CN101503605B - SBS universal glue sizing agent and preparation thereof - Google Patents

Abstract

The invention discloses a solid universal glue slurry, which is prepared from: 60 portions of environment-friendly solvent, 17 portions of oxidation modified SBS, 8 portions of terpine resin, 3 portions of petroleum resin, 5 portions of rosin, 1 portion of filling, 2 portions of antifreeze agent, and 3 portions of plasticizer. The solid universal glue slurry prepared by a process has the characteristics of environmental protection, convenient use and good using effect, so the solid universal glue can be widely used for manufacturing solid universal glue.

Description

A kind of SBS universal glue sizing agent and preparation method thereof

Technical field

The present invention relates to a kind of SBS universal glue sizing agent, the invention still further relates to a kind of preparation method of SBS universal glue sizing agent.

Background technology

At present, the tackiness agent of the common use of the industry of decorations both at home and abroad is traditional solvent-borne type and aq. type multi-purpose adhesive, and the solvent-borne type multi-purpose adhesive mainly contains two kinds, a kind of is the SBS multi-purpose adhesive, another kind is a general chloroprene adhesive, though comparing with general chloroprene adhesive, the SBS multi-purpose adhesive has: environmental protection, inexpensive, admittedly contain height, the brushing area is big, development time is long, advantages such as easy construction, there are many deficiencies but it is the same with general chloroprene adhesive, as: 1, the a large amount of solvent of waste during making, generally contain 64%～77% solvent, when construction was dry, these solvents all were not recovered but directly are discharged in the atmosphere, so not only loss the energy but also caused environmental pollution; Need metal bucket to pack when 2, transporting, make transportation and storage very bother; 3, the use of metal bucket has not only increased the cost of product, and the environmental pollution that also brings of discarded metal bucket, so develop the research schedule that SBS universal glue sizing agent a kind of simple in structure, easy to use has been put on people.

Summary of the invention

In order to overcome the deficiencies in the prior art, the invention provides the good SBS universal glue sizing agent of a kind of result of use.

Another object of the present invention is that a kind of method of producing above-mentioned SBS universal glue sizing agent will be provided.

The technical solution adopted for the present invention to solve the technical problems is:

A kind of SBS universal glue sizing agent, become the starting material of umber to make by following quality group: environmentally friendly solvent: 60 parts, oxidation modification SBS:17 part, terpine resin: 8 parts, petroleum resin: 3 parts, rosin: 5 parts, filler: 1 part, frostproofer: 2 parts, softening agent: 3 parts, its preparation method comprises the steps:

1): take by weighing various raw materials in proportion;

2): stir 3～5 hours up to dissolving fully after in environmentally friendly solvent, adding oxidation modification SBS, terpine resin, petroleum resin, rosin, filler, frostproofer, softening agent;

3): adopt environmentally friendly solvent) with step 2 solution that draws under 30 ℃ with viscosity controller between 300～500cps;

4): adopt 80～100 purpose filter screens that the solution that step 3) draws is filtered.

The invention has the beneficial effects as follows:, have environmental protection, easy to use, characteristics that result of use is good, thereby be widely used in the making of SBS universal glue by the SBS universal glue sizing agent that this technology is made.

A kind of SBS universal glue sizing agent, become the starting material of umber to make by following quality group: environmentally friendly solvent: 60 parts, oxidation modification SBS:17 part, terpine resin: 8 parts, petroleum resin: 3 parts, rosin: 5 parts, filler: 1 part, frostproofer: 2 parts, softening agent: 3 parts, its preparation method comprises the steps:

Embodiment

1): take by weighing various raw materials in proportion;

2): stir 3～5 hours up to dissolving fully after in environmentally friendly solvent, adding oxidation modification SBS, terpine resin, petroleum resin, rosin, filler, frostproofer, softening agent;

3): adopt environmentally friendly solvent) with step 2 solution that draws under 30 ℃ with viscosity controller between 300～500cps;

4): adopt 80～100 purpose filter screens that the solution that step 3) draws is filtered.

By the SBS universal glue sizing agent that this technology is made, have environmental protection, easy to use, characteristics that result of use is good, thereby be widely used in the making of SBS universal glue.

Claims (1)

1. SBS universal glue sizing agent becomes the starting material of umber to make by following quality group:

Environmentally friendly solvent: 60 parts, oxidation modification SBS:17 part, terpine resin: 8 parts, petroleum resin: 3 parts, rosin: 5 parts, filler: 1 part, frostproofer: 2 parts, softening agent: 3 parts, its preparation method comprises the steps:

1): take by weighing various raw materials in proportion;

2): stir 3～5 hours up to dissolving fully after in environmentally friendly solvent, adding oxidation modification SBS, terpine resin, petroleum resin, rosin, filler, frostproofer, softening agent;

3): adopt environmentally friendly solvent) with step 2 solution that draws under 30 ℃ with viscosity controller between 300～500cps;

4): adopt 80～100 purpose filter screens that the solution that step 3) draws is filtered.