl chloride, and to the 60-100 order, because of useless PVC opaque amount fluctuation is bigger, so should come resize ratio according to the quality of useless PVC opaque amount, the addition of useless PVC powder is 100 parts in this example through abrasive dust.
Described plasticizing agent is POP, and heat stabilizer is JX-03S-5, and sliding agent is a paraffin, and fire retardant is TBBPA, and stearic acid is 1801, and ultra-violet absorber is UV-531.
The production technology of above-mentioned external wall decorative material, carry out as follows:
(1) presses the composition of raw materials batching;
(2) by behind useless PVC powder for preparing and the useless CHARACTERISTICS OF TAILINGS SAND adding batch mixer, carry out low-speed running, and add heat stabilizer, batch mixer is mentioned at a high speed;
(3), add plasticizing agent and fire retardant, stearic acid below 60 ℃;
(4) adding sliding agent, ultra-violet absorber below 75 ℃;
(5) in the time of 135 ℃, material put into discharging after 35 ℃ of the cold mixer coolings;
(6) extruder is preheated to starts main frame and material loading after the set point of temperature, adjust and determine technological parameter: 178 ℃ in a. barrel temperature one district, 182 ℃ in two districts, 188 ℃ in three districts, 189 ℃ in four districts.B. the merging core temperature is 180 ℃.C. die temperature is 190 ℃.D. engine speed 8.2r/min.E. feeding rotating speed 13.6r/min.
(7) sheet material by Vacuum shaping mould cooling and shaping, cuts into blank after the traction again after the extruder die cavity is extruded, and cooling water should be controlled at 25 ℃.
Above-mentioned external wall decorative material, according to the GB/T18103-2003 evaluation criteria, its testing result such as following table:
Testing result
Claims (4)
1, a kind of external wall decorative material, make by following materials based on weight:
(1) useless PVC powder is 100 parts;
(2) useless CHARACTERISTICS OF TAILINGS SAND 150-200 part;
(3) auxiliary agent 8-12 part.
2, external wall decorative material according to claim 1, it is characterized in that, in the described CHARACTERISTICS OF TAILINGS SAND, in parts by weight, contain: the iron of 50-60 part silica, 2-3 part alundum (Al, 3.5-4 part manganese oxide, 3-3.5 part magnesia, 5.5-6 part, the sulphur and the phosphorus of trace.
3, external wall decorative material according to claim 1 is characterized in that, described auxiliary agent is made up of following materials based on weight: 0.8 part in plasticizing agent, 3.8 parts of heat stabilizers, 1 part of sliding agent, 1.2 parts of fire retardants, 0.5 part of stearic acid, 2.1 parts of ultra-violet absorbers.
4, a kind of production technology by the described external wall decorative material of claim 1, its step is as follows:
(1) presses the composition of raw materials batching;
(2) by behind useless PVC powder for preparing and the useless CHARACTERISTICS OF TAILINGS SAND adding batch mixer, carry out low-speed running, and add heat stabilizer, batch mixer is mentioned at a high speed;
(3), add plasticizing agent and fire retardant, stearic acid below 60 ℃;
(4) adding sliding agent, ultra-violet absorber below 75 ℃;
(5) in the time of 135 ℃, material put into discharging after 35 ℃ of the cold mixer coolings;
(6) extruder is preheated to starts main frame and material loading after the set point of temperature, adjust and determine technological parameter: 178 ℃ in a. barrel temperature one district, 182 ℃ in two districts, 188 ℃ in three districts, 189 ℃ in four districts; B. the merging core temperature is 180 ℃; C. die temperature is 190 ℃; D. engine speed 8.2r/min; E. feeding rotating speed 13.6r/min;
(7) sheet material by Vacuum shaping mould cooling and shaping, cuts into blank after the traction again after the extruder die cavity is extruded, and cooling water should be controlled at 25 ℃.