CN101531736A - Synthetic styrene-acrylic latex - Google Patents
Synthetic styrene-acrylic latex Download PDFInfo
- Publication number
- CN101531736A CN101531736A CN200910119369A CN200910119369A CN101531736A CN 101531736 A CN101531736 A CN 101531736A CN 200910119369 A CN200910119369 A CN 200910119369A CN 200910119369 A CN200910119369 A CN 200910119369A CN 101531736 A CN101531736 A CN 101531736A
- Authority
- CN
- China
- Prior art keywords
- emulsion
- monomer
- water
- acrylic latex
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses synthetic styrene-acrylic latex, which includes components by weight: 2-4 parts of crylic acid, 5-8 parts of iso-octyl acrylate, 10-15 parts of styrene, 6-9 parts of butyl acrylate, 0.4-0.8 part of emulsifying agent, 0.1-0.4 part of ammonium persulfate and 65-80 parts of ionic water. Because soft monomer and hard monomer proportion MAA:St:BA is 36:25:36, the obtained emulsion has high hardness, and good anti-aging performance, when amount of seed emulsion is 10-12%, comprehensive properties of the obtained emulsion are best, and proper amount of carboxyl functional monomer is added to significantly improve polymerization stability of the emulsion, calcium ionic stability, emulsion viscosity and film water absorption rate.
Description
Technical field
The present invention relates to a kind of emulsion coatings, particularly relate to a kind of synthetic styrene-acrylic latex.
Background technology
Acrylic polymer becomes the outstanding person with its superior film-forming properties, good oil-proofness and weathering resistance, good cementability in numerous polymer emulsion products.Introduce the cinnamic acrylic emulsion system of hard monomer, abbreviate the benzene emulsion as, have higher weathering resistance, tint retention, pollution resistance etc.Benzene emulsion is mainly as aspects such as building coating, paper making and cloth coating tackiness agent.As tackiness agent, its hardness height, water-tolerant.In addition, it also can be widely used as floor polisher, sand texture coating, concavo-convex priming paint etc.Along with the progress of nucleocapsid technology, interpenetrating polymer networks and emulsifier-free emulsion polymerization, will be more extensive also to the research of benzene emulsion purposes.
In recent years the consumption market of global benzene emulsion is in steady-state growth, and is wherein especially very fast with developing country's demand growth such as Asia and South America.China will be because rapid development of economy will keep the situation of growth to the demand of coating such as benzene emulsion, and new achievement in research will give benzene emulsion more commercial viability.The production of China's benzene emulsion at present disperses very much, and the competition between medium-sized and small enterprises is also very fierce, and the large enterprises with scale grow up, and quality product is very different, and main drawback is water resisting property difference and easily yellowing, and next amount of being to use is bigger than normal.
The gordian technique that the synthetic styrene-acrylic emulsion substitutes styrene-butadiene emulsion is the challenge of performances such as hardness of film and weathering resistance, and this is the target that the ordinary emulsion product is difficult to realize.
Summary of the invention
The object of the present invention is to provide a kind of stability better, be difficult for that brightness reversion, fine size viscosity are low, good fluidity, do not produce the synthetic styrene-acrylic latex of oil mark.
For achieving the above object, technical solution of the present invention is:
The present invention is a kind of synthetic styrene-acrylic latex, and its raw material component concentration by weight is:
Monomer: methacrylic acid (MAA) 2 ~ 4
Isooctyl acrylate monomer 5 ~ 8
Vinylbenzene (St) 10 ~ 15
Butyl acrylate (BA) 6 ~ 9
Emulsifying agent: alkylphenol-polyethenoxy (10) ether (OP-10) 0.4 ~ 0.8
Initiator: ammonium persulphate 0.1 ~ 0.4
Water: ionized water 65 ~ 80.
Described synthetic styrene-acrylic latex, its raw material also comprises following component, is weight part:
Witco 1298 Soft Acid 0.1 ~ 0.5
Acrylamide 0.4 ~ 0.8
Diethanolamine 0.4 ~ 0.8
N-hydroxypropyl solution 0.3 ~ 0.7.
