CN101475705A - Lead chromate yellow intimating pigment special for rubber and plastic industry and preparation thereof - Google Patents
Lead chromate yellow intimating pigment special for rubber and plastic industry and preparation thereof Download PDFInfo
- Publication number
- CN101475705A CN101475705A CNA2008102043449A CN200810204344A CN101475705A CN 101475705 A CN101475705 A CN 101475705A CN A2008102043449 A CNA2008102043449 A CN A2008102043449A CN 200810204344 A CN200810204344 A CN 200810204344A CN 101475705 A CN101475705 A CN 101475705A
- Authority
- CN
- China
- Prior art keywords
- pigment
- lead chromate
- intimating
- yellow
- extender
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention provides a special mimic lead chromate yellow pigment used in rubber and plastic industries and a preparation method thereof. The pigment comprises the following components in percentage by weight: 9 to 35 percent of azo pigment, 0 to 10 percent of white pigment and 60 to 91 percent of inert pigment. The mimic lead chromate yellow pigment is a lead-free chromium-free environment-friendly product, and the light fastness, heat resistance, acid resistance and alkali resistance of the pigment are obviously better than those of lead chromate yellow pigments. Due to adopting lead-free and chromium-free raw materials, the preparation method solves the problem of waste liquid pollution caused by toxic harmful ion during the preparation of the lead chromate yellow pigment.
Description
Technical field
The present invention relates to a kind of pigment and preparation method, be specifically related to a kind of pigment of unleaded, Chrome-free.
Background technology
Plumbous chromium series yellow ultramarine is produced existing more than 80 year history in China, lead-chrome yellow pigment is a kind of Yellow organic dye of bright-coloured color, and strong covering power, anti-solvent, heat-resisting, cheap, advantage such as turnout is big are arranged and is subjected to the welcome of coatings industry, rubber plastic industry deeply.
Plumbous chromium series yellow ultramarine is owing to be to make lead-chrome yellow pigment with water miscible lead salt and water miscible chromic salt, so the liquid waste disposal leaded, that contain chromium ion in the making processes is a serious problem.
Play European Union in July, 2006 and forbid that leaded, chromium, cadmium, the plastics of mercury, electronic product enter Europe.The whole world will enter pigment and some harmful solvent slops that forbidding contains " plumbous chromium " in 2008.Therefore from environmental angle, to the protection HUMAN HEALTH, it is extremely urgent that a kind of yellow ultramarine of cheapness of unleaded Chrome-free replaces plumbous chromium series yellow ultramarine, is the needs in market.
Summary of the invention
The technical issues that need to address of the present invention provide a kind of rubber, the special-purpose lead chromate yellow intimating pigment of plastics and preparation method, to overcome the above-mentioned defective that prior art exists.
The lead chromate yellow intimating pigment of rubber of the present invention, plastic industry special use, its component comprises azophosphine pigment, white pigment and pigment extender, weight percent content is:
Azo pigment 9~35
White pigment 0~10%
Pigment extender 60~91%
The per-cent sum of said components is 100%;
Preferably:
Azo pigment 27%
White pigment 6%
Pigment extender 67%
Preferably:
Azo pigment 9.1%
White pigment 0%
Pigment extender 90.9%
Preferably:
Azo pigment 30.3%
White pigment 9.1%
Pigment extender 60.6%
Described azophosphine pigment is selected from more than one among permanent yellow H10G or the permanent yellow HR;
Described white pigment is selected from rutile titanium dioxide or anatase titanium dioxide;
Described pigment extender is selected from barium sulfate, water-ground limestone or light calcium carbonate;
Preferably, the lead chromate yellow intimating pigment of described rubber, plastic industry special use, its component also comprises wetting agent, its weight consumption is 0.005~25% of azophosphine pigment, white pigment and a pigment extender gross weight, described wetting agent is selected from polyvalent alcohol or polynary fat, the propylene glycol of preferred E.I.Du Pont Company;
Preferably, the lead chromate yellow intimating pigment of described rubber, plastic industry special use, its component also comprises dispersion agent, its weight consumption is 0.005~30% of azophosphine pigment, white pigment and a pigment extender gross weight, and described dispersion agent is selected from sodium butylnaphthalenesulfonate (being commonly called as Nekal BX), carboxylic acid sodium or poly carboxylic acid sodium;
Add wetting agent or/and dispersion agent mainly is in order to change wettability and the dispersiveness of azo pigment in rubber, plastics.
The preparation method of the lead chromate yellow intimating pigment of rubber of the present invention, plastic industry special use comprises the steps:
The water that adds mixture total weight amount 0~40% in the mixture of azophosphine pigment, white pigment and pigment extender mixes, shear-mixed in dispersion machine then, perhaps mix, make dispersible pigment color paste, then successively at 50~100 ℃ of dryings, the acquisition finished product of pulverizing, sieve at ball mill grinding.
As required, can add wetting agent and/or dispersion agent, shear-mixed in dispersion machine is made dispersible pigment color paste then;
The present invention is the pigment of the lead chromate yellow intimating of a kind of rubber, plastic industry special use, is a kind of environmentfriendly products of unleaded Chrome-free, and the photostabilization of pigment, thermotolerance, acid resistance, alkali resistance are also obviously strong than plumbous chromium series yellow ultramarine.Preparation method of the present invention owing to adopted the raw material of unleaded chromium, has solved the poisonous and harmful ionic waste water pollution problem that lead-chrome yellow pigment causes in preparation.
Embodiment
Embodiment 1
4 kilograms of permanent yellow H10G, 1 kilogram of rutile titanium dioxide, 4 kilograms are drawn back powder and 10 kilograms of lime carbonate, add 6 kg of water in dispersion machine, shear-mixed 2 hours is made dispersible pigment color paste, 90 ℃ of dryings, pulverizes, sieves, and obtains finished product.
Adopt imitative lead-chrome yellow standard to detect, the result is as follows:
Sequence number | Project | Index | Measured value |
1 | Relative color strength (with the standard model ratio) ),% | 95—105 | 103 |
2 | Total color difference ,≤ | 1.0 | 0.4 |
3 | ΔL | -0.7~0.7 | -0.35 |
4 | Δa | -0.7~0.7 | -0.22 |
5 | Δb | -0.7~0.7 | -0.14 |
6 | 105 ℃ of volatile matters, % ,≤ | 1.0 | 0.3 |
7 | Screenings (45 μ m screen cloth), % ,≤ | 0.5 | 0.1 |
In the last table: the brightness of Δ L representative color, wherein: on the occasion of representing the brightness height, negative value is represented low lightness; Δ a represents form and aspect, and wherein: on the occasion of the red phase of representative, negative value is represented blue phase; Δ b represents form and aspect, and wherein: on the occasion of the yellow phase of representative, negative value is represented green phase.
Embodiment 2
1 kilogram of permanent yellow HR, 0.3 kilogram of wetting agent and 10 kilograms of barium sulfate are dropped into ball mill grinding after 5 hours, be packaged as finished product through sieving.
The chemical name of wetting agent is a propylene glycol, adopts the product of E.I.Du Pont Company;
Adopt imitative lead-chrome yellow standard to detect, the result is as follows:
Sequence number | Project | Index | Measured value |
1 | Relative color strength (with the standard model ratio) ),% | 95—105 | 100 |
2 | Total color difference ,≤ | 1.0 | 0.4 |
3 | ΔL | -0.7~0.7 | -0.25 |
4 | Δa | -0.7~0.7 | -0.32 |
5 | Δb | -0.7~0.7 | -0.04 |
6 | 105 ℃ of volatile matters, % ,≤ | 1.0 | 0.3 |
7 | Screenings (45 μ m screen cloth), % ,≤ | 0.5 | 0.25 |
In the last table: the brightness of Δ L representative color, wherein: on the occasion of representing the brightness height, negative value is represented low lightness; Δ a represents form and aspect, and wherein: on the occasion of the red phase of representative, negative value is represented blue phase; Δ b represents form and aspect, and wherein: on the occasion of the yellow phase of representative, negative value is represented green phase.
Embodiment 3
3 kilograms of permanent yellow H10G, 2 kilograms of permanent yellow HR, 1.5 kilograms of rutile titanium dioxides, 4.5 kilograms of Nekal BXs and 10 kilograms of barium sulfate are added 6 kg of water in dispersion machine, shear-mixed, make dispersible pigment color paste, through 100 ℃ of dryings, pulverize, sieving is packaged as finished product.
Adopt imitative lead-chrome yellow product standard to detect, the result is as follows:
Sequence number | Project | Index | Measured value |
1 | Relative color strength (with the standard model ratio) ),% | 95—105 | 102 |
2 | Total color difference ,≤ | 1.0 | 0.5 |
3 | ΔL | -0.7~0.7 | -0.3 |
4 | Δa | -0.7~0.7 | -0.4 |
5 | Δb | -0.7~0.7 | -0.2 |
6 | 105 ℃ of volatile matters, % ,≤ | 1.0 | 0.3 |
7 | Screenings (45 μ m screen cloth), % ,≤ | 0.5 | 0.22 |
In the last table: the brightness of Δ L representative color, wherein: on the occasion of representing the brightness height, negative value is represented low lightness; Δ a represents form and aspect, and wherein: on the occasion of the red phase of representative, negative value is represented blue phase; Δ b represents form and aspect, and wherein: on the occasion of the yellow phase of representative, negative value is represented green phase.
Claims (8)
1. the lead chromate yellow intimating pigment of rubber, plastic industry special use is characterized in that, its component comprises azophosphine pigment, white pigment and pigment extender, and weight percent content is:
Azo pigment 9~35%
White pigment 0~10%
Pigment extender 60~91%
The per-cent sum of said components is 100%.
2. the lead chromate yellow intimating pigment of rubber according to claim 1, plastic industry special use is characterized in that, weight percent content is:
Azo pigment 27%
White pigment 6%
Pigment extender 67%
Preferably:
Azo pigment 9.1%
White pigment 0%
Pigment extender 90.9%.
3. the lead chromate yellow intimating pigment of rubber according to claim 1, plastic industry special use is characterized in that, weight percent content is:
Azo pigment 30.3%
White pigment 9.1%
Pigment extender 60.6%.
4. the lead chromate yellow intimating pigment of rubber according to claim 1, plastic industry special use is characterized in that, described azophosphine pigment is selected from more than one among permanent yellow H10G or the permanent yellow HR;
Described white pigment is selected from rutile titanium dioxide or anatase titanium dioxide;
Described pigment extender is selected from barium sulfate, water-ground limestone or light calcium carbonate.
5. the lead chromate yellow intimating pigment of rubber according to claim 1, plastic industry special use, it is characterized in that, its component also comprises wetting agent, its weight consumption is 0.005~25% of azophosphine pigment, white pigment and a pigment extender gross weight, and described wetting agent is selected from polyvalent alcohol or polynary fat.
6. the lead chromate yellow intimating pigment of rubber according to claim 1, plastic industry special use, it is characterized in that, its component also comprises dispersion agent, its weight consumption is 0.005~30% of azophosphine pigment, white pigment and a pigment extender gross weight, and described dispersion agent is selected from sodium butylnaphthalenesulfonate, carboxylic acid sodium or poly carboxylic acid sodium.
7. the method for the lead chromate yellow intimating pigment of each described rubber of preparation claim 1~6, plastic industry special use is characterized in that, comprises the steps:
The water that adds mixture total weight amount 0~40% in the mixture of azophosphine pigment, white pigment and pigment extender mixes, shear-mixed in dispersion machine then, perhaps mix, make dispersible pigment color paste, then successively at 50~100 ℃ of dryings, the acquisition finished product of pulverizing, sieve at ball mill grinding.
8. method according to claim 7 is characterized in that, adds wetting agent and/or dispersion agent, and shear-mixed in dispersion machine is made dispersible pigment color paste then.