CN101508805A - Electrostatic resistant polythene mining tube mother material and preparation method thereof - Google Patents
Electrostatic resistant polythene mining tube mother material and preparation method thereof Download PDFInfo
- Publication number
- CN101508805A CN101508805A CNA2009103009346A CN200910300934A CN101508805A CN 101508805 A CN101508805 A CN 101508805A CN A2009103009346 A CNA2009103009346 A CN A2009103009346A CN 200910300934 A CN200910300934 A CN 200910300934A CN 101508805 A CN101508805 A CN 101508805A
- Authority
- CN
- China
- Prior art keywords
- mining
- polyethylene
- mother material
- tube mother
- electrostatic resistant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an antistatic polyethylene mining pipe parent stock and a preparation method thereof. The stock is prepared by the raw materials with the following weight portions: 90 to 110 portions of polyethylene, 5 to 20 portions of metal particles, 5 to 30 portions of flame retardant, 1 to 8 portions of stabilizer, 0.5 to 3 portions of surfactant and 4 to 20 portions of carbon black. By adding metal particles in the antistatic polyethylene mining pipe parent stock, the invention can decrease the resistance of antistatic polyethylene mining pipe parent stock and thus decreasing the static rate of polyethylene mining tubular parent stock. According to the experimental detection, adding metal particles into polyethylene can decrease the resistance of antistatic polyethylene mining pipe parent stock to below 50 omega, far lower than the resistance of prior antistatic polyethylene mining pipe parent stock added with antistatic material. The amount of added metal particles is 5 to 20, thus not only guaranteeing the antistatic performance of polyethylene pipe but also little affecting the toughness, strength and corrosion resistance of polyethylene pipe.
Description
Technical field
The present invention relates to a kind of antistatic master batch, particularly a kind of electrostatic resistant polythene mining tube mother material and preparation method thereof.
Background technology
Material alkene IXI is easy to generate the critical defect that spark, easy-to-rust, quality heavily wait because of there is collision in metal tube, and present mining pipe is all being changed to plastics tubing substantially.But plastics tubing in use easily produces static, has so just restricted the use range of plastics tubing greatly, in the hole, ore deposit, easily produces electrostatic plastics tubing very easily initiation fire or gas explosion especially.The making method of existing antistatic plastic pipe adopts in base-material more is added various antistatic materials and solves, and as carbon black etc., but in actual applications, the resistance of pipeline is still higher, and antistatic effect still is not very desirable, can't satisfy the requirement of mining pipe.
Summary of the invention
The technical problem to be solved in the present invention is, good electrostatic resistant polythene mining tube mother material of a kind of antistatic effect and preparation method thereof is provided, and can overcome the deficiencies in the prior art.
Technical scheme of the present invention is: it is to be made by following quality proportion raw material:
90~110 parts of polyethylene, 5~20 parts of metallic particles, 5~30 parts of fire retardants, 1~8 part of stablizer, 0.5~3 part in tensio-active agent, 4~20 parts of carbon blacks.
Described metallic particles is shot copper or aluminum shot.
Described fire retardant is aluminium hydroxide, antimonous oxide or magnesium hydroxide.
Described stablizer is antioxidant 1010, oxidation inhibitor 168 or antioxidant 2246 etc.
Described tensio-active agent is a silane coupling agent.
It is that metallic particles is carried out surface-active-treatment with tensio-active agent; metallic particles after will handling then and other do not drop into high-speed mixer with raw material by the quality proportioning; under 70~100 ℃ temperature, mix, obtain electrostatic resistant polythene mining tube mother material by the dual-screw pelletizer granulation at last through high-speed mixer.
Be case problem HU compared with the prior art, the present invention is by adding metallic particles in electrostatic resistant polythene mining tube mother material, so just can reduce the resistance of electrostatic resistant polythene mining tube mother material, test detection factually and in polyethylene, add the resistance that metallic particles can make electrostatic resistant polythene mining tube mother material and be reduced to below 50 Ω, far below the existing resistance that is added with the electrostatic resistant polythene mining tube mother material of antistatic material.The amount that metallic particles adds is 5~20, can guarantee the static resistance of electrostatic resistant polythene mining tube mother material like this, also can be very not big to the toughness of polythene mining tube, intensity and performance impact such as anticorrosive.
Following table is some contrast tables of electrostatic resistant polythene mining tube mother material of the present invention and industry quality index,
Sequence number | Project | Testing method | Unit | Quality index | Detected result |
1 | Outward appearance | Range estimation | The black even particle | The black even particle | |
2 | Density | GB/T1033 | g/cm 3 | 1.05-1.1 | 1.08 |
3 | Embrittlement temperature | GB/T5470 | ℃ | ≤-60 | -66 |
4 | Melt flow rate (MFR) (190 ℃, 21.6kg) | GB/T3682 | g/10min | 0.1-0.2 | 0.14 |
5 | Surface resistivity | GB1410 | Ω | ≤50 | 42 |
6 | The flaming combustion time (arithmetical av of every group of 6 battens) | MT181 | s | ≤1s | 0.7 |
7 | The flaming combustion time (every group of 6 battens any one) | MT181 | s | ≤2s | 1.2 |
8 | The flameless combustion time (arithmetical av of every group of 6 battens) | MT181 | s | ≤3s | 2.1 |
9 | The flameless combustion time (every group of 6 battens any one) | MT181 | s | ≤5s | 3.8 |
As can be seen from the above table, every index of the present invention all can be fine, and high request satisfy the industry index, can be competent at the anlistatig requirement of mining pipe fully, have good value for applications.
Embodiment
Embodiments of the invention 1: it carries out surface-active-treatment with 5kg copper particle with the 0.5kg silane coupling agent; then the copper particle after the surface-active-treatment, 90kg polyethylene, 25kg aluminium hydroxide, 2kg antioxidant 1010 and 20kg carbon black are dropped into high-speed mixer; through high-speed mixing, mixed compound is sent into the dual-screw pelletizer granulation just can obtain electrostatic resistant polythene mining tube mother material under 90 ℃ temperature.
Embodiment 2: it carries out surface-active-treatment with 5kg copper particle with the 0.5kg silane coupling agent; then the copper particle after the surface-active-treatment, 90kg polyethylene, 5kg aluminium hydroxide, 1kg antioxidant 1010 and 4kg carbon black are dropped into high-speed mixer; through high-speed mixing, mixed compound is sent into the dual-screw pelletizer granulation just can obtain electrostatic resistant polythene mining tube mother material under 70 ℃ temperature.
Embodiment 3: it carries out surface-active-treatment with 20kg copper particle with the 3kg silane coupling agent; then the copper particle after the surface-active-treatment, 110kg polyethylene, 30kg antimonous oxide, 8kg oxidation inhibitor 168 and 20kg carbon black are dropped into high-speed mixer; through high-speed mixing, mixed compound is sent into the dual-screw pelletizer granulation just can obtain electrostatic resistant polythene mining tube mother material under 100 ℃ temperature.
Embodiment 4: it carries out surface-active-treatment with the 13kg aluminum particulate with the 2kg silane coupling agent; then the aluminum particulate after the surface-active-treatment, 100kg polyethylene, 15kg magnesium hydroxide, 5kg antioxidant 2246 and 12kg carbon black are dropped into high-speed mixer; through high-speed mixing, mixed compound is sent into the dual-screw pelletizer granulation just can obtain electrostatic resistant polythene mining tube mother material under 80 ℃ temperature.
Claims (6)
- [claim 1] a kind of electrostatic resistant polythene mining tube mother material is characterized in that: it is to be made by following quality proportion raw material:90~110 parts of polyethylene, 5~20 parts of metallic particles, 5~30 parts of fire retardants, 1~8 part of stablizer, 0.5~3 part in tensio-active agent, 4~20 parts of carbon blacks.
- [claim 2] electrostatic resistant polythene mining tube mother material according to claim 1 is characterized in that: described metallic particles is shot copper or aluminum shot.
- [claim 3] electrostatic resistant polythene mining tube mother material according to claim 1 is characterized in that: described fire retardant is aluminium hydroxide, antimonous oxide or magnesium hydroxide.
- [claim 4] electrostatic resistant polythene mining tube mother material according to claim 1 is characterized in that: described stablizer is antioxidant 1010, oxidation inhibitor 168 or antioxidant 2246.
- [claim 5] electrostatic resistant polythene mining tube mother material according to claim 1 is characterized in that: described tensio-active agent is a silane coupling agent.
- [claim 6] is as the preparation method of each described electrostatic resistant polythene mining tube mother material of claim 1 to 5; it is characterized in that: it is that metallic particles is carried out surface-active-treatment with tensio-active agent; metallic particles after will handling then and other do not drop into high-speed mixer with raw material by the quality proportioning; under 70~100 ℃ temperature, mix, obtain electrostatic resistant polythene mining tube mother material by the dual-screw pelletizer granulation at last through high-speed mixer.