After adopting such scheme, because the present invention takes following measure:
(1) the soft or hard monomer ratio is MAA: St: BA=36: 25: 36, and gained emulsion hardness height, ageing resistance is good.
When (2) consumption of seed emulsion was 10%-12%, gained emulsion over-all properties was best.
(3) add the carboxyl function monomer obviously to the viscosity of the polymerization stability of emulsion, Calcium ion stability, emulsion and the water-intake rate influence of filming.The consumption of functional groups is controlled in 4%, and adds the emulsion property that can obtain optimum in the later stage of polyreaction.
So the present invention has the following advantages:
(1) processing White Board styrene-butadiene latex bonding strength height commonly used, water-tolerant, low price, but the easy yellowing of with the passing of time filming, stability of emulsion is poor; And styrene-acrylic latex is stablized ageing-resistant, nondiscoloration, gained White Board glossiness, smoothness height;
(2) at the bottom of the fine size viscosity, good fluidity, do not produce oil mark.With other tackiness agent relatively have foaming less, advantage that corruption is few, and price comparison is cheap.
(3) the coating fluid strong adhesion that is mixed and made into mutually of styrene-acrylic latex and pigment, mineral filler and other additives, coating do not come off, dry linting not; Rate of descent in the coating fluid 4h of preparation≤5% is easy to construction; In the high-speed coating course of processing, coating fluid is through shearing test repeatedly, has not breakdown of emulsion, do not send out and rise, do not lump, and mechanical workout adaptability is characteristics preferably; In certain temperature (5~50 ℃) scope, viscosity changes little, is applicable to prepare the latex coating liquid that satisfies the process for processing of different type of machines White Board.
The invention provides dual cross-linked core-shell structure emulsion system, this system is the new type structure of hud product of little crosslinked, the housing room temperature external crosslinking of a kind of nucleome.Form structural performance by adjusting the little crosslinking degree of nucleome, nucleocapsid dimension scale, changing, further enhance product performance, especially hardness of film.It has established solid more theory widely and application foundation for the series emulsion coating products of colonizing properties excellence.
The present invention is further illustrated below in conjunction with the drawings and specific embodiments.
Description of drawings
Fig. 1 is preparation flow figure of the present invention.
Embodiment
One, prescription:
Below be the several embodiment of synthetic styrene-acrylic latex of the present invention, but the present invention is not limited thereto.
Embodiment 1:
A kind of synthetic styrene-acrylic latex, its raw material component concentration by weight is:
Methacrylic acid 2
Isooctyl acrylate monomer 5
Vinylbenzene 10
Butyl acrylate 6
Alkylphenol-polyethenoxy (10) ether 0.4
Ammonium persulphate 0.1
Ionized water 65.
Witco 1298 Soft Acid 0.1
Acrylamide 0.4
Diethanolamine 0.4
N-hydroxypropyl solution 0.3.
Embodiment 2:
A kind of synthetic styrene-acrylic latex, its raw material component concentration by weight is:
Vinylformic acid 4
Isooctyl acrylate monomer 8
Vinylbenzene 15
Butyl acrylate 9
. alkylphenol-polyethenoxy (10) ether 0.8
Ammonium persulphate 0.4
Ionized water 80
Witco 1298 Soft Acid 0.5
Acrylamide 0.8
Diethanolamine 0.8
N-hydroxypropyl solution 0.7.
Embodiment 3:
A kind of synthetic styrene-acrylic latex, its raw material component concentration by weight is:
Vinylformic acid 3
Isooctyl acrylate monomer 6
Vinylbenzene 13
Butyl acrylate 7
Alkylphenol-polyethenoxy (10) ether 0.6
Ammonium persulphate 0.3
Ionized water 70
Witco 1298 Soft Acid 0.3
Acrylamide 0.6
Diethanolamine 0.6
N-hydroxypropyl solution 0.5.
Embodiment 4:
A kind of synthetic styrene-acrylic latex, its raw material component concentration by weight is:
Vinylformic acid 3
Isooctyl acrylate monomer 6
Vinylbenzene 12
Butyl acrylate 7
Alkylphenol-polyethenoxy (10) ether 0.5
Ionized water 75.
Embodiment 5:
A kind of synthetic styrene-acrylic latex, its raw material component concentration by weight is:
Methacrylic acid 3
Isooctyl acrylate monomer 7
Vinylbenzene 14
Butyl acrylate 8
Ionized water 72.
Two, preparation method:
The preparation method of synthetic styrene-acrylic latex, its preparation process is as follows:
(1) earlier the pre-emulsification under the greenhouse of monomer, partial emulsifier and water is made pre-emulsion, the four-hole boiling flask that agitator, reflux condensing tube etc. will be housed then places the water-bath of temperature control unit;
(2) an amount of initiator, sodium bicarbonate and water are placed reactor, be warming up to 80 ℃-90 ℃, get the part pre-emulsion as seed, slowly be added drop-wise in the reactor, treat that emulsion is blue phase, insulation 15min obtains seed emulsion;
(3) drip remaining pre-emulsified monomer, initiator solution then simultaneously, be controlled in the 4h and drip off;
(4) drip off after, be warming up to 80 ℃-90 ℃, insulation is lowered the temperature behind the 1h, the pH value of regulating emulsion with ammoniacal liquor is 7-8, filters discharging.
Three, performance test:
Solid content is with reference to GB1725-79 standard; Hardness of film is with reference to GB/T1730-93 standard; Sticking power is with reference to GB1720-79 standard; The emulsion package stability; Whether emulsion in 50 ℃ constant temperature oven, observing emulsion has layering or demulsifying phenomenon if being placed 7d; Calcium ion stability; Get the 20g emulsion, add 10%CaCl
2Aqueous solution 20g shakes all, and whether place 24h observation emulsion has layering or demulsifying phenomenon; Water tolerance is with reference to GB1733-93 standard; Water-intake rate: with reference to HG/T2-1612-85 standard.Emulsion and the main performance index of filming are as shown in table 1.
Table 1. emulsion and the salient features of filming
The test item test result
Outward appearance milky white, semi-transparent, band blue light
Solid content % 43.2
PH value 3 ~ 6
Viscosity/(mPas) 10 ~ 100
Calcium ion stability does not have flocculation
Particle diameter/nm 54.5
Package stability is good
Water-intake rate/% 0.08
Hardness 0.73
Sticking power/level 1 ~ 2
Monomer conversion/%〉98
Claims (3)
1, a kind of synthetic styrene-acrylic latex is characterized in that: its raw material component concentration by weight is:
Monomer: methacrylic acid 2 ~ 4
Isooctyl acrylate monomer 5 ~ 8
Vinylbenzene 10 ~ 15
Butyl acrylate 6 ~ 9
Emulsifying agent: alkylphenol-polyethenoxy (10) ether 0.4 ~ 0.8
Initiator: ammonium persulphate 0.1 ~ 0.4
Water: ionized water 65 ~ 80.
2, synthetic styrene-acrylic latex according to claim 1 is characterized in that: its raw material also comprises following component, is weight part:
Witco 1298 Soft Acid 0.1 ~ 0.5
Acrylamide 0.4 ~ 0.8
Diethanolamine 0.4 ~ 0.8
N-hydroxypropyl solution 0.3 ~ 0.7.
3, the preparation method of synthetic styrene-acrylic latex according to claim 1, it is characterized in that: its preparation process is as follows: (1) makes pre-emulsion with the pre-emulsification under the greenhouse of monomer, partial emulsifier and water earlier, and the four-hole boiling flask that agitator, reflux condensing tube etc. will be housed then places the water-bath of temperature control unit; (2) an amount of initiator, N-hydroxypropyl solution and water are placed reactor, be warming up to 80 ℃-90 ℃, get the part pre-emulsion as seed, slowly be added drop-wise in the reactor, treat that emulsion is blue phase, insulation 15min obtains seed emulsion; (3) drip remaining pre-emulsified monomer, initiator solution then simultaneously, be controlled in the 4h and drip off; (4) drip off after, be warming up to 80 ℃-90 ℃, insulation is lowered the temperature behind the 1h, the pH value of regulating emulsion with ammoniacal liquor is 7-8, filters discharging